CN104151767A - 一种填充改性abs材料 - Google Patents

一种填充改性abs材料 Download PDF

Info

Publication number
CN104151767A
CN104151767A CN201410394716.4A CN201410394716A CN104151767A CN 104151767 A CN104151767 A CN 104151767A CN 201410394716 A CN201410394716 A CN 201410394716A CN 104151767 A CN104151767 A CN 104151767A
Authority
CN
China
Prior art keywords
filling
parts
abs material
modified abs
combination
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410394716.4A
Other languages
English (en)
Inventor
陆春华
陆培芳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU EXCELLENCE ENGINEERING PLASTICS Co Ltd
Original Assignee
SUZHOU EXCELLENCE ENGINEERING PLASTICS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU EXCELLENCE ENGINEERING PLASTICS Co Ltd filed Critical SUZHOU EXCELLENCE ENGINEERING PLASTICS Co Ltd
Priority to CN201410394716.4A priority Critical patent/CN104151767A/zh
Publication of CN104151767A publication Critical patent/CN104151767A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种填充改性ABS材料，由以下重量份数的组分组成：ABS，30～60份；茂金属聚烯烃弹性体，15～20份；增韧剂，1～3份；抗氧剂，1～5份；热稳定剂，2～5份；相容剂，5～15份；玻璃纤维，10～12份；无机填料，6～10份。本发明提供的填充改性ABS材料，通过对ABS的填充改性，使得材料的机械性能提高，便于进行加工，使用范围广。

Description

一种填充改性ABS材料
技术领域
本发明涉及一种高分子材料领域，特别涉及一种改性ABS树脂。
背景技术
ABS树脂是一种强度高、韧性好、易于加工成型的热塑型高分子材料。ABS工程塑料具有优良的综合性能，有极好的冲击强度、尺寸稳定性及电性能。通过对ABS树脂进行改性，有利于其成型加工，拓展其使用范围。
基于以上所述，一种填充改性ABS材料的开发将很有必要性。
发明内容
针对现有技术中的上述缺陷，本发明提供提供一种填充改性ABS材料，以改善ABS加工性及力学性能。
为了实现上述目标，本发明采用如下的技术方案：
一种填充改性ABS材料，由以下重量份数的组分组成：
优选的是，所述的填充改性ABS材料，其中，所述茂金属聚烯烃弹性体为茂金属聚乙烯弹性体或茂金属聚丙烯弹性体中的一种或多种的组合。
优选的是，所述的填充改性ABS材料，其中，所述增韧剂为超支化聚酯、超支化聚酰胺或超支化聚醇的一种或多种的组合。
优选的是，所述的填充改性ABS材料，其中，所述抗氧剂为以受阻酚类抗氧剂为主抗氧剂，以硫代二丙酸双酯为辅助抗氧剂，主抗氧剂与辅助抗氧剂的摩尔比为2∶1。
优选的是，所述的填充改性ABS材料，其中，所述热稳定剂为酚类热稳定剂或胺类热稳定剂中的一种或多种的组合，
优选的是，所述的填充改性ABS材料，其中，所述相容剂为超支化聚胺酯或EVOH-PPMA大分子相容剂的一种或多种的组合。
优选的是，所述的填充改性ABS材料，其中，所述玻璃纤维为单丝直径为9μm～15μm的高强度玻璃纤维。
优选的是，所述的填充改性ABS材料，其中，所述无机填料为滑石粉、云母粉、高岭土或硅灰石粉的一种或多种的组合。
本发明提供的填充改性ABS材料有益效果：通过对ABS的填充改性，使得材料的机械性能提高，便于进行加工，使用范围广。
具体实施方式
下面对本发明做进一步的详细说明，以令本领域技术人员参照说明书文字能够据以实施。
实施例1
一种填充改性ABS材料，由以下重量份数的组分组成：
ABS，30份；
茂金属聚烯烃弹性体，20份；所述茂金属聚烯烃弹性体为茂金属聚乙烯弹性体。
增韧剂，3份；所述增韧剂为超支化聚酯。
抗氧剂，5份；所述抗氧剂为以受阻酚类抗氧剂为主抗氧剂，以硫代二丙酸双酯为辅助抗氧剂，主抗氧剂与辅助抗氧剂的摩尔比为2∶1。
热稳定剂，5份；所述热稳定剂为酚类热稳定剂。
相容剂，15份；所述相容剂为超支化聚胺酯。
玻璃纤维，12份；所述玻璃纤维为单丝直径为9μm的高强度玻璃纤维。
无机填料，10份，所述无机填料为滑石粉。
实施例2
一种填充改性ABS材料，由以下重量份数的组分组成：
ABS，60份；
茂金属聚烯烃弹性体，15份；所述茂金属聚烯烃弹性体为茂金属聚丙烯弹性体。
增韧剂，1份；所述增韧剂为超支化聚酰胺。
抗氧剂，1份；所述抗氧剂为以受阻酚类抗氧剂为主抗氧剂，以硫代二丙酸双酯为辅助抗氧剂，主抗氧剂与辅助抗氧剂的摩尔比为2∶1。
热稳定剂，2份；所述热稳定剂为胺类热稳定剂。
相容剂，5份；所述相容剂为EVOH-PPMA大分子相容剂。
玻璃纤维，10份；所述玻璃纤维为单丝直径为15μm的高强度玻璃纤维。
无机填料，6份，所述无机填料为云母粉。
实施例3
一种填充改性ABS材料，由以下重量份数的组分组成：
ABS，50份；
茂金属聚烯烃弹性体，17份；所述茂金属聚烯烃弹性体为茂金属聚乙烯弹性体。
增韧剂，2份；所述增韧剂为超支化聚醇。
抗氧剂，2份；所述抗氧剂为以受阻酚类抗氧剂为主抗氧剂，以硫代二丙酸双酯为辅助抗氧剂，主抗氧剂与辅助抗氧剂的摩尔比为2∶1。
热稳定剂，3份；所述热稳定剂为酚类热稳定剂。
相容剂，10份；所述相容剂为超支化聚胺酯。
玻璃纤维，10份；所述玻璃纤维为单丝直径为9μm的高强度玻璃纤维。
无机填料，6份，所述无机填料为高岭土。
尽管本发明的实施方案已公开如上，但其并不仅仅限于说明书和实施方式中所列运用，它完全可以被适用于各种适合本发明的领域，对于熟悉本领域的人员而言，可容易地实现另外的修改，因此在不背离权利要求及等同范围所限定的一般概念下，本发明并不限于特定的细节。

Claims (8)

1.一种填充改性ABS材料，其特征在于，由以下重量份数的组分组成： 
2.如权利要求1所述的填充改性ABS材料，其特征在于，所述茂金属聚烯烃弹性体为茂金属聚乙烯弹性体或茂金属聚丙烯弹性体中的一种或多种的组合。 
3.如权利要求1所述的填充改性ABS材料，其特征在于，所述增韧剂为超支化聚酯、超支化聚酰胺或超支化聚醇的一种或多种的组合。 
4.如权利要求1所述的填充改性ABS材料，其特征在于，所述抗氧剂为以受阻酚类抗氧剂为主抗氧剂，以硫代二丙酸双酯为辅助抗氧剂，主抗氧剂与辅助抗氧剂的摩尔比为2∶1。 
5.如权利要求1所述的填充改性ABS材料，其特征在于，所述热稳定剂为酚类热稳定剂或胺类热稳定剂中的一种或多种的组合。 
6.如权利要求1所述的填充改性ABS材料，其特征在于，所述相容剂为超支化聚胺酯或EVOH-PPMA大分子相容剂的一种或多种的组合。 
7.如权利要求1所述的填充改性ABS材料，其特征在于，所述玻璃纤维为单丝直径为9μm～15μm的高强度玻璃纤维。 
8.如权利要求1所述的填充改性ABS材料，其特征在于，所述无机填料为滑石粉、云母粉、高岭土或硅灰石粉的一种或多种的组合。 
CN201410394716.4A 2014-08-12 2014-08-12 一种填充改性abs材料 Pending CN104151767A (zh)