CN105038006A - 一种抗低温脆性pvc管材及其制备方法 - Google Patents

一种抗低温脆性pvc管材及其制备方法 Download PDF

Info

Publication number
CN105038006A
CN105038006A CN201510436956.0A CN201510436956A CN105038006A CN 105038006 A CN105038006 A CN 105038006A CN 201510436956 A CN201510436956 A CN 201510436956A CN 105038006 A CN105038006 A CN 105038006A
Authority
CN
China
Prior art keywords
parts
pvc
pvc pipe
low temperature
brittleness
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510436956.0A
Other languages
English (en)
Inventor
凌雪木
杨秋慧
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LIUZHOU LIANHAI TECHNOLOGY Co Ltd
Original Assignee
LIUZHOU LIANHAI TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LIUZHOU LIANHAI TECHNOLOGY Co Ltd filed Critical LIUZHOU LIANHAI TECHNOLOGY Co Ltd
Priority to CN201510436956.0A priority Critical patent/CN105038006A/zh
Publication of CN105038006A publication Critical patent/CN105038006A/zh
Pending legal-status Critical Current

Abstract

本发明涉及复合材料领域，具体地说是一种抗低温脆性PVC管材及其制备方法。所述PVC管材包括以下原料组分及重量份：PVC120-150份、增韧剂5-12份、活性纳米碳酸钙6-8份、稳定剂8-12份、APAO4-10份。采用本发明中PVC管材制备的PVC管抗冲击性能、耐寒性、耐候性好，低温脆性比现有技术中PVC管有很大提高；本发明中PVC管材易于加工，各原料组分之间相同性好；PVC管材的原料成本和生产成本低。

Description

一种抗低温脆性PVC管材及其制备方法
技术领域
本发明涉及复合材料领域，具体地说是一种抗低温脆性PVC管材及其制备方法。
背景技术
聚氯乙烯(PVC)是世界上仅次于聚乙烯的第二大塑料品种，具有良好的机械和物理性能，由其制成的PVC管材因自重轻，具有良好的机械和物理性能，由其制成的PVC管材因耐腐蚀，耐压强度高，安全方便等特点得到了广泛应用，目前约70%的PVC管材用于排水/给水等建筑领域，但PVC管最大的缺陷就是耐寒性和低温抗冲击性能较差，使用温度下限约-15℃，极大限制了PVC管的使用，例如PVC管材在中国北方使用时，冬天极易发生脆裂。通常在PVC管中加入各类助剂改善低温脆性，常用的有包括二元醇的脂肪酸醋、直链醇的邻苯二甲酸脂和环氧脂肪酸单脂等的增塑剂，包括氯化聚乙烯(CPE)和丁氰橡胶等改性剂，包括聚氨醋和SBS等的热塑性弹性体，填充剂和其它助剂。但是在PVC基材中添加大量多种类的各种添加剂容易各原料组分之间相容性差以及加工性能差的缺点，而且为了使得PVC管材具有优良的低温脆性而使用多种添加剂增加了生产成本。现有技术中的添加剂种类和规格繁多，对于如何获得一种兼顾低温脆性，加工性能以及生产成本的PVC管材，现有技术中没有技术启示。
发明内容
针对现有技术的不足，本发明提供一种抗低温脆性PVC管材及其制备方法。。
本发明的方案是通过这样实现的：
一种抗低温脆性PVC管材，该管材包括以下重量比的原料：PVC120-150份、增韧剂5-12份、活性纳米碳酸钙6-8份、稳定剂8-12份、APAO4-10份。
优选的，该管材包括以下重量比的原料：PVC130份、增韧剂8份、活性纳米碳酸钙6份、稳定剂10份、APAO8份。
优选的，所述增韧剂为氯化聚乙烯。
优选的，所述稳定剂为钙锌复合稳定剂。
一种抗低温脆性PVC管材的制备方法，包括以下步骤：
（1）将PVC120-150份、增韧剂5-12份、活性纳米碳酸钙6-8份、稳定剂8-12份、APAO4-10份进行高速混合；
（2）经冷混机使得物料冷却至45℃；
（3）用双螺杆挤出机挤出成粉，双螺杆挤出机的挤出温度为115℃。
本发明具备以下良好效果：
（1）本发明制备的PVC管抗冲击性能、耐寒性、耐候性好，低温脆性比现有技术中PVC管有很大提高。
（2）本发明中PVC管材易于加工，各原料组分之间相同性好。
（3）本发明的高强度PVC管材成本低廉、经济效益显著。
具体实施方式
以下结合实施例描述本发明的一种抗低温脆性PVC管材及其制备方法，这些描述并不是对本发明内容作进一步的限定。
实施例1
一种抗低温脆性PVC管材，该管材包括以下重量比的原料：PVC130份、增韧剂氯化聚乙烯8份、活性纳米碳酸钙6份、钙锌复合稳定剂10份、APAO8份。
制备上述抗低温脆性PVC管材的方法，包括以下步骤：
（1）将PVC130份、增韧剂氯化聚乙烯8份、活性纳米碳酸钙6份、钙锌复合稳定剂10份、APAO8份进行高速混合；
（2）经冷混机使得物料冷却至45℃；
（3）用双螺杆挤出机挤出成粉，双螺杆挤出机的挤出温度为115℃。
实施例2
一种抗低温脆性PVC管材，该管材包括以下重量比的原料：PVC120份、增韧剂氯化聚乙烯5份、活性纳米碳酸钙8份、钙锌复合稳定剂8份、APAO4份。
制备上述抗低温脆性PVC管材的方法，包括以下步骤：
（1）将PVC120份、增韧剂氯化聚乙烯5份、活性纳米碳酸钙8份、钙锌复合稳定剂8份、APAO4份进行高速混合；
（2）经冷混机使得物料冷却至45℃；
（3）用双螺杆挤出机挤出成粉，双螺杆挤出机的挤出温度为115℃。
实施例3
一种抗低温脆性PVC管材，该管材包括以下重量比的原料：PVC150份、增韧剂氯化聚乙烯12份、活性纳米碳酸钙7份、钙锌复合稳定剂12份、APAO10份。
制备上述抗低温脆性PVC管材的方法，包括以下步骤：
（1）将PVC120-150份、增韧剂氯化聚乙烯5-12份、活性纳米碳酸钙6-8份、钙锌复合稳定剂8-12份、APAO4-10份进行高速混合；
（2）经冷混机使得物料冷却至45℃；
（3）用双螺杆挤出机挤出成粉，双螺杆挤出机的挤出温度为115℃。

Claims (5)

1.一种抗低温脆性PVC管材，其特征在于，该管材包括以下重量比的原料：PVC120-150份、增韧剂5-12份、活性纳米碳酸钙6-8份、稳定剂8-12份、APAO4-10份。
2.根据权利要求1所述的抗低温脆性PVC管材，其特征在于，该管材包括以下重量比的原料：PVC130份、增韧剂8份、活性纳米碳酸钙6份、稳定剂10份、APAO8份。
3.根据权利要求1或2所述的抗低温脆性PVC管材，其特征在于，所述增韧剂为氯化聚乙烯。
4.根据权利要求3所述的抗低温脆性PVC管材及其制备方法，其特征在于，所述稳定剂为钙锌复合稳定剂。
5.一种抗低温脆性PVC管材的制备方法，其特征在于，包括以下步骤：
（1）将PVC120-150份、增韧剂5-12份、活性纳米碳酸钙6-8份、稳定剂8-12份、APAO4-10份进行高速混合；
（2）经冷混机使得物料冷却至45℃；
（3）用双螺杆挤出机挤出成粉，双螺杆挤出机的挤出温度为115℃。
CN201510436956.0A 2015-07-23 2015-07-23 一种抗低温脆性pvc管材及其制备方法 Pending CN105038006A (zh)