Summary of the invention
In view of this, the present invention is directed to the disappearance of prior art existence, its main purpose is to provide one and takes off film liquid, its can effectively solve existing employing sodium hydroxide take off film exist take off the film time long, take off the sordid problem of film.
For achieving the above object, the present invention adopts following technical scheme:
One takes off film liquid, is made up of the raw material of following weight proportion:
Potassium hydroxide 80%~85%;
Trolamine 8.5%~15%;
Polyoxyethylene nonylphenol ether 21 1%~2%;
Ethylene glycol monobutyl ether 0.3%~0.5%;
Methyl alcohol 2%~3%;
Acetone 0.5%~1%.
The present invention compared with prior art has obvious advantage and beneficial effect, particularly, and as shown from the above technical solution:
What adopt the present invention formula takes off film liquid, and it takes off film speed and takes off film ability is nearly five times of sodium hydroxide, thereby has greatly improved production efficiency, and has effectively improved while taking off film copper face and taken off the problems such as film is not clean.
Embodiment
The open one of the present invention takes off film liquid, is made up of the raw material of following weight proportion:
Potassium hydroxide 80%~85%;
Trolamine 8.5%~15%;
Polyoxyethylene nonylphenol ether 21 1%~2%;
Ethylene glycol monobutyl ether 0.3%~0.5%;
Methyl alcohol 2%~3%;
Acetone 0.5%~1%.
The present invention will be described to use specific embodiment below, and " part " that following examples are used is based on weight.
Embodiment 1
80 weight part potassium hydroxide, 14 weight part trolamines, 1.8 weight part polyoxyethylene nonylphenol ether 21,0.4 weight part ethylene glycol monobutyl ethers, 2.8 weight part methyl alcohol and 1.0 weight part acetone are put into container successively to stir to make and takes off film liquid.
Embodiment 2
81 weight part potassium hydroxide, 15 weight part trolamines, 1.0 weight part polyoxyethylene nonylphenol ether 21,0.5 weight part ethylene glycol monobutyl ethers, 2.0 weight part methyl alcohol and 0.5 weight part acetone are put into container successively to stir to make and takes off film liquid.
Embodiment 3
82 weight part potassium hydroxide, 13 weight part trolamines, 2.0 weight part polyoxyethylene nonylphenol ether 21,0.4 weight part ethylene glycol monobutyl ethers, 2.1 weight part methyl alcohol and 0.5 weight part acetone are put into container successively to stir to make and takes off film liquid.
Embodiment 4
82.5 weight part potassium hydroxide, 11.6 weight part trolamines, 1.5 weight part polyoxyethylene nonylphenol ether 21,0.5 weight part ethylene glycol monobutyl ethers, 3.0 weight part methyl alcohol and 0.9 weight part acetone are put into container successively to stir to make and takes off film liquid.
Embodiment 5
83 weight part potassium hydroxide, 12 weight part trolamines, 1.7 weight part polyoxyethylene nonylphenol ether 21,0.45 weight part ethylene glycol monobutyl ethers, 2.0 weight part methyl alcohol and 0.85 weight part acetone are put into container successively to stir to make and takes off film liquid.
Embodiment 6
83.5 weight part potassium hydroxide, 10.2 weight part trolamines, 2.0 weight part polyoxyethylene nonylphenol ether 21,0.3 weight part ethylene glycol monobutyl ethers, 3.0 weight part methyl alcohol and 1.0 weight part acetone are put into container successively to stir to make and takes off film liquid.
Embodiment 7
84 weight part potassium hydroxide, 9.9 weight part trolamines, 1.6 weight part polyoxyethylene nonylphenol ether 21,0.5 weight part ethylene glycol monobutyl ethers, 3.0 weight part methyl alcohol and 1.0 weight part acetone are put into container successively to stir to make and takes off film liquid.
Embodiment 8
85 weight part potassium hydroxide, 8.5 weight part trolamines, 2.0 weight part polyoxyethylene nonylphenol ether 21,0.5 weight part ethylene glycol monobutyl ethers, 3.0 weight part methyl alcohol and 1.0 weight part acetone are put into container successively to stir to make and takes off film liquid.
Above embodiment's 1~8 takes off film liquid formula as shown in following table 1.
Table 1 embodiment's 1~8 takes off film liquid formula
The small size figure that film liquid is less than 0.1mm to thickness respectively that takes off that above-mentioned each embodiment is made takes off film, in the present embodiment, selection thickness is that the dry film of 80 μ m describes, take off film temperature and be chosen in 60 degree, measure taking off the film time, and adopting microscopic examination residue, specific experiment data are as shown in table 2 below.
The film liquid that takes off of table 2 embodiment 1~8 takes off the film time and residual
Embodiment |
1 |
2 |
3 |
4 |
5 |
6 |
7 |
8 |
Take off the film time (min) |
5.0 |
4.8 |
4.9 |
5.0 |
5.0 |
4.8 |
5.1 |
4.7 |
Residue |
Nothing |
Nothing |
Nothing |
Nothing |
Nothing |
Nothing |
Nothing |
Nothing |
As shown in Table 2: what adopt the present invention formula takes off film liquid, and it takes off film speed and takes off film ability is nearly five times of sodium hydroxide, thereby has greatly improved production efficiency, and effectively improved while taking off film copper face and taken off the problems such as film is not clean.
The above, it is only preferred embodiment of the present invention, not technical scope of the present invention is imposed any restrictions, therefore any trickle amendment, equivalent variations and modification that every foundation technical spirit of the present invention is done above embodiment all still belong in the scope of technical solution of the present invention.