CN105904560A - Production technique of corrosion-resistant solid wood frame - Google Patents

Production technique of corrosion-resistant solid wood frame Download PDF

Info

Publication number
CN105904560A
CN105904560A CN201610268439.1A CN201610268439A CN105904560A CN 105904560 A CN105904560 A CN 105904560A CN 201610268439 A CN201610268439 A CN 201610268439A CN 105904560 A CN105904560 A CN 105904560A
Authority
CN
China
Prior art keywords
part
soak
picture frame
corrosion
timber
Prior art date
Application number
CN201610268439.1A
Other languages
Chinese (zh)
Inventor
陈凯
Original Assignee
宁国市鼎轩文化创意有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 宁国市鼎轩文化创意有限公司 filed Critical 宁国市鼎轩文化创意有限公司
Priority to CN201610268439.1A priority Critical patent/CN105904560A/en
Publication of CN105904560A publication Critical patent/CN105904560A/en

Abstract

The invention provides a production technique of a corrosion-resistant solid wood frame and relates to the field of wood processing. The production technique comprises four steps including raw material treatment, cutting, assembling and paint coating. The raw material treatment step comprises four substeps including bleaching, soaking, drying and compressing. According to the production technique, frame bar wood used by the frame is subjected to corrosion resistance treatment such as soaking with a soak solution and varnish coating, so that the corrosion resistance of the frame is further optimized based on the prior art by means of the production technique, and the service life of the frame is effectively prolonged.

Description

A kind of production technology of corrosion-resistant solid wood picture frame

Technical field

The present invention relates to timber manufacture field, be specifically related to the production of a kind of corrosion-resistant solid wood picture frame Technique.

Background technology

Picture frame be by four edges frame assembled for protection and exhibition and ornament draw, calligraphy, and The inlaying device strengthening its representability and design, its Main Function is to protect the corner angle of picture Smooth, drawing paper will not be caused folding line, be a life very useful, that the use cycle is the longest Apply flexibly product.

Chinese invention patent application publication No. CN 102805511 A discloses a kind of handicraft picture frame Production method, this invention with wooden boards such as Lignum paulowniae, Zelkova schneideriana Hand.-Mazz., Lignum seu Ramulus Cunninghamiae Lanceolatae, Masson Pine as raw material, Then carry out hot-water soak, dry, frame processed, use the picture frame produced of the method the most flat Whole, smooth, it is unlikely to deform, but, this invented technology is relatively simple, and antiseptic property is bad.

Summary of the invention

For the deficiencies in the prior art, the invention provides the production of a kind of corrosion-resistant solid wood picture frame Technique, carries out multistep preservative treatment by the moulding timber being used picture frame so that the present invention On the basis of prior art, optimize the antiseptic property of picture frame further, effectively extend picture frame Service life.

For realizing object above, the present invention is achieved by the following technical programs:

The production technology of a kind of corrosion-resistant solid wood picture frame, comprises the steps:

S1. raw material disposal: a. floats color: select, without mould trace, the wood plank of free from insect pests, to immerse H2O2 In solution, soak 10-20min;

B. soak: the timber after drift color process is put in the soak of 55-65 DEG C and soak, after 6h Take out, place into and the soak of room temperature continues soak 2-3h, soak water surface ratio and soaked timber Plate face height 2-5cm;

C. it is dried: soaked timber is put into evacuation 15-30min in vacuum equipment, takes out, Being placed in vacuum equipment, in 85-100 DEG C, evacuation is dried 6h;

D. compression: dried timber is put on hot press and carries out thermosetting compression process;

S2. cut: the size measuring out by picture frame cuts timber extremely required moulding, and corner is 45 °, Sanding again, makes inside casing, after polished polishing, standby;

S3. assemble: four mouldings of cut 45 ° are assembled into frame to connecting in order;

S4. japanning: give the one layer of varnish of picture frame brushing assembled.

Further, in described step S1, H2O2 solution concentration is 5-10%.

Further, the H2O2 solution in described step S1 contains the penetrating agent of 1%.

Further, in described step S1, penetrating agent is ammonium lignosulphonate.

Further, in described step S1, soak is become to be grouped into by following: nano-tourmaline powder 3-5 part, dodecylbenzene sodium sulfonate 5-8 part, Pentachorophenol 3-5 part, calcium sulfate 4-6 part, first Base sodium silicate 2-4 part, alcohol ether glucoside 3-5 part, tricresyl phosphate 4-6 part, penta sodium pentachlorophenate 6-8 Part, hydroxypropyl methyl cellulose 6-7 part, sodium laureth sulfate 4-6 part, alkylnaphthalene sulphur Hydrochlorate 2-4 part, fatty alcohol-polyoxyethylene ether 2-3 part, Ludox 4-6 part, Borax 5-9 part, Biuret 2-5 part, Fe2O3Powder 2-5 part.

Further, in described step S4, varnish is acrylic lacquer.

The present invention adds penetrating agent in drift color step, further enhancing the whiteness of timber, with It is beneficial to timber subsequent treatment;Soaking step uses containing the soak of Pentachorophenol, allows preserving timber Material is immersed in timber texture, thus effectively enhances the decay resistance of picture frame pair;Additionally, Water content in timber is uniform to use vacuum drying ensure that, can reduce timber crimp contraction, Deformation rate;Finally with acrylic lacquer brushing wooden frame surface, the color and luster that wooden frame is excellent can be given, With good guarantor's light, guarantor's color, fast light, weatherability and resistance to acids and bases;The present invention passes through technique Reconfigure, design, process, further enhancing the decay resistance of picture frame, thus have In the service life extending picture frame of effect, additionally present invention process is simple, and Practical Performance is strong.

Detailed description of the invention

For making the purpose of the embodiment of the present invention, technical scheme and advantage clearer, below will knot Close embodiments of the invention, the technical scheme in the embodiment of the present invention is carried out clearly and completely Describe.Based on the embodiment in the present invention, those of ordinary skill in the art are not making creation The every other embodiment obtained under property work premise, broadly falls into the scope of protection of the invention.

Embodiment 1:

The production technology of a kind of corrosion-resistant solid wood picture frame, comprises the steps:

S1. raw material disposal: a. floats color: selecting without mould trace, the wood plank of free from insect pests, immersion contains Have 1% ammonium lignosulphonate 5% H2O2In solution, soak 20min;

B. soak: the timber chosen is put in the soak of 55 DEG C and soak, take out after 6h, Placing into and continue in the soak of room temperature to soak 2h, it is higher than being soaked timber plate face to soak the water surface 2cm;

C. it is dried: soaked timber is put into evacuation 15min in vacuum equipment, takes out, put In vacuum equipment, in 85 DEG C, evacuation is dried 6h;D. compression: dried timber is put Thermosetting compression process is carried out on hot press;

S2. cut: the size measuring out by picture frame cuts timber extremely required moulding, and corner is 45 °, Sanding again, makes inside casing, after polished polishing, standby;

S3. assemble: four mouldings of cut 45 ° are assembled into frame to connecting in order;

S4. japanning: give the one layer of acrylic lacquer of picture frame brushing assembled.

Soak is become to be grouped into by following: 3 parts of nano-tourmaline powder, dodecylbenzene sodium sulfonate 5 Part, Pentachorophenol 3 parts, 4 parts of calcium sulfate, sodium methyl silicate 2 parts, alcohol ether glucoside 3 parts, phosphorus Acid front three phenyl ester 4 parts, penta sodium pentachlorophenate 6 parts, hydroxypropyl methyl cellulose 6 parts, lauryl alcohol gathers Ether sodium sulfovinate 4 parts, alkylnaphthalene sulfonate 2 parts, fatty alcohol-polyoxyethylene ether 2 parts, silicon is molten 4 parts of glue, Borax 5 parts, biuret 2 parts, 2 parts of Fe2O3 powder.

Embodiment 2:

The production technology of a kind of corrosion-resistant solid wood picture frame, comprises the steps:

S1. raw material disposal: a. floats color: selecting without mould trace, the wood plank of free from insect pests, immersion contains Have 1% ammonium lignosulphonate 6% H2O2In solution, soak 18min;

B. soak: the timber chosen is put in the soak of 58 DEG C and soak, take out after 6h, Placing into and continue in the soak of room temperature to soak 2.5h, it is higher than being soaked timber plate face to soak the water surface 3cm;

C. it is dried: soaked timber is put into evacuation 20min in vacuum equipment, takes out, put In vacuum equipment, in 90 DEG C, evacuation is dried 6h;D. compression: dried timber is put Thermosetting compression process is carried out on hot press;

S2. cut: the size measuring out by picture frame cuts timber extremely required moulding, and corner is 45 °, Sanding again, makes inside casing, after polished polishing, standby;

S3. assemble: four mouldings of cut 45 ° are assembled into frame to connecting in order;

S4. japanning: give the one layer of acrylic lacquer of picture frame brushing assembled.

Soak is become to be grouped into by following: 4 parts of nano-tourmaline powder, dodecylbenzene sodium sulfonate 6 Part, Pentachorophenol 4 parts, 5 parts of calcium sulfate, sodium methyl silicate 3 parts, alcohol ether glucoside 4 parts, phosphorus Acid front three phenyl ester 5 parts, penta sodium pentachlorophenate 7 parts, hydroxypropyl methyl cellulose 6 parts, lauryl alcohol gathers Ether sodium sulfovinate 5, alkylnaphthalene sulfonate 3 parts, fatty alcohol-polyoxyethylene ether 2 parts, Ludox 5 Part, Borax 6 parts, biuret 3 parts, Fe2O33 parts of powder.

Embodiment 3:

The production technology of a kind of corrosion-resistant solid wood picture frame, comprises the steps:

S1. raw material disposal: a. floats color: selecting without mould trace, the wood plank of free from insect pests, immersion contains Have 1% ammonium lignosulphonate 7% H2O2In solution, soak 16min;

B. soak: the timber chosen is put in the soak of 60 DEG C and soak, take out after 6h, Placing into and continue in the soak of room temperature to soak 2.5h, it is higher than being soaked timber plate face to soak the water surface 4cm;

C. it is dried: soaked timber is put into evacuation 25min in vacuum equipment, takes out, put In vacuum equipment, in 95 DEG C, evacuation is dried 6h;D. compression: dried timber is put Thermosetting compression process is carried out on hot press;

S2. cut: the size measuring out by picture frame cuts timber extremely required moulding, and corner is 45 °, Sanding again, makes inside casing, after polished polishing, standby;

S3. assemble: four mouldings of cut 45 ° are assembled into frame to connecting in order;

S4. japanning: give the one layer of acrylic lacquer of picture frame brushing assembled.

Soak is become to be grouped into by following: 4 parts of nano-tourmaline powder, dodecylbenzene sodium sulfonate 7 Part, Pentachorophenol 4 parts, 5 parts of calcium sulfate, sodium methyl silicate 3 parts, alcohol ether glucoside 4 parts, phosphorus Acid front three phenyl ester 5 parts, penta sodium pentachlorophenate 7 parts, hydroxypropyl methyl cellulose 7 parts, lauryl alcohol gathers Ether sodium sulfovinate 5 parts, alkylnaphthalene sulfonate 3 parts, fatty alcohol-polyoxyethylene ether 3 parts, silicon is molten 5 parts of glue, Borax 8 parts, biuret 4 parts, 4 parts of Fe2O3 powder.

Embodiment 4:

The production technology of a kind of corrosion-resistant solid wood picture frame, comprises the steps:

S1. raw material disposal: a. floats color: selecting without mould trace, the wood plank of free from insect pests, immersion contains Have 1% ammonium lignosulphonate 10% H2O2In solution, soak 10min;

B. soak: the timber chosen is put in the soak of 65 DEG C and soak, take out after 6h, Placing into and continue in the soak of room temperature to soak 3h, it is higher than being soaked timber plate face to soak the water surface 5cm;

C. it is dried: soaked timber is put into evacuation 30min in vacuum equipment, takes out, put In vacuum equipment, in 100 DEG C, evacuation is dried 6h;D. compression: dried timber is put Thermosetting compression process is carried out on hot press;

S2. cut: the size measuring out by picture frame cuts timber extremely required moulding, and corner is 45 °, Sanding again, makes inside casing, after polished polishing, standby;

S3. assemble: four mouldings of cut 45 ° are assembled into frame to connecting in order;

S4. japanning: give the one layer of acrylic lacquer of picture frame brushing assembled.

Soak is become to be grouped into by following: 5 parts of nano-tourmaline powder, dodecylbenzene sodium sulfonate 8 Part, Pentachorophenol 5 parts, 6 parts of calcium sulfate, sodium methyl silicate 4 parts, alcohol ether glucoside 5 parts, phosphorus Acid front three phenyl ester 6 parts, penta sodium pentachlorophenate 8 parts, hydroxypropyl methyl cellulose 7 parts, lauryl alcohol gathers Ether sodium sulfovinate 6 parts, alkylnaphthalene sulfonate 4 parts, fatty alcohol-polyoxyethylene ether 3 parts, silicon is molten 6 parts of glue, Borax 9 parts, biuret 5 parts, 5 parts of Fe2O3 powder.

Above example only in order to technical scheme to be described, is not intended to limit;Although With reference to previous embodiment, the present invention is described in detail, those of ordinary skill in the art It is understood that the technical scheme described in foregoing embodiments still can be modified by it, Or wherein portion of techniques feature is carried out equivalent;And these amendments or replacement, not The essence making appropriate technical solution departs from the spirit and scope of various embodiments of the present invention technical scheme.

Claims (6)

1. the production technology of a corrosion-resistant solid wood picture frame, it is characterised in that comprise the steps:
S1. raw material disposal: a. floats color: select, without mould trace, the wood plank of free from insect pests, to immerse H2O2 In solution, soak 10-20min;
B. soak: the timber after drift color process is put in the soak of 55-65 DEG C and soak, after 6h Take out, place into and the soak of room temperature continues soak 2-3h, soak water surface ratio and soaked timber Plate face height 2-5cm;
C. it is dried: soaked timber is taken out, is placed in vacuum equipment, takes out in 85-100 DEG C Vacuum drying 6h;
D. compression: dried timber is put on hot press and carries out thermosetting compression process;
S2. cut: the size measuring out by picture frame cuts timber extremely required moulding, and corner is 45 °, Sanding again, makes inside casing, after polished polishing, standby;
S3. assemble: four mouldings having cut 45 ° are assembled into frame to connecting in order;
S4. japanning: give the one layer of varnish of picture frame brushing assembled.
The production technology of corrosion-resistant solid wood picture frame the most as claimed in claim 1, it is characterised in that H described in step S12O2Solution concentration is 5-10%.
The production technology of corrosion-resistant solid wood picture frame the most as claimed in claim 1 or 2, its feature It is, the H described in step S12O2Solution contains the penetrating agent of 1%.
The production technology of corrosion-resistant solid wood picture frame the most as claimed in claim 3, it is characterised in that Penetrating agent described in step S1 is ammonium lignosulphonate.
The production technology of corrosion-resistant solid wood picture frame the most as claimed in claim 1, it is characterised in that In described step S1, soak is become to be grouped into by following: nano-tourmaline powder 3-5 part, dodecane Base benzene sulfonic acid sodium salt 5-8 part, Pentachorophenol 3-5 part, calcium sulfate 4-6 part, sodium methyl silicate 2-4 part, Alcohol ether glucoside 3-5 part, tricresyl phosphate 4-6 part, penta sodium pentachlorophenate 6-8 part, hydroxypropyl methyl Cellulose 6-7 part, sodium laureth sulfate 4-6 part, alkylnaphthalene sulfonate 2-4 part, fat Fat polyoxyethylenated alcohol 2-3 part, Ludox 4-6 part, Borax 5-9 part, biuret 2-5 part, Fe2O3Powder 2-5 part.
The production technology of corrosion-resistant solid wood picture frame the most as claimed in claim 1, it is characterised in that Varnish described in step S4 is acrylic lacquer.
CN201610268439.1A 2016-04-25 2016-04-25 Production technique of corrosion-resistant solid wood frame CN105904560A (en)