CN104194445A - Chlorinated rubber exterior wall coating - Google Patents
Chlorinated rubber exterior wall coating Download PDFInfo
- Publication number
- CN104194445A CN104194445A CN201410482986.0A CN201410482986A CN104194445A CN 104194445 A CN104194445 A CN 104194445A CN 201410482986 A CN201410482986 A CN 201410482986A CN 104194445 A CN104194445 A CN 104194445A
- Authority
- CN
- China
- Prior art keywords
- parts
- wall coating
- exterior wall
- chlorinated rubber
- external wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a chlorinated rubber exterior wall coating, which is prepared from the following raw materials in parts by weight: 100 parts of chlorinated rubber, 2-10 parts of linaloe wood oil, 15-25 parts of china clay, 10-20 parts of nitrobenzene, 30-40 parts of chlorcosane, 15-35 parts of methacrylic acid, 35-55 parts of bentonite, 25-35 parts of a plastifier, 20-30 parts of ethyl alcohol, 20-30 parts of butyl acrylate, 5-15 parts of xylene, 10-30 parts of a mildewproof agent, 15-35 parts of polyvinyl alcohol, and 20-40 parts of methyl methacrylate. The chlorinated rubber exterior wall coating is uniform after stirring, and the solid content is 50-60%; the surface drying time is 1-2 hours, the chlorinated rubber exterior wall coating does not bubble after being soaked in water for 5-7 days and powder does not drop off; the exterior wall coating is not caked at the temperature of 10 DEG C below zero, and after the exterior wall coating is soaked in alkaline water for 48-72 hours, the exterior wall coating is still normal; and exterior wall coating films are scouring resistant, and after the exterior wall coating films are scoured for 1200-1500 times, bottoms are not exposed, so that the exterior wall coating can be widely produced and can be used for continuously replacing existing materials.
Description
Technical field
The application belongs to paint field, relates in particular to a kind of chlorinated rubber external wall coating.
Background technology
Coating, in China, tradition name is called paint.So-called coating is to be coated in protected or decorated body surface; and can form with coated article the continuous film of firm attachment; normally take resin or oil or emulsion as main; add or do not add pigment, filler; add corresponding additive, with organic solvent or the formulated thick liquid of clorafin.China's coating circle more authoritative < < coating process > > mono-book is definition like this: " coating is a kind of material; this material can be coated in article surface by different construction technologies, forms and adheres to firmly, has some strength, continuous solid film.The film common name forming is like this filmed, and claims again paint film or coating." paint finishing can and form the material of complete and tough and tensile protective membrane with the fine bonding of body material in body surface, is called coating.Coating and paint are identical concepts.Paint is people's custom titles used for a long time, introduces after China, just utilizes in building trade always.The effect of coating may be summarized to be three aspects: provide protection, decoration function, specific function effect.The general composition of coating: comprise filmogen, color stuffing, solvent, auxiliary agent.
China's paint industry grows stronger day by day under the promotion of downstream industry, and as the building coating of one of them branch, has also obtained significant progress.Statistic data demonstration, within 2011, Chinese architecture coating amounts to approximately 351.82 ten thousand tons of output, increases by a year-on-year basis more than 30%.As can be seen here, although Chinese architecture paint industry has experienced the impact of global financial crisis in 2008, the pressure that the prices of raw and semifnished materials go up and Central Bank increases the interest and brings, its growth momentum does not still subtract, and is also keeping higher rate of increase.Due to reasons such as cement contraction or construction wrong, external wall can produce crack, the phenomenon such as seep water, leak, this problem causes social extensive concern, should develop multi-functional elastic water-proof wallcovering products such as integrating decoration, anticracking, waterproof from 1997.
Exterior coating, for brushing the outer wall face of building, so a most important index is exactly ultraviolet radiation resisting, requires to reach long-time irradiation nondiscoloration.Exterior coating has also required water repelling property, and requiring has from washing property.It is hard and smooth, dirty once rushing that paint film is wanted.It is energy because it also has a water resisting property that exterior coating can be used for interior wall brushing; And interior wall coating does not possess anti-solarization function, so can not be interior wall coating when exterior coating use.Development has the high performance outer wall paint that high-weatherability, contamination resistance and unfading are good, improve weathering resistance and the contamination resistance of aqueous latex paint, improves solvent type exterior wall coating property.And universal along with humanity concept, and the formation of novel harmonious society, design the chlorinated rubber external wall coating that a kind of time of drying is short and low-temperature stability is excellent and be very important.
Summary of the invention
The technical problem solving:
The application, for above-mentioned technical problem, provides a kind of chlorinated rubber external wall coating, solves existing chlorinated rubber external wall coating water tolerance and alkali resistance is poor, time of drying is long, the not resistance to technical problem such as scrub.
Technical scheme:
A chlorinated rubber external wall coating, the raw materials by weight portion proportioning of described chlorinated rubber external wall coating is as follows: 100 parts of chlorinated rubbers; Shiu oil 2-10 part; China clay 15-25 part; Oil of mirbane 10-20 part; Clorafin 30-40 part; Methacrylic acid 15-35 part; Wilkinite 35-55 part; Softening agent 25-35 part; Ethanol 20-30 part; Butyl acrylate 20-30 part; Dimethylbenzene 5-15 part; Mould inhibitor 10-30 part; Polyvinyl alcohol 15-35 part; Methyl methacrylate 20-40 part.
As a preferred technical solution of the present invention: the raw materials by weight portion proportioning of described chlorinated rubber external wall coating is as follows: 100 parts of chlorinated rubbers; 6 parts of shiu oils; 20 parts of china clay; 15 parts, oil of mirbane; 35 parts of clorafins; 25 parts of methacrylic acids; 45 parts of wilkinites; 30 parts, softening agent; 25 parts of ethanol; 25 parts of butyl acrylates; 10 parts of dimethylbenzene; 20 parts of mould inhibitors; 25 parts of polyvinyl alcohol; 30 parts of methyl methacrylates.
As a preferred technical solution of the present invention: described softening agent adopts dibutyl phthalate.
As a preferred technical solution of the present invention: described mould inhibitor adopts zinc naphthenate.
Beneficial effect:
A kind of chlorinated rubber external wall coating of the present invention adopts above technical scheme compared with prior art, has following technique effect: 1, product is even after stirring, solid content 50-60%; 2, surface drying time 1-2h soaks non-foaming after 5-7d, dry linting not in water; 3 ,-10 ℃ do not lump, and soak 48-72h without extremely in buck; 4, film resistance to scrub 1200-1500 time not show-through, can the not division of history into periods of widespread production for current material.
Embodiment
Embodiment 1:
A chlorinated rubber external wall coating, its raw materials by weight portion proportioning is as follows: 100 parts of chlorinated rubbers; 2 parts of shiu oils; 15 parts of china clay; 10 parts, oil of mirbane; 30 parts of clorafins; 15 parts of methacrylic acids; 35 parts of wilkinites; 25 parts of dibutyl phthalates; 20 parts of ethanol; 20 parts of butyl acrylates; 5 parts of dimethylbenzene; 10 parts of zinc naphthenates; 15 parts of polyvinyl alcohol; 20 parts of methyl methacrylates.
Shiu oil, china clay, oil of mirbane, clorafin, methacrylic acid and wilkinite are packed in ball milling, ball milling 30min, then add dibutyl phthalate, ethanol, butyl acrylate, dimethylbenzene and zinc naphthenate, after ball milling 30min, add chlorinated rubber, continue ball milling 4h, finally, remaining raw material is all dropped into ball milling 30min in ball mill, both obtained finished product.
Product solid content 50%; Surface drying time 2h soaks non-foaming after 5d, dry linting not in water;-10 ℃ do not lump, and soak 48h without extremely in buck; Film resistance to scrub 1200 times not show-through.
Embodiment 2:
A chlorinated rubber external wall coating, its raw materials by weight portion proportioning is as follows: 100 parts of chlorinated rubbers; 10 parts of shiu oils; 25 parts of china clay; 20 parts, oil of mirbane; 40 parts of clorafins; 35 parts of methacrylic acids; 55 parts of wilkinites; 35 parts of dibutyl phthalates; 30 parts of ethanol; 30 parts of butyl acrylates; 15 parts of dimethylbenzene; 30 parts of zinc naphthenates; 35 parts of polyvinyl alcohol; 40 parts of methyl methacrylates.
Shiu oil, china clay, oil of mirbane, clorafin, methacrylic acid and wilkinite are packed in ball milling, ball milling 30min, then add dibutyl phthalate, ethanol, butyl acrylate, dimethylbenzene and zinc naphthenate, after ball milling 30min, add chlorinated rubber, continue ball milling 5h, finally, remaining raw material is all dropped into ball milling 30min in ball mill, both obtained finished product.
Product solid content 60%; Surface drying time 1.5h soaks non-foaming after 6d, dry linting not in water;-10 ℃ do not lump, and soak 56h without extremely in buck; Film resistance to scrub 1400 times not show-through.
Embodiment 3:
A chlorinated rubber external wall coating, its raw materials by weight portion proportioning is as follows: 100 parts of chlorinated rubbers; 6 parts of shiu oils; 20 parts of china clay; 15 parts, oil of mirbane; 35 parts of clorafins; 25 parts of methacrylic acids; 45 parts of wilkinites; 30 parts of dibutyl phthalates; 25 parts of ethanol; 25 parts of butyl acrylates; 10 parts of dimethylbenzene; 20 parts of zinc naphthenates; 25 parts of polyvinyl alcohol; 30 parts of methyl methacrylates.
Shiu oil, china clay, oil of mirbane, clorafin, methacrylic acid and wilkinite are packed in ball milling, ball milling 30min, then add dibutyl phthalate, ethanol, butyl acrylate, dimethylbenzene and zinc naphthenate, after ball milling 30min, add chlorinated rubber, continue ball milling 4.5h, finally, remaining raw material is all dropped into ball milling 30min in ball mill, both obtained finished product.
Product solid content 55%; Surface drying time 1h soaks non-foaming after 7d, dry linting not in water;-10 ℃ do not lump, and soak 72h without extremely in buck; Film resistance to scrub 1500 times not show-through.
Composition all components in above embodiment all can business be bought.
Above-described embodiment is just for content of the present invention is set forth, rather than restriction, therefore in the implication suitable with claims of the present invention and any change in scope, all should think to be included in the scope of claims.
Claims (4)
1. a chlorinated rubber external wall coating, is characterized in that the raw materials by weight portion proportioning of described chlorinated rubber external wall coating is as follows: 100 parts of chlorinated rubbers; Shiu oil 2-10 part; China clay 15-25 part; Oil of mirbane 10-20 part; Clorafin 30-40 part; Methacrylic acid 15-35 part; Wilkinite 35-55 part; Softening agent 25-35 part; Ethanol 20-30 part; Butyl acrylate 20-30 part; Dimethylbenzene 5-15 part; Mould inhibitor 10-30 part; Polyvinyl alcohol 15-35 part; Methyl methacrylate 20-40 part.
2. a kind of chlorinated rubber external wall coating according to claim 1, is characterized in that the raw materials by weight portion proportioning of described chlorinated rubber external wall coating is as follows: 100 parts of chlorinated rubbers; 6 parts of shiu oils; 20 parts of china clay; 15 parts, oil of mirbane; 35 parts of clorafins; 25 parts of methacrylic acids; 45 parts of wilkinites; 30 parts, softening agent; 25 parts of ethanol; 25 parts of butyl acrylates; 10 parts of dimethylbenzene; 20 parts of mould inhibitors; 25 parts of polyvinyl alcohol; 30 parts of methyl methacrylates.
3. a kind of chlorinated rubber external wall coating according to claim 1, is characterized in that: described softening agent adopts dibutyl phthalate.
4. a kind of chlorinated rubber external wall coating according to claim 1, is characterized in that: described mould inhibitor adopts zinc naphthenate.