CN104356714A - Primer-free UV (ultraviolet) paint for melamine veneers - Google Patents
Primer-free UV (ultraviolet) paint for melamine veneers Download PDFInfo
- Publication number
- CN104356714A CN104356714A CN201410697954.2A CN201410697954A CN104356714A CN 104356714 A CN104356714 A CN 104356714A CN 201410697954 A CN201410697954 A CN 201410697954A CN 104356714 A CN104356714 A CN 104356714A
- Authority
- CN
- China
- Prior art keywords
- parts
- propylene glycol
- diacrylates
- ethoxy
- acrylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a primer-free UV (ultraviolet) paint for melamine veneers, which is composed of the following components in parts by weight: 8-9 parts of epoxy acrylate, 1-2 parts of ethoxy ethoxy acrylate, 1-2 parts of isodecanol polyethenoxy ether, 5-6 parts of 2-hydroxyethyl acrylate, 7-8 parts of neopentyl glycol diacrylate, 1-2 parts of alpha-hydroxyketone, 3-4 parts of 2-hydroxypropyl acrylate, 5-6 parts of tripropylene glycol diacrylate and 1-2 parts of polyvinylpyrrolidone. After being cured, the primer-free UV paint for melamine veneers has the advantages of excellent adhesive force, favorable glossiness, high hardness, flat and smooth surface of the cured film, and favorable fullness.
Description
Technical field
The present invention relates to and exempt from end UV coating for melamine decorative veneer.
Background technology
The UV coating of existing melamine decorative veneer, the sticking power after its solidification, glossiness, hardness all have much room for improvement.
Summary of the invention
The object of the present invention is to provide and a kind ofly exempt from end UV coating for melamine decorative veneer, its solidification postadhesion power is excellent, glossiness good, hardness is high, and cured film surfacing is smooth, and fullness ratio is good.
For achieving the above object, to be that design is a kind of exempt from end UV coating for melamine decorative veneer to technical scheme of the present invention, composed of the following components by weight:
8 ~ 9 parts of epoxy acrylates,
1 ~ 2 part of ethoxy ethoxy acrylate,
1 ~ 2 part of isomery ten polyoxyethylenated alcohol,
5 ~ 6 parts of Hydroxyethyl acrylates,
7 ~ 8 parts of neopentylglycol diacrylates,
1 ~ 2 part of Alpha-hydroxy ketone,
3 ~ 4 parts of Propylene glycol monoacrylates,
5 ~ 6 parts of tri (propylene glycol) diacrylates,
1 ~ 2 part of polyvinylpyrrolidone.
Preferably, described exempt from end UV coating for melamine decorative veneer, composed of the following components by weight:
8.9 parts of epoxy acrylates,
1.2 parts of ethoxy ethoxy acrylate,
1.2 parts of isomery ten polyoxyethylenated alcohol,
5.6 parts of Hydroxyethyl acrylates,
7.8 parts of neopentylglycol diacrylates,
1.2 parts of Alpha-hydroxy ketones,
3.4 parts of Propylene glycol monoacrylates,
5.6 parts of tri (propylene glycol) diacrylates,
1.2 parts of polyvinylpyrrolidones.
Preferably, described exempt from end UV coating for melamine decorative veneer, composed of the following components by weight:
9 parts of epoxy acrylates,
2 parts of ethoxy ethoxy acrylate,
2 parts of isomery ten polyoxyethylenated alcohol,
6 parts of Hydroxyethyl acrylates,
8 parts of neopentylglycol diacrylates,
2 parts of Alpha-hydroxy ketones,
4 parts of Propylene glycol monoacrylates,
6 parts of tri (propylene glycol) diacrylates,
2 parts of polyvinylpyrrolidones.
Preferably, described exempt from end UV coating for melamine decorative veneer, composed of the following components by weight:
8 parts of epoxy acrylates,
1 part of ethoxy ethoxy acrylate,
1 part of isomery ten polyoxyethylenated alcohol,
5 parts of Hydroxyethyl acrylates,
7 parts of neopentylglycol diacrylates,
1 part of Alpha-hydroxy ketone,
3 parts of Propylene glycol monoacrylates,
5 parts of tri (propylene glycol) diacrylates,
1 part of polyvinylpyrrolidone.
Advantage of the present invention and beneficial effect are: provide a kind of and exempt from end UV coating for melamine decorative veneer, and its solidification postadhesion power is excellent, glossiness good, hardness is high, and cured film surfacing is smooth, and fullness ratio is good.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
An end UV coating is exempted from for melamine decorative veneer, composed of the following components by weight:
8.9 parts of epoxy acrylates,
1.2 parts of ethoxy ethoxy acrylate,
1.2 parts of isomery ten polyoxyethylenated alcohol,
5.6 parts of Hydroxyethyl acrylates,
7.8 parts of neopentylglycol diacrylates,
1.2 parts of Alpha-hydroxy ketones,
3.4 parts of Propylene glycol monoacrylates,
5.6 parts of tri (propylene glycol) diacrylates,
1.2 parts of polyvinylpyrrolidones.
Embodiment 2
An end UV coating is exempted from for melamine decorative veneer, composed of the following components by weight:
9 parts of epoxy acrylates,
2 parts of ethoxy ethoxy acrylate,
2 parts of isomery ten polyoxyethylenated alcohol,
6 parts of Hydroxyethyl acrylates,
8 parts of neopentylglycol diacrylates,
2 parts of Alpha-hydroxy ketones,
4 parts of Propylene glycol monoacrylates,
6 parts of tri (propylene glycol) diacrylates,
2 parts of polyvinylpyrrolidones.
Embodiment 3
An end UV coating is exempted from for melamine decorative veneer, composed of the following components by weight:
8 parts of epoxy acrylates,
1 part of ethoxy ethoxy acrylate,
1 part of isomery ten polyoxyethylenated alcohol,
5 parts of Hydroxyethyl acrylates,
7 parts of neopentylglycol diacrylates,
1 part of Alpha-hydroxy ketone,
3 parts of Propylene glycol monoacrylates,
5 parts of tri (propylene glycol) diacrylates,
1 part of polyvinylpyrrolidone.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (4)
1. exempt from end UV coating for melamine decorative veneer, it is characterized in that, composed of the following components by weight:
8 ~ 9 parts of epoxy acrylates,
1 ~ 2 part of ethoxy ethoxy acrylate,
1 ~ 2 part of isomery ten polyoxyethylenated alcohol,
5 ~ 6 parts of Hydroxyethyl acrylates,
7 ~ 8 parts of neopentylglycol diacrylates,
1 ~ 2 part of Alpha-hydroxy ketone,
3 ~ 4 parts of Propylene glycol monoacrylates,
5 ~ 6 parts of tri (propylene glycol) diacrylates,
1 ~ 2 part of polyvinylpyrrolidone.
2. according to claim 1ly exempt from end UV coating for melamine decorative veneer, it is characterized in that, composed of the following components by weight:
8.9 parts of epoxy acrylates,
1.2 parts of ethoxy ethoxy acrylate,
1.2 parts of isomery ten polyoxyethylenated alcohol,
5.6 parts of Hydroxyethyl acrylates,
7.8 parts of neopentylglycol diacrylates,
1.2 parts of Alpha-hydroxy ketones,
3.4 parts of Propylene glycol monoacrylates,
5.6 parts of tri (propylene glycol) diacrylates,
1.2 parts of polyvinylpyrrolidones.
3. according to claim 1ly exempt from end UV coating for melamine decorative veneer, it is characterized in that, composed of the following components by weight:
9 parts of epoxy acrylates,
2 parts of ethoxy ethoxy acrylate,
2 parts of isomery ten polyoxyethylenated alcohol,
6 parts of Hydroxyethyl acrylates,
8 parts of neopentylglycol diacrylates,
2 parts of Alpha-hydroxy ketones,
4 parts of Propylene glycol monoacrylates,
6 parts of tri (propylene glycol) diacrylates,
2 parts of polyvinylpyrrolidones.
4. according to claim 1ly exempt from end UV coating for melamine decorative veneer, it is characterized in that, composed of the following components by weight:
8 parts of epoxy acrylates,
1 part of ethoxy ethoxy acrylate,
1 part of isomery ten polyoxyethylenated alcohol,
5 parts of Hydroxyethyl acrylates,
7 parts of neopentylglycol diacrylates,
1 part of Alpha-hydroxy ketone,
3 parts of Propylene glycol monoacrylates,
5 parts of tri (propylene glycol) diacrylates,
1 part of polyvinylpyrrolidone.