CN103275588B - A kind of Furan resin fireproof paint for wood material - Google Patents
A kind of Furan resin fireproof paint for wood material Download PDFInfo
- Publication number
- CN103275588B CN103275588B CN201310196876.3A CN201310196876A CN103275588B CN 103275588 B CN103275588 B CN 103275588B CN 201310196876 A CN201310196876 A CN 201310196876A CN 103275588 B CN103275588 B CN 103275588B
- Authority
- CN
- China
- Prior art keywords
- parts
- wood material
- fireproof paint
- furan resin
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of Furan resin fireproof paint for wood material, it is characterized in that it is mainly made up according to weight proportion of following raw materials according: 180-190 part furane resin, 20-25 part lime, 15-20 part mibk, 12 parts of dicumyl peroxides, 15 parts of Potassium tripolyphosphates, 15-20 part dicumyl peroxide, 8-10 part Dyhard RU 100,20-22 part barium sulfate, 10-12 part phenol, 10-13 part clorafin, 12-16 part urea and 15 parts of zinc oxide.The present invention proves through commerical test, carries out covering with paint process to the surface of wood materials, and the furane resin fire protection coating of formation has that cohesive strength is high, the distinguishing feature of good flame resistance, and organic solvent-free volatilization in the curing process, environmental protection.
Description
Technical field
The present invention relates to a kind of Furan resin fireproof paint for wood material.
Technical background
Various new building structural materials and finishing material although the world today has developed production, because timber has the good characteristic of its uniqueness, wooden facing gives a kind of special graceful perception, and this is that other finishing material cannot be by comparison.So timber, in construction work especially furnishing fields, remains consequence.Because material of construction consumption is very large, directly have influence on the cost of engineering, usual building materials expense accounts for the over half of project total cost, therefore when considering technical feature, must take into account economy.But tree growth is slow, and China is again one of country of poor forest resources, this need use a large amount of timber with the economic construction of China's high speed development, the contradiction that formation becomes increasingly conspicuous.Therefore, in construction work, timber must be used economically, by strengthening process such as the preservation of timber against decay, mildew-resistant, fire prevention or waterproof, make it have environmental compatibility widely, weather resistance and using function adaptability good, extend working life, also and will pollute little to the toxic side effect of human body, visual performance is good simultaneously.But existing wood materials is easy to be ignited under the environment of naked light, may cause serious fire.So need the surface-coated one deck frie retardant coating at timber, be used for improving the security used.
Summary of the invention
The present invention seeks to, in order to overcome the deficiencies in the prior art, to provide a kind of Furan resin fireproof paint for wood material.
For solving the problem, technical scheme provided by the invention is: a kind of Furan resin fireproof paint for wood material, it is characterized in that it is mainly made up according to weight proportion of following raw materials according: 180-190 part furane resin, 20-25 part lime, 15-20 part mibk, 12 parts of dicumyl peroxides, 15 parts of Potassium tripolyphosphates, 15-20 part dicumyl peroxide, 8-10 part Dyhard RU 100,20-22 part barium sulfate, 10-12 part phenol, 10-13 part clorafin, 12-16 part urea and 15 parts of zinc oxide.
Also containing 11-15 part phosphalugel and 10-12 part stearic acid.
Beneficial effect of the present invention: prove through commerical test, carries out covering with paint process to the surface of wood materials, and the furane resin fire protection coating of formation has that cohesive strength is high, the distinguishing feature of good flame resistance, and organic solvent-free volatilization in the curing process, environmental protection.
Embodiment
Embodiment 1
A kind of Furan resin fireproof paint for wood material to be stirred by stirrer high speed dispersion according to weight proportion by following raw materials according and makes: 180-190 part furane resin, 20-25 part lime, 15-20 part mibk, 12 parts of dicumyl peroxides, 15 parts of Potassium tripolyphosphates, 15-20 part dicumyl peroxide, 8-10 part Dyhard RU 100,20-22 part barium sulfate, 10-12 part phenol, 10-13 part clorafin, 12-16 part urea and 15 parts of zinc oxide.
Embodiment 2
A kind of Furan resin fireproof paint for wood material to be stirred by stirrer high speed dispersion according to weight proportion by following raw materials according and makes: 180-190 part furane resin, 20-25 part lime, 15-20 part mibk, 12 parts of dicumyl peroxides, 15 parts of Potassium tripolyphosphates, 15-20 part dicumyl peroxide, 8-10 part Dyhard RU 100,20-22 part barium sulfate, 10-12 part phenol, 10-13 part clorafin, 12-16 part urea, 15 parts of zinc oxide, 11-15 part phosphalugel and 10-12 part stearic acid.
Embodiment 3
The basic mechanical design feature detected result of product prepared by the present invention is as following table 1:
Table 1
| Project | Technical indicator |
| Water regain/(g/10mi n) | ≤1.7 |
| Alkali resistance (48h) | Without exception |
| Flame retardant resistance (charing height), m(A class) | 0.38-0.41 |
| Water tolerance (96h) | Without exception |
| Mean particle size, μm | 75-78 |
| Cohesive strength/MPa | Standard state |
Claims (2)
1. a Furan resin fireproof paint for wood material, it is characterized in that it is mainly made up according to weight proportion of following raw materials according: 180-190 part furane resin, 20-25 part lime, 15-20 part mibk, 15 parts of Potassium tripolyphosphates, 27-32 part dicumyl peroxide, 8-10 part Dyhard RU 100,20-22 part barium sulfate, 10-12 part phenol, 10-13 part clorafin, 12-16 part urea and 15 parts of zinc oxide.
2. a kind of Furan resin fireproof paint for wood material according to claim 1, is characterized in that also containing 11-15 part phosphalugel and 10-12 part stearic acid.