CN104194344B - 一种导电性增强的橡胶 - Google Patents
一种导电性增强的橡胶 Download PDFInfo
- Publication number
- CN104194344B CN104194344B CN201410480267.5A CN201410480267A CN104194344B CN 104194344 B CN104194344 B CN 104194344B CN 201410480267 A CN201410480267 A CN 201410480267A CN 104194344 B CN104194344 B CN 104194344B
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- electric conductivity
- strengthens
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种导电性增强的橡胶，由下列重量份的原料制成：硅橡胶150‑300份、偶联剂10‑50份、增塑剂20‑80份、硫化剂30‑50份、防老剂20‑50份、阻燃剂10‑30份、补强剂20‑40份和导电助剂10‑30份。本发明所述的导电性增强的橡胶具有增强的导电性，十分适于用在通讯、电厂等领域。
Description
技术领域
本发明涉及橡胶领域，具体的说，本发明涉及一种导电性增强的橡胶。
背景技术
橡胶是具有可逆形变的高弹性聚合物材料，在室温下富有弹性，在很小的外力作用下能产生较大形变，除去外力后能恢复原状。橡胶属于完全无定型聚合物，导电橡胶通常是指体积电阻在109的欧姆厘米以内，由于橡胶是优良的绝缘体，体积电阻大于1014左右。导电炭黑填充的导电橡胶，体积电阻通常可保持在几千欧姆，由于现有的配方中使用了单一的炭黑，其抗拉强度只能达到12Mpa，远远不能满足实际的需要。
发明内容
本发明的目的在于提供一种导电性增强的橡胶。
为了实现本发明的目的，本发明提供一种导电性增强的橡胶，由下列重量份的原料制成：硅橡胶150-300份、偶联剂10-50份、增塑剂20-80份、硫化剂30-50份、防老剂20-50份、阻燃剂10-30份、补强剂20-40份和导电助剂10-30份。
优选地，本发明所述的导电性增强的橡胶由下列重量份的原料制成：硅橡胶180份、偶联剂15份、增塑剂30份、硫化剂35份、防老剂25份、阻燃剂15份、补强剂25份和导电助剂20份。
更优选地，所述偶联剂为γ-巯丙基三甲氧基硅烷。
更优选地，所述增塑剂为二甘醇单丁醚己二酸酯。
更优选地，所述硫化剂为过氧化二异丙苯。
更优选地，所述防老剂为N-(1，3-二甲基)丁基-N’-苯基对苯二胺。
更优选地，所述阻燃剂为氢氧化镁。
更优选地，所述补强剂为炭黑。
更优选地，所述导电助剂为4-[(6-溴代-4-氧代-2-硫代-1，2，3，4-四氢喹唑啉)甲基]苯甲酸。
本发明还提供4-[(6-溴代-4-氧代-2-硫代-1，2，3，4-四氢喹唑啉)甲基]苯甲酸在用作橡胶导电助剂中的用途。
本发明所述的导电性增强的橡胶具有增强的导电性，十分适于用在通讯、电厂等领域。
具体实施方式
以下通过具体实施方式的描述对本发明作进一步说明，但这并非是对本发明的限制，本领域技术人员根据本发明的基本思想，可以做出各种修改或改进，但是只要不脱离本发明的基本思想，均在本发明的范围之内。
实施例1
称取硅橡胶1800克、γ-巯丙基三甲氧基硅烷150克、二甘醇单丁醚己二酸酯300克、过氧化二异丙苯350克、N-(1，3-二甲基)丁基-N’-苯基对苯二胺250克、氢氧化镁150克、炭黑250克和4-[(6-溴代-4-氧代-2-硫代-1，2，3，4-四氢喹唑啉)甲基]苯甲酸200克；
将双辊开炼机的前辊温控制在120℃，后辊温控制在110℃，将硅橡胶、γ-巯丙基三甲氧基硅烷、二甘醇单丁醚己二酸酯、过氧化二异丙苯、N-(1，3-二甲基)丁基-N’-苯基对苯二胺、氢氧化镁、炭黑和4-[(6-溴代-4-氧代-2-硫代-1，2，3，4-四氢喹唑啉)甲基]苯甲酸依次加入双辊开炼机中，薄通5次，然后静置5小时，转移到QLB-D400X400X2型平板硫化机中压制片材，平板硫化机模板温度为140℃，模压力为0.5Mpa，模压时间10分钟。
实施例2
按照和实施例1相同的方式制备导电性增强的橡胶，不同之处在于不使用4-[(6-溴代-4-氧代-2-硫代-1，2，3，4-四氢喹唑啉)甲基]苯甲酸。
实验例
性能测试
(1)ASTMD412-1998(2002)来测定橡胶的拉伸强度；
(2)GB/T1692-1992来测定橡胶绝缘电阻率。
结果
实施例1的样品：拉伸强度为18.5Mpa，体积电阻率为3.3×107Ω·cm。
实施例2的样品：拉伸强度为13.2Mpa，体积电阻率为1.6×108Ω·cm。
由上述结果可见，在加入导电助剂之后，橡胶的强度和导电性得到显著增强，并且加入前和加入后结果进行比较，差异具有统计学意义(P＜0.05)。
Claims (2)
1.一种导电性增强的橡胶，其特征在于，由下列重量份的原料制成：硅橡胶180份、γ-巯丙基三甲氧基硅烷15份、二甘醇单丁醚己二酸酯30份、过氧化二异丙苯35份、N-(1,3-二甲基)丁基-N’-苯基对苯二胺25份、氢氧化镁15份、炭黑25份和4-[(6-溴代-4-氧代-2-硫代-1,2,3,4-四氢喹唑啉)甲基]苯甲酸20份。
2.4-[(6-溴代-4-氧代-2-硫代-1,2,3,4-四氢喹唑啉)甲基]苯甲酸在用作橡胶导电助剂中的用途。