CN1043354C - 硬硅钙石保温涂料 - Google Patents

硬硅钙石保温涂料 Download PDF

Info

Publication number
CN1043354C
CN1043354C CN93111990A CN93111990A CN1043354C CN 1043354 C CN1043354 C CN 1043354C CN 93111990 A CN93111990 A CN 93111990A CN 93111990 A CN93111990 A CN 93111990A CN 1043354 C CN1043354 C CN 1043354C
Authority
CN
China
Prior art keywords
insulation coating
hard rankinite
hard
agent
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN93111990A
Other languages
English (en)
Other versions
CN1085582A (zh
Inventor
王曼龙
谭兴弟
刘春木
段树男
杨波
唐谊光
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ACADEMY OF BUILDING MATERIALS INDUSTRIAL SCIENCES SICHUAN PROV
Original Assignee
ACADEMY OF BUILDING MATERIALS INDUSTRIAL SCIENCES SICHUAN PROV
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ACADEMY OF BUILDING MATERIALS INDUSTRIAL SCIENCES SICHUAN PROV filed Critical ACADEMY OF BUILDING MATERIALS INDUSTRIAL SCIENCES SICHUAN PROV
Priority to CN93111990A priority Critical patent/CN1043354C/zh
Publication of CN1085582A publication Critical patent/CN1085582A/zh
Application granted granted Critical
Publication of CN1043354C publication Critical patent/CN1043354C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明提供一种硬硅钙石保温涂料，其组份配比为(以重量%计)硬硅钙石料浆40-70，无机纤维10-30，无机填料5-10、渗透剂0.5-4，粘结剂5-20，该涂料保温范围在-40～1000℃，节能效果好，粘结强度高，性能稳定，使用安全，施工方便。

Description

硬硅钙石保温涂料
本发明涉及一种保温涂料，特别是涉及一种硬硅钙石保温涂料。
目前保温材料一般多采用海泡石、蛭石、硅藻土、膨润土等天然矿物为原料，而海泡石在我国属稀少矿源，无大矿集中开采，质次价高，而蛭石，硅藻土容重过大，其保温材料容重一般大于250kg/m3，干燥收缩率大于30％，材料用量相应增大，且使用温度一般不高于600℃。中国专利1058925A公开了一种憎水复合硅酸盐保温涂料及其制造方法，以硅酸铝、硅酸镁纤维为主料，加入无机矿物如石棉绒，珍珠岩、膨润土、硅藻土等作填料，配合以渗透剂，粘合剂构成。其中使用了国际上限用且具有致癌因素的石棉绒，造成产品的不安全性。该保温涂料的干密度为180～204kg/m3，常温导热系数为0.0502W/m.k，最高使用温度为700℃，产品粘结力为1220N。
本发明的目的是在于提供一种以硬硅钙石料浆为主料，且容重低，干密度小，导热系数小，粘结力强，使用温度可达1000℃的硬硅钙石保温涂料。
本发明硬硅钙石保温涂料包括硬硅钙石料浆40～70％(重量)、无机纤维10-30％(重量)、无机填料5-10％(重量)、渗透剂0.5-4％(重量)、粘结剂5-20％(重量)。
其中硬硅钙石料浆是由硅质材料高纯石英砂、钙质材料石灰和助剂在高压下经动态水热过程合成的新型矿物，耐热温度高达1050℃，其化学式为6SiO2,6CaO、H2O，它是由40-100μm的球藻状颗粒集合体与水组成的分散系统，其中的颗粒集合体又是由5-10μm长的硬硅钙石纤维状晶体相互穿插编织而成。这种微观结构使硬硅钙石料浆具有多孔性和干燥成型性，从而使以该人工合成矿物为主料的保温涂料具有优良而稳定的性能，如容重低，干密度小，导热系数小及使用温度高等，经浓缩后所得的浆体其固含量为5-50％。
本发明硬硅钙石保温涂料中的无机纤维是水镁石纤维，硅酸铝纤维、玻璃纤维、矿物棉纤维、如岩棉、矿棉等中至少一种，一般长度为0.5-2cm。水镁石纤维对人体无毒害，质轻、易分散、成浆量大，是取代石棉纤维的理想材料。硅酸铝纤维耐热温度较高，一般用于高温型保温涂料。玻璃纤维增强效果好，但分散较困难，添加量不易过大。
本发明硬硅钙石保温涂料中的无机填料是膨胀珍珠岩、粉煤灰漂珠、膨胀蛭石、硅藻土、膨润土、陶土粉中至少一种，粒度一般为0.1～3mm。
本发明硬硅钙石保温涂料中的渗透剂是磺化琥珀酸酯类中至少一种，如快T(琥珀酸二辛酯磺酸钠)、OT(琥珀酸酯磺酸钠)、磺化琥珀酸癸酯等或JFC(聚氧乙烯醚类化合物)。是一种能对纤维起渗透、松解作用的表面活性剂。
本发明硬硅钙石保温涂料中的粘结剂可以是有机粘结剂、如乙烯-聚醋酸乙烯乳胶、聚醋酸乙烯白乳胶、聚乙烯醇、聚乙烯醇编甲醛、羧甲基纤维素等，也可以是无机粘结剂如磷酸铝，硅酸钠等，为获得宽温域内的高粘结强度，一般以无机粘结剂中至少一种与有机粘结剂混合使用。
本发明硬硅钙石保温涂料使用时，以涂料∶水=1∶0.5～1的比例与水混合，配制成施工用涂料进行涂覆。
本发明硬硅钙石保温涂料由于主要原料硬硅钙石具有封闭微孔结构，比表面积大，吸附力强，抗干燥收缩等优良性能，因而在该保温涂料中无需加入充气剂、膨胀剂，悬浮剂等其它保温涂料中常用的添加剂，简化生产工艺，降低生产成本。该保温涂料的优点在于容重低，粘结性强、导热系数小，适用温域宽(-40～1000℃)，无毒污染、施工方便，适用于各型设备、管道的隔热保温。
下面详细说明本发明实施例。
实施例1：300型硬硅钙石保温涂料
配比：
硬硅钙石料浆(固含量10％)    250(单位：Kg)
水镁石纤维                  30
岩棉纤维                    20
膨胀珍珠岩                  30
JFC                         8
聚醋酸乙烯白乳胶            12
聚乙烯醇缩甲醛              40
水                          250
制备：将上述纤维物质与渗透剂在水中浸泡12-24小时，移入搅拌机中打浆，再将其余物料加入搅拌机，使其充分混合，发泡，复合成均匀膏体，最后置于消泡池中，静置24小时，制成本发明保温涂料。产品性能指标如表1所示。
实施例2：600型硬硅钙石保温涂料
配比：
硬硅钙石料浆(固含量10％)    300
水镁石纤维                  50
玻璃纤维                    10
膨胀蛭石                    20
硅藻土                      10
快T                         5
OT                          5
乙烯-聚醋酸乙烯乳胶         10
聚乙烯醇(8％)               50
磷酸铝(831高温胶)           3
硅酸钠(水玻璃)              2
水                          300
制备同实施例1，产品性能指标如表1所示。
实施例3：1000型硬硅钙石保温涂料
配比：
硬硅钙石料浆(固含量10％)    250
硅酸铝纤维                  35
玻璃纤维                    3
粉煤灰漂珠                  20
快T                         4
聚乙烯醇(8％)               20
羧甲基纤维素                10
磷酸铝                      13
水                          230
制备方法同实施例1，产品性能如表1所示。
表1：硬硅钙石保温涂料主要技术指标
浆体密度                ＜1000kg/m3
干燥密度                ＜180kg/m3
浆体收缩率            ＜15％
粘结强度              50kpa
抗拉强度             ＞0.1Mpa
pH值                 7～8
工程导热系数方程λ=0.0273＋0.00022tcpW/mk
最高使用温度        1000℃
最低使用温度        -40℃
注*：本发明技术指标参照四川省地方标准DB51/1-91
《涂敷型复合硅酸盐绝热材料节能与安全标准》进
行测定。

Claims (1)

1、一种硬硅钙石保温涂料，其特征在于各组份配比为(以重量％计)：
硬硅钙石料浆    40～70
无机纤维        10～30
无机填料        5～10
渗透剂          0.5～4
粘结剂          5～20其中，无机纤维是水镁石纤维、硅酸铝纤维、玻璃纤维、矿物棉纤维中至少一种，长度为0.5-2cm；无机填料是膨胀珍珠岩、粉煤灰漂珠、膨胀蛭石、硅藻土、膨润土、陶土粉中至少一种，粒度为0.1-3mm；渗透剂是磺化琥珀酸酯类中至少一种；粘结剂是乙烯一聚醋酸乙烯乳胶、聚醋酸乙烯白乳胶、聚乙烯醇、聚乙烯醇缩甲醛、羧甲基纤维素，磷酸铝、硅酸钠中至少一种。
CN93111990A 1993-10-13 1993-10-13 硬硅钙石保温涂料 Expired - Fee Related CN1043354C (zh)