CN104310881A - Asbestos tile and preparation method thereof - Google Patents
Asbestos tile and preparation method thereof Download PDFInfo
- Publication number
- CN104310881A CN104310881A CN201410516637.6A CN201410516637A CN104310881A CN 104310881 A CN104310881 A CN 104310881A CN 201410516637 A CN201410516637 A CN 201410516637A CN 104310881 A CN104310881 A CN 104310881A
- Authority
- CN
- China
- Prior art keywords
- parts
- asbestos tile
- asbestos
- preparation
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an asbestos tile. The asbestos tile comprises the following components in parts by weight: 40 to 50 parts of cement, 30 to 40 parts of yellow sand, 10 to 20 parts of asbestos fibers, 5 to 10 parts of straws, 5 to 10 parts of coal gangue and 2 to 3 parts of thickening agent. The invention also discloses a preparation method of the asbestos tile. By reasonably selecting the components of the asbestos tile and reasonably proportioning the components, the prepared asbestos tile has the advantages of high strength, fire resistance, damp resistance, corrosion resistance, cold resistance, heat preservation, heat resistance, sound insulation, insulation and the like; moreover, the preparation method is simple and easy to produce.
Description
Technical field
The present invention relates to a kind of asbestos tile and preparation method thereof, belong to a watt manufacture technology field.
Background technology
Asbestos tile is roof flashing material, it have individual and effectively utilize that area is large, fire prevention, the advantage such as moistureproof, anticorrosion, heat-resisting, cold-resistant, light weight.The formula of traditional asbestos tile and making method utilize fibrous magnesium silicate and cement to form for raw material pressurizes through making sheet, is divided into large ripple, medium wave, small echo three kinds from specification, also has the herring-bone of covering ridge supporting with these three kinds watts respectively to carry on the back watt in addition.Traditional asbestos tile, at aspect of performance, cannot meet the requirement of system watt technology now.
Summary of the invention
For solving the deficiencies in the prior art, the object of the present invention is to provide asbestos tile of a kind of properties excellence and preparation method thereof.
For achieving the above object, the present invention is achieved by the following technical solutions:
A kind of asbestos tile, it is characterized in that, comprise following component, and the parts by weight of each component is respectively:
Cement: 40-50 part;
Yellow sand: 30-40 part;
Fibrous magnesium silicate: 10-20 part;
Stalk: 5-10 part;
Coal gangue: 5-10 part;
Tackifier: 2-3 part.
Preferably, described a kind of asbestos tile, comprises following component, and the parts by weight of each component are respectively:
Cement: 50 parts;
Yellow sand: 30 parts;
Fibrous magnesium silicate: 20 parts;
Stalk: 10 parts;
Coal gangue: 5 parts;
Tackifier: 3 parts;
Water: 70 parts.
Further, described tackifier are styrene-butadiene rubber(SBR).
And the preparation method of above-mentioned asbestos tile, it is characterized in that, concrete steps are: according to weight fraction ratio: add in stirrer by cement, yellow sand, fibrous magnesium silicate, stalk, coal gangue, tackifier, water, stir, then utilize after beating cloth device filtering excessive moisture and become base, utilize the compression moulding of vertical compression machine, after then air-dry, send into sintering oven to fire, after cooling, obtain asbestos tile.
And the sintering temperature of asbestos tile is 1100-1500 DEG C.
The invention has the beneficial effects as follows: the present invention is by reasonably choosing the component of asbestos tile, by each component good compatibility each other, the asbestos tile that the present invention is prepared has that intensity is high, fire prevention, moistureproof, anticorrosion, cold-proof, be incubated, heat-resisting, sound insulation, the advantage such as insulation, and preparation method is simple, be easy to produce.
Embodiment
Below in conjunction with embodiment, concrete introduction is carried out to the present invention.
embodiment 1
By cement: 40 parts; Yellow sand: 30 parts; Fibrous magnesium silicate: 10 parts; Stalk: 10 parts; Coal gangue: 10 parts; Styrene-butadiene rubber(SBR): 2 parts add in stirrer, stir, then utilizes after beating cloth device filtering excessive moisture and becomes base, utilize the compression moulding of vertical compression machine, and after then air-dry, feeding sintering oven is fired, and sintering temperature is 1100 DEG C, obtains asbestos tile after cooling.
embodiment 2
By cement: 50 parts; Yellow sand: 40 parts; Fibrous magnesium silicate: 20 parts; Stalk: 5 parts; Coal gangue: 5 parts; Styrene-butadiene rubber(SBR): 3 parts add in stirrer, stir, then utilizes after beating cloth device filtering excessive moisture and becomes base, utilize the compression moulding of vertical compression machine, and after then air-dry, feeding sintering oven is fired, and sintering temperature is 1500 DEG C, obtains asbestos tile after cooling.
embodiment 3
By cement: 45 parts; Yellow sand: 35 parts; Fibrous magnesium silicate: 15 parts; Stalk: 8 parts; Coal gangue: 8 parts; Styrene-butadiene rubber(SBR): 3 parts add in stirrer, stir, then utilizes after beating cloth device filtering excessive moisture and becomes base, utilize the compression moulding of vertical compression machine, and after then air-dry, feeding sintering oven is fired, and sintering temperature is 1400 DEG C, obtains asbestos tile after cooling.
embodiment 4
By cement: 50 parts; Yellow sand: 30 parts; Fibrous magnesium silicate: 20 parts; Stalk: 10 parts; Coal gangue: 5 parts; Styrene-butadiene rubber(SBR): 3 parts; Water: 70 parts; Add in stirrer, stir, then utilize after beating cloth device filtering excessive moisture and become base, utilize the compression moulding of vertical compression machine, after then air-dry, feeding sintering oven is fired, and sintering temperature is 1300 DEG C, obtains asbestos tile after cooling.
The advantages such as the asbestos tile that above-described embodiment 1-4 prepares has that intensity is high, fire prevention, moistureproof, anticorrosion, cold-proof, insulation, heat-resisting, sound insulation, insulation, and preparation method is simple, is easy to production.
The present invention is illustrated according to above-described embodiment, should be appreciated that above-described embodiment does not limit the present invention in any form, and all employings are equal to replacement or the technical scheme that obtains of equivalent transformation mode, all drop within protection scope of the present invention.
Claims (5)
1. an asbestos tile, is characterized in that, comprises following component, and the parts by weight of each component are respectively:
Cement: 40-50 part;
Yellow sand: 30-40 part;
Fibrous magnesium silicate: 10-20 part;
Stalk: 5-10 part;
Coal gangue: 5-10 part;
Tackifier: 2-3 part.
2. a kind of asbestos tile according to claim 1, is characterized in that, comprises following component, and the parts by weight of each component are respectively:
Cement: 50 parts;
Yellow sand: 30 parts;
Fibrous magnesium silicate: 20 parts;
Stalk: 10 parts;
Coal gangue: 5 parts;
Tackifier: 3 parts;
Water: 70 parts.
3. a kind of asbestos tile according to claim 1, is characterized in that, described tackifier are styrene-butadiene rubber(SBR).
4. the preparation method of the asbestos tile described in any one of a claim 1-3 claim, it is characterized in that, concrete steps are: according to weight fraction ratio: add in stirrer by cement, yellow sand, fibrous magnesium silicate, stalk, coal gangue, tackifier, water, stir, then utilize after beating cloth device filtering excessive moisture and become base, utilize the compression moulding of vertical compression machine, after then air-dry, send into sintering oven to fire, after cooling, obtain asbestos tile.
5. the preparation method of asbestos tile according to claim 4, is characterized in that, the sintering temperature of asbestos tile is 1100-1500 DEG C.