CN104294581A - 一种竹纤维的碱性处理方法 - Google Patents

一种竹纤维的碱性处理方法 Download PDF

Info

Publication number
CN104294581A
CN104294581A CN201410582518.0A CN201410582518A CN104294581A CN 104294581 A CN104294581 A CN 104294581A CN 201410582518 A CN201410582518 A CN 201410582518A CN 104294581 A CN104294581 A CN 104294581A
Authority
CN
China
Prior art keywords
bamboo fibre
bamboo fiber
treatment method
bamboo
basic treatment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410582518.0A
Other languages
English (en)
Inventor
王小飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU WEIFENG TEXTILE Co Ltd
Original Assignee
CHANGSHU WEIFENG TEXTILE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU WEIFENG TEXTILE Co Ltd filed Critical CHANGSHU WEIFENG TEXTILE Co Ltd
Priority to CN201410582518.0A priority Critical patent/CN104294581A/zh
Publication of CN104294581A publication Critical patent/CN104294581A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种竹纤维的碱性处理方法,将竹纤维真空干燥12~48h,与碱性溶液以1:10~20的质量比进行混合,30~40℃水浴反应60~90min,取出0℃以下冷冻干燥24~48h,再真空干燥10~16h;本发明的竹纤维的碱性处理方法,以碱性溶液处理竹纤维,提高了其与聚丙烯复合时的界面相容性,使得竹纤维聚丙烯复合材料得到更广泛的应用。

Description

一种竹纤维的碱性处理方法
技术领域
本发明属于针纺织技术领域,涉及一种竹纤维的处理方法,具体涉及一种竹纤维的碱性处理方法。
背景技术
竹原纤维是一种全新的天然纤维,是采用物理、化学相结合的方法制取的天然竹纤维,天然竹原纤维与竹浆纤维有着本质的区别,竹原纤维属于天然纤维,竹浆纤维属于化学纤维。竹原纤维的研制成功标志着又一天然纤维的诞生,其符合国家产业发展政策。
竹纤维纵向表面光滑、均一,有多条较浅的沟槽;横截面接近椭圆形,边沿不规则。这种表面结构使得竹纤维具有一定的抱合力,有利于纤维的成纱。
其横截面为高度中空的特殊结构,能在瞬间吸引大量水分和透过大量气体,纵向平直,表面沟槽形成的孔隙能够产生较强的毛细管效应,使得竹纤维具有良好的吸湿放湿性能。
竹子中的天然抗菌成分,始终能够结合在纤维素大分子上。所以竹纤维织物经反复洗涤、日晒也不会失去其独特的抗菌性能。
竹纤维含有叶绿素铜钠,使其纺织品具有良好的除臭作用,叶绿素铜钠还是安全、优良的紫外线吸收剂,可在一定程度减小紫外线对人体的伤害。有实验表明:竹纤维的紫外线穿透率为0.6%,是棉的41.6倍。竹纤维能够100%降解,是绿色环保产品。
竹纤维与棉纤维混纺,可改善竹纤维的可纺性、抗起毛起球性、尺寸稳定性及丰满感等性能,并赋予产品独特的丝质感、透气性、悬垂性、柔软性、舒适性。
竹纤维与羊毛混纺可以生产轻薄干爽型织物,产品具有手感滑爽、悬垂飘逸、舒适凉爽等特点,适合于夏季服用,突破了毛织物的服用局限性,丰富了毛纺面料品种,提高面料档次和附加值。
因此竹纤维产品可广泛应用于内衣裤、衬衫、运动装和婴儿服装,尤其是夏季各种时装及床单、被褥、毛巾、浴巾等家纺产品的理想面料。
塑料的广泛使用,使环境负荷迅速增加,天然复合材料受到广泛关注。竹塑复合材料兼有竹材和塑料的优点。聚丙烯(PP)/竹纤维复合材料的开发与应用,可达到节省原料资源,保护环境的目的,但具有极性基团的竹纤维与非极性的PP界面相容性差,使其复合材料应用受到局限。
发明内容
有鉴于此,本发明的目的在于提供一种竹纤维的碱性处理方法,以提高竹纤维与聚丙烯复合时的界面相容性。
为实现上述目的,本发明提供如下技术方案:
一种竹纤维的碱性处理方法,包括下述步骤:
将竹纤维真空干燥12~48h,与碱性溶液以1:10~20的质量比进行混合,30~40℃水浴反应60~90min,取出0℃以下冷冻干燥24~48h,再真空干燥10~16h。
优选的,所述的竹纤维细度为100~300目。
优选的,将竹纤维真空干燥24h。
优选的,所述的碱性溶液为氢氧化钠溶液或氢氧化钾溶液。
进一步的,所述的碱性溶液浓度为1~10wt%。
更进一步的,所述的碱性溶液浓度为5wt%。
优选的,将竹纤维与碱性溶液混合后,35℃水浴反应80min。
优选的,取出0℃以下冷冻干燥36h,再真空干燥12h。
本发明的竹纤维的碱性处理方法,以碱性溶液处理竹纤维,提高了其与聚丙烯复合时的界面相容性,使得竹纤维聚丙烯复合材料得到更广泛的应用。
具体实施方式
下面将对本发明实施例中的技术方案进行详细的描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动的前提下所获得的所有其他实施例,都属于本发明保护的范围。
实施例1
将100目竹纤维真空干燥12h,与1wt%氢氧化钠溶液以1:20的质量比进行混合,30℃水浴反应90min,取出0℃以下冷冻干燥24h,再真空干燥16h,备用,与pp进行复合后纺丝。
实施例2
将300目竹纤维真空干燥48h,与10%氢氧化钾溶液以1:10的质量比进行混合,40℃水浴反应60min,取出0℃以下冷冻干燥48h,再真空干燥10h,备用,与pp进行复合后纺丝。
实施例3
将200目竹纤维真空干燥24h,与5wt%氢氧化钠溶液以1:15的质量比进行混合,35℃水浴反应80min,取出0℃以下冷冻干燥36h,再真空干燥12h,备用,与pp进行复合后纺丝。
于本领域技术人员而言,显然本发明不限于上述示范性实施例的细节,而且在不背离本发明的精神或基本特征的情况下,能够以其他的具体形式实现本发明。因此,无论从哪一点来看,均应将实施例看作是示范性的,而且是非限制性的,本发明的范围由所附权利要求而不是上述说明限定,因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
此外,应当理解,虽然本说明书按照实施方式加以描述,但并非每个实施方式仅包含一个独立的技术方案,说明书的这种叙述方式仅仅是为清楚起见,本领域技术人员应当将说明书作为一个整体,各实施例中的技术方案也可以经适当组合,形成本领域技术人员可以理解的其他实施方式。

Claims (8)

1.一种竹纤维的碱性处理方法,其特征在于,包括下述步骤:
将竹纤维真空干燥12~48h,与碱性溶液以1:10~20的质量比进行混合,30~40℃水浴反应60~90min,取出0℃以下冷冻干燥24~48h,再真空干燥10~16h。
2.根据权利要求1所述的竹纤维的碱性处理方法,其特征在于:所述的竹纤维细度为100~300目。
3.根据权利要求1所述的竹纤维的碱性处理方法,其特征在于:将竹纤维真空干燥24h。
4.根据权利要求1所述的竹纤维的碱性处理方法,其特征在于:所述的碱性溶液为氢氧化钠溶液或氢氧化钾溶液。
5.根据权利要求4所述的竹纤维的碱性处理方法,其特征在于:所述的碱性溶液浓度为1~10wt%。
6.根据权利要求5所述的竹纤维的碱性处理方法,其特征在于:所述的碱性溶液浓度为5wt%。
7.根据权利要求1所述的竹纤维的碱性处理方法,其特征在于:将竹纤维与碱性溶液混合后,35℃水浴反应80min。
8.根据权利要求1所述的竹纤维的碱性处理方法,其特征在于:取出0℃以下冷冻干燥36h,再真空干燥12h。
CN201410582518.0A 2014-10-27 2014-10-27 一种竹纤维的碱性处理方法 Pending CN104294581A (zh)