CN104213414A - 一种聚酰亚胺干法纺丝油剂 - Google Patents

一种聚酰亚胺干法纺丝油剂 Download PDF

Info

Publication number
CN104213414A
CN104213414A CN201410439681.1A CN201410439681A CN104213414A CN 104213414 A CN104213414 A CN 104213414A CN 201410439681 A CN201410439681 A CN 201410439681A CN 104213414 A CN104213414 A CN 104213414A
Authority
CN
China
Prior art keywords
parts
polyoxyethylene ether
spinning oil
fatty alcohol
diethanolamine salt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410439681.1A
Other languages
English (en)
Other versions
CN104213414B (zh
Inventor
王士华
苗岭
严成
张清华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU AOSHEN NEW MATERIAL CO Ltd
Original Assignee
JIANGSU AOSHEN NEW MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU AOSHEN NEW MATERIAL CO Ltd filed Critical JIANGSU AOSHEN NEW MATERIAL CO Ltd
Priority to CN201410439681.1A priority Critical patent/CN104213414B/zh
Publication of CN104213414A publication Critical patent/CN104213414A/zh
Application granted granted Critical
Publication of CN104213414B publication Critical patent/CN104213414B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种聚酰亚胺干法纺丝油剂，由下述重量份配比的原料组成，二甲基硅油30-60份、精炼矿物油10-30份、失水山梨醇单油酸酯聚氧乙烯醚3-9份、十二烷基磷酸酯二乙醇胺盐5-10份、十六烷基磷酸钾8-14份、脂肪醇聚氧乙烯醚10-20份。本发明由二甲基硅油、精炼矿物油、失水山梨醇单油酸酯聚氧乙烯醚、十二烷基磷酸酯二乙醇胺盐、十六烷基磷酸钾、脂肪醇聚氧乙烯醚组成，其配方合理，使用效果好，生产成本低。本发明还很好的解决了纤维之间静电大、退绕性不良及丝束集束不良等问题。

Description

一种聚酰亚胺干法纺丝油剂
技术领域
本发明涉及一种纺丝油剂，特别是一种聚酰亚胺干法纺丝油剂。
背景技术
聚酰亚胺纤维具有优异的热稳定性、耐辐射性能、不燃烧性，良好的力学性能，可在高温、放射和高腐蚀等极其恶劣的环境条件下长期使用，自上世纪90年代以来，其在高温滤料等方面到日益广泛的应用。
目前聚酰亚胺纤维的生产主要集中在国外且工艺路线都是湿法纺丝，干法工艺生产的聚酰亚胺纤维在国内外是首次开发，还处于开发生产的初期阶段，国内没有专用的纺丝油剂。因此，急需开发一种生产成本低、抗静电性优良且性能稳定的聚酰亚胺干法纺丝油剂。
发明内容
本发明要解决的技术问题是针对现有技术的不足，提出一种生产成本低、抗静电性优良且性能稳定，可解决退绕性不良及丝束集束不良等问题的聚酰亚胺干法纺丝油剂。
本发明要解决的技术问题是通过以下技术方案实现的，一种聚酰亚胺干法纺丝油剂，其特点是：由下述重量份配比的原料组成，二甲基硅油30-60份、精炼矿物油10-30份、失水山梨醇单油酸酯聚氧乙烯醚3-9份、十二烷基磷酸酯二乙醇胺盐5-10份、十六烷基磷酸钾8-14份、脂肪醇聚氧乙烯醚10-20份。
本发明要解决的技术问题还可以通过以下技术方案来进一步实现，由下述重量份配比的原料组成，二甲基硅油36份、精炼矿物油13份、失水山梨醇单油酸酯聚氧乙烯醚5份、十二烷基磷酸酯二乙醇胺盐7份、十六烷基磷酸钾10份、脂肪醇聚氧乙烯醚15份。
与现有技术相比，本发明由二甲基硅油、精炼矿物油、失水山梨醇单油酸酯聚氧乙烯醚、十二烷基磷酸酯二乙醇胺盐、十六烷基磷酸钾、脂肪醇聚氧乙烯醚组成，其配方合理，使用效果好，生产成本低。本发明还很好的解决了纤维之间静电大、退绕性不良及丝束集束不良等问题。
具体实施方式
以下进一步描述本发明的具体技术方案，以便于本领域的技术人员进一步地理解本发明，而不构成其权利的限制。
一种聚酰亚胺干法纺丝油剂，由下述重量份配比的原料组成，二甲基硅油30-60份、精炼矿物油10-30份、失水山梨醇单油酸酯聚氧乙烯醚3-9份、十二烷基磷酸酯二乙醇胺盐5-10份、十六烷基磷酸钾8-14份、脂肪醇聚氧乙烯醚10-20份。
将二甲基硅油和精炼矿物油混合均匀，升温至40℃，加入失水山梨醇单油酸酯聚氧乙烯醚，搅拌30分钟，升温至60℃，加入十六烷基磷酸钾和脂肪醇聚氧乙烯醚，搅拌20分钟，降温至40℃，再加入十二烷基磷酸酯二乙醇胺盐，继续搅拌40分钟，之后冷却至25℃，得到聚酰亚胺干法纺丝油剂。
实施例1，一种聚酰亚胺干法纺丝油剂，由下述重量份配比的原料组成，由下述重量份配比的原料组成，二甲基硅油36份、精炼矿物油13份、失水山梨醇单油酸酯聚氧乙烯醚5份、十二烷基磷酸酯二乙醇胺盐7份、十六烷基磷酸钾10份、脂肪醇聚氧乙烯醚15份。将二甲基硅油和精炼矿物油混合均匀，升温至40℃，加入失水山梨醇单油酸酯聚氧乙烯醚，搅拌30分钟，升温至60℃，加入十六烷基磷酸钾和脂肪醇聚氧乙烯醚，搅拌20分钟，降温至40℃，再加入十二烷基磷酸酯二乙醇胺盐，继续搅拌40分钟，之后冷却至25℃，得到聚酰亚胺干法纺丝油剂。
将实施例1与日本进口的聚酰亚胺干法纺丝油剂进行对比实验，油剂在纺丝过程中测定数据对比如下：
从上表可知，本发明的聚酰亚胺干法纺丝油剂与进口产品相比：
A.     本发明的聚酰亚胺干法纺丝油剂在低速下F/N摩擦较小，在高速下F/N摩擦较大；
B.     本发明的聚酰亚胺干法纺丝油剂的静电要小于进口油剂。
使用油剂后纺成聚酰亚胺纤维性能测试比较如下：
从上表可以看出，从对聚酰亚胺纤维的线密度、断裂强度、断裂伸长率等方面的测试结果可以看出，本发明的聚酰亚胺干法纺丝油剂在以上性能方面优于进口产品。
成品丝在使用时的各项性能测试比较如下：
 
从上表可以看出：本发明的聚酰亚胺干法纺丝油剂，在退绕张力、退绕性上和进口产品基本相同，但在抗静电效果上得到了显著提高。
实施例2，一种聚酰亚胺干法纺丝油剂，由下述重量份配比的原料组成，二甲基硅油30份、精炼矿物油30份、失水山梨醇单油酸酯聚氧乙烯醚3份、十二烷基磷酸酯二乙醇胺盐10份、十六烷基磷酸钾8份、脂肪醇聚氧乙烯醚20份。
实施例3，一种聚酰亚胺干法纺丝油剂，二甲基硅油60份、精炼矿物油10份、失水山梨醇单油酸酯聚氧乙烯醚9份、十二烷基磷酸酯二乙醇胺盐5份、十六烷基磷酸钾14份、脂肪醇聚氧乙烯醚10份。
实施例4，一种聚酰亚胺干法纺丝油剂，由下述重量份配比的原料组成，二甲基硅油31份、精炼矿物油22份、失水山梨醇单油酸酯聚氧乙烯醚7份、十二烷基磷酸酯二乙醇胺盐5份、十六烷基磷酸钾10份、脂肪醇聚氧乙烯醚16份。

Claims (1)

1.一种聚酰亚胺干法纺丝油剂，其特征在于：由下述重量份配比的原料组成，
   二甲基硅油                    30-60份
精炼矿物油                    10-30份
失水山梨醇单油酸酯聚氧乙烯醚    3-9份
十二烷基磷酸酯二乙醇胺盐       5-10份
十六烷基磷酸钾                 8-14份
脂肪醇聚氧乙烯醚              10-20份
根据权利要求1所述的聚酰亚胺干法纺丝油剂，其特征在于：由下述重量份配比的原料组成，
二甲基硅油                       36份
精炼矿物油                       13份
失水山梨醇单油酸酯聚氧乙烯醚      5份
十二烷基磷酸酯二乙醇胺盐          7份
十六烷基磷酸钾                   10份
脂肪醇聚氧乙烯醚                 15份。
CN201410439681.1A 2014-09-01 2014-09-01 一种聚酰亚胺干法纺丝油剂 Active CN104213414B (zh)