CN104233429A - 一种铍铝合金阳极氧化方法 - Google Patents

一种铍铝合金阳极氧化方法 Download PDF

Info

Publication number
CN104233429A
CN104233429A CN201410408119.2A CN201410408119A CN104233429A CN 104233429 A CN104233429 A CN 104233429A CN 201410408119 A CN201410408119 A CN 201410408119A CN 104233429 A CN104233429 A CN 104233429A
Authority
CN
China
Prior art keywords
beryllium
washing
2min
aluminum alloy
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410408119.2A
Other languages
English (en)
Inventor
贾卫东
魏军锋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xian Sanwei Security Technology Co Ltd
Original Assignee
Xian Sanwei Security Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xian Sanwei Security Technology Co Ltd filed Critical Xian Sanwei Security Technology Co Ltd
Priority to CN201410408119.2A priority Critical patent/CN104233429A/zh
Publication of CN104233429A publication Critical patent/CN104233429A/zh
Pending legal-status Critical Current

Abstract

一种铍铝合金阳极氧化方法，属于金属处理工艺领域，包括如下步骤：（1）将铍铝合金进行抛光；（2）将挂具上的旧氧化膜去除，与夹具夹好并接触良好；（3）用NaOH20g/L碱洗，除油温度为80℃~85℃，时间为5s~10s；（4）先用流动热水水洗，再用流动冷水洗；（5）室温下出光,时间为3s~5s；（6）去离子水洗0.5min~2min；（7）阳极氧化：铬酐130g/L，硼酸7g/L,温度5℃~15℃，时间为90min，电流密度为10~60A/dm2；（8）流动冷水洗0.5min~2min；（9）热水封闭或重铬酸盐封闭，提高氧化膜耐蚀性；（10）流动冷水洗0.5min~2min；（11）高压空气吹干后拆除夹具；之后喷涂漆；（12）在70℃~80℃的温度下烘干24h。通过对铍铝合金进行氧化，可以得到有较好绝缘性的氧化膜层，有效延长了铍铝合金的使用寿命，本发明所述铍铝合金阳极氧化方法操作简单，且易于推广。

Description

一种铍铝合金阳极氧化方法
技术领域
本发明属于金属处理工艺领域，尤其涉及一种铍铝合金阳极氧化方法。
背景技术
铍铝合金具有质量轻、比强度高、比刚度高、热稳定好、高韧性、抗腐蚀等特点，结合了铍的低密度与铝的易加工性等许多优良特性，在航天、航空、计算机制造、汽车领域及高精、高速度电焊机器制造工业中有广阔的应用前景，已成为一种越来越重要的新型材料，由于合金中铝相固有的特性，铍铝合金存在耐磨性、硬度和耐蚀性不足的制约，限制了铍铝合金的应用，为了拓展铍铝合金的应用范围，延长其使用寿命，须对铝合金进行表面处理。
发明内容
本发明旨在解决上述问题，提供一种铍铝合金阳极氧化方法。
一种铍铝合金阳极氧化方法，其特征在于包括如下步骤：（1）将铍铝合金进行抛光；（2）将挂具上的旧氧化膜去除，与夹具夹好并接触良好；（3）用NaOH20g/L碱洗，除油温度为80℃~85℃，时间为5s~10s；（4）先用流动热水水洗，再用流动冷水洗；（5）室温下出光,时间为3s~5s；（6）去离子水洗0.5min~2min；（7）阳极氧化：铬酐130g/L，硼酸7g/L,温度5℃~15℃，时间为90min，电流密度为10~60A/dm2；（8）流动冷水洗0.5min~2min；（9）热水封闭或重铬酸盐封闭，提高氧化膜耐蚀性；（10）流动冷水洗0.5min~2min；（11）高压空气吹干后拆除夹具；之后喷涂漆；（12）在70℃~80℃的温度下烘干24h。
本发明所述的一种铍铝合金阳极氧化方法，其特征在于所述步骤（4）中的水洗时间为0.5min~2min。
本发明所述的一种铍铝合金阳极氧化方法，其特征在于所述步骤（5）中所述的出光剂为HNO3300~400ml/L。
本发明所述的一种铍铝合金阳极氧化方法，其特征在于所述步骤（7）中所述的阳极材料为铅板。
本发明所述的一种铍铝合金阳极氧化方法，通过对铍铝合金进行氧化，可以得到有较好绝缘性的氧化膜层，有效延长了铍铝合金的使用寿命，本发明所述铍铝合金阳极氧化方法操作简单，且易于推广。
具体实施方式
 本发明一种铍铝合金阳极氧化方法，其特征在于包括如下步骤：（1）将铍铝合金进行抛光；（2）将挂具上的旧氧化膜去除，与夹具夹好并接触良好；（3）用NaOH20g/L碱洗，除油温度为80℃~85℃，时间为5s~10s；（4）先用流动热水水洗，再用流动冷水洗；（5）室温下出光,时间为3s~5s；（6）去离子水洗0.5min~2min；（7）阳极氧化：铬酐130g/L，硼酸7g/L,温度5℃~15℃，时间为90min，电流密度为10~60A/dm2；（8）流动冷水洗0.5min~2min；（9）热水封闭或重铬酸盐封闭，提高氧化膜耐蚀性；（10）流动冷水洗0.5min~2min；（11）高压空气吹干后拆除夹具；之后喷涂漆；（12）在70℃~80℃的温度下烘干24h。
本发明所述的一种铍铝合金阳极氧化方法，其特征在于所述步骤（4）中的水洗时间为0.5min~2min。所述步骤（5）中所述的出光剂为HNO3300~400ml/L。所述步骤（7）中所述的阳极材料为铅板。 

Claims (4)

1.一种铍铝合金阳极氧化方法，其特征在于包括如下步骤：（1）将铍铝合金进行抛光；（2）将挂具上的旧氧化膜去除，与夹具夹好并接触良好；（3）用NaOH20g/L碱洗，除油温度为80℃~85℃，时间为5s~10s；（4）先用流动热水水洗，再用流动冷水洗；（5）室温下出光,时间为3s~5s；（6）去离子水洗0.5min~2min；（7）阳极氧化：铬酐130g/L，硼酸7g/L,温度5℃~15℃，时间为90min，电流密度为10~60A/dm2；（8）流动冷水洗0.5min~2min；（9）热水封闭或重铬酸盐封闭，提高氧化膜耐蚀性；（10）流动冷水洗0.5min~2min；（11）高压空气吹干后拆除夹具；之后喷涂漆；（12）在70℃~80℃的温度下烘干24h。
2.如权利要求1所述的一种铍铝合金阳极氧化方法，其特征在于所述步骤（4）中的水洗时间为0.5min~2min。
3.如权利要求1所述的一种铍铝合金阳极氧化方法，其特征在于所述步骤（5）中所述的出光剂为HNO3300~400ml/L。
4.如权利要求1所述的一种铍铝合金阳极氧化方法，其特征在于所述步骤（7）中所述的阳极材料为铅板。
CN201410408119.2A 2014-08-19 2014-08-19 一种铍铝合金阳极氧化方法 Pending CN104233429A (zh)