CN104212351A - 高速公路涂料 - Google Patents
高速公路涂料 Download PDFInfo
- Publication number
- CN104212351A CN104212351A CN201310735470.8A CN201310735470A CN104212351A CN 104212351 A CN104212351 A CN 104212351A CN 201310735470 A CN201310735470 A CN 201310735470A CN 104212351 A CN104212351 A CN 104212351A
- Authority
- CN
- China
- Prior art keywords
- motorway
- coupling agent
- silane coupling
- coating according
- expressway
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高速公路涂料,其主要组成成分有:乳化沥青、无机颜料、APP短纤维、分散剂及偶联剂等助剂:该高速公路涂料寿命长、耐水性能好、具有特别优良的耐摩擦性能。
Description
技术领域
本发明涉及精细化工技术领域,尤指一种高速公路涂料。
背景技术
高速公路上,高速行驶的多种多样的汽车、尤其是重载汽车,有很大的摩擦力和相当的冲击力,常用的水泥混凝土路面和沥青路面很容易出现损伤、龟裂:高速公路的维修不但费时、费力、费钱,也影响正常的运营,对用户带来不便,使经济效益严重下滑。
发明内容
本发明的目的旨在解决现有技术之不足,提供高速公路涂料,其技术方案是这样实现的:
一种高速公路涂料:其组分组成的质量百分比为:乳化沥青43-60%、无机颜料20-40%、APP短纤维3-5%、分散剂0.2-1.0%、含环氧基的硅烷偶联剂0.2-0.6%、去离子水10-20%、消泡剂与成膜助剂适量;所用的乳化沥青固含量不小于45%,pH值7.0-9.0,其成膜性能优良,成膜牢固、耐水、寿命长:所用的无机颜料是石英粉与重晶石粉质量比1:1的混合物,粒度为325目,通过硅烷偶联剂与成膜剂乳化沥青结合,使涂膜密实,与基材集采结合牢固;所用的含环氧基的硅烷偶联剂为硅烷偶联剂KH560;硅烷偶联剂KH560是目前发现的唯一的可用于水性环境的硅烷偶联剂,其不但使涂膜密实、牢固,而且使涂膜与基材结合牢固,整体性能极佳,耐摩擦、耐冲击、寿命长。
本发明高速公路涂料,制造简单,将各种原材料放入球磨机中研磨3-5小时,放出后过滤、调节粘度、包装即为成品。
具体实施方式
为了本发明的更好地理解与实施,下面给出具体实施例;
实施例一
将乳化沥青500g、无机颜料300g、APP短纤维40g、分散剂NNO 5g 、硅烷偶联剂KH560 4.5g、去离子水144g、消泡剂3.0g、成膜助剂乙二醇3.5g,放入实验用球磨机中研磨3小时,放出后过滤、调节粘度、包装即为成品。
实施例二
将乳化沥青500kg、无机颜料300kg、APP短纤维40kg、分散剂NNO 5kg 、硅烷偶联剂KH560 4.5kg、去离子水144kg、消泡剂3.0kg、成膜助剂乙二醇3.5kg,放入球磨机中研磨4小时,放出后过滤、调节粘度、包装即为成品。
实施例三
将乳化沥青250kg、无机颜料150kg、APP短纤维20kg、分散剂NNO 2.5kg 、硅烷偶联剂KH560 2.5kg、去离子水72kg、消泡剂1.5kg、成膜助剂乙二醇1.5kg,放入球磨机中研磨4小时,放出后过滤、调节粘度、包装即为成品。
以上述实施方式仅仅是对本发明的优选实施方式进行描述,并非对本明的范围进行限定,在不脱离本发明技术精神的前提下,本领域工程技术人员对本发明的技术方案作出的各种变形和改性,均应落入本发明的权利要求书确定的保护范围内。
Claims (5)
1.一种高速公路涂料,其特征是:其组分组成的质量百分比为:乳化沥青43-60%、无机颜料20-40%、APP短纤维3-5%、分散剂0.2-1.0%、含环氧基的硅烷偶联剂0.2-0.6%、去离子水10-20%、消泡剂与成膜助剂适量。
2.根据权利要求1所述的一种高速公路涂料,其特征是:所述的乳化沥青固含量不小于45%,pH值7.0-9.0。
3.根据权利要求1所述的一种高速公路涂料,其特征是:所述的无机颜料是石英粉与重晶石粉质量比1:1的混合物,粒度为325目。
4.根据权利要求1所述的一种高速公路涂料,其特征是:所述的APP短纤维的长度一般为3-5mm。
5.根据权利要求1所述的一种高速公路涂料,其特征是:所述的含环氧基的硅烷偶联剂为硅烷偶联剂KH560。