CN104402413B - 一种高韧性陶瓷喷嘴及其制作方法 - Google Patents

一种高韧性陶瓷喷嘴及其制作方法 Download PDF

Info

Publication number
CN104402413B
CN104402413B CN201410590664.8A CN201410590664A CN104402413B CN 104402413 B CN104402413 B CN 104402413B CN 201410590664 A CN201410590664 A CN 201410590664A CN 104402413 B CN104402413 B CN 104402413B
Authority
CN
China
Prior art keywords
powder
ceramic nozzle
high tenacity
hour
auxiliary agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410590664.8A
Other languages
English (en)
Other versions
CN104402413A (zh
Inventor
夏建国
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Haimen Huaxia Li Li Network Technology Service Co., Ltd.
Original Assignee
ANHUI WANJIE HYDRAULIC TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI WANJIE HYDRAULIC TECHNOLOGY Co Ltd filed Critical ANHUI WANJIE HYDRAULIC TECHNOLOGY Co Ltd
Priority to CN201410590664.8A priority Critical patent/CN104402413B/zh
Publication of CN104402413A publication Critical patent/CN104402413A/zh
Application granted granted Critical
Publication of CN104402413B publication Critical patent/CN104402413B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高韧性陶瓷喷嘴，其特征在于，由下列重量份的原料制成：氧化铝65-75、硅线石2.3-3.7、白云石1-3、蓝晶石5-8、珍珠粉3-6、电石泥3-5、预糊化淀粉1-2、PVC粉2-3、二氧化硅18-30、生石灰1.1-1.5、顺丁烯二酸酐3-4、三乙醇胺2-3、脂肪醇聚氧乙烯醚4-6、氧化石蜡皂0.4-0.8、助剂3-4、适量水；本发明工艺简便设计合理，添加多种有机和无机添加剂有效提高了产品的技术指标，制得的陶瓷喷嘴具有韧性高、抗震性能优、耐疲劳性能好、耐磨等优点。

Description

一种高韧性陶瓷喷嘴及其制作方法
技术领域
本发明涉及一种陶瓷喷嘴制备工艺，属于喷嘴成型技术领域，具体涉及一种高韧性陶瓷喷嘴及其制作方法。
背景技术
陶瓷喷嘴自上个世纪九时年代引入中国以来，材料不断的改进更新，从氧化物陶瓷逐渐发展到氮化物陶瓷和碳化物陶瓷，而生产工艺及制备方法落后，致使现有技术中陶瓷喷嘴存在诸多缺陷，比如硬度不高、耐磨性差、防腐蚀防冲蚀能力弱、延展性不大等。为克服现有技术的不足，有必要对现有陶瓷喷嘴生产技术加以改进，从而制得适合不同需求的具有成本低、功能多元化、阻燃、硬度高、耐磨、防辐射等功能的陶瓷喷嘴。
发明内容
本发明的目的就是提供一种高韧性陶瓷喷嘴及其制作方法，以克服现有技术的不足。
本发明的目的是这样实现的：
一种高韧性陶瓷喷嘴，其特征在于，由下列重量份的原料制成：氧化铝65-75、硅线石2.3-3.7、白云石1-3、蓝晶石5-8、珍珠粉3-6、电石泥3-5、预糊化淀粉1-2、PVC粉2-3、二氧化硅18-30、生石灰1.1-1.5、顺丁烯二酸酐3-4、三乙醇胺2-3、脂肪醇聚氧乙烯醚4-6、氧化石蜡皂0.4-0.8、助剂3-4、适量水。
所述的助剂由下列重量份原料制成：聚乙烯醇17-21、石墨粉3-5、长石2-4、煤矸石4-6、丙烯酸2.1-4.1、烯丙基聚乙二醇3.2-4.5、过氧化苯甲酰1.2-3.3、二月桂酸二丁基锡0.2-0.4、六偏磷酸钠1-2、硫酸锌2-3、亚硒酸钠0.4-0.8、纳米级硅酸镁2-4，其制备方法是将长石、煤矸石粉碎至120-150目，加入石墨粉、硫酸锌搅拌混匀于710-820℃下煅烧2-3小时，水淬，然后再加入丙烯酸、烯丙基聚乙二醇、过氧化苯甲酰搅拌混匀，在70-90℃水浴温度下高速研磨浆料粒径至15μm以下，喷雾干燥成粉末，将制得的粉末与聚乙烯醇、六偏磷酸钠、纳米级硅酸镁及其他剩余成分混合，研磨1-2小时即得。
所述的一种高韧性陶瓷喷嘴的制备方法，其特征在于包括以下步骤：
（1）将硅线石、白云石、蓝晶石放入煅烧炉中于750-880℃下煅烧2-3小时，用1-3‰的氯化钙溶液淬火，待温度降至40-60℃时加入氧化铝粉碎至120-180目；
（2）取珍珠粉、电石泥、预糊化淀粉搅拌混匀，加入PVC粉、二氧化硅混匀于570-660℃下煅烧1-2小时，冷却至室温研磨30-40分钟，加入顺丁烯二酸酐、三乙醇胺、脂肪醇聚氧乙烯醚高速研磨至浆料粒径20-30μm，喷雾干燥；
（3）将步骤（1）、（2）反应物料混匀，加水打浆制成固含量为50-60%的浆料，再加入其他剩余成分依此循环搅拌研磨8-10次，每次研磨2小时以上；
（4）将上述浆料注入模具中成型，经修坯、干燥、装炉于1550℃～1870℃烧结5-10小时，冷却出料。
本发明有以下有益效果：本发明工艺简便设计合理，添加多种有机和无机添加剂有效提高了产品的技术指标，制得的陶瓷喷嘴具有韧性高、抗震性能优、耐疲劳性能好、耐磨等优点。
具体实施方式
所述的一种高韧性陶瓷喷嘴，其特征在于，由下列重量份的原料制成：氧化铝67、硅线石2.7、白云石3、蓝晶石5、珍珠粉6、电石泥5、预糊化淀粉1、PVC粉3、二氧化硅30、生石灰1.4、顺丁烯二酸酐4、三乙醇胺3、脂肪醇聚氧乙烯醚6、氧化石蜡皂0.7、助剂3、适量水。
所述的助剂由下列重量份原料制成：聚乙烯醇18、石墨粉4、长石2、煤矸石6、丙烯酸2.8、烯丙基聚乙二醇3.8、过氧化苯甲酰1.9、二月桂酸二丁基锡0.3、六偏磷酸钠1、硫酸锌2、亚硒酸钠0.4、纳米级硅酸镁2，其制备方法是将长石、煤矸石粉碎至120-150目，加入石墨粉、硫酸锌搅拌混匀于710-820℃下煅烧2-3小时，水淬，然后再加入丙烯酸、烯丙基聚乙二醇、过氧化苯甲酰搅拌混匀，在70-90℃水浴温度下高速研磨浆料粒径至15μm以下，喷雾干燥成粉末，将制得的粉末与聚乙烯醇、六偏磷酸钠、纳米级硅酸镁及其他剩余成分混合，研磨1-2小时即得。
制作方法包括以下步骤：
（1）将硅线石、白云石、蓝晶石放入煅烧炉中于750-880℃下煅烧2-3小时，用1-3‰的氯化钙溶液淬火，待温度降至40-60℃时加入氧化铝粉碎至120-180目；
（2）取珍珠粉、电石泥、预糊化淀粉搅拌混匀，加入PVC粉、二氧化硅混匀于570-660℃下煅烧1-2小时，冷却至室温研磨30-40分钟，加入顺丁烯二酸酐、三乙醇胺、脂肪醇聚氧乙烯醚高速研磨至浆料粒径20-30μm，喷雾干燥；
（3）将步骤（1）、（2）反应物料混匀，加水打浆制成固含量为50-60%的浆料，再加入其他剩余成分依此循环搅拌研磨8-10次，每次研磨2小时以上；
（4）将上述浆料注入模具中成型，经修坯、干燥、装炉于1550℃～1870℃烧结5-10小时，冷却出料。
使用本实施例生产的陶瓷喷嘴具有良好的耐腐蚀性和耐磨性，经测试其致密度达97.49％以上，体积密度为3.19g/cm3，收缩率为22.46％；喷嘴的孔道内部光洁度好，喷射效果理想。

Claims (1)

1.一种高韧性陶瓷喷嘴，其特征在于，由下列重量份的原料制成：氧化铝65-75、硅线石2.3-3.7、白云石1-3、蓝晶石5-8、珍珠粉3-6、电石泥3-5、预糊化淀粉1-2、PVC粉2-3、二氧化硅18-30、生石灰1.1-1.5、顺丁烯二酸酐3-4、三乙醇胺2-3、脂肪醇聚氧乙烯醚4-6、氧化石蜡皂0.4-0.8、助剂3-4、适量水；所述的助剂由下列重量份原料制成：聚乙烯醇17-21、石墨粉3-5、长石2-4、煤矸石4-6、丙烯酸2.1-4.1、烯丙基聚乙二醇3.2-4.5、过氧化苯甲酰1.2-3.3、二月桂酸二丁基锡0.2-0.4、六偏磷酸钠1-2、硫酸锌2-3、亚硒酸钠0.4-0.8、纳米级硅酸镁2-4，其制备方法是将长石、煤矸石粉碎至120-150目，加入石墨粉、硫酸锌搅拌混匀于710-820℃下煅烧2-3小时，水淬，然后再加入丙烯酸、烯丙基聚乙二醇、过氧化苯甲酰搅拌混匀，在70-90℃水浴温度下高速研磨浆料粒径至15μm以下，喷雾干燥成粉末，将制得的粉末与聚乙烯醇、六偏磷酸钠、纳米级硅酸镁及其他剩余成分混合，研磨1-2小时即得。
CN201410590664.8A 2014-10-29 2014-10-29 一种高韧性陶瓷喷嘴及其制作方法 Active CN104402413B (zh)