CN104312381A - Noise-reduction anti-rusting paint for power distribution cabinet and preparation method for noise-reduction anti-rusting paint - Google Patents
Noise-reduction anti-rusting paint for power distribution cabinet and preparation method for noise-reduction anti-rusting paint Download PDFInfo
- Publication number
- CN104312381A CN104312381A CN201410630407.2A CN201410630407A CN104312381A CN 104312381 A CN104312381 A CN 104312381A CN 201410630407 A CN201410630407 A CN 201410630407A CN 104312381 A CN104312381 A CN 104312381A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- noise
- power distribution
- distribution cabinet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a noise-reduction anti-rusting paint for a power distribution cabinet. The noise-reduction anti-rusting paint is characterized in that the noise-reduction anti-rusting paint is prepared from the following raw materials in parts by weight: 3 to 5 parts of natural iron red, 1 to 2 parts of lead pigment, 3 to 5 parts of boron mud powder, 2 to 3 parts of zinc cyanuric acid, 4 to 5 parts of tricresyl phosphate, 2 to 3 parts of phenyl phosphate ester, 2 to 3 parts of lanolin magnesium soap, 32 to 35 parts of E-51 epoxy resin, 20 to 24 parts of amino resin, 3 to 4 parts of tributyl methyl ether, 9 to 12 parts of dimethylbenzene, 5 to 7 parts of talc powder, 1 to 2 parts of anilino-methyl-triethoxysilane, 7 to 9 parts of methyl ethyl ketone and 4 to 7 parts of auxiliaries. According to the paint, the added auxiliaries have a good noise reduction effect, are highly dispersed without precipitation in the paint, and also have a good anti-rusting function, so that the service life of the power distribution cabinet is prolonged, and after the paint forms a film, the film is smooth and high in illumination resistance, and also has high humidity resistance, and potential safety hazards are reduced.
Description
Technical field
The present invention relates to a kind of paint and preparation method thereof, particularly a kind of power distribution cabinet noise reduction rust-inhibiting paint and preparation method thereof.
Background technology
The effect of power distribution cabinet is that distribution controls by power distribution to each load position, and short circuit, overload and electric leakage time carry out power-off protection.The frequent species of power distribution cabinet has the board-like power distribution cabinet of fixed face, protected type power distribution cabinet, drawer-type distribution box and power and lighting power distribution cabinet etc.Be in outdoor transformation cabinet work under bad environment, and noise when working is very large, bring very large constant to the resident family living in surrounding is in life, and harm humans is healthy.In general, the harm of noise to the mankind is mainly reflected in hearing damage; Noise can have a strong impact on auditory organ, even makes people lose hearing, common to all.But, have delicate inherence " contact " between ear and eyes, when function of noise is in auditory organ, also can by neural effect " involving " visual organ, make the eyesight weaken of people; Noise also has the cardiovascular systems of victimization, neural system, impact is slept, and causes the multiple harm such as tired.For at psychological aspects, first noise can cause sleep bad, attention can not be concentrated, the mental symptoms such as hypomnesis, then causes mood confusing, emotional lability, and even patience reduces, short-tempered, finally produces a series of diseases such as hypertension, ulcer, diabetes, this illness is called psychosomatic disease by psychology, means the disease on the health that caused by psychological factor.So there is the effect well reducing noise for the auxiliary agent of this situation paint interpolation of the present invention, improve the living environment of people to a great extent, and power distribution cabinet is in and outdoor often exposes to the sun and rain by wind, also should require to have the effect of the aspects such as good antirust, moistureproof, uvioresistant.
Summary of the invention
The object of this invention is to provide a kind of power distribution cabinet noise reduction rust-inhibiting paint and preparation method thereof.
In order to realize object of the present invention, the present invention is by following scheme implementation:
A kind of power distribution cabinet noise reduction rust-inhibiting paint, is made up of the raw material of following weight part: natural iron oxide red 3-5, lead pigment 1-2, boron mud powder 3-5, cyanuric acid zinc 2-3, tritolyl phosphate 4-5, phosphoric acid phenolic ester 2-3, lanolin magnesium soap 2-3, E-51 epoxy resin 32-35, aminoresin 20-24, three fourth MEE 3-4, dimethylbenzene 9-12, talcum powder 5-7, anilinomethyl triethoxysilane 1-2, methylethylketone 7-9, auxiliary agent 4-7;
Described auxiliary agent is made up of the raw material of following weight part: urotropine 3-5, tallow amine 3-4, benzotriazole 5-7, methyl acrylate 3-5, β-dimethyl-aminoethylmethacrylate 8-12,2,2,4-trimethylammonium-1,3-pentanediol mono isobutyrate 1-2, ethanol 15-20, shellac 4-6, organobentonite 8-12, fatty alcohol-polyoxyethylene ether 0.4-0.8, propylene glycol fatty acid ester 1-2, diethylenetriamine 1-2, di-t-butyl peroxide 1-2, corundum-mullite powder 7-11, glass fibre 7-10, carbon fiber 3-5, polyoxyethylene 2-4, deionized water 4-6; Preparation method is that organobentonite, corundum-mullite powder, shellac and ethanol are added in high-speed mixer by (1), high-speed stirring 10-20 minute, be heated to 60-80 ° of C, add diethylenetriamine, di-t-butyl peroxide, methyl acrylate and β-dimethyl-aminoethylmethacrylate again, continue stirring reaction 1-2 hour; (2) glass fibre, carbon fiber, fatty alcohol-polyoxyethylene ether, polyoxyethylene and deionized water are mixed, high speed shear forms liquid mixture; (3) product of step (2) to be added in fluidized-bed with Air Fluidized, to be sprayed on the product of step (1), then add all the other surplus materialss and fully grind.
A kind of power distribution cabinet noise reduction rust-inhibiting paint of the present invention, be made up of following concrete steps:
(1) natural iron oxide red, lead pigment, boron mud powder, talcum powder are added in dimethylbenzene and methylethylketone, ultrasonic disperse 20-30 minute, when being heated to 50-80 ° of C, add tritolyl phosphate, lanolin magnesium soap, auxiliary agent continuation stirring reaction 30-40 minute;
(2) product of step (1) is continued raised temperature to 70-90 ° of C, add E-51 epoxy resin, aminoresin, three fourth MEEs, anilinomethyl triethoxysilane, 1200-1400 rev/min of lower high-speed mixing stirring reaction 1-2 hour;
(3) surplus materials is added in the product of step (2), is added to grinding machine for grinding after mixing and is uniformly dispersed, filter and obtain the material that fineness is 20-40 μm, pack.
Advantage of the present invention is: the auxiliary agent that paint of the present invention adds has the function well reducing noise, and good dispersity in paint, not sedimentation, and there is excellent rust inhibition, extend the work-ing life of power distribution cabinet, after paint film forming, film is smooth, and resistance to light application time is long, also there is excellent humidity resistance, reduce potential safety hazard.
specific embodiments
Below by specific examples, the present invention is described in detail.
A kind of power distribution cabinet noise reduction rust-inhibiting paint, is made up of the raw material of following weight part (kilogram): natural iron oxide red 3, lead pigment 1, boron mud powder 3, cyanuric acid zinc 2, tritolyl phosphate 4, phosphoric acid phenolic ester 3, lanolin magnesium soap 2, E-51 epoxy resin 33, aminoresin 23, three fourth MEE 3, dimethylbenzene 10, talcum powder 5, anilinomethyl triethoxysilane 1, methylethylketone 8, auxiliary agent 6;
Described auxiliary agent is made up of the raw material of following weight part (kilogram): urotropine 3, tallow amine 4, benzotriazole 5, methyl acrylate 4, β-dimethyl-aminoethylmethacrylate 10,2,2,4-trimethylammonium-1,3-pentanediol mono isobutyrate 2, ethanol 18, shellac 4, organobentonite 10, fatty alcohol-polyoxyethylene ether 0.7, propylene glycol fatty acid ester 1, diethylenetriamine 1, di-t-butyl peroxide 1, corundum-mullite powder 7, glass fibre 8, carbon fiber 5, polyoxyethylene 4, deionized water 6; Preparation method is that organobentonite, corundum-mullite powder, shellac and ethanol are added in high-speed mixer by (1), high-speed stirring 10-20 minute, be heated to 60-80 ° of C, add diethylenetriamine, di-t-butyl peroxide, methyl acrylate and β-dimethyl-aminoethylmethacrylate again, continue stirring reaction 1-2 hour; (2) glass fibre, carbon fiber, fatty alcohol-polyoxyethylene ether, polyoxyethylene and deionized water are mixed, high speed shear forms liquid mixture; (3) product of step (2) to be added in fluidized-bed with Air Fluidized, to be sprayed on the product of step (1), then add all the other surplus materialss and fully grind.
A kind of power distribution cabinet noise reduction rust-inhibiting paint of the present invention, be made up of following concrete steps:
(1) natural iron oxide red, lead pigment, boron mud powder, talcum powder are added in dimethylbenzene and methylethylketone, ultrasonic disperse 20-30 minute, when being heated to 50-80 ° of C, add tritolyl phosphate, lanolin magnesium soap, auxiliary agent continuation stirring reaction 30-40 minute;
(2) product of step (1) is continued raised temperature to 70-90 ° of C, add E-51 epoxy resin, aminoresin, three fourth MEEs, anilinomethyl triethoxysilane, 1200-1400 rev/min of lower high-speed mixing stirring reaction 1-2 hour;
(3) surplus materials is added in the product of step (2), is added to grinding machine for grinding after mixing and is uniformly dispersed, filter and obtain the material that fineness is 20-40 μm, pack.
Paint outward appearance of the present invention is without the phenomenon of skinning and lump, snappiness is tested: 50mm, experiment of hardness: 3H, sticking power experiment (cross-hatching)≤1 grade, resistance to salt water experiment (sodium-chlor of 3%, 18d): bubble-free, nothing are peeled off, thermotolerance experiment (100 ± 2 DEG C, 4h): no sag, nothing cracking wrinkling without foaming, recombination loss factor: 20 ° of C:0.123,40 ° of C:0.138.
Claims (2)
1. a power distribution cabinet noise reduction rust-inhibiting paint, it is characterized in that, be made up of the raw material of following weight part: natural iron oxide red 3-5, lead pigment 1-2, boron mud powder 3-5, cyanuric acid zinc 2-3, tritolyl phosphate 4-5, phosphoric acid phenolic ester 2-3, lanolin magnesium soap 2-3, E-51 epoxy resin 32-35, aminoresin 20-24, three fourth MEE 3-4, dimethylbenzene 9-12, talcum powder 5-7, anilinomethyl triethoxysilane 1-2, methylethylketone 7-9, auxiliary agent 4-7;
Described auxiliary agent is made up of the raw material of following weight part: urotropine 3-5, tallow amine 3-4, benzotriazole 5-7, methyl acrylate 3-5, β-dimethyl-aminoethylmethacrylate 8-12,2,2,4-trimethylammonium-1,3-pentanediol mono isobutyrate 1-2, ethanol 15-20, shellac 4-6, organobentonite 8-12, fatty alcohol-polyoxyethylene ether 0.4-0.8, propylene glycol fatty acid ester 1-2, diethylenetriamine 1-2, di-t-butyl peroxide 1-2, corundum-mullite powder 7-11, glass fibre 7-10, carbon fiber 3-5, polyoxyethylene 2-4, deionized water 4-6; Preparation method is that organobentonite, corundum-mullite powder, shellac and ethanol are added in high-speed mixer by (1), high-speed stirring 10-20 minute, be heated to 60-80 ° of C, add diethylenetriamine, di-t-butyl peroxide, methyl acrylate and β-dimethyl-aminoethylmethacrylate again, continue stirring reaction 1-2 hour; (2) glass fibre, carbon fiber, fatty alcohol-polyoxyethylene ether, polyoxyethylene and deionized water are mixed, high speed shear forms liquid mixture; (3) product of step (2) to be added in fluidized-bed with Air Fluidized, to be sprayed on the product of step (1), then add all the other surplus materialss and fully grind.
2. a kind of power distribution cabinet noise reduction rust-inhibiting paint according to claim 1, is characterized in that, be made up of following concrete steps:
(1) natural iron oxide red, lead pigment, boron mud powder, talcum powder are added in dimethylbenzene and methylethylketone, ultrasonic disperse 20-30 minute, when being heated to 50-80 ° of C, add tritolyl phosphate, lanolin magnesium soap, auxiliary agent continuation stirring reaction 30-40 minute;
(2) product of step (1) is continued raised temperature to 70-90 ° of C, add E-51 epoxy resin, aminoresin, three fourth MEEs, anilinomethyl triethoxysilane, 1200-1400 rev/min of lower high-speed mixing stirring reaction 1-2 hour;
(3) surplus materials is added in the product of step (2), is added to grinding machine for grinding after mixing and is uniformly dispersed, filter and obtain the material that fineness is 20-40 μm, pack.