CN104231877A - 一种具有耐高温作用的涂料 - Google Patents

一种具有耐高温作用的涂料 Download PDF

Info

Publication number
CN104231877A
CN104231877A CN201410416931.XA CN201410416931A CN104231877A CN 104231877 A CN104231877 A CN 104231877A CN 201410416931 A CN201410416931 A CN 201410416931A CN 104231877 A CN104231877 A CN 104231877A
Authority
CN
China
Prior art keywords
parts
raw material
coating
sizing agent
high temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410416931.XA
Other languages
English (en)
Inventor
张保峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI BODA CELLULOSE TECHNOLOGY Co Ltd
Original Assignee
ANHUI BODA CELLULOSE TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI BODA CELLULOSE TECHNOLOGY Co Ltd filed Critical ANHUI BODA CELLULOSE TECHNOLOGY Co Ltd
Priority to CN201410416931.XA priority Critical patent/CN104231877A/zh
Publication of CN104231877A publication Critical patent/CN104231877A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种具有耐高温作用的涂料，其是由下述重量份的原料制得：聚酯树脂48-55，四甲氧基甲基甘脲1-2、氧化铜1-3、羟乙基纤维素1-2、碳酸二甲酯3-5、氮化硼0.2-0.5，氯化石蜡1-2、抗氧剂1680.4-0.5、苯甲酸1-2、硅酸钠0.5-0.8，云母粉2-3、膨润土1-2、甲乙酮0.1-0.2、钛白粉1-2、复配胶黏剂1-2；本发明的粉末涂料,耐候性能大大提高同时耐高温性能好，寿命长，使用环境多。

Description

一种具有耐高温作用的涂料
技术领域
本发明涉及粉末涂料领域，确切地说是一种具有耐高温作用的涂料 。
背景技术
    粉末涂料是一种新型的不含溶剂100%固体粉末状涂料。具有无溶剂、无污染、可回收、环保、节省能源和资源、减轻劳动强度和涂膜机械强度高等特点。而纤维素在涂料中的得应用很多，可以起到涂料韧性的作用。
发明内容
本发明的目的在于提供一种具有耐高温作用的涂料 。
上述目的通过以下方案实现：
    一种具有耐高温作用的涂料 ，其特征在于：其是由下述重量份的原料制得：聚酯树脂48-55，四甲氧基甲基甘脲 1-2、氧化铜1-3、羟乙基纤维素1-2、碳酸二甲酯3-5、氮化硼0.2-0.5，氯化石蜡1-2、抗氧剂168 0.4-0.5、苯甲酸1-2、硅酸钠0.5-0.8，云母粉2-3、膨润土1-2、甲乙酮0.1-0.2、钛白粉1-2、复配胶黏剂1-2；
复配胶黏剂是由下述重量份的原料制得：
丁苯橡胶4-6，安息香0.1-0.5， 丙酮1-2、松油1-2、酚醛树脂0.8-0.9、羟基丙烯酸树脂 1-2、锌粉0.1-0.2、二氧化硅1-2、尿酸0.1-0.5、羟甲基纤维素1-2、抗氧剂1076  1-2、聚醚醚酮1-2;
复配胶黏剂的制备方法为：将各原料混匀后，于80-90℃混炼10-20min，取出后，粉碎，过100-200目筛，即得。
所述的一种具有耐高温作用的涂料 ，其特征在于：
制备方法包括以下步骤：
（1）所有物料按配比称取，置于高速混合机，900-1000转/分混合13-15min；
（2）双螺杆挤出机挤出；
（3）挤出料片经粉碎，过200-300目筛，即得。
本发明的有益效果为：本发明的粉末涂料,耐候性能大大提高同时耐高温性能好，寿命长，使用环境多。
 
具体实施方式
 一种具有耐高温作用的涂料 ，其是由下述重量（kg)的原料制得：聚酯树脂48，四甲氧基甲基甘脲 1、氧化铜1、羟乙基纤维素2、碳酸二甲酯3、氮化硼0.5，氯化石蜡1、抗氧剂168 0.4、苯甲酸1、硅酸钠0.5，云母粉2、膨润土2、甲乙酮0.2、钛白粉2、复配胶黏剂2；
复配胶黏剂是由下述重量（kg)的原料制得：
丁苯橡胶6，安息香0.5， 丙酮1、松油2、酚醛树脂0.9、羟基丙烯酸树脂 2、锌粉0.2、二氧化硅2、尿酸0.5、羟甲基纤维素2、抗氧剂1076  1、聚醚醚酮2;
复配胶黏剂的制备方法为：将各原料混匀后，于88℃混炼13min，取出后，粉碎，过200目筛，即得。
所述的一种具有耐高温作用的涂料 ，制备方法包括以下步骤：
（1）所有物料按配比称取，置于高速混合机，1000转/分混合15min；
（2）双螺杆挤出机挤出；
（3）挤出料片经粉碎，过300目筛，即得。
本实施例产品的涂装方法为一般的静电喷涂，固化条件：200oC/18-23min，所得涂层平滑、完整，人工加速老化时间为≥1400h。

Claims (2)

1.一种具有耐高温作用的涂料 ，其特征在于：其是由下述重量份的原料制得：聚酯树脂48-55，四甲氧基甲基甘脲 1-2、氧化铜1-3、羟乙基纤维素1-2、碳酸二甲酯3-5、氮化硼0.2-0.5，氯化石蜡1-2、抗氧剂168 0.4-0.5、苯甲酸1-2、硅酸钠0.5-0.8，云母粉2-3、膨润土1-2、甲乙酮0.1-0.2、钛白粉1-2、复配胶黏剂1-2；
复配胶黏剂是由下述重量份的原料制得：
丁苯橡胶4-6，安息香0.1-0.5， 丙酮1-2、松油1-2、酚醛树脂0.8-0.9、羟基丙烯酸树脂 1-2、锌粉0.1-0.2、二氧化硅1-2、尿酸0.1-0.5、羟甲基纤维素1-2、抗氧剂1076  1-2、聚醚醚酮1-2;
复配胶黏剂的制备方法为：将各原料混匀后，于80-90℃混炼10-20min，取出后，粉碎，过100-200目筛，即得。
2.根据权利要求1所述的一种具有耐高温作用的涂料 ，其特征在于：
制备方法包括以下步骤：
（1）所有物料按配比称取，置于高速混合机，900-1000转/分混合13-15min；
（2）双螺杆挤出机挤出；
（3）挤出料片经粉碎，过200-300目筛，即得。
CN201410416931.XA 2014-08-22 2014-08-22 一种具有耐高温作用的涂料 Pending CN104231877A (zh)