CN104387077B - 一种高耐磨性陶瓷及其制备方法 - Google Patents

一种高耐磨性陶瓷及其制备方法 Download PDF

Info

Publication number
CN104387077B
CN104387077B CN201410590784.8A CN201410590784A CN104387077B CN 104387077 B CN104387077 B CN 104387077B CN 201410590784 A CN201410590784 A CN 201410590784A CN 104387077 B CN104387077 B CN 104387077B
Authority
CN
China
Prior art keywords
weight part
add
minute
hour
stir
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410590784.8A
Other languages
English (en)
Other versions
CN104387077A (zh
Inventor
夏建国
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing Gao Hang United Technology Co ltd
Zhaoqing City Enterprise From Ceramics Co ltd
Original Assignee
ANHUI WANJIE HYDRAULIC TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI WANJIE HYDRAULIC TECHNOLOGY Co Ltd filed Critical ANHUI WANJIE HYDRAULIC TECHNOLOGY Co Ltd
Priority to CN201410590784.8A priority Critical patent/CN104387077B/zh
Publication of CN104387077A publication Critical patent/CN104387077A/zh
Application granted granted Critical
Publication of CN104387077B publication Critical patent/CN104387077B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种高耐磨性陶瓷，由下列重量份的原料制成：透锂长石12-15、正硅酸乙酯3-4、SiC微粉78-82、碳纤维4-5、煤矸石5-7、磷酸钙3-4、磷酸镁2-3、去离子水适量、乙醇适量、助剂4-6；本发明的陶瓷使用了SiC、磷酸钙、磷酸镁、碳纤维，使得陶瓷耐磨性极高，而且韧性好，不易破碎，耐振动，耐热性好，使用寿命长；通过使用本发明的助剂，能够增加陶瓷的表面光滑性、耐磨性和耐热性。

Description

一种高耐磨性陶瓷及其制备方法
技术领域
本发明涉及陶瓷材料领域，尤其涉及一种高耐磨性陶瓷及其制备方法。
背景技术
目前通道、管道用的材料有铝合金材料、陶瓷等，铝合金材料耐磨性差，槽道容易消失，要经常更换，成本高；目前所用的陶瓷材料脆性大，耐磨性不太高，不耐冷热刺激，耐酸碱性差，因此需要研究耐磨性好，硬度高，韧性好，耐震动，耐热，耐腐蚀等性能优异的陶瓷材料，以降低成本。
发明内容
本发明的目的在于提供一种高耐磨性陶瓷及其制备方法，该陶瓷耐磨性极高，而且韧性好，不易破碎，耐振动，耐热性好，使用寿命长。
本发明的技术方案如下：
一种高耐磨性陶瓷，其特征在于由下列重量份的原料制成：透锂长石12-15、正硅酸乙酯3-4、SiC微粉78-82、碳纤维4-5、煤矸石5-7、磷酸钙3-4、磷酸镁2-3、去离子水适量、乙醇适量、助剂4-6；
所述助剂由下列重量份的原料制成：高岭土3-4、稀土1-2、四盐基铬酸锌0.3-0.4、纳米氮化硅0.8-1.2、纳米硼纤维0.6-0.9、纳米碳0.3-0.4、硅烷偶联剂kh-5500.6-0.8、聚乙二醇0.3-0.4、水7-11；制备方法为：将聚乙二醇加入水中，搅拌均匀，加入高岭土，搅拌20-30分钟，再加入一半重量份的硅烷偶联剂kh-550，搅拌10-15分钟，再加入稀土，搅拌反应20-30分钟，再加入剩余重量份的硅烷偶联剂kh-550，搅拌10-15分钟，再加入其他剩余成分，搅拌反应20-30分钟，超声分散6-8分钟，过滤，烘干，粉碎，过40目筛，在氮气氛围下，1380-1440℃下煅烧2-3个小时，粉碎，过40目筛，即得。
所述高耐磨性陶瓷的制备方法，其特征在于包括以下步骤：
（1）将透锂长石、煤矸石混合，球磨，过200目筛，加入0.6-0.8倍重量份的乙醇，送入球磨机中球磨24-27个小时，得到球磨料；
（2）将第（1）步得到的球磨料粉碎，在氮气氛围下，850-900℃下煅烧2-3个小时，取出粉碎，过50目筛，得到颗粒；
（3）取30-40重量份的乙醇，加入正硅酸乙酯，搅拌至溶解，加入磷酸钙、磷酸镁，搅拌得到混合物料，将SiC微粉边翻腾搅拌边喷入混合物料，加热至70-80℃，持续翻腾搅拌至乙醇完全蒸发，粉碎，过50目筛，得到颗粒；
（4）将第（2）步和第（3）步得到的颗粒与其他剩余成分混合，按料：球：水=1:1.4:0.7，球磨24-30个小时，造型，在氮气氛围中，700-800℃下预烧1.5-2个小时，再在1680-1720℃下煅烧4-5个小时，即得。
本发明的有益效果
本发明的陶瓷使用了SiC、磷酸钙、磷酸镁、碳纤维，使得陶瓷耐磨性极高，而且韧性好，不易破碎，耐振动，耐热性好，使用寿命长；通过使用本发明的助剂，能够增加陶瓷的表面光滑性、耐磨性和耐热性。
具体实施方式
一种高耐磨性陶瓷，由下列重量份（公斤）的原料制成：透锂长石14、正硅酸乙酯3.5、SiC微粉79、碳纤维4.5、煤矸石6、磷酸钙3.6、磷酸镁2.5、去离子水适量、乙醇适量、助剂5；
所述助剂由下列重量份（公斤）的原料制成：高岭土3.5、稀土1.5、四盐基铬酸锌0.3、纳米氮化硅1、纳米硼纤维0.7、纳米碳0.3、硅烷偶联剂kh-5500.7、聚乙二醇0.3、水8；制备方法为：将聚乙二醇加入水中，搅拌均匀，加入高岭土，搅拌25分钟，再加入一半重量份的硅烷偶联剂kh-550，搅拌13分钟，再加入稀土，搅拌反应25分钟，再加入剩余重量份的硅烷偶联剂kh-550，搅拌13分钟，再加入其他剩余成分，搅拌反应25分钟，超声分散7分钟，过滤，烘干，粉碎，过40目筛，在氮气氛围下，1400℃下煅烧2.5个小时，粉碎，过40目筛，即得。
所述高耐磨性陶瓷的制备方法，包括以下步骤：
（1）将透锂长石、煤矸石混合，球磨，过200目筛，加入0.7倍重量份的乙醇，送入球磨机中球磨26个小时，得到球磨料；
（2）将第（1）步得到的球磨料粉碎，在氮气氛围下，880℃下煅烧2.5个小时，取出粉碎，过50目筛，得到颗粒；
（3）取35重量份的乙醇，加入正硅酸乙酯，搅拌至溶解，加入磷酸钙、磷酸镁，搅拌得到混合物料，将SiC微粉边翻腾搅拌边喷入混合物料，加热至75℃，持续翻腾搅拌至乙醇完全蒸发，粉碎，过50目筛，得到颗粒；
（4）将第（2）步和第（3）步得到的颗粒与其他剩余成分混合，按料：球：水=1:1.4:0.7，球磨27个小时，造型，在氮气氛围中，750℃下预烧1.8个小时，再在1700℃下煅烧4.5个小时，即得。
实验数据：
该实施例陶瓷的维氏硬度为89GPa，抗弯强度为1100MPa，断裂韧性为12MPa·m1/2。

Claims (2)

1.一种耐磨性陶瓷，其特征在于由下列重量份的原料制成：透锂长石12-15、正硅酸乙酯3-4、SiC微粉78-82、碳纤维4-5、煤矸石5-7、磷酸钙3-4、磷酸镁2-3、去离子水适量、乙醇适量、助剂4-6；
所述助剂由下列重量份的原料制成：高岭土3-4、稀土氧化物1-2、四盐基铬酸锌0.3-0.4、纳米氮化硅0.8-1.2、纳米硼纤维0.6-0.9、纳米碳0.3-0.4、硅烷偶联剂kh-5500.6-0.8、聚乙二醇0.3-0.4、水7-11；助剂的制备方法为：将聚乙二醇加入水中，搅拌均匀，加入高岭土，搅拌20-30分钟，再加入一半重量份的硅烷偶联剂kh-550，搅拌10-15分钟，再加入稀土，搅拌反应20-30分钟，再加入剩余重量份的硅烷偶联剂kh-550，搅拌10-15分钟，再加入其他剩余成分，搅拌反应20-30分钟，超声分散6-8分钟，过滤，烘干，粉碎，过40目筛，在氮气氛围下，1380-1440℃下煅烧2-3个小时，粉碎，过40目筛，即得。
2.根据权利要求1所述耐磨性陶瓷的制备方法，其特征在于包括以下步骤：
（1）将透锂长石、煤矸石混合，球磨，过200目筛，加入0.6-0.8倍重量份的乙醇，送入球磨机中球磨24-27个小时，得到球磨料；
（2）将第（1）步得到的球磨料粉碎，在氮气氛围下，850-900℃下煅烧2-3个小时，取出粉碎，过50目筛，得到颗粒；
（3）取30-40重量份的乙醇，加入正硅酸乙酯，搅拌至溶解，加入磷酸钙、磷酸镁，搅拌得到混合物料，将SiC微粉边翻腾搅拌边喷入混合物料，加热至70-80℃，持续翻腾搅拌至乙醇完全蒸发，粉碎，过50目筛，得到颗粒；
（4）将第（2）步和第（3）步得到的颗粒与其他剩余成分混合，按料：球：水=1:1.4:0.7，球磨24-30个小时，造型，在氮气氛围中，700-800℃下预烧1.5-2个小时，再在1680-1720℃下煅烧4-5个小时，即得。
CN201410590784.8A 2014-10-29 2014-10-29 一种高耐磨性陶瓷及其制备方法 Expired - Fee Related CN104387077B (zh)