CN104371389A - 一种含有新型光引发剂的涂料 - Google Patents
一种含有新型光引发剂的涂料 Download PDFInfo
- Publication number
- CN104371389A CN104371389A CN201410654776.5A CN201410654776A CN104371389A CN 104371389 A CN104371389 A CN 104371389A CN 201410654776 A CN201410654776 A CN 201410654776A CN 104371389 A CN104371389 A CN 104371389A
- Authority
- CN
- China
- Prior art keywords
- degree
- novel photoinitiator
- amount
- warming
- hydroxylated material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种化学工业产品,尤其是一种含有新型光引发剂的涂料。其组分重量配比为:蜡酯12~17%;桐油20~30%;环氧树脂10~16%;改性醇酸树脂3~6%;棕榈油精酯12~16%;甲基丙烯酸树脂5~8%;半亚光丙烯颜料1~3%;新型光引发剂3~6%;聚乙烯醇缩丁醛5~10%;其余为稀料。它耐光性、耐候性好,着色力、遮盖力强,附着力强使用后不易开裂。
Description
技术领域
本发明涉及一种化学工业产品,尤其是一种含有新型光引发剂的涂料。
背景技术
漆膜表面出现深浅大小各不相同的裂纹,如从裂纹处能见到下层表面,则称为"开裂";如漆膜呈现龟背花纹样的细小裂纹,则称为"龟裂"。
问题原因:一、底漆与面漆不配套,涂膜受外界影响(机械作用,温度变化等)而产生收缩应力,引起漆膜龟裂或开裂。二、底漆未干透即涂覆(喷、刷、辊涂)面漆,或第一层面漆过厚,未经干透又涂第二层面漆,使两层漆内外伸缩不一致。三、室内用漆用于室外或金属表面底漆用于木材。四、木质底材含有松脂未经清除和处理,日久会渗出漆膜,造成局部龟裂。五、木材含水率太高,日久发生变形引起开裂;六、固化剂加入过多,或者使用错误的固化剂;七、施工过厚;八、施工环境恶劣,温差大、湿度大,漆膜受冷热而伸缩,引起龟裂。
发明内容
本发明旨在解决上述技术问题,提供了一种含有新型光引发剂的涂料,它耐光性、耐候性好,着色力、遮盖力强,附着力强使用后不易开裂,其采用的技术方案如下:
一种含有新型光引发剂的涂料,其特征在于:其组分重量配比为:
蜡酯 12~17%;
桐油 20~30%;
环氧树脂 10~16%;
改性醇酸树脂 3~6%;
棕榈油精酯 12~16%;
甲基丙烯酸树脂 5~8%;
半亚光丙烯颜料 1~3%;
新型光引发剂 3~6%;
聚乙烯醇缩丁醛 5~10%;
其余为稀料;
所述新型光引发剂由以下方法制备:以下均以摩尔分数表示,将1份4-轻基二苯甲酮,1~3份甲醛加入到反应容器中,混合均匀后,加入0.0102~0.012份碱做催化剂,在搅拌条件下,加热保持微沸腾(90~99℃)1h~3h;然后升高温度到140~160℃,进行减压反应10~15分钟,反应结束后冷却到90℃~110℃收集产物,将产物加入到10~20份的去离子水中沉淀,经抽滤后得到新型光引发剂。
在上述技术方案基础上,所述碱为氢氧化钠、氢氧化钡、氨水或氧化锌。
在上述技术方案基础上,所述改性醇酸树脂通过以下步骤制成:
a)称取羟基物质的量为5~5.3摩尔的三羟甲基丙烷、羟基物质的量为1.5~1.7摩尔的邻苯二甲酸酐、羟基物质的量为0.7~0.92摩尔的己二酸酐和羟基物质的量为0.7~0.92的异壬酸;
b)将异壬酸、三羟甲基丙烷、邻苯二甲酸酐和己二酸酐放入反应釜中,升温至85~100度,开始搅拌,再以70~85度/h的升温速度升温至160士5度,放出反应所产生的水,升温至210士5度,反应至酸值为18~20KOH mg/g,停止反应,降温至140度,然后加入溶剂稀释至质量浓度为42%,即得醇酸树脂,其中所述的溶剂由200#汽油、三甲苯和醋酸乙酯按质量比为70:36:3配成。
本发明具有如下优点:耐光性、耐候性好,着色力、遮盖力强,附着力强使用后不易开裂。
具体实施方式
实施例1
一种含有新型光引发剂的涂料,其特征在于:其组分重量配比为:蜡酯12%、桐油20%、环氧树脂10%、改性醇酸树脂3%、棕榈油精酯12%、甲基丙烯酸树脂5%、半亚光丙烯颜料1%、新型光引发剂3%、聚乙烯醇缩丁醛5%,其余为稀料;所述新型光引发剂由以下方法制备:以下均以摩尔分数表示,将1份4-轻基二苯甲酮,1~3份甲醛加入到反应容器中,混合均匀后,加入0.0102份碱做催化剂,在搅拌条件下,加热保持微沸腾90℃1h;然后升高温度到140℃,进行减压反应10分钟,反应结束后冷却到90℃收集产物,将产物加入到10份的去离子水中沉淀,经抽滤后得到新型光引发剂。
优选的,所述碱为氢氧化钠。所述改性醇酸树脂通过以下步骤制成:
a)称取羟基物质的量为5摩尔的三羟甲基丙烷、羟基物质的量为1.5摩尔的邻苯二甲酸酐、羟基物质的量为0.7摩尔的己二酸酐和羟基物质的量为0.7的异壬酸;
b)将异壬酸、三羟甲基丙烷、邻苯二甲酸酐和己二酸酐放入反应釜中,升温至85度,开始搅拌,再以70度/h的升温速度升温至160度,放出反应所产生的水,升温至210度,反应至酸值为18KOH mg/g,停止反应,降温至140度,然后加入溶剂稀释至质量浓度为42%,即得醇酸树脂,其中所述的溶剂由200#汽油、三甲苯和醋酸乙酯按质量比为70:36:3配成。
耐光性:颜料在一定光照下保持其原有颜色的性能。一般采用八级制表示,八级最好。
耐候性:颜料在一定的天然或人工气候条件下,保持其原有性能的能力。一般采用五级制表示,五级最好。
着色力:着色颜料吸收入射光的能力。可用相当于标准颜料样品着色力的相对百分率表示。
遮盖力:在成膜物质中覆盖底材表面颜色的能力。常用遮盖1平方米面积的色漆中所含颜料的克数表示。
通过实验其耐光性为六级,耐候性为四级,着色力为40%,遮盖力为4克/平方米。
实施例2
一种含有新型光引发剂的涂料,其特征在于:其组分重量配比为:蜡酯17%、桐油30%、环氧树脂16%、改性醇酸树脂6%、棕榈油精酯16%、甲基丙烯酸树脂5~8%、半亚光丙烯颜料3%、新型光引发剂6%、聚乙烯醇缩丁醛10%,其余为稀料;所述新型光引发剂由以下方法制备:以下均以摩尔分数表示,将1份4-轻基二苯甲酮,3份甲醛加入到反应容器中,混合均匀后,加入0.012份碱做催化剂,在搅拌条件下,加热保持微沸腾(99℃)3h;然后升高温度到160℃,进行减压反应15分钟,反应结束后冷却到110℃收集产物,将产物加入到20份的去离子水中沉淀,经抽滤后得到新型光引发剂。
优选的,所述碱为氨水。所述改性醇酸树脂通过以下步骤制成:
a)称取羟基物质的量为5.3摩尔的三羟甲基丙烷、羟基物质的量为1.7摩尔的邻苯二甲酸酐、羟基物质的量为0.92摩尔的己二酸酐和羟基物质的量为0.92的异壬酸;
b)将异壬酸、三羟甲基丙烷、邻苯二甲酸酐和己二酸酐放入反应釜中,升温至100度,开始搅拌,再以85度/h的升温速度升温至165度,放出反应所产生的水,升温至215度,反应至酸值为20KOH mg/g,停止反应,降温至140度,然后加入溶剂稀释至质量浓度为42%,即得醇酸树脂,其中所述的溶剂由200#汽油、三甲苯和醋酸乙酯按质量比为70:36:3配成。
通过实验其耐光性为七级,耐候性为五级,着色力为42%,遮盖力为5克/平方米。
上面以举例方式对本发明进行了说明,但本发明不限于上述具体实施例,凡基于本发明所做的任何改动或变型均属于本发明要求保护的范围。
Claims (3)
1.一种含有新型光引发剂的涂料,其特征在于:其组分重量配比为:
蜡酯12~17%;
桐油20~30%;
环氧树脂10~16%;
改性醇酸树脂3~6%;
棕榈油精酯12~16%;
甲基丙烯酸树脂5~8%;
半亚光丙烯颜料1~3%;
新型光引发剂3~6%;
聚乙烯醇缩丁醛5~10%;
其余为稀料;
所述新型光引发剂由以下方法制备:以下均以摩尔分数表示,将1份4-轻基二苯甲酮,1~3份甲醛加入到反应容器中,混合均匀后,加入0.0102~0.012份碱做催化剂,在搅拌条件下,加热保持微沸腾(90~99℃)1h~3h;然后升高温度到140~160℃,进行减压反应10~15分钟,反应结束后冷却到90℃~110℃收集产物,将产物加入到10~20份的去离子水中沉淀,经抽滤后得到新型光引发剂。
2.根据权利要求1所述的一种含有新型光引发剂的涂料,其特征在于:所述碱为氢氧化钠、氢氧化钡、氨水或氧化锌。
3.根据权利要求1所述的一种含有新型光引发剂的涂料,其特征在于:所述改性醇酸树脂通过以下步骤制成:
a)称取羟基物质的量为5~5.3摩尔的三羟甲基丙烷、羟基物质的量为1.5~1.7摩尔的邻苯二甲酸酐、羟基物质的量为0.7~0.92摩尔的己二酸酐和羟基物质的量为0.7~0.92的异壬酸;
b)将异壬酸、三羟甲基丙烷、邻苯二甲酸酐和己二酸酐放入反应釜中,升温至85~100度,开始搅拌,再以70~85度/h的升温速度升温至160士5度,放出反应所产生的水,升温至210士5度,反应至酸值为18~20KOH mg/g,停止反应,降温至140度,然后加入溶剂稀释至质量浓度为42%,即得醇酸树脂,其中所述的溶剂由200#汽油、三甲苯和醋酸乙酯按质量比为70:36:3配成。