CN104162746A - 一种新型导流孔抗变形焊接方法 - Google Patents

一种新型导流孔抗变形焊接方法 Download PDF

Info

Publication number
CN104162746A
CN104162746A CN201310184173.9A CN201310184173A CN104162746A CN 104162746 A CN104162746 A CN 104162746A CN 201310184173 A CN201310184173 A CN 201310184173A CN 104162746 A CN104162746 A CN 104162746A
Authority
CN
China
Prior art keywords
deflector hole
welding
deformation
welding method
novel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310184173.9A
Other languages
English (en)
Inventor
李刚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHONGYU ENVIRONMENTAL TECHNOLOGY Co Ltd
Original Assignee
ZHONGYU ENVIRONMENTAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHONGYU ENVIRONMENTAL TECHNOLOGY Co Ltd filed Critical ZHONGYU ENVIRONMENTAL TECHNOLOGY Co Ltd
Priority to CN201310184173.9A priority Critical patent/CN104162746A/zh
Publication of CN104162746A publication Critical patent/CN104162746A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种新型导流孔抗变形焊接方法，其特征是，包含以下步骤,步骤S1：制造待焊接配件，具体到膜工艺处理设备双向导流孔套环的2个组件；步骤S2：制造符合设计要求的焊装模具，按照双向导流孔套环成型件的公差需求，制造合格的模具；步骤S3：选用新型低温软性抗疲劳焊料，通入二氧化碳气体形成环状冷却区，进行焊接；步骤S4：焊接完成，改变二氧化碳气体成风洞，获得理想焊接件。本发明的导流孔抗变形焊接方法，能够解决传统焊接技术带来的产品变形问题，减少了产品的报废率，提高了双向导流孔套环的质量和使用的工艺可靠性。

Description

一种新型导流孔抗变形焊接方法
技术领域
本发明涉及水处理膜工艺设备领域，更具体的说，是一种自主开发的新型导流孔抗变形焊接方法，专门应用于振动膜水处理工艺设备具有超高平整度需求和抗变形需求的焊接件应用上面。
背景技术
焊接技术在工业中广泛应用，最常见也最难解决的问题，那就是焊接变形，焊接变形有许多种类，不同种类的焊接变形所产生的原因也不尽相同。能够解决变形的常用工艺措施是采用反变形法，通过事先估计好焊接结构变形的大小和方向，然后在组合点固焊时给予一个相反方向的变形来抵消焊接变形,这是使焊后构件保持设计要求的一种工艺方法。
发明内容
本发明的目的是提供一种新型导流孔抗变形焊接方法，解决现有焊接技术中焊接变形的问题。
本发明解决其技术问题所采用的技术方案是：
一种新型导流孔抗变形焊接方法，其特征是，
包含以下步骤：
步骤S1：制造待焊接配件，具体到膜工艺处理设备双向导流孔套环的2个组件；
步骤S2：制造符合设计要求的焊装模具，按照双向导流孔套环成型件的公差需求，制造合格的模具；
步骤S3：选用新型低温软性抗疲劳焊料，通入二氧化碳气体形成环状冷却区，进行焊接；
步骤S4：焊接完成，改变二氧化碳气体成风洞，获得理想焊接件。
本发明的有益效果是：
1、在焊接过程中，此方法是将零部件加以固定，通过采用焊接夹具，增加结构在焊接时的刚性，同时采用和双向导流孔套环公差要求匹配的工装模具，保持焊接件整体温度一致，平衡金属热变形力，矫正焊接构件的局部变形，提高双向导流孔套环的抗变形能力，达到平整度需求，解决了焊接件典型的对角变形和波浪变形等问题；
2、焊接新技术中，采用新型低温软性抗疲劳焊料，导流孔抗变形焊接方法中，对焊接剂的优选，采用低温软性抗疲劳焊料应用，降低焊接件的疲劳应力，减少金属原子间层错缺陷，提高使用寿命的抗疲劳强度。
附图说明
图1为本发明的工艺流程示意图。
图2为本发明的所焊接的成品振动膜处理设备用导流孔套环的立体结构示意图。
具体实施方式
面结合具体实施例，进一步阐述本发明。应理解，这些实施例仅用于说明本发明而不用于限制本发明的范围。此外应理解，在阅读了本发明讲授的内容之后，本领域技术人员可以对本发明作各种改动或修改，这些等价形式同样落在申请所附权利要求书所限定的范围。
如图1、2所示，一种新型导流孔抗变形焊接方法，其特征是，包含以下步骤,
步骤S1：制造待焊接配件，具体到膜工艺处理设备双向导流孔套环的2个组件；
步骤S2：制造符合设计要求的焊装模具，按照双向导流孔套环成型件的公差需求，制造合格的模具；
步骤S3：选用新型低温软性抗疲劳焊料，通入二氧化碳气体形成环状冷却区，进行焊接；
步骤S4：焊接完成，改变二氧化碳气体成风洞，获得理想焊接件。
在焊接过程中，此方法是将零部件加以固定，通过采用焊接夹具，增加结构在焊接时的刚性，同时采用和双向导流孔套环公差要求匹配的工装模具，保持焊接件整体温度一致，平衡金属热变形力，矫正焊接构件的局部变形，提高双向导流孔套环的抗变形能力，达到平整度需求，解决了焊接件典型的对角变形和波浪变形等问题；
焊接新技术中，采用新型低温软性抗疲劳焊料。导流孔抗变形焊接方法中，对焊接剂的优选，采用低温软性抗疲劳焊料应用，降低焊接件的疲劳应力，减少金属原子间层错缺陷，提高使用寿命的抗疲劳强度。

Claims (1)

1.一种新型导流孔抗变形焊接方法，其特征是，包含以下步骤,
步骤S1：制造待焊接配件，具体到膜工艺处理设备双向导流孔套环的2个组件；
步骤S2：制造符合设计要求的焊装模具，按照双向导流孔套环成型件的公差需求，制造合格的模具；
步骤S3：选用新型低温软性抗疲劳焊料，通入二氧化碳气体形成环状冷却区，进行焊接；
步骤S4：焊接完成，改变二氧化碳气体成风洞，获得理想焊接件。
CN201310184173.9A 2013-05-19 2013-05-19 一种新型导流孔抗变形焊接方法 Pending CN104162746A (zh)