CN104277512A - High-viscosity rosin paint - Google Patents
High-viscosity rosin paint Download PDFInfo
- Publication number
- CN104277512A CN104277512A CN201410451794.3A CN201410451794A CN104277512A CN 104277512 A CN104277512 A CN 104277512A CN 201410451794 A CN201410451794 A CN 201410451794A CN 104277512 A CN104277512 A CN 104277512A
- Authority
- CN
- China
- Prior art keywords
- parts
- minute
- mentioned
- add
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses high-viscosity rosin paint. The high-viscosity rosin paint is prepared from the following raw materials in parts by weight: 2-3 parts of maleic rosin, 1-2 parts of chitosan, 0.6-1 part of ethylene carbonate, 2-3 parts of calcium phosphate, 0.6-1 part of hexabromocyclododecane, 2-4 parts of dioctyl sebacate, 1-2 parts of aluminum oxide, 4-6 parts of polytetrafluoroethylene wax, 2-3 parts of tailings, 0.6-1 part of 3-aminopropyltrimethoxysilane, 10-13 parts of quartz sands, 140-200 parts of styrene, 500-600 parts of deionized water, 150-200 parts of methyl acrylate, 4-6 parts of ammonium persulfate, 5-8 parts of OP-10 and 4-6 parts of bonding auxiliaries. The high-viscosity rosin paint is added with the maleic rosin, so that the compatibility among the materials can be effectively prevented, the film-forming effects can be improved, the bonding performances with a basal material can be improved, the peel strength can be improved and the service life can be prolonged.
Description
Technical field
The present invention relates generally to paint field, particularly relates to a kind of high viscosity rosin coating.
Background technology
Be applied to body surface can be formed there is protection, the class I liquid I of solid-state film of decoration or property (as insulation, anticorrosion, mark etc.) or the general name of solid material, comprise oil (property) paint, water-miscible paint, powder coating.Paint is flowable liquid coating, comprises oil (property) paint and water-miscible paint.Paint take organic solvent as medium or high solid, solvent-free oil-base paint.Water-miscible paint is used water dissolving or the coating with water-dispersion.Coating is as one of the main material of house decoration, and the large percentage accounted in decorations, buys the whether qualified environment directly having influence on overall finishing effect and room of coating, sometimes even can produce harm greatly to the health of human body.At present along with the generation of various coating, the quality requirements of coating is also improved constantly, and improve constantly coating quality and can play very large help for building, life.
Summary of the invention
The object of the invention is just to provide a kind of high viscosity rosin coating.
The present invention is achieved by the following technical solutions:
A kind of high viscosity rosin coating, is characterized in that what it was made up of the raw material of following weight parts:
Maleated rosin 2-3, chitosan 1-2, NSC 11801 0.6-1, calcium phosphate 2-3, hexabromocyclododecane 0.6-1, dioctyl sebacate 2-4, aluminum oxide 1-2, tetrafluoroethylene wax 4-6, tailings 2-3,3-aminopropyl trimethoxysilane 0.6-1, quartz sand 10-13, vinylbenzene 140-200, deionized water 500-600, methyl acrylate 150-200, ammonium persulphate 4-6, OP-10 5-8, adhesive aid 4-6;
Described adhesive aid is made up of each raw material of following weight parts:
Alumina gel 20-30, exsiccated ammonium alum 1-3, lanolin 1-2, polyethylene glycol dimethacrylate 0.6-1, dehydrated alcohol 3-4, methyl acrylate 2-4, Potassium Persulphate 2-3, emulsifier op-10 0.5-1, Camphorwood micro mist 2-4, deionized water 15-20;
Dehydrated alcohol is heated to 70-75 DEG C, adds lanolin, stir, obtain alcohol lipoprotein solution;
Join in Alumina gel by Camphorwood micro mist, add polyethylene glycol dimethacrylate, raised temperature is 55-60 DEG C, 100-200 rev/min of dispersed with stirring 3-5 minute, obtains dispersion liquid;
Potassium Persulphate is mixed with methyl acrylate, 2-3 minute is uniformly mixed at 60-70 DEG C, add dispersion liquid, be stirred to normal temperature, add above-mentioned alcohol lipoprotein solution, 60-100 rev/min is uniformly mixed 5-10 minute, adds each raw material of residue, 200-400 rev/min of dispersed with stirring 3-5 minute, obtains described adhesive aid.
2, a preparation method for high viscosity rosin coating as claimed in claim 1, is characterized in that comprising the following steps:
(1) get the 80-90% mixing of the 80-90% of above-mentioned vinylbenzene weight, methyl acrylate weight, obtain monomer a;
(2) get OP-10, add the 30-40% of above-mentioned deionized water weight, stir, obtain pre-emulsion;
(3) get ammonium persulphate, add the 10-20% of residue deionized water weight, stir, obtain initiator solution;
(4) get above-mentioned monomer a, the 40-50% of pre-emulsion weight, the 50-60% of initiator solution weight, mixing, adds trimellitate, insulated and stirred 10-20 minute at 75-80 DEG C, obtains premix monomer;
(5) by remaining vinylbenzene, methyl acrylate mixing, add hexabromocyclododecane, dioctyl sebacate after stirring, 100-200 rev/min of dispersed with stirring 10-16 minute, obtains modified monomer;
(6) above-mentioned modified monomer is mixed with remaining pre-emulsion, remaining initiator solution, insulated and stirred 30-50 minute at 70-90 DEG C, drip above-mentioned premix monomer, time for adding is 2-3 hour, at 80-85 DEG C, 2-3 hour is incubated after dropwising, reduce temperature to 40-50 DEG C, regulate pH value to 7-8, filter with 200-250 order filter sieve;
(7) material above-mentioned steps (6) obtained mixes with each raw material of residue, and 800-1200 rev/min of dispersed with stirring 20-30 minute, obtains described high viscosity rosin coating.
Advantage of the present invention is:
Coating of the present invention adds maleated rosin, effectively can promote the consistency of each storeroom, improve film-formation result, improves the adhesive property with base material, improves peel strength, increases the service life.The Camphorwood micro mist added in adhesive aid of the present invention has good resistance to abrasion, Heat stability is good chemical stability, Alumina gel mixes with exsiccated ammonium alum, lanolin, Isooctyl acrylate monomer, Potassium Persulphate, there is excellent adhesive property, coatingsurface resistance and stability can be strengthened.
Embodiment
Embodiment 1
A kind of high viscosity rosin coating, is characterized in that what it was made up of the raw material of following weight parts:
Maleated rosin 3, chitosan 2, NSC 11801 0.6, calcium phosphate 2, hexabromocyclododecane 0.6, dioctyl sebacate 4, aluminum oxide 1, tetrafluoroethylene wax 6, tailings 2,3-aminopropyl trimethoxysilane 0.6, quartz sand 13, vinylbenzene 200, deionized water 600, methyl acrylate 200, ammonium persulphate 4, OP-10 5, adhesive aid 4;
Described adhesive aid is made up of each raw material of following weight parts:
Alumina gel 20, exsiccated ammonium alum 1, lanolin 2, polyethylene glycol dimethacrylate 0.6, dehydrated alcohol 4, methyl acrylate 4, Potassium Persulphate 2, emulsifier op-10 0.5, Camphorwood micro mist 4, deionized water 20;
Dehydrated alcohol is heated to 75 DEG C, adds lanolin, stir, obtain alcohol lipoprotein solution;
Join in Alumina gel by Camphorwood micro mist, add polyethylene glycol dimethacrylate, raised temperature is 60 DEG C, and 200 revs/min of dispersed with stirring 5 minutes, obtain dispersion liquid;
Potassium Persulphate is mixed with methyl acrylate, at 60 DEG C, is uniformly mixed 3 minutes, adds dispersion liquid, be stirred to normal temperature, add above-mentioned alcohol lipoprotein solution, 100 revs/min are uniformly mixed 10 minutes, add each raw material of residue, 400 revs/min of dispersed with stirring 5 minutes, obtain described adhesive aid.
A preparation method for high viscosity rosin coating, is characterized in that comprising the following steps:
(1) get 90% of above-mentioned vinylbenzene weight, 90% mixing of methyl acrylate weight, obtain monomer a;
(2) get OP-10, add 40% of above-mentioned deionized water weight, stir, obtain pre-emulsion;
(3) get ammonium persulphate, add 20% of residue deionized water weight, stir, obtain initiator solution;
(4) get above-mentioned monomer a, 50% of pre-emulsion weight, 60% of initiator solution weight, mixing, add trimellitate, at 75-80 DEG C, insulated and stirred 20 minutes, obtains premix monomer;
(5) by remaining vinylbenzene, methyl acrylate mixing, add hexabromocyclododecane, dioctyl sebacate after stirring, 200 revs/min of dispersed with stirring 16 minutes, obtain modified monomer;
(6) above-mentioned modified monomer is mixed with remaining pre-emulsion, remaining initiator solution, insulated and stirred 50 minutes at 90 DEG C, drip above-mentioned premix monomer, time for adding is 3 hours, at 85 DEG C, 2 hours are incubated after dropwising, reduce temperature to 50 DEG C, regulate pH value to 8, filter with 250 order filter sieve;
(7) material above-mentioned steps (6) obtained mixes with each raw material of residue, and 1200 revs/min of dispersed with stirring 30 minutes, obtain described high viscosity rosin coating.
Performance test:
Unit elongation: >=300%;
Watertightness: 0.3MPa (one hour waterproof).
Claims (2)
1. a high viscosity rosin coating, is characterized in that what it was made up of the raw material of following weight parts:
Maleated rosin 2-3, chitosan 1-2, NSC 11801 0.6-1, calcium phosphate 2-3, hexabromocyclododecane 0.6-1, dioctyl sebacate 2-4, aluminum oxide 1-2, tetrafluoroethylene wax 4-6, tailings 2-3,3-aminopropyl trimethoxysilane 0.6-1, quartz sand 10-13, vinylbenzene 140-200, deionized water 500-600, methyl acrylate 150-200, ammonium persulphate 4-6, OP-10 5-8, adhesive aid 4-6;
Described adhesive aid is made up of each raw material of following weight parts:
Alumina gel 20-30, exsiccated ammonium alum 1-3, lanolin 1-2, polyethylene glycol dimethacrylate 0.6-1, dehydrated alcohol 3-4, methyl acrylate 2-4, Potassium Persulphate 2-3, emulsifier op-10 0.5-1, Camphorwood micro mist 2-4, deionized water 15-20;
Dehydrated alcohol is heated to 70-75 DEG C, adds lanolin, stir, obtain alcohol lipoprotein solution;
Join in Alumina gel by Camphorwood micro mist, add polyethylene glycol dimethacrylate, raised temperature is 55-60 DEG C, 100-200 rev/min of dispersed with stirring 3-5 minute, obtains dispersion liquid;
Potassium Persulphate is mixed with methyl acrylate, 2-3 minute is uniformly mixed at 60-70 DEG C, add dispersion liquid, be stirred to normal temperature, add above-mentioned alcohol lipoprotein solution, 60-100 rev/min is uniformly mixed 5-10 minute, adds each raw material of residue, 200-400 rev/min of dispersed with stirring 3-5 minute, obtains described adhesive aid.
2. a preparation method for high viscosity rosin coating as claimed in claim 1, is characterized in that comprising the following steps:
(1) get the 80-90% mixing of the 80-90% of above-mentioned vinylbenzene weight, methyl acrylate weight, obtain monomer a;
(2) get OP-10, add the 30-40% of above-mentioned deionized water weight, stir, obtain pre-emulsion;
(3) get ammonium persulphate, add the 10-20% of residue deionized water weight, stir, obtain initiator solution;
(4) get above-mentioned monomer a, the 40-50% of pre-emulsion weight, the 50-60% of initiator solution weight, mixing, adds trimellitate, insulated and stirred 10-20 minute at 75-80 DEG C, obtains premix monomer;
(5) by remaining vinylbenzene, methyl acrylate mixing, add hexabromocyclododecane, dioctyl sebacate after stirring, 100-200 rev/min of dispersed with stirring 10-16 minute, obtains modified monomer;
(6) above-mentioned modified monomer is mixed with remaining pre-emulsion, remaining initiator solution, insulated and stirred 30-50 minute at 70-90 DEG C, drip above-mentioned premix monomer, time for adding is 2-3 hour, at 80-85 DEG C, 2-3 hour is incubated after dropwising, reduce temperature to 40-50 DEG C, regulate pH value to 7-8, filter with 200-250 order filter sieve;
(7) material above-mentioned steps (6) obtained mixes with each raw material of residue, and 800-1200 rev/min of dispersed with stirring 20-30 minute, obtains described high viscosity rosin coating.