CN1042811C - Method for prodn. of composite decoration board made of bamboo and china fir wood - Google Patents
Method for prodn. of composite decoration board made of bamboo and china fir wood Download PDFInfo
- Publication number
- CN1042811C CN1042811C CN94117289A CN94117289A CN1042811C CN 1042811 C CN1042811 C CN 1042811C CN 94117289 A CN94117289 A CN 94117289A CN 94117289 A CN94117289 A CN 94117289A CN 1042811 C CN1042811 C CN 1042811C
- Authority
- CN
- China
- Prior art keywords
- china fir
- bamboo
- decoration board
- board made
- mentioned
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a composite decorative board made of bamboo and China fir wood, which is a decorative board formed by gluing treated bamboo chips and treated fir wood strips. A making method of the composite decorative board has 16 process flows of sawing, chipping, rough milling, mould proof and vermin proof treatment, bleaching, baking, finish milling, sizing, gluing, secondary mould proof and vermin proof treatment, drying, planing, finish planing, cutting, rabbetting, etc. The product of the present invention has the advantages of high strength, favorable abrasive resistance, fluent texture, clarity, beautiful appearance, smooth and clean and soft color, light and tough material, moisture resistance, easy drying, thermal protection and heat radiation, etc.
Description
The present invention relates to the production technology of composite decorating board, particularly relate to a kind of production method of composite decoration board made of bamboo and China fir wood.
Along with living standards of the people improve, people require more and more higher to interior decoration, indoor floor and dado decoration etc. have entered huge numbers of families, and various ornament materials are answered people's demand and given birth to, and than relatively large employing marble, steel brick, ceramic tile, raised flooring etc. are arranged, our province mountain area forest tree resource is abundant, wherein especially with aboundresources such as bamboo, China firs, the bamboo China fir resource of fully developing mountain areas develops local economy, improving the people's livelihood, is a crucial economic development problem.
The objective of the invention is to seek mountain area bamboo China fir resource, the method for development and production composite decoration board made of bamboo and China fir wood of making full use of.
The object of the present invention is achieved like this, and the production method of composite decoration board made of bamboo and China fir wood may further comprise the steps in regular turn:
1) at first use sawing machine sawed-off respectively mao bamboon and China fir;
2) use the fragmentation machine to above-mentioned sawed-off mao bamboon and China fir difference fragmentation;
3) with rough milling machine the mao bamboon and the China fir of above-mentioned fragmentation are rough milled respectively;
4) carry out anti-mould and anti-moth and handle, used pharmaceutical formulation is:
Carbendazim 1.2% (weight ratio)+alum 2%+ potassium chloride 3 ‰+penta sodium pentachlorophenate 0.3% with the running water dissolving, was put into boiling 30 minutes (with fuel or feeding Steam Heating) then;
5) bleaching, with 5% bleaching powder+sodium pyrosulfite 1%, soak at room temperature 5 hours;
6) oven dry, sulfur, the spatial concentration of pressing the 10g/ cubic meter, and under 75～85 ℃ of conditions, dried about 30 hours, make moisture＜13% of bamboo chip and China fir;
7) with the finish-milling machine bamboo chip and the China fir of above-mentioned oven dry carried out finish-milling respectively;
8) respectively to the bamboo chip and the China fir applying glue of above-mentioned finish-milling, the glue prescription is:
Urea-formaldehyde glue+1.5% curing agent+0.3% paraffin wax emulsion+0.02% melamine; Glue-spread is 100～130g/ square centimeter, with glue spreader respectively to the bamboo chip and the China fir applying glue of above-mentioned finish-milling.
9) above-mentioned applying glue bamboo chip and applying glue China fir glue together the formation composite decoration board made of bamboo and China fir wood; The gummed process is: with electrothermal hot press or steam hot pressing, plus-pressure 18Kg/ square centimeter, be 15 minutes pressing time.
In order to make the different size specification requirement to this product of composite decoration board made of bamboo and China fir wood better quality and society, the present invention also proposes further to handle the production method of improving composite decoration board made of bamboo and China fir wood, and its method may further comprise the steps in regular turn:
10) composite decoration board made of bamboo and China fir wood that gummed is formed carries out the anti-mould and anti-moth processing second time, brushes on four sides with 2% sodium fluoride aqueous solution;
11) the composite decoration board made of bamboo and China fir wood drying that above-mentioned anti-mould and anti-moth is handled under 70～85 ℃ of conditions, was dried 12 hours, and moisture content is controlled at＜and 13%;
12) with planer the composite decoration board made of bamboo and China fir wood of above-mentioned oven dry is carried out planer;
13) with the adjustable cast iron planes machine composite decoration board made of bamboo and China fir wood of above-mentioned planer is carried out adjustable cast iron planes;
14) the composite decoration board made of bamboo and China fir wood of above-mentioned adjustable cast iron planes on request size block;
15) mill out technology groove with the composite decoration board made of bamboo and China fir wood tongue and groove of tongue and groove machine, and in the bottom to blocking.Remaining mass check back packing is entered the storehouse.
The present invention compares as wooden composite decorating board or bamboo composite decorating board with existing other has following advantage:
1. intensity is big, and wearability is good;
2. civilian texture is perfectly straight, and is clear attractive in appearance, and color is bright and clean soft;
3. China fir material material is gently tough, moisture-proof, and easily dry, warming, bamboo is easily dispelled the heat.
Claims (2)
1, the production method of composite decoration board made of bamboo and China fir wood may further comprise the steps in regular turn:
1) at first use sawing machine sawed-off respectively mao bamboon and China fir;
2) use the fragmentation machine to above-mentioned sawed-off mao bamboon and China fir difference fragmentation;
3) with rough milling machine the mao bamboon and the China fir of above-mentioned fragmentation are rough milled respectively;
4) carry out anti-mould and anti-moth and handle, used pharmaceutical formulation is:
Carbendazim 1.2% (weight ratio)+alum 2%+ potassium chloride 3 ‰+penta sodium pentachlorophenate 0.3% with the running water dissolving, was put into boiling 30 minutes (with fuel or feeding Steam Heating) then;
5) bleaching, with 5% bleaching powder+sodium pyrosulfite 1%, soak at room temperature 5 hours;
6) oven dry, sulfur, the spatial concentration of pressing the 10g/ cubic meter, and under 75～85 ℃ of conditions, dried about 30 hours, make moisture＜13% of bamboo chip and China fir;
7) with the finish-milling machine bamboo chip and the China fir of above-mentioned oven dry carried out finish-milling respectively;
8) respectively to the bamboo chip and the China fir applying glue of above-mentioned finish-milling, the glue prescription is:
Urea-formaldehyde glue+1.5% curing agent+0.3% paraffin wax emulsion+0.02% melamine; Glue-spread is 100～130g/ square centimeter, with glue spreader respectively to the bamboo chip and the China fir applying glue of above-mentioned finish-milling;
9) above-mentioned applying glue bamboo chip and applying glue China fir glue together the formation composite decoration board made of bamboo and China fir wood; The gummed process is: with electrothermal hot press or steam hot pressing, plus-pressure 18Kg/ square centimeter, be 15 minutes pressing time.
2, the production method of composite decoration board made of bamboo and China fir wood according to claim 1 is characterized by in regular turn and may further comprise the steps:
10) composite decoration board made of bamboo and China fir wood that gummed is formed carries out the anti-mould and anti-moth processing second time, brushes on four sides with 2% sodium fluoride aqueous solution;
11) the composite decoration board made of bamboo and China fir wood drying that above-mentioned anti-mould and anti-moth is handled under 70～85 ℃ of conditions, was dried 12 hours, and moisture content is controlled at＜and 13%;
12) with planer the composite decoration board made of bamboo and China fir wood of above-mentioned oven dry is carried out planer;
13) with the adjustable cast iron planes machine composite decoration board made of bamboo and China fir wood of above-mentioned planer is carried out adjustable cast iron planes;
14) the composite decoration board made of bamboo and China fir wood of above-mentioned adjustable cast iron planes on request size block;
15) mill out technology groove with the composite decoration board made of bamboo and China fir wood tongue and groove of tongue and groove machine, and in the bottom to blocking.