CN103275563B - Chlorinated rubber fireproof paint for wood material - Google Patents
Chlorinated rubber fireproof paint for wood material Download PDFInfo
- Publication number
- CN103275563B CN103275563B CN201310196995.9A CN201310196995A CN103275563B CN 103275563 B CN103275563 B CN 103275563B CN 201310196995 A CN201310196995 A CN 201310196995A CN 103275563 B CN103275563 B CN 103275563B
- Authority
- CN
- China
- Prior art keywords
- parts
- chlorinated rubber
- wood material
- rubber fireproof
- fireproof paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses chlorinated rubber fireproof paint for a wood material, which is characterized by being mainly prepared from the following raw materials in parts by weight: 60-66 parts of chlorinated rubber, 25 parts of bamboo short fiber, 15 parts of methyl isobutyl ketone, 12 parts of dicumyl peroxide, 5 parts of potassium tripolyphosphate, 20 parts of benzoyl peroxide, 10 parts of phenol, 10-13 parts of chlorinated paraffin wax, 12 parts of urea and 15 parts of kaolin. Industrial tests prove that the product disclosed by the invention can perform coating treatment on the surface of a wood material, and the formed chlorinated rubber fireproof coating has the remarkable characteristics of high binding strength and good fire retardance; and no organic solvent is volatilized in the curing process, thus achieving the effect of environment friendliness.
Description
Technical field
The present invention relates to a kind of wood materials chlorinated rubber frie retardant coating.
Technical background
Various new building structural materials and finishing material although the world today has developed production, because timber has the good characteristic of its uniqueness, wooden facing gives a kind of special graceful perception, and this is that other finishing material cannot be by comparison.So timber, in construction work especially furnishing fields, remains consequence.Because material of construction consumption is very large, directly have influence on the cost of engineering, usual building materials expense accounts for the over half of project total cost, therefore when considering technical feature, must take into account economy.But tree growth is slow, and China is again one of country of poor forest resources, this need use a large amount of timber with the economic construction of China's high speed development, the contradiction that formation becomes increasingly conspicuous.Therefore, in construction work, timber must be used economically, by strengthening process such as the preservation of timber against decay, mildew-resistant, fire prevention or waterproof, make it have environmental compatibility widely, weather resistance and using function adaptability good, extend working life, also and will pollute little to the toxic side effect of human body, visual performance is good simultaneously.But existing wood materials is easy to be ignited under the environment of naked light, may cause serious fire.So need the surface-coated one deck frie retardant coating at timber, be used for improving the security used.
Summary of the invention
The present invention seeks to overcome the deficiencies in the prior art, a kind of wood materials chlorinated rubber frie retardant coating is provided.
For solving the problem, technical scheme provided by the invention is: a kind of wood materials chlorinated rubber frie retardant coating, it is characterized in that it is mainly made up according to weight proportion of following raw materials according: 60-66 part chlorinated rubber, 25 parts of bamboo staple fibres, 15 parts of mibks, 12 parts of dicumyl peroxides, 5 parts of Potassium tripolyphosphates, 20 parts of benzoyl peroxides, 10 parts of phenol, 10-13 part clorafin, 12 parts of urea and 15 parts of kaolin.
Also containing 11-15 part phosphalugel and 8-10 part Dyhard RU 100.
Beneficial effect of the present invention: prove through commerical test, carries out covering with paint process to the surface of wood materials, and the chlorinated rubber fire protection coating of formation has that cohesive strength is high, the distinguishing feature of good flame resistance, and organic solvent-free volatilization in the curing process, environmental protection.
Embodiment
Embodiment 1
A kind of wood materials chlorinated rubber frie retardant coating to be stirred by stirrer high speed dispersion according to weight proportion by following raw materials according and makes: 60-66 part chlorinated rubber, 25 parts of bamboo staple fibres, 15 parts of mibks, 12 parts of dicumyl peroxides, 5 parts of Potassium tripolyphosphates, 20 parts of benzoyl peroxides, 10 parts of phenol, 10-13 part clorafin, 12 parts of urea and 15 parts of kaolin.
Embodiment 2
A kind of wood materials chlorinated rubber frie retardant coating to be stirred by stirrer high speed dispersion according to weight proportion by following raw materials according and makes: 60-66 part chlorinated rubber, 25 parts of bamboo staple fibres, 15 parts of mibks, 12 parts of dicumyl peroxides, 5 parts of Potassium tripolyphosphates, 20 parts of benzoyl peroxides, 10 parts of phenol, 10-13 part clorafin, 12 parts of urea, 15 parts of kaolin, 11-15 part phosphalugel and 8-10 part Dyhard RU 100.
Embodiment 3
The basic mechanical design feature detected result of product prepared by the present invention is as following table 1:
Table 1
| Project | Technical indicator |
| Water regain/(g/10mi n) | ≤1.7 |
| Alkali resistance (48h) | Without exception |
| Flame retardant resistance (charing height), m(A class) | 0.40-0.41 |
| Water tolerance (96h) | Without exception |
| Mean particle size, μm | 75-83 |
| Cohesive strength/MPa | Standard state |
Claims (2)
1. a wood materials chlorinated rubber frie retardant coating, it is characterized in that it is mainly made up according to weight proportion of following raw materials according: 60-66 part chlorinated rubber, 25 parts of bamboo staple fibres, 15 parts of mibks, 12 parts of dicumyl peroxides, 5 parts of Potassium tripolyphosphates, 20 parts of benzoyl peroxides, 10 parts of phenol, 10-13 part clorafin, 12 parts of urea and 15 parts of kaolin.
2. a kind of wood materials chlorinated rubber frie retardant coating according to claim 1, is characterized in that also containing 11-15 part phosphalugel and 8-10 part Dyhard RU 100.