CN104353432A - Super absorbent resin-based absorbent and preparation method thereof - Google Patents
Super absorbent resin-based absorbent and preparation method thereof Download PDFInfo
- Publication number
- CN104353432A CN104353432A CN201410432609.6A CN201410432609A CN104353432A CN 104353432 A CN104353432 A CN 104353432A CN 201410432609 A CN201410432609 A CN 201410432609A CN 104353432 A CN104353432 A CN 104353432A
- Authority
- CN
- China
- Prior art keywords
- high hydroscopic
- hydroscopic resin
- parts
- kayexalate
- magnesium sulfate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a super absorbent resin-based absorbent which is mainly prepared from the following materials in parts by weight: 50 parts of a super absorbent resin, 2-8 parts of sodium polystyrenesulfonate, 1-5 parts of calcium chloride, and 1-5 parts of magnesium sulfate. The invention further provides a preparation method of the super absorbent resin-based absorbent. Compared with the prior art, the obtained super absorbent resin-based absorbent is simple in process, large in water absorption and long in service life, and does not cause environmental pollution.
Description
Technical field
The present invention relates to a kind of hygroscopic agent and preparation method thereof, be specifically related to a kind ofly with high hydroscopic resin made by main carriers, there is aromatic of efficient absorbent effect and preparation method thereof.
Background technology
Hygroscopic agent refer to can from air any one material of absorbing moisture, also known as drier.Conventional solid moisture absorbent has silica gel, aluminium oxide, molecular sieve etc., and these materials have strong compatibility to moisture.The hygroscopic agent scope of application is extensive, can be placed on wardrobe extract humidity, prevent clothes mouldy spoiled, can be placed on except absorbing moisture in automobile, can also draw peculiar smell in car, can also be placed in room, absorbs the moisture of air, reduces indoor humidity.
At present, there are some defects in traditional hygroscopic agent, such as water absorption is few, and service life is short, greatly limit the application of hygroscopic agent.
Summary of the invention
Goal of the invention: in order to overcome the deficiencies in the prior art, the invention provides a kind of high hydroscopic resin base hygroscopic agent and preparation method thereof.
Technical scheme: for achieving the above object, the invention provides a kind of high hydroscopic resin base hygroscopic agent, and it is mainly made by the raw material of following weight ratio:
High hydroscopic resin 50 parts, kayexalate 2-8 part, calcium chloride 1-5 part, magnesium sulfate 1-5 part.
As preferably, described high hydroscopic resin base hygroscopic agent is mainly made by the raw material of following weight ratio:
High hydroscopic resin 50 parts, kayexalate 4-6 part, calcium chloride 2-4 part, magnesium sulfate 2-4 part.
Preferred as another kind, described high hydroscopic resin base hygroscopic agent is mainly made by the raw material of following weight ratio:
High hydroscopic resin 50 parts, kayexalate 2 parts, 1 part, calcium chloride, 1 part, magnesium sulfate.
Preferred as another kind, described high hydroscopic resin base hygroscopic agent is mainly made by the raw material of following weight ratio:
High hydroscopic resin 50 parts, kayexalate 8 parts, 5 parts, calcium chloride, 5 parts, magnesium sulfate.
Preferred as another kind, described high hydroscopic resin base hygroscopic agent is mainly made by the raw material of following weight ratio:
High hydroscopic resin 50 parts, kayexalate 2-8 part, calcium chloride 1-5 part, magnesium sulfate 1-5 part.
Present invention also offers the preparation method of described high hydroscopic resin base hygroscopic agent, it is mainly made by following steps:
(1) get high hydroscopic resin, join in kayexalate solution, stir 8-12 hour;
(2) solid in separation solution, dry, add calcium chloride and magnesium sulfate, mix, to obtain final product.
As preferably, the concentration of described kayexalate solution is (100-200) mg/mL.
High hydroscopic resin of the present invention is the super absorbent resin according to prescription in the applicant's publication application (CN201310317160.4 and CN201310316832.X) and preparation method's gained.
Beneficial effect: the present invention is relative to prior art, and the high hydroscopic resin base hygroscopic agent of gained, technique is simple, and water absorption is large, long service life, non-environmental-pollution.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is further described.
Embodiment 1:
Prescription:
High hydroscopic resin 50g, kayexalate 2g, calcium chloride 1g, magnesium sulfate 1g.
Preparation method:
(1) get high hydroscopic resin, join in kayexalate solution, stir 8 hours;
(2) solid in separation solution, dry, add calcium chloride and magnesium sulfate, mix, to obtain final product.
The concentration of described kayexalate solution is 100mg/mL.
Embodiment 2:
Prescription:
High hydroscopic resin 50g, kayexalate 8g, calcium chloride 5g, magnesium sulfate 5g.
Preparation method:
(1) get high hydroscopic resin, join in kayexalate solution, stir 12 hours;
(2) solid in separation solution, dry, add calcium chloride and magnesium sulfate, mix, to obtain final product.
The concentration of described kayexalate solution is 200mg/mL.
Embodiment 3:
Prescription:
High hydroscopic resin 50g, kayexalate 5g, calcium chloride 3g, magnesium sulfate 3g.
Preparation method:
(1) get high hydroscopic resin, join in kayexalate solution, stir 10 hours;
(2) solid in separation solution, dry, add calcium chloride and magnesium sulfate, mix, to obtain final product.
The concentration of described kayexalate solution is 150mg/mL.
Embodiment 4:
Prescription:
High hydroscopic resin 50g, kayexalate 4g, calcium chloride 2g, magnesium sulfate 2g.
Preparation method:
(1) get high hydroscopic resin, join in kayexalate solution, stir 9 hours;
(2) solid in separation solution, dry, add calcium chloride and magnesium sulfate, mix, to obtain final product.
The concentration of described kayexalate solution is 120mg/mL.
Embodiment 5:
Prescription:
High hydroscopic resin 50g, kayexalate 6g, calcium chloride 4g, magnesium sulfate 4g.
Preparation method:
(1) get high hydroscopic resin, join in kayexalate solution, stir 11 hours;
(2) solid in separation solution, dry, add calcium chloride and magnesium sulfate, mix, to obtain final product.
The concentration of described kayexalate solution is 180mg/mL.
Experimental example water absorbing agent Performance Detection of the present invention
Table 1 hygroscopic agent performance test results of the present invention
Contrast 1 group and adopt prescription of the present invention and preparation method, replace the hygroscopic agent of described high hydroscopic resin gained with shitosan;
Contrast 2 groups of employings, high hydroscopic resin, kayexalate, calcium chloride and magnesium sulfate are without process, and direct physical mixes the hygroscopic agent of gained;
Table 1 gained hygroscopic agent of the present invention performance test results (n=3)
Note: with contrast 1 group or contrast 2 groups and compare, * P<0.05
By upper Biao Ke get, compared with two control groups, the embodiment of the present invention 3,4 and 5 gained hygroscopic agent is through detecting, result shows its maximum water absorption and significantly improves, and under the condition of relative humidity 80%, service life can reach about 90 days, and service life obviously extends, and has significant moisture pick-up properties.
Claims (7)
1. a high hydroscopic resin base hygroscopic agent, is characterized in that, it is mainly made by the raw material of following weight ratio:
High hydroscopic resin 50 parts, kayexalate 2-8 part, calcium chloride 1-5 part, magnesium sulfate 1-5 part.
2. high hydroscopic resin base hygroscopic agent according to claim 1, is characterized in that, it is mainly made by the raw material of following weight ratio:
High hydroscopic resin 50 parts, kayexalate 4-6 part, calcium chloride 2-4 part, magnesium sulfate 2-4 part.
3. high hydroscopic resin base hygroscopic agent according to claim 1, is characterized in that, it is mainly made by the raw material of following weight ratio:
High hydroscopic resin 50 parts, kayexalate 2 parts, 1 part, calcium chloride, 1 part, magnesium sulfate.
4. high hydroscopic resin base hygroscopic agent according to claim 1, is characterized in that, it is mainly made by the raw material of following weight ratio:
High hydroscopic resin 50 parts, kayexalate 8 parts, 5 parts, calcium chloride, 5 parts, magnesium sulfate.
5. high hydroscopic resin base hygroscopic agent according to claim 1, is characterized in that, it is mainly made by the raw material of following weight ratio:
High hydroscopic resin 50 parts, kayexalate 2-8 part, calcium chloride 1-5 part, magnesium sulfate 1-5 part.
6. the preparation method of the high hydroscopic resin base hygroscopic agent described in any one of claim 1-5, is characterized in that, it is mainly made by following steps:
(1) get high hydroscopic resin, join in kayexalate solution, stir 8-12 hour;
(2) solid in separation solution, dry, add calcium chloride and magnesium sulfate, mix, to obtain final product.
7. the preparation method of high hydroscopic resin base hygroscopic agent according to claim 6, is characterized in that, the concentration of described kayexalate solution is (100-200) mg/mL.