CN104292634A - Stable acid and alkali resistant plastic - Google Patents
Stable acid and alkali resistant plastic Download PDFInfo
- Publication number
- CN104292634A CN104292634A CN201410517717.3A CN201410517717A CN104292634A CN 104292634 A CN104292634 A CN 104292634A CN 201410517717 A CN201410517717 A CN 201410517717A CN 104292634 A CN104292634 A CN 104292634A
- Authority
- CN
- China
- Prior art keywords
- parts
- acid
- glycerol
- alkali
- resistant plastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to stable acid and alkali resistant plastic which is prepared from the following components in parts by weight: 8-14 parts of polypropylene, 3-7 parts of calcium carbonate, 6-10 parts of unsaturated polyester resin, 3-5 parts of an initiator, 3-9 parts of glycerol triglycerate, 5-9 parts of glycerol, 1-5 parts of stearic acid, 3-5 parts of a flame retardant, 4-8 parts of phosphate and 6-8 parts of reinforced fibers. The stable acid and alkali resistant plastic provided by the invention has the beneficial effects that the plastic is strong in stability, has good acid and alkali resistance and can be normally used under severe environments.
Description
Technical field
The present invention relates to a kind of stable acid and alkali-resistance plastics.
Background technology
Plastics take monomer as raw material, by the macromolecular compound of addition polymerization or polycondensation polymerized, is commonly called as plastics or resin.Can freely change composition and body styles.Be made up of additives such as synthetic resins and filler, softening agent, stablizer, lubricant, colorants.Present most plastics resistance to chemical attack, transparent or translucent, quality are light, and produce cheap.But present most of plastics all can not meet the requirement of mechanical property, intensity is poor, toughness is also bad, under the occasion of some high strength, can not meet need of work.Therefore a kind of plastics with good mechanical properties of high strength are needed.
Summary of the invention
For the deficiencies in the prior art, the technical problem to be solved in the present invention is, provides a kind of plastics, and stability is strong, has the ability of good acid and alkali-resistance, can normally use in the presence of a harsh environment.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of stable acid and alkali-resistance plastics, and following component consumption is with weight parts:
Polypropylene 8-14 part, calcium carbonate 3-7 part, unsaturated polyester resin 6-10 part, initiator 3-5 part, glycerol glycerinate 3-9 part, glycerol 5-9 part, stearic acid 1-5 part, fire retardant 3-5 part, phosphoric acid salt 4-8 part, fortifying fibre 6-8 part.
The invention has the beneficial effects as follows, plastics of the present invention, stability is strong, has the ability of good acid and alkali-resistance, can normally use in the presence of a harsh environment.
Embodiment
embodiment 1
Stable acid and alkali-resistance plastics, following component consumption is with weight parts:
Polypropylene 8 parts, 3 parts, calcium carbonate, unsaturated polyester resin 6 parts, initiator 3 parts, glycerol glycerinate 3 parts, glycerol 5 parts, stearic acid 1 part, fire retardant 3 parts, phosphoric acid salt 4 parts, fortifying fibre 6 parts.
embodiment 2
Stable acid and alkali-resistance plastics, following component consumption is with weight parts:
Polypropylene 14 parts, 7 parts, calcium carbonate, unsaturated polyester resin 10 parts, initiator 5 parts, glycerol glycerinate 9 parts, glycerol 9 parts, stearic acid 5 parts, fire retardant 5 parts, phosphoric acid salt 8 parts, fortifying fibre 8 parts.
Claims (1)
1. stable acid and alkali-resistance plastics, is characterized in that: following component consumption is with weight parts:
Polypropylene 8-14 part, calcium carbonate 3-7 part, unsaturated polyester resin 6-10 part, initiator 3-5 part, glycerol glycerinate 3-9 part, glycerol 5-9 part, stearic acid 1-5 part, fire retardant 3-5 part, phosphoric acid salt 4-8 part, fortifying fibre 6-8 part.