CN104356478A - 一种硬度高、断裂韧性高的pe管的制备方法 - Google Patents
一种硬度高、断裂韧性高的pe管的制备方法 Download PDFInfo
- Publication number
- CN104356478A CN104356478A CN201410617374.8A CN201410617374A CN104356478A CN 104356478 A CN104356478 A CN 104356478A CN 201410617374 A CN201410617374 A CN 201410617374A CN 104356478 A CN104356478 A CN 104356478A
- Authority
- CN
- China
- Prior art keywords
- pipe
- percent
- weight
- preparation
- hardness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种硬度高、断裂韧性高的PE管的制备方法。它采用以下技术方案:其是由重量百分比17%~41%的聚乙烯;23%~26%的尼龙6;28%~34%的陶瓷微粒;0.1%~2%的色母粒;0.3%~1.2%的稳定剂;2%~8%的消泡剂;2%~10%的抗氧化剂在反应釜中混合反应后,蒸干水分,投入挤出机,通过所述挤出机内的螺杆将混合料推入挤出模头,成型后经真空冷却定型,由引出机牵引出成型的PE管材,再经切割机根据要求的长度切断,得到PE管材成品。本发明具有以下有益效果:连接可靠;低温抗冲击性好;抗应力开裂性好;耐化学腐蚀性好;耐老化,使用寿命长;耐磨性好;可挠性好;水流阻力小等优点。
Description
技术领域
本发明涉及PE管技术领域,具体涉及一种硬度高、断裂韧性高的PE管的制备方法。
背景技术
PE管目前中国的市政管材市场,塑料管道正在稳步发展,PE管、PP-R管、UPVC管都占有一席之地,其中PE管强劲的发展势头最为令人瞩目。PE管的使用领域广泛,其中给水管和燃气管是其两个最大的应用市场。
给水用PE管材是传统的钢铁管材、聚氯乙烯饮用水管的换代产品。给水管必须承受一定的压力,通常要选用分子量大、机械性能较好的PE树脂。
发明内容
本发明的目的是提供一种与现有技术相比硬度更高、断裂韧性高的PE管的制备方法。
为了实现上述目的,本发明是采用以下技术方案:一种硬度高、断裂韧性高的PE管的制备方法,其是由重量百分比17%~41%的聚乙烯;23%~26%的尼龙6;28%~34%的陶瓷微粒;0.1%~2%的色母粒;0.3%~1.2%的稳定剂;2%~8%的消泡剂;2%~10%的抗氧化剂在反应釜中混合反应后,蒸干水分,投入挤出机,通过所述挤出机内的螺杆将混合料推入挤出模头,成型后经真空冷却定型,由引出机牵引出成型的PE管材,再经切割机根据要求的长度切断,得到PE管材成品。
进一步地,所述聚乙烯选用高密度聚乙烯。
进一步地,所述稳定剂包括热稳定剂、光稳定剂。
进一步地,所述陶瓷微粒粒径为10~35μm。
进一步地,所述反应温度为220~230℃,反应时间1~4h。
进一步地,所述真空冷却温度为30~45℃。
本发明具有以下有益效果:PE管材材质是无毒的,不会腐蚀和结垢,有效提高管网水质;PE管具有良好的耐水锤压力的能力,供水的安全性被提高,同时增强了可靠性;PE管有很好的可溶接性和柔韧性,铺设时更加方便快捷,还安全可靠;PE管的铺设速度可以很快,损坏费用和维护费用不高,只要接头良好就可以承受轴向负荷而不发生泄漏或者脱开;PE管材的原料经济实惠。
具体实施方式
下面对本发明做进一步详细的说明。
实施例一:
选用重量百分比41%的聚乙烯;23%的尼龙6;28%的陶瓷微粒; 2%的色母粒;1%的稳定剂;2%的消泡剂;3%的抗氧化剂在反应温度为220℃的反应釜中混合反应3h后,蒸干水分,投入挤出机,通过所述挤出机内的螺杆将混合料推入挤出模头,成型后经30℃真空冷却定型,由引出机牵引出成型的PE管材,再经切割机根据要求的长度切断,得到PE管材成品。
实施例二:
选用重量百分比35%的聚乙烯;25%的尼龙6;30%的陶瓷微粒; 0.8%的色母粒;1.2%的稳定剂;3%的消泡剂;5%的抗氧化剂在反应温度为225℃的反应釜中混合反应3h后,蒸干水分,投入挤出机,通过所述挤出机内的螺杆将混合料推入挤出模头,成型后经40℃真空冷却定型,由引出机牵引出成型的PE管材,再经切割机根据要求的长度切断,得到PE管材成品。
实施例三:
选用重量百分比30%的聚乙烯;26%的尼龙6;34%的陶瓷微粒; 1%的色母粒;1%的稳定剂;4%的消泡剂;4%的抗氧化剂在反应温度为230℃的反应釜中混合反应3h后,蒸干水分,投入挤出机,通过所述挤出机内的螺杆将混合料推入挤出模头,成型后经45℃真空冷却定型,由引出机牵引出成型的PE管材,再经切割机根据要求的长度切断,得到PE管材成品。
最后说明的是,以上实施例仅用以说明本发明的技术方案而非限制,本领域普通技术人员对本发明的技术方案所做的其他修改或者等同替换,只要不脱离本发明技术方案的精神和范围,均应涵盖在本发明的权利要求范围当中。
Claims (6)
1.一种硬度高、断裂韧性高的PE管的制备方法,其特征在于,其是由重量百分比17%~41%的聚乙烯;23%~26%的尼龙6;28%~34%的陶瓷微粒;0.1%~2%的色母粒;0.3%~1.2%的稳定剂;2%~8%的消泡剂;2%~10%的抗氧化剂在反应釜中混合反应后,蒸干水分,投入挤出机,通过所述挤出机内的螺杆将混合料推入挤出模头,成型后经真空冷却定型,由引出机牵引出成型的PE管材,再经切割机根据要求的长度切断,得到PE管材成品。
2.根据权利要求1所述的一种硬度高、断裂韧性高的PE管的制备方法,其特征在于,所述聚乙烯选用高密度聚乙烯。
3.根据权利要求1所述的一种硬度高、断裂韧性高的PE管的制备方法,其特征在于,所述稳定剂包括热稳定剂、光稳定剂。
4.根据权利要求1所述的一种硬度高、断裂韧性高的PE管的制备方法,其特征在于,所述陶瓷微粒粒径为10~35μm。
5.根据权利要求1所述的一种硬度高、断裂韧性高的PE管的制备方法,其特征在于,所述反应温度为220~230℃,反应时间1~4h。
6.根据权利要求1所述的一种硬度高、断裂韧性高的PE管的制备方法,其特征在于,所述真空冷却温度为30~45℃。