CN104176977A - 一种使用废旧陶瓷制成的仿石涂料及其制作方法 - Google Patents

一种使用废旧陶瓷制成的仿石涂料及其制作方法 Download PDF

Info

Publication number
CN104176977A
CN104176977A CN201310188377.XA CN201310188377A CN104176977A CN 104176977 A CN104176977 A CN 104176977A CN 201310188377 A CN201310188377 A CN 201310188377A CN 104176977 A CN104176977 A CN 104176977A
Authority
CN
China
Prior art keywords
stone
coating
emulsion
water
waste ceramic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310188377.XA
Other languages
English (en)
Inventor
张力
孙阳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LIAONING MINGSHANG BUILDING MATERIAL INDUSTRIAL Co Ltd
Original Assignee
LIAONING MINGSHANG BUILDING MATERIAL INDUSTRIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LIAONING MINGSHANG BUILDING MATERIAL INDUSTRIAL Co Ltd filed Critical LIAONING MINGSHANG BUILDING MATERIAL INDUSTRIAL Co Ltd
Priority to CN201310188377.XA priority Critical patent/CN104176977A/zh
Publication of CN104176977A publication Critical patent/CN104176977A/zh
Pending legal-status Critical Current

Abstract

一种使用废旧陶瓷制成的仿石涂料,包括色浆和仿石涂料。色浆包括:水、粉碎陶瓷、氧化铁黄和氧化铁红。仿石涂料配方:水、增稠剂、乳液和消泡剂。其制作方法为:1、水、乳液和憎水剂低速分散机进行分散。2、转移至高速分散机;同时加入为混合物质量比5%的石英砂和10%的乳液进行共和混合分散。3、取石英砂经过水洗处理,加入粉碎的废旧陶瓷,同时加入色浆;4、烘干、煅烧、冷却,得到成品。废旧陶瓷经过粉碎、筛分、高温煅烧着色,具有色彩艳丽,稳定均匀、永不退色、高质感的特点,实现了废旧陶瓷的再次利用,具有节能环保的特点。为高耐污、高粘接强度、高耐久性的仿石建材。

Description

一种使用废旧陶瓷制成的仿石涂料及其制作方法
技术领域
本发明属于仿石涂料及其制作方法领域,特别涉及一种使用废旧陶瓷制成的仿石涂料及其制作方法。
背景技术
目前制作的仿石涂料存在色彩不均匀,染色不耐久的问题,造成目前的仿石涂料的稳定性差。
发明内容
本发明的目的是提供一种色彩均匀,染色耐久的仿石涂料,解决目前仿石涂料的稳定性差的问题。
采用的技术方案是:
一种使用废旧陶瓷制成的仿石涂料,包括色浆和仿石涂料。其特征在于:
色浆包括:水、粉碎陶瓷、氧化铁黄和氧化铁红,其质量比为1-2:90-95:1-3:1-3上述比例均为质量比。
仿石涂料配方:水、增稠剂、乳液和消泡剂。1-2:10-20:10-15:1-3。
色浆和仿石涂料质量比为5:7。
制作如权利要求1所述的一种使用废旧陶瓷制成的仿石涂料的方法,其特征在于:包括下列步骤:
第一步:取质量比为:水10-20、乳液5-10和憎水剂2-9,放入低速分散机进行分散,500转/分。
第二步:将上一步低速分散得到的混合物转移至高速分散机。同时加入为混合物质量比5%的石英砂,以及混合物质量比10%的乳液进行共和混合,1500转/分进行分散。
第三步、取石英砂100目,经过水洗处理,加入粉碎的废旧陶瓷,同时加入色浆。
第四步、将上一步得到的混合物放入烘干炉500℃,1-2小时 烘干,然后转入回转炉煅烧2-3小时,700℃。
第五步,冷却,得到成品。
    本申请中所述的比例和百分数均为质量比和质量百分数。
其优点在于:
废旧陶瓷经过粉碎、筛分、高温煅烧着色,具有色彩艳丽,稳定均匀、永不退色、高质感的特点,实现了废旧陶瓷的再次利用,具有节能环保的特点。为高耐污、高粘接强度、高耐久性的仿石建材。
具体实施方式
实施例1
一种使用废旧陶瓷制成的仿石涂料,包括色浆和仿石涂料。
色浆包括:水1、粉碎陶瓷90、氧化铁黄 1  (规格S110)和氧化铁红1 (规格S920)。上述比例均为质量比。
仿石涂料配方:水1、增稠剂10、乳液10和消泡剂1。上述比例均为质量比。
色浆和仿石涂料质量比为5:7。
一种使用废旧陶瓷制成的仿石涂料的生产方法,包括下列步骤:
第一步:取质量比为:水10、乳液5和憎水剂2,放入低速分散机进行分散,500转/分。
第二步:将上一步低速分散得到的混合物转移至高速分散机。同时加入为混合物质量比5%的石英砂(100目),以及混合物质量比10%的乳液进行共和混合,1500转/分进行分散。
第三步、取石英砂100目,经过水洗处理,加入粉碎的废旧陶瓷,同时加入色浆。
第四步、将上一步得到的混合物放入烘干炉500℃,1小时 烘干,然后转入回转炉煅烧2小时,700℃。
第五步,冷却,得到成品。
实施例2
一种使用废旧陶瓷制成的仿石涂料,包括色浆和仿石涂料。
色浆包括:水2、粉碎陶瓷95、氧化铁黄3 (规格S110)和氧化铁红3(规格S920)。上述比例均为质量比。
仿石涂料配方:水2、增稠剂20、乳液(丙烯酸树脂) 15和消泡剂3。
一种使用废旧陶瓷制成的仿石涂料的生产方法,包括下列步骤:
第一步:取质量比为:水20、乳液10和憎水剂9,放入低速分散机进行分散,500转/分。
第二步:将上一步低速分散得到的混合物转移至高速分散机。同时加入为混合物质量比5%的石英砂(100目),以及混合物质量比10%的乳液进行共和混合,1500转/分进行分散。
第三步、取石英砂100目,经过水洗处理,加入粉碎的废旧陶瓷,同时加入色浆。
第四步、将上一步得到的混合物放入烘干炉500℃,2小时 烘干,然后转入回转炉煅烧3小时,700℃。
第五步,冷却,得到成品。
实施例3
一种使用废旧陶瓷制成的仿石涂料,包括色浆和仿石涂料。
色浆包括:水1.5、粉碎陶瓷92、氧化铁黄 2.5 (规格S110)。上述比例均为质量比。
仿石涂料配方:水1.5、增稠剂15、乳液12和消泡剂2。
一种使用废旧陶瓷制成的仿石涂料的生产方法,包括下列步骤:
第一步:取质量比为:水12、乳液8和憎水剂7,放入低速分散机进行分散,500转/分。
第二步:将上一步低速分散得到的混合物转移至高速分散机。同时加入为混合物质量比5%的石英砂(100目),以及混合物质量比10%的乳液进行共和混合,1500转/分进行分散。
第三步、取石英砂100目,经过水洗处理,加入粉碎的废旧陶瓷,同时加入色浆。
第四步、将上一步得到的混合物放入烘干炉500℃,1.6小时 烘干,然后转入回转炉煅烧2.5小时,700℃。
第五步,冷却,得到成品。

Claims (2)

1.一种使用废旧陶瓷制成的仿石涂料,包括色浆和仿石涂料;其特征在于:
色浆包括:水、粉碎陶瓷、氧化铁黄和氧化铁红,其质量比为1-2:90-95:1-3:1-3上述比例均为质量比;
仿石涂料配方:水、增稠剂、乳液和消泡剂;1-2:10-20:10-15:1-3;
色浆和仿石涂料质量比为5:7。
2.制作如权利要求1所述的一种使用废旧陶瓷制成的仿石涂料的方法,其特征在于:包括下列步骤:
第一步:取质量比为:水10-20、乳液5-10和憎水剂2-9,放入低速分散机进行分散,500转/分;
第二步:将上一步低速分散得到的混合物转移至高速分散机;同时加入为混合物质量比5%的石英砂,以及混合物质量比10%的乳液进行共和混合,1500转/分进行分散;
第三步、取石英砂100目,经过水洗处理,加入粉碎的废旧陶瓷,同时加入色浆;
第四步、将上一步得到的混合物放入烘干炉500℃,1-2小时 烘干,然后转入回转炉煅烧2-3小时,700℃;
第五步,冷却,得到成品。
CN201310188377.XA 2013-05-21 2013-05-21 一种使用废旧陶瓷制成的仿石涂料及其制作方法 Pending CN104176977A (zh)