CN104211323A - 一种制造实验室用耐腐蚀、耐高温台面的方法 - Google Patents
一种制造实验室用耐腐蚀、耐高温台面的方法 Download PDFInfo
- Publication number
- CN104211323A CN104211323A CN201310211197.9A CN201310211197A CN104211323A CN 104211323 A CN104211323 A CN 104211323A CN 201310211197 A CN201310211197 A CN 201310211197A CN 104211323 A CN104211323 A CN 104211323A
- Authority
- CN
- China
- Prior art keywords
- corrosion
- table top
- resistant
- table surface
- high temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种制造实验室用耐腐蚀、耐高温台面的方法，包括如下步骤：一）分别取质量比如下的材料：1份不饱和树脂，1份100目的石英砂，1份300目的石英粉，0.024份的固化剂，0.015份的促进剂，0.02份的302胶衣，以及0.03份的乙烯基树脂和0.01份的特黑色素；二）将步骤一）中原材料混合均匀，加入水，搅拌混合成均匀粘稠乳状混合物；三）将步骤二）中所得粘稠乳状混合物倒入模具，风化干硬，出模即得仿水泥台面。通过不饱和树脂、石英砂、石英粉以及乙烯基树脂的混合后加水得均匀乳液，所制得的台面板，既具有水泥面板的硬度，同时使得该面板具有优良的耐腐蚀和耐高温性能。
Description
技术领域
本发明涉及一种制造实验室用耐腐蚀、耐高温台面的方法。
背景技术
实验室内的器材设备，需面临多种实验环境，其用途要求实验室内的器材设备具有一定耐腐蚀和耐高温的性能。而现有在使用的各类面板中，主要提供的功能为支撑力好，具有一定的强度和韧性，远远达不到实验室用器材设备的性能指标。
发明内容
本发明要解决的技术问题是提供一种制造实验室用耐腐蚀、耐高温台面的方法，可以有效提高台面耐腐蚀、耐高温的性能。
为解决上述技术问题，本发明采用的技术方案是：一种制造实验室用耐腐蚀、耐高温台面的方法，包括如下步骤：一）、分别取质量比如下的材料：1份不饱和树脂，1份100目的石英砂，1份300目的石英粉，0.024份的固化剂，0.015份的促进剂，0.02份的302胶衣，以及0.03份的乙烯基树脂和0.01份的特黑色素；二）、将步骤一）中原材料混合均匀，加入水，搅拌混合成均匀粘稠乳状混合物；三）、将步骤二）中所得粘稠乳状混合物倒入模具，风化干硬，出模即得仿水泥台面。
作为一种改进，所述步骤一）中的不饱和树脂为DC196不饱和树脂。
作为一种改进，所述步骤二）中加入水的质量为混合原材料的30%到50%。
作为一种改进，所述步骤二）中加入水的质量为混合原材料的40%。
本发明采用的技术方案，其有益效果在于：通过不饱和树脂、石英砂、 石英粉以及乙烯基树脂的混合后加水得均匀乳液，然后将所得乳液导入模具风干出模所制得的台面，既具有水泥面板的硬度，同时不饱和树脂的加入，使得该面板具有优良的耐腐蚀和耐高温性能。
具体实施方式
本发明提供的一种制造实验室用耐腐蚀、耐高温台面的方法，包括如下步骤：
一）、分别取质量比如下的材料：1份不饱和树脂，1份100目的石英砂，1份300目的石英粉，0.024份的固化剂，0.015份的促进剂，0.02份的302胶衣，以及0.03份的乙烯基树脂和0.01份的特黑色素；二）、将步骤一）中原材料混合均匀，加入水，搅拌混合成均匀粘稠乳状混合物；三）、将步骤二）中所得粘稠乳状混合物倒入模具，风化干硬，出模即得仿水泥台面。
本实施例中，所述步骤一）中的不饱和树脂为DC196不饱和树脂。
本实施例中，所述步骤二）中加入水的质量为混合原材料的40%。
除上述优选实施例外，本发明还有其他的实施方式，本领域技术人员可以根据本发明作出各种改变和变形，只要不脱离本发明的精神，均应属于本发明所附权利要求所定义的范围。
Claims (4)
1.一种制造实验室用耐腐蚀、耐高温台面的方法，其特征在于：包括如下步骤：一）、分别取质量比如下的材料：1份不饱和树脂，1份100目的石英砂，1份300目的石英粉，0.024份的固化剂，0.015份的促进剂，0.02份的302胶衣，以及0.03份的乙烯基树脂和0.01份的特黑色素；二）、将步骤一）中原材料混合均匀，加入水，搅拌混合成均匀粘稠乳状混合物；三）、将步骤二）中所得粘稠乳状混合物倒入模具，风化干硬，出模即得仿水泥台面。
2.根据权利要求1所述的一种制造实验室用耐腐蚀、耐高温台面的方法，其特征在于：所述步骤一）中的不饱和树脂为DC196不饱和树脂。
3.根据权利要求1所述的一种制造实验室用耐腐蚀、耐高温台面的方法，其特征在于：所述步骤二）中加入水的质量为混合原材料的30%到50%。
4.根据权利要求3所述的一种制造实验室用耐腐蚀、耐高温台面的方法，其特征在于：所述步骤二）中加入水的质量为混合原材料的40%。