CN104327594B - A kind of insulating black ink eliminating ITO line shadow and preparation method thereof - Google Patents
A kind of insulating black ink eliminating ITO line shadow and preparation method thereof Download PDFInfo
- Publication number
- CN104327594B CN104327594B CN201410429163.1A CN201410429163A CN104327594B CN 104327594 B CN104327594 B CN 104327594B CN 201410429163 A CN201410429163 A CN 201410429163A CN 104327594 B CN104327594 B CN 104327594B
- Authority
- CN
- China
- Prior art keywords
- ito
- carbon black
- gloss oil
- modified epoxy
- specific
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of insulating black ink eliminating ITO line shadow and preparation method thereof, modified epoxy (or modified polyester resin) used meets the requirement of blanking ITO technique;Binder is the main film forming substance of this black out ink, has the ability being attached on ITO and strengthening glass, is provided simultaneously with high-insulativity.It is Tong Bu with the refractive index of ito film layer that selected modified epoxy possesses light folding rate after reacting with firming agent.Different anaclasis can not be produced and cause different aberration.And can allow the carbon black of specific colourity in binder good dispersion, mobility is little, can give ink film related physical and chemical.When silk screen printing figure, specific blackness carbon black is made to form the print material of certain viscosity, to complete the figure transfer of mode of printing.After printing solidification, make to be formed between specific blackness carbon black and the filler particles of specific refraction and base material stable bond so that it is the ring meeting touch screen industry surveys requirement and printing precision requirement.
Description
Technical field
The present invention relates to ink area, particularly relate to a kind of insulating black ink eliminating ITO line shadow and preparation method thereof.
Background technology
Touch screen (capacitive touch screen), main flow uses G (face glass)+G (glass ITO)+G (glass ITO) or G (glass surface
Plate) the mutual capacitance type capacitance plate of+F (thin film ITO)+F (thin film ITO) structure.Along with the Consumer's Experience of terminal client improves constantly, consumption
The requirement that person is light, thin to terminal intelligent product appearance, each touch screen module manufacturing enterprise have developed gentlier, thinner, cost more
Low OGS (integrated capacitor screen) touch screen module, i.e. uses the structure of monolithic G, replaces traditional G+G+G or G+F+F structure.
Thus saving 2 G (ito coated glass) or 2 F (ITO plated film PET), the production technology of simplification improves production efficiency, reduces
Production cost, and touch screen module (ITO Sensor) accomplished the thinnest, can be designed that gentlier, thinner smart mobile phone,
Panel computer or other touch-control products.As a ring important in touch screen production link, the research and development of ink also to adapt to therewith
The requirement of OGS technique;Owing to OGS touch screen is applied to electronic applications, need by ESD antistatic testing standard, and on market its
The insulating properties of his ink all can not be tested by the high-pressure electrostatic of ESD, causes touch screen to be highly prone to static interference in use,
There is touching not accurate situation.
Summary of the invention
Embodiment of the present invention technical problem to be solved is, it is provided that a kind of insulating black ink eliminating ITO line shadow.
The insulating black ink of described elimination ITO line shadow, includes following composition by weight percentage: modified epoxy gloss oil
70~80% or saturated polyester gloss oil 60~70% coordinate amino resins 10%, insulation carbon black 15~18%, powder body 5%, point
Powder 2~3%, levelling agent 1~2%, defoamer 1~2%;Described modified epoxy gloss oil admittedly containing 65%, solvent DBE15%,
Solvent isophorone 20%, saturated polyester gloss oil admittedly containing 65%, solvent isophorone 20%, 150# solvent 15%.
The present embodiment additionally provides the manufacture method of a kind of insulating black ink eliminating ITO line shadow, comprises the steps:
Prepare gloss oil: first pour in Scattered Kettle by solvent DBE15 part, isophorone 20 parts, stirring at low speed, in whipping process, claim
Measure 65 parts of modified epoxy solids, slowly pour in Scattered Kettle, improve rotating speed and rise to 1200 turns, continue 6 hours~8 hours
Solid is completely dissolved complete prepared A gloss oil;
Preparation mixing slurry: weigh 70 parts of A gloss oil in reactor, low speed 200 turns stirring, stir while at the uniform velocity add insulate carbon black 15%~
18%, powder body 5%, dispersant 2%~3%, levelling agent 1%~2%, defoamer 1%~2%, stirring obtain for 20~30 minutes
To mixed slurry B;
Preparing finished product: mixed slurry B carries out after stirring sand milling, sand milling temperature controls at 40 DEG C-65 DEG C, and 3 fineness of sand milling control
3 μm~5 μm obtain finished product C.
Implement the embodiment of the present invention, have the advantages that
Modified epoxy (or modified polyester resin) used by the embodiment of the present invention meets the requirement of blanking ITO technique.Binder is this
The main film forming substance of black out ink, has the ability being attached on ITO and strengthening glass, is provided simultaneously with high-insulativity (pressurization
5000V voltage measurement resistance wants >=4G Europe).Selected modified epoxy possesses light folding rate with firming agent after reacting wants and ITO
The refractive index of film layer synchronizes.Different anaclasis can not be produced and cause different aberration.And the carbon black of specific colourity can be allowed to connect
Good dispersion in splicing, mobility is little, can give ink film related physical and chemical.When silk screen printing figure, make spy
Determine blackness carbon black and form the print material of certain viscosity, to complete the figure transfer of mode of printing.After printing solidification, make specific blackness carbon
Stable bond is formed so that it is the ring meeting touch screen industry surveys requirement and printing between filler particles and the base material of black and specific refraction
Required precision.
Accompanying drawing explanation
Fig. 1 is embodiment of the present invention structural representation;
Fig. 2 is the embodiment of the present invention non-printing-ink schematic diagram;
Fig. 3 is embodiment of the present invention printing-ink schematic diagram.
Detailed description of the invention
For making the object, technical solutions and advantages of the present invention clearer, below in conjunction with accompanying drawing, the present invention is made further
Ground describes in detail.
The embodiment of the present invention eliminates the insulating black ink of ITO line shadow, includes following composition by weight percentage: modified epoxy
Resin gloss oil 70~80%, insulation carbon black 15~18%, powder body 5%, dispersant 2~3%, levelling agent 1~2%, defoamer 1~
2%;Described modified epoxy gloss oil admittedly containing 65%, solvent DBE15%, solvent isophorone 20%.
The present embodiment additionally provides the manufacture method of a kind of insulating black ink eliminating ITO line shadow, comprises the steps:
Prepare gloss oil: first pour in Scattered Kettle by solvent DBE15 part isophorone 20 parts, stirring at low speed, in whipping process, weigh
Go out 65 parts of modified epoxy solids, slowly pour in Scattered Kettle, improve rotating speed and rise to 1200 turns, continue 6 hours~8 hours admittedly
Body is completely dissolved complete prepared A gloss oil;
Preparation mixing slurry: weigh 70 parts of A gloss oil in reactor, low speed 200 turns stirring, stir while at the uniform velocity add insulate carbon black 15%~
18%, powder body 5%, dispersant 2%~3%, levelling agent 1%~2%, defoamer 1%~2%, stirring obtain for 20~30 minutes
To mixed slurry B;
Preparing finished product: mixed slurry B carries out after stirring sand milling, sand milling temperature controls at 40 DEG C-65 DEG C, and 3 fineness of sand milling control
3 μm~5 μm obtain finished product C.
Modified epoxy (or modified polyester resin) used meets the requirement of blanking ITO technique.Binder is this blanking
The main film forming substance of ink, has the ability being attached on ITO and strengthening glass, is provided simultaneously with high-insulativity (pressurization 5000V
Voltage measurement resistance wants >=4G Europe).Selected modified epoxy possesses light folding rate after reacting with firming agent will be with ito film layer
Refractive index synchronize.Different anaclasis can not be produced and cause different aberration.And the carbon black of specific colourity can be allowed in binder
Middle good dispersion, mobility are little, can give ink film related physical and chemical.When silk screen printing figure, make specific black
Degree carbon black forms the print material of certain viscosity, to complete the figure transfer of mode of printing.Printing solidification after, make specific blackness carbon black and
Stable bond is formed so that it is the ring meeting touch screen industry surveys requirement and printing precision between filler particles and the base material of specific refraction
Requirement.
The carbon black of the specific blackness used by 3.2 and the filler of specific refractive index can be given mileage and reach handset touch panel
Industry standard.This formula it is crucial that this carbon black selected colourity film forming after cover the strengthening glass of hollow out in ITO and ITO gap
After glass, making human eye observe, can not discover obvious aberration, principle is, specific blackness on the ito layer with in gap: as figure
Shown in 1;
In terms of Visual Observations Observations region from Fig. 1, observation indoor, outdoor, due to specific blackness and the use of the filler of specific refractive index, as
Shown in Fig. 2;
When in the case of specific blackness, as shown in Figure 3;
Understanding from the graph, when angle of incidence is identical, and refraction angle is identical, simultaneously in the case of specific blackness, we just do not see I by Visual Observations Observations
The level difference of TO layer and non-ITO layer, thus the effect of the shadow that reaches to disappear.In the case of specific blackness, ITO layer (reflects blue light)
Non-ITO layer (reflects white light), and two kinds of reflection light (utilize the absorption to light of the specific black powder) and allow reflection light in the case of specific blackness
Wave band reaches unanimity.Thus during eye-observation, reflection photochromism is also consistent.
Dispersant helps the uniform filling of the carbon black specific refractive index of specific blackness, is stable in the presence of in binder.Levelling agent,
Defoamer makes to reach smooth, planarization effects without steam bubble, levelling during ink film forming.
Above disclosed it is only one preferred embodiment of the present invention, certainly can not limit the right of the present invention with this
Scope, the equivalent variations therefore made according to the claims in the present invention, still belong to the scope that the present invention is contained.
Claims (2)
1. the insulating black ink eliminating ITO line shadow, it is characterised in that: include following composition by weight percentage: modified
Epoxy resin gloss oil 70~80%, insulation carbon black 15~18%, powder body 5%, dispersant 2~3%, levelling agent 1~2%, defoamer 1~
2%;Described modified epoxy gloss oil admittedly containing 65%, solvent DBE15%, solvent isophorone 20%.
2. the manufacture method of the insulating black ink of an elimination ITO line shadow as claimed in claim 1, it is characterised in that: include
Following steps:
Prepare gloss oil: first pour in Scattered Kettle by solvent DBE15 part, isophorone 20 parts, stirring at low speed, in whipping process,
Weigh 65 parts of modified epoxy solids, slowly pour in Scattered Kettle, improve rotating speed and rise to 1200 turns, continue 6 hours~8 little
Time solid be completely dissolved complete prepared A gloss oil;
Preparation mixing slurry: weigh 70 parts of A gloss oil in reactor, low speed 200 turns stirring, stir while at the uniform velocity add insulation carbon black
15%~18%, powder body 5%, dispersant 2%~3%, levelling agent 1%~2%, defoamer 1%~2%, stirring obtain for 20~30 minutes
Mixed slurry B;
Preparing finished product: mixed slurry B carries out after stirring sand milling, sand milling temperature controls at 40 DEG C-65 DEG C, 3 fineness of sand milling
Control to obtain finished product C in 3 μm~5 μm.