CN104149418A - 一种隔热防紫外线的太阳膜 - Google Patents
一种隔热防紫外线的太阳膜 Download PDFInfo
- Publication number
- CN104149418A CN104149418A CN201410377197.0A CN201410377197A CN104149418A CN 104149418 A CN104149418 A CN 104149418A CN 201410377197 A CN201410377197 A CN 201410377197A CN 104149418 A CN104149418 A CN 104149418A
- Authority
- CN
- China
- Prior art keywords
- film
- solar film
- heat insulation
- antiultraviolet
- insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种隔热防紫外线的太阳膜，将紫外线吸收剂、荧光增白剂和PET聚酯基料混合成膜，该膜的两表面均溅射有金属层。本发明所提供的隔热防紫外线的太阳膜通过添加紫外线吸收剂和荧光增白剂达到防紫外线的效果；通过溅射金属层，达到隔热效果；由于并不是将原料混合之后成膜，而是将金属溅射在膜的表面，通过调整溅射金属层数使膜层清晰，提高了隔热防紫外线的太阳膜的清晰度。
Description
技术领域
本发明涉及一种隔热防紫外线的太阳膜。
背景技术
紫外线是一种波长比可见光短的看不见的光线，波长范围：280nm-400nm，具有显著的化学效应。紫外线不单单来自太阳光，各种人造光源，如紫外线灯、电脑、电视等也会产生一定的紫外线。过量的紫外线照射对人的皮肤和眼睛有一定的伤害，紫外线能破坏人体皮肤细胞，导致皱纹、色斑，使皮肤未老先衰，严重时产生日光性皮炎及晒伤，或皮肤和黏膜的日光性角化症，引起癌变。紫外线所产生的紫外线会引起人体疲劳、家具变色及脆化，尤其是对幼儿、学生及女士的伤害更为严重，长时间的紫外线照射最终将导致人体产生恶性黑色素细胞癌。
为了保护汽车和防止紫外线对人体的伤害，通常都会在汽车的玻璃上贴防紫外线太阳膜，现有技术中的防紫外线太阳膜，由于将所有原料混合之后成膜，导致清晰度较差。
发明内容
为了提高清晰度，同时达到隔热防紫外线的效果，本发明提供一种隔热防紫外线的太阳膜。
为了解决以上技术问题，本发明的技术方案是：一种隔热防紫外线的太阳膜，将紫外线吸收剂、荧光增白剂和PET聚酯基料混合成膜，该膜的两表面均溅射有金属层。
作为优选，上述技术方案中所述紫外线吸收剂为2-(2’-羟基-3’，5’-二叔丁基苯基)-5-氯代苯并三唑、2-羟基-4-正辛氧基二苯甲酮、(2-羟基-4-甲氧苯基)苯基酮、2-[2-羟基-5-(1，1，3，3-四甲丁基)苯基]苯并三唑中的任意一种。
作为优选，上述技术方案中所述紫外线吸收剂和荧光增白剂两者用量为任意比例，两者占总重量的20～25％。
作为优选，上述技术方案中所述金属层中的金属是铜、不锈钢、镍、银或硅。
作为优选，上述技术方案中所述荧光增白剂是双苯并噁唑。
本发明所提供的隔热防紫外线的太阳膜通过添加紫外线吸收剂和荧光增白剂达到防紫外线的效果；通过溅射金属层，达到隔热效果；由于并不是将原料混合之后成膜，而是将金属溅射在膜的表面，通过调整溅射金属层数使膜层清晰，提高了隔热防紫外线的太阳膜的清晰度。
具体实施方式
下面结合具体实施例对本发明作进一步详述。
实施例1
一种隔热防紫外线的太阳膜，将邻苯二甲酸和丙二醇共聚得到的PET聚酯、2-(2’-羟基-3’，5’-二叔丁基苯基)-5-氯代苯并三唑和双苯并噁唑混合成膜，其中，PET聚酯质量分数是80％，2-(2’-羟基-3’，5’-二叔丁基苯基)-5-氯代苯并三唑质量分数是10％，双苯并噁唑质量分数是10％，该膜的两表面均溅射有铜。
实施例2
一种隔热防紫外线的太阳膜，将邻苯二甲酸和丙二醇共聚得到的PET聚酯、2-(2’-羟基-3’，5’-二叔丁基苯基)-5-氯代苯并三唑和双苯并噁唑，其中，PET聚酯质量分数是75％，2-(2’-羟基-3’，5’-二叔丁基苯基)-5-氯代苯并三唑质量分数是15％，双苯并噁唑质量分数是10％，该膜的两表面均溅射有镍。
根据需要可以溅射多层金属，以达到更好的隔热效果。
为了验证上述实施例的效果，通过紫外线强度检测仪检测，经过隔热防紫外线的太阳膜阻挡的光线中紫外线强度结果几乎为零，因此本发明提供的隔热防紫外线的太阳膜达到了防紫外线的效果，由于并不是将原料混合之后成膜，而是将金属溅射在膜的表面，通过调整溅射金属层数使膜层清晰，提高了隔热防紫外线的太阳膜的清晰度。
本领域的技术人员可以对发明进行各种改动和变型而不脱离本发明的精神和范围。这样，倘若本发明的这些修改和变型属于本发明权利要求及其等同技术的范围之内，则本发明也意图包括这些改动和变型在内。
Claims (5)
1.一种隔热防紫外线的太阳膜，其特征在于，将紫外线吸收剂、荧光增白剂和PET聚酯基料混合成膜，该膜的两表面均溅射有金属层。
2.根据权利要求1所述的隔热防紫外线的太阳膜，其特征在于，所述紫外线吸收剂为2-(2’-羟基-3’，5’-二叔丁基苯基)-5-氯代苯并三唑、2-羟基-4-正辛氧基二苯甲酮、(2-羟基-4-甲氧苯基)苯基酮、2-[2-羟基-5-(1，1，3，3-四甲丁基)苯基]苯并三唑中的任意一种。
3.根据权利要求1所述的隔热防紫外线的太阳膜，其特征在于，所述紫外线吸收剂和荧光增白剂两者用量为任意比例，两者占总重量的20～25％。
4.根据权利要求1所述的隔热防紫外线的太阳膜，其特征在于，所述金属层中的金属是铜、不锈钢、镍、银或硅。
5.根据权利要求1所述的隔热防紫外线的太阳膜，其特征在于，所述荧光增白剂是双苯并噁唑。