CN104387946A - Bottom-free UV (Ultraviolet) coating for melamine veneer - Google Patents
Bottom-free UV (Ultraviolet) coating for melamine veneer Download PDFInfo
- Publication number
- CN104387946A CN104387946A CN201410698086.XA CN201410698086A CN104387946A CN 104387946 A CN104387946 A CN 104387946A CN 201410698086 A CN201410698086 A CN 201410698086A CN 104387946 A CN104387946 A CN 104387946A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- exempting
- free
- benzophenone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a bottom-free UV (Ultraviolet) coating for a melamine veneer. The bottom-free UV coating comprises the following components in parts by weight: 7-8 parts of iso-octyl acrylate, 6-7 parts of propoxylated neopentyl glycol diacrylate, 7-8 parts of polyurethane acrylate, 6-7 parts of hydroxypropyl methacrylate, 4-5 parts of hydroxyethyl methacrylate, 4-5 parts of dipropylene glycol diacrylate, 6-7 parts of benzophenone and 1-2 parts of iso-tridecanol polyoxyethylene ether. After being cured, the bottom-free UV coating for the melamine veneer is excellent in adhesive force, good in glossiness and high in rigidity, and a cured film has flat and smooth surface and good plumpness.
Description
Technical field
The present invention relates to melamine decorative veneer with exempting from end UV coating.
Background technology
The UV coating of existing melamine decorative veneer, the sticking power after its solidification, glossiness, hardness all have much room for improvement.
Summary of the invention
The object of the present invention is to provide a kind of melamine decorative veneer with exempting from end UV coating, its solidification postadhesion power is excellent, glossiness good, hardness is high, and cured film surfacing is smooth, and fullness ratio is good.
For achieving the above object, technical scheme of the present invention designs a kind of melamine decorative veneer with exempting from end UV coating, composed of the following components by weight:
7 ~ 8 parts of Isooctyl acrylate monomers,
6 ~ 7 part of third oxidation neopentylglycol diacrylate,
7 ~ 8 parts of urethane acrylates,
6 ~ 7 parts of Rocryl 410s,
4 ~ 5 parts of hydroxyethyl methylacrylates,
4 ~ 5 parts of dipropylene,
6 ~ 7 parts of benzophenone,
1 ~ 2 part of isomerous tridecanol polyoxyethylene ether.
Preferably, described melamine decorative veneer is with exempting from end UV coating, composed of the following components by weight:
7.8 parts of Isooctyl acrylate monomers,
6.7 part of third oxidation neopentylglycol diacrylate,
7.8 parts of urethane acrylates,
6.7 parts of Rocryl 410s,
4.5 parts of hydroxyethyl methylacrylates,
4.5 parts of dipropylene,
6.7 parts of benzophenone,
1.2 parts of isomerous tridecanol polyoxyethylene ethers.
Preferably, described melamine decorative veneer is with exempting from end UV coating, composed of the following components by weight:
8 parts of Isooctyl acrylate monomers,
7 part of third oxidation neopentylglycol diacrylate,
8 parts of urethane acrylates,
7 parts of Rocryl 410s,
5 parts of hydroxyethyl methylacrylates,
5 parts of dipropylene,
7 parts of benzophenone,
2 parts of isomerous tridecanol polyoxyethylene ethers.
Preferably, described melamine decorative veneer is with exempting from end UV coating, composed of the following components by weight:
7 parts of Isooctyl acrylate monomers,
6 part of third oxidation neopentylglycol diacrylate,
7 parts of urethane acrylates,
6 parts of Rocryl 410s,
4 parts of hydroxyethyl methylacrylates,
4 parts of dipropylene,
6 parts of benzophenone,
1 part of isomerous tridecanol polyoxyethylene ether.
Advantage of the present invention and beneficial effect are: provide a kind of melamine decorative veneer with exempting from end UV coating, and its solidification postadhesion power is excellent, glossiness good, hardness is high, and cured film surfacing is smooth, and fullness ratio is good.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A kind of melamine decorative veneer is with exempting from end UV coating, composed of the following components by weight:
7.8 parts of Isooctyl acrylate monomers,
6.7 part of third oxidation neopentylglycol diacrylate,
7.8 parts of urethane acrylates,
6.7 parts of Rocryl 410s,
4.5 parts of hydroxyethyl methylacrylates,
4.5 parts of dipropylene,
6.7 parts of benzophenone,
1.2 parts of isomerous tridecanol polyoxyethylene ethers.
Embodiment 2
A kind of melamine decorative veneer is with exempting from end UV coating, composed of the following components by weight:
8 parts of Isooctyl acrylate monomers,
7 part of third oxidation neopentylglycol diacrylate,
8 parts of urethane acrylates,
7 parts of Rocryl 410s,
5 parts of hydroxyethyl methylacrylates,
5 parts of dipropylene,
7 parts of benzophenone,
2 parts of isomerous tridecanol polyoxyethylene ethers.
Embodiment 3
A kind of melamine decorative veneer is with exempting from end UV coating, composed of the following components by weight:
7 parts of Isooctyl acrylate monomers,
6 part of third oxidation neopentylglycol diacrylate,
7 parts of urethane acrylates,
6 parts of Rocryl 410s,
4 parts of hydroxyethyl methylacrylates,
4 parts of dipropylene,
6 parts of benzophenone,
1 part of isomerous tridecanol polyoxyethylene ether.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (4)
1. melamine decorative veneer is with exempting from end UV coating, it is characterized in that, composed of the following components by weight:
7 ~ 8 parts of Isooctyl acrylate monomers,
6 ~ 7 part of third oxidation neopentylglycol diacrylate,
7 ~ 8 parts of urethane acrylates,
6 ~ 7 parts of Rocryl 410s,
4 ~ 5 parts of hydroxyethyl methylacrylates,
4 ~ 5 parts of dipropylene,
6 ~ 7 parts of benzophenone,
1 ~ 2 part of isomerous tridecanol polyoxyethylene ether.
2. melamine decorative veneer according to claim 1 is with exempting from end UV coating, it is characterized in that, composed of the following components by weight:
7.8 parts of Isooctyl acrylate monomers,
6.7 part of third oxidation neopentylglycol diacrylate,
7.8 parts of urethane acrylates,
6.7 parts of Rocryl 410s,
4.5 parts of hydroxyethyl methylacrylates,
4.5 parts of dipropylene,
6.7 parts of benzophenone,
1.2 parts of isomerous tridecanol polyoxyethylene ethers.
3. melamine decorative veneer according to claim 1 is with exempting from end UV coating, it is characterized in that, composed of the following components by weight:
8 parts of Isooctyl acrylate monomers,
7 part of third oxidation neopentylglycol diacrylate,
8 parts of urethane acrylates,
7 parts of Rocryl 410s,
5 parts of hydroxyethyl methylacrylates,
5 parts of dipropylene,
7 parts of benzophenone,
2 parts of isomerous tridecanol polyoxyethylene ethers.
4. melamine decorative veneer according to claim 1 is with exempting from end UV coating, it is characterized in that, composed of the following components by weight:
7 parts of Isooctyl acrylate monomers,
6 part of third oxidation neopentylglycol diacrylate,
7 parts of urethane acrylates,
6 parts of Rocryl 410s,
4 parts of hydroxyethyl methylacrylates,
4 parts of dipropylene,
6 parts of benzophenone,
1 part of isomerous tridecanol polyoxyethylene ether.