CN104231491A - 刚性无机粒子改性聚氯乙烯塑料粒子 - Google Patents
刚性无机粒子改性聚氯乙烯塑料粒子 Download PDFInfo
- Publication number
- CN104231491A CN104231491A CN201410550006.6A CN201410550006A CN104231491A CN 104231491 A CN104231491 A CN 104231491A CN 201410550006 A CN201410550006 A CN 201410550006A CN 104231491 A CN104231491 A CN 104231491A
- Authority
- CN
- China
- Prior art keywords
- polyvinyl chloride
- differential equations
- polynite
- lubricant
- particle according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种刚性无机粒子改性聚氯乙烯塑料粒子,包括聚氯乙烯、无机刚性粒子、蒙脱土、稳定剂、增塑剂、润滑剂及抗氧化剂,所述塑料粒子配方中各成分的重量百分比为聚氯乙烯90~95%、无机刚性粒子5~10%、蒙脱土10~15%、稳定剂1.5~3.5%、增塑剂1.5~2.5%、润滑剂0.5~2.5%,抗氧化剂2~4.5%。通过上述方式,本发明提供了一种刚性无机粒子改性聚氯乙烯塑料粒子,该塑料粒子制成的聚氯乙烯复合塑料的拉伸强度、断裂伸长率和缺口冲击强度分别比PVC基体提高了3倍,有较高的韧性及强度。
Description
技术领域
本发明涉及聚氯乙烯塑料粒子,特别是涉及一种刚性无机粒子改性聚氯乙烯塑料粒子。
背景技术
聚氯乙烯,它是一种用途很广的材料,经常用于我们的生活中。比如PVC管,PVC地板,PVC墙纸等等。
聚氯乙烯虽然用于广泛,但其热稳定性差,不易加工。不能直接使用,必须经过改性混配,添加相关助剂,PVC一般先要改性造粒,制备成粒子后,塑化更充分,加工也更容易,尤其是工艺是注塑的产品。
发明内容
本发明主要解决的技术问题是提供一种刚性无机粒子改性聚氯乙烯塑料粒子,该塑料粒子制成的聚氯乙烯复合塑料的拉伸强度、断裂伸长率和缺口冲击强度分别比PVC基体提高了3倍,有较高的韧性及强度。
为解决上述技术问题,本发明采用的一个技术方案是:提供一种刚性无机粒子改性聚氯乙烯塑料粒子,包括聚氯乙烯、无机刚性粒子、蒙脱土、稳定剂、增塑剂、润滑剂及抗氧化剂,所述塑料粒子配方中各成分的重量百分比为聚氯乙烯90~95%、无机刚性粒子5~10%、蒙脱土10~15%、稳定剂1.5~3.5%、增塑剂1.5~2.5%、润滑剂0.5~2.5%,抗氧化剂2~4.5%。
在本发明一个较佳实例中,所述塑料粒子配方中各成分的重量百分比为聚氯乙烯92~95%、无机刚性粒子6~9.5%、蒙脱土12~15%、稳定剂2~3.5%、增塑剂1.8~2.5%、润滑剂1~2.5%、抗氧化剂3~4.5%。
在本发明一个较佳实例中,所述无机刚性粒子为纳米碳酸钙或纳米亚硫酸钙中的一种。
在本发明一个较佳实例中,所述蒙脱土为二甲基双氢化牛脂季铵盐改性的纳剂蒙脱土。
在本发明一个较佳实例中,所述稳定剂为月桂酸酯类、马来酸酯类或硫醇类中的一种。
在本发明一个较佳实例中,所述增塑剂为邻苯二甲酸二(2-乙基己基)酯(DEHP)。
在本发明一个较佳实例中,所述润滑剂为硬脂酸钙。
在本发明一个较佳实例中,所述抗氧剂为萘胺、二苯胺、对苯二胺中的一种。
本发明的有益效果是:本发明一种刚性无机粒子改性聚氯乙烯塑料粒子,该塑料粒子制成的聚氯乙烯复合塑料的拉伸强度、断裂伸长率和缺口冲击强度分别比PVC基体提高了3倍,有较高的韧性及强度。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅是本发明的一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例,都属于本发明保护的范围。
本发明实施例提供如下技术方案;
在本发明一个实施例中,一种刚性无机粒子改性聚氯乙烯塑料粒子,包括聚氯乙烯、无机刚性粒子、蒙脱土、稳定剂、增塑剂、润滑剂及抗氧化剂,所述塑料粒子配方中各成分的重量百分比为聚氯乙烯90~95%、无机刚性粒子5~10%、蒙脱土10~15%、稳定剂1.5~3.5%、增塑剂1.5~2.5%、润滑剂0.5~2.5%,抗氧化剂2~4.5%。
进一步,所述塑料粒子配方中各成分的重量百分比为聚氯乙烯92~95%、无机刚性粒子6~9.5%、蒙脱土12~15%、稳定剂2~3.5%、增塑剂1.8~2.5%、润滑剂1~2.5%、抗氧化剂3~4.5%。
进一步,所述无机刚性粒子为纳米碳酸钙或纳米亚硫酸钙中的一种。
进一步,所述蒙脱土为二甲基双氢化牛脂季铵盐改性的纳剂蒙脱土,蒙脱土在一定程度上可改善复合塑料的力学性能、热稳定性和阻燃性。
进一步,所述稳定剂为月桂酸酯类、马来酸酯类或硫醇类中的一种。
进一步,所述增塑剂为邻苯二甲酸二(2-乙基己基)酯(DEHP)。
进一步,所述润滑剂为硬脂酸钙。
进一步,所述抗氧剂为萘胺、二苯胺、对苯二胺中的一种。
本发明的有益效果是:本发明一种刚性无机粒子改性聚氯乙烯塑料粒子,该塑料粒子制成的聚氯乙烯复合塑料的拉伸强度、断裂伸长率和缺口冲击强度分别比PVC基体提高了3倍,有较高的韧性及强度。
以上所述仅为本发明的实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书内容所作的等效结构或等效流程变换,或直接或间接运用在其它相关的技术领域,均同理包括在本发明的专利保护范围内。
Claims (8)
1.一种刚性无机粒子改性聚氯乙烯塑料粒子,其特征在于,包括聚氯乙烯、无机刚性粒子、蒙脱土、稳定剂、增塑剂、润滑剂及抗氧化剂,所述塑料粒子配方中各成分的重量百分比为聚氯乙烯90~95%、无机刚性粒子5~10%、蒙脱土10~15%、稳定剂1.5~3.5%、增塑剂1.5~2.5%、润滑剂0.5~2.5%,抗氧化剂2~4.5%。
2.根据权利要求1所述的刚性无机粒子改性聚氯乙烯塑料粒子,其特征在于,所述塑料粒子配方中各成分的重量百分比为聚氯乙烯92~95%、无机刚性粒子6~9.5%、蒙脱土12~15%、稳定剂2~3.5%、增塑剂1.8~2.5%、润滑剂1~2.5%、抗氧化剂3~4.5%。
3.根据权利要求1所述的刚性无机粒子改性聚氯乙烯塑料粒子,其特征在于,所述无机刚性粒子为纳米碳酸钙或纳米亚硫酸钙中的一种。
4.根据权利要求1所述的刚性无机粒子改性聚氯乙烯塑料粒子,其特征在于,所述蒙脱土为二甲基双氢化牛脂季铵盐改性的纳剂蒙脱土。
5.根据权利要求1所述的刚性无机粒子改性聚氯乙烯塑料粒子,其特征在于,所述稳定剂为月桂酸酯类、马来酸酯类或硫醇类中的一种。
6.根据权利要求1所述的刚性无机粒子改性聚氯乙烯塑料粒子,其特征在于,所述增塑剂为邻苯二甲酸二(2-乙基己基)酯(DEHP)。
7.根据权利要求1所述的刚性无机粒子改性聚氯乙烯塑料粒子,其特征在于,所述润滑剂为硬脂酸钙。
8.根据权利要求1所述的刚性无机粒子改性聚氯乙烯塑料粒子,其特征在于,所述抗氧剂为萘胺、二苯胺、对苯二胺中的一种。