CN104341844A - Ceramic tile surface putty and preparation method thereof - Google Patents
Ceramic tile surface putty and preparation method thereof Download PDFInfo
- Publication number
- CN104341844A CN104341844A CN201410639220.9A CN201410639220A CN104341844A CN 104341844 A CN104341844 A CN 104341844A CN 201410639220 A CN201410639220 A CN 201410639220A CN 104341844 A CN104341844 A CN 104341844A
- Authority
- CN
- China
- Prior art keywords
- ceramic tile
- putty
- water
- component
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses ceramic tile surface putty, which comprises an ingredient A and an ingredient B, wherein the ingredient A consists of the following ingredients in parts by weight: 30-33 parts of water, 1-2 parts of cellulose, 10-12 parts of styrene-acrylic emulsion, 50-52 parts of ground calcium carbonate and 4-6 parts of accessory ingredient; the ingredient B is silicate. The invention also discloses a preparation method for the ceramic tile surface putty. The preparation method comprises the following steps: stirring and evenly mixing the water, the cellulose, the styrene-acrylic emulsion, the ground calcium carbonate and the accessory ingredient to obtain the ingredient A, and mixing the ingredient A with the silicate at a proper ratio. In the above way, the preparation method is simple, and the prepared putty has the advantages of strong binding power, flaking resistance, small possibility of falling, no toxin or flavor, safety and environment protection.
Description
Technical field
The present invention relates to paint field, particularly relate to a kind of ceramic tile face putty and preparation method thereof.
Background technology
Putty (fillering) is a kind of decoration type material of smooth surface of wall, is a kind of thick slurry coating material, is that coating whitewashes front requisite a kind of product.Painting imposes on priming paint or is directly coated with and imposes on object, in order to remove coated article rugged defect on the surface.Because the quality of putty and the quality of batch to scrape directly affect the effect after last emulsion paint brushing.Putty directly determines the over-all properties after emulsion paint film forming, Integral decoration effect and decoration quality.
There are some problems, due to ceramic tile surface smoother, but after carrying out criticizing scrape with conventional putty when criticizing Puttying to ceramic tile metope, its sticking power is poor, insufficient strength, easily come off, these all can have influence on follow-up effect, and have influence on the painting brushing effects of emulsion paint.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of ceramic tile face putty, and preparation method is simple, and putty cohesive force is strong, does not flake, difficult drop-off, and nontoxic, tasteless, safety and environmental protection.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: provide a kind of ceramic tile face putty, comprise component A and B component, described component A is grouped into by the one-tenth of following parts by weight: water: 30-33 part; Mierocrystalline cellulose: 1-2 part; Benzene emulsion: 10-12 part; Water-ground limestone: 50-52 part; Auxiliary agent: 4-6 part; Described B component is silicate.
In a preferred embodiment of the present invention, described Mierocrystalline cellulose is Natvosol, has good thickening, suspension, dispersion, emulsification, bonding film forming, protects moisture and provides the characteristics such as protective colloid.
In a preferred embodiment of the present invention, granularity >=400 order of described water-ground limestone is high whiteness fine powder, as the high quality filler brightened, the glossiness of coating can be improved, play the effect of reinforcement simultaneously, the volume of product can be increased simultaneously, reduce costs.
In a preferred embodiment of the present invention, described auxiliary agent comprises: defoamer, film coalescence aid and sterilant.
Present invention also offers the preparation method of above-mentioned this ceramic tile face putty, another technical solution used in the present invention is: the preparation method of a kind of ceramic tile face putty, comprises the following steps:
The auxiliary agent of the benzene emulsion of the Natvosol of the water of 30-33 part, 1-2 part, 10-12 part, the water-ground limestone of 50-52 part and 4-6 part is joined in groove tank, mixes with certain rotating speed low rate mixing, after filtration, obtain component A; Again described component A is mixed with the Mixing ratio by weight of B component silicate by 17:3, i.e. obtained described ceramic tile face putty.
In a preferred embodiment of the present invention, with the rotating speed low rate mixing 10-15 minute of 100 revs/min.
The invention has the beneficial effects as follows: the water that the present invention adopts Reasonable to make a gesture of measuring, Mierocrystalline cellulose, benzene emulsion, water-ground limestone and auxiliary agent obtain component A, then component A and silicate are mixed by rational weight proportion, preparation method is simple, cost is low; Wherein silicate itself has good hardness and caking ability, water-ground limestone can play the effect of reinforcement, adjusting viscosity as filler, Mierocrystalline cellulose and benzene emulsion etc. have increases viscosity, improve effect that is flexible, protection moisture, and auxiliary agent plays the effect such as sterilization, froth breaking; Therefore ceramic tile face of the present invention putty has cohesive force by force, does not flake after brushing, the feature of difficult drop-off, and nontoxic, tasteless, safety and environmental protection.
Embodiment
Be described in detail below in conjunction with to preferred embodiment of the present invention, can be easier to make advantages and features of the invention be readily appreciated by one skilled in the art, thus more explicit defining is made to protection scope of the present invention.
The embodiment of the present invention comprises:
Embodiment one:
The film coalescence aid of the water of 30 parts, the Natvosol of 1 part, the benzene emulsion of 12 parts, the water-ground limestone of 52 parts, the defoamer of 1 part, the sterilant of 2 parts and 1 part is joined in groove tank, with the rotating speed low rate mixing 10-15 minute of 100 revs/min, after filtration, obtain component A; Again described component A is mixed with the Mixing ratio by weight of B component silicate by 17:3, i.e. obtained described ceramic tile face putty.
Wherein, granularity >=400 order of described water-ground limestone.
Embodiment two:
The film coalescence aid of the water of 31.5 parts, the Natvosol of 2 parts, the benzene emulsion of 10.5 parts, the water-ground limestone of 51.5 parts, the defoamer of 2 parts, the sterilant of 1.5 parts and 1 part is joined in groove tank, with the rotating speed low rate mixing 10-15 minute of 100 revs/min, after filtration, obtain component A; Again described component A is mixed with the Mixing ratio by weight of B component silicate by 17:3, i.e. obtained described ceramic tile face putty.
Wherein, granularity >=400 order of described water-ground limestone.
Embodiment three:
The film coalescence aid of the water of 33 parts, the Natvosol of 1 part, the benzene emulsion of 10 parts, the water-ground limestone of 50 parts, the defoamer of 2 parts, the sterilant of 2 parts and 2 parts is joined in groove tank, with the rotating speed low rate mixing 10-15 minute of 100 revs/min, after filtration, obtain component A; Again described component A is mixed with the Mixing ratio by weight of B component silicate by 17:3, i.e. obtained described ceramic tile face putty.
Wherein, granularity >=400 order of described water-ground limestone.
The technical indicator of the ceramic tile face putty obtained by above three kinds of embodiments is as follows:
The constructional method of this ceramic tile face putty, comprises the steps:
(1) base cleaning, cleans ceramic tile face or mosaic surface with clear water or washing composition;
(2) thin batch one time (require show-through, consumption is at 0.5kg/m2), after 24 hours, criticize painting one time (consumption is at 0.6-0.8kg/m2) again;
If (3) wide seam face brick, criticizes filleting mouth with flat putty and make it concordant with tile surface, criticize again after it parches and embeddingly once (if mosaic, this operation can be saved);
(4) criticize and be coated with exterior wall light face putty 2 to 3 times, take advantage of Sand paper for polishing when not parching;
(5) roller coating universal primer and finish paint.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every utilize description of the present invention to do equivalent structure or equivalent flow process conversion; or be directly or indirectly used in other relevant technical fields, be all in like manner included in scope of patent protection of the present invention.
Claims (6)
1. a ceramic tile face putty, is characterized in that, comprises component A and B component, and described component A is grouped into by the one-tenth of following parts by weight:
Water: 30-33 part;
Mierocrystalline cellulose: 1-2 part;
Benzene emulsion: 10-12 part;
Water-ground limestone: 50-52 part;
Auxiliary agent: 4-6 part;
Described B component is silicate.
2. ceramic tile face according to claim 1 putty, is characterized in that, described Mierocrystalline cellulose is Natvosol.
3. ceramic tile face according to claim 1 putty, is characterized in that, granularity >=400 order of described water-ground limestone.
4. ceramic tile face according to claim 1 putty, it is characterized in that, described auxiliary agent comprises: defoamer, film coalescence aid and sterilant.
5. a preparation method for ceramic tile face putty, is characterized in that, comprises the following steps:
The auxiliary agent of the benzene emulsion of the Natvosol of the water of 30-33 part, 1-2 part, 10-12 part, the water-ground limestone of 50-52 part and 4-6 part is joined in groove tank, mixes with certain rotating speed low rate mixing, after filtration, obtain component A; Again described component A is mixed with the Mixing ratio by weight of B component silicate by 17:3, i.e. obtained described ceramic tile face putty.
6. the preparation method of ceramic tile face according to claim 5 putty, is characterized in that, with the rotating speed low rate mixing 10-15 minute of 100 revs/min.