CN104119709A - 一种耐碱多彩涂料 - Google Patents
一种耐碱多彩涂料 Download PDFInfo
- Publication number
- CN104119709A CN104119709A CN201410374945.XA CN201410374945A CN104119709A CN 104119709 A CN104119709 A CN 104119709A CN 201410374945 A CN201410374945 A CN 201410374945A CN 104119709 A CN104119709 A CN 104119709A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- resisting
- alkaline
- multicolor finish
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种耐碱多彩涂料，其原料按重量份数配比如下：硝酸纤维素100份；甲苯45-55份；焦磷酸钠5-15份；醋酸异丙酯10-20份；硼酸钠15-35份；醋酸正丙酯15-25份；去离子水80-90份；醋酸正丁酯20-30份；颜料10-20份；正丁醇25-35份；甲基乙基硫醚30-40份；异丙醇10-30份；增塑剂4-10份；醋酸乙酯20-40份；顺丁烯二酸酐15-35份；聚酰胺25-45份；产品搅拌时不粘连，涂膜耐擦洗性4000-5000次；在20℃水中浸泡60-90d后不起泡、不掉粉；在饱和氢氧化钙中浸泡30-60d无变化；表干20-30min，实干4-6h，涂膜色彩鲜艳、装饰效果好，可以广泛生产并不断代替现有材料。
Description
技术领域
本申请属于涂料领域，尤其涉及一种耐碱多彩涂料。
背景技术
涂料，在中国传统名称为油漆。所谓涂料是涂覆在被保护或被装饰的物体表面，并能与被涂物形成牢固附着的连续薄膜，通常是以树脂、或油、或乳液为主，添加或不添加颜料、填料，添加相应助剂，用有机溶剂或硼酸钠配制而成的粘稠液体。中国涂料界比较权威的《涂料工艺》一书是这样定义的：“涂料是一种材料，这种材料可以用不同的施工工艺涂覆在物件表面，形成粘附牢固、具有一定强度、连续的固态薄膜。这样形成的膜通称涂膜，又称漆膜或涂层。”涂料涂饰于物体表面能与基体材料很好粘结并形成完整而坚韧保护膜的物料，称为涂料。涂料与油漆是同一概念。油漆是人们沿用已久的习惯名称，引进我国后，就一直利用在建筑行业。涂料的作用可以概括为三个方面：保护作用，装饰作用，特殊功能作用。涂料的一般组成：包含成膜物质、颜填料、溶剂、助剂。
涂料是指应用于物体表面而能结成坚韧保护膜的物料的总称，建筑涂料是涂料中的一个重要类别，在我国，一般将用于建筑物内墙，外墙，顶棚，地面，卫生间的涂料称为建筑涂料。硝酸纤维素俗称硝化纤维素，为纤维素与硝酸酯化反应的产物。以棉纤维为原料的硝酸纤维素称为硝化棉。硝酸纤维素是一种白色纤维状聚合物，耐水、耐稀酸、耐弱碱和各种油类。聚合度不同，其强度亦不同，但都是热塑性物质。在阳光下易变色，且极易燃烧。
所谓耐碱多彩涂料是由不相容的两相成分组成，其中一相分散介质为连续相，另一相为分散相，涂装时，通过一次性喷涂，便可得到豪华、美观、耐碱多彩的图案。而随着人性化理念的普及，及新型和谐社会的构成，设计一种耐水性、耐擦洗性及耐碱性优异的耐碱多彩涂料是非常必要的。
发明内容
解决的技术问题：
本申请针对上述技术问题，提供一种耐碱多彩涂料，解决现有耐碱多彩涂料耐水性和耐擦洗性差、装饰效果差、不耐碱腐蚀等技术问题。
技术方案：
一种耐碱多彩涂料，所述耐碱多彩涂料的原料按重量份数配比如下：硝酸纤维素100份；甲苯45-55份；焦磷酸钠5-15份；醋酸异丙酯10-20份；硼酸钠15-35份；醋酸正丙酯15-25份；去离子水80-90份；醋酸正丁酯20-30份；颜料10-20份；正丁醇25-35份；甲基乙基硫醚30-40份；异丙醇10-30份；增塑剂4-10份；醋酸乙酯20-40份；顺丁烯二酸酐15-35份；聚酰胺25-45份。
作为本发明的一种优选技术方案：所述耐碱多彩涂料的原料按重量份数配比如下：硝酸纤维素100份；甲苯50份；焦磷酸钠10份；醋酸异丙酯15份；硼酸钠25份；醋酸正丙酯20份；去离子水85份；醋酸正丁酯25份；颜料15份；正丁醇30份；甲基乙基硫醚35份；异丙醇20份；增塑剂8份；醋酸乙酯30份；顺丁烯二酸酐25份；聚酰胺35份。
作为本发明的一种优选技术方案：所述颜料采用氧化铁红、氧化铁绿或氧化铁黄。
作为本发明的一种优选技术方案：所述增塑剂采用邻苯二甲酸二丁酯。
有益效果：
本发明所述一种耐碱多彩涂料采用以上技术方案与现有技术相比，具有以下技术效果：1、产品搅拌时不粘连，涂膜耐擦洗性4000-5000次；2、在20℃水中浸泡60-90d后不起泡、不掉粉；3、在饱和氢氧化钙中浸泡30-60d无变化；4、表干20-30min，实干4-6h，涂膜色彩鲜艳、装饰效果好，可以广泛生产并不断代替现有材料。
具体实施方式
实施例1:
一种耐碱多彩涂料，其原料按重量份数配比如下：硝酸纤维素100份；甲苯45份；焦磷酸钠5份；醋酸异丙酯10份；硼酸钠15份；醋酸正丙酯15份；去离子水80份；醋酸正丁酯20份；氧化铁绿10份；正丁醇25份；甲基乙基硫醚30份；异丙醇10份；邻苯二甲酸二丁酯4份；醋酸乙酯20份；顺丁烯二酸酐15份；聚酰胺25份。
将硝酸纤维素、焦磷酸钠、醋酸异丙酯、硼酸钠和醋酸正丙酯加入去离子水中，加热至40℃搅拌3h，加入醋酸正丁酯、正丁醇、甲基乙基硫醚、异丙醇、顺丁烯二酸酐和邻苯二甲酸二丁酯，升温至50℃用球磨机球磨10min，加入甲苯和剩余原料，升温至60℃搅拌10h后既得成品。
涂膜耐擦洗性4000次；在20℃水中浸泡60d后不起泡、不掉粉；在饱和氢氧化钙中浸泡30d无变化；表干30min，实干6h。
实施例2:
一种耐碱多彩涂料，其原料按重量份数配比如下：硝酸纤维素100份；甲苯55份；焦磷酸钠15份；醋酸异丙酯20份；硼酸钠35份；醋酸正丙酯25份；去离子水90份；醋酸正丁酯30份；氧化铁黄20份；正丁醇35份；甲基乙基硫醚40份；异丙醇30份；邻苯二甲酸二丁酯10份；醋酸乙酯40份；顺丁烯二酸酐35份；聚酰胺45份。
将硝酸纤维素、焦磷酸钠、醋酸异丙酯、硼酸钠和醋酸正丙酯加入去离子水中，加热至40℃搅拌3h，加入醋酸正丁酯、正丁醇、甲基乙基硫醚、异丙醇、顺丁烯二酸酐和邻苯二甲酸二丁酯，升温至50℃用球磨机球磨10min，加入甲苯和剩余原料，升温至60℃搅拌10h后既得成品。
涂膜耐擦洗性4500次；在20℃水中浸泡80d后不起泡、不掉粉；在饱和氢氧化钙中浸泡45d无变化；表干250min，实干5h。
实施例3:
一种耐碱多彩涂料，其原料按重量份数配比如下：硝酸纤维素100份；甲苯50份；焦磷酸钠10份；醋酸异丙酯15份；硼酸钠25份；醋酸正丙酯20份；去离子水85份；醋酸正丁酯25份；氧化铁红15份；正丁醇30份；甲基乙基硫醚35份；异丙醇20份；邻苯二甲酸二丁酯8份；醋酸乙酯30份；顺丁烯二酸酐25份；聚酰胺35份。
将硝酸纤维素、焦磷酸钠、醋酸异丙酯、硼酸钠和醋酸正丙酯加入去离子水中，加热至40℃搅拌3h，加入醋酸正丁酯、正丁醇、甲基乙基硫醚、异丙醇、顺丁烯二酸酐和邻苯二甲酸二丁酯，升温至50℃用球磨机球磨10min，加入甲苯和剩余原料，升温至60℃搅拌10h后既得成品。
涂膜耐擦洗性5000次；在20℃水中浸泡90d后不起泡、不掉粉；在饱和氢氧化钙中浸泡60d无变化；表干20min，实干4h。
以上实施例中的组合物所有组分均可以商业购买。
上述实施例只是用于对本发明的内容进行阐述，而不是限制，因此在与本发明的权利要求书相当的含义和范围内的任何改变，都应该认为是包括在权利要求书的范围内。
Claims (4)
1.一种耐碱多彩涂料，其特征在于所述耐碱多彩涂料的原料按重量份数配比如下：硝酸纤维素100份；甲苯45-55份；焦磷酸钠5-15份；醋酸异丙酯10-20份；硼酸钠15-35份；醋酸正丙酯15-25份；去离子水80-90份；醋酸正丁酯20-30份；颜料10-20份；正丁醇25-35份；甲基乙基硫醚30-40份；异丙醇10-30份；增塑剂4-10份；醋酸乙酯20-40份；顺丁烯二酸酐15-35份；聚酰胺25-45份。
2.根据权利要求1所述的一种耐碱多彩涂料，其特征在于所述耐碱多彩涂料的原料按重量份数配比如下：硝酸纤维素100份；甲苯50份；焦磷酸钠10份；醋酸异丙酯15份；硼酸钠25份；醋酸正丙酯20份；去离子水85份；醋酸正丁酯25份；颜料15份；正丁醇30份；甲基乙基硫醚35份；异丙醇20份；增塑剂8份；醋酸乙酯30份；顺丁烯二酸酐25份；聚酰胺35份。
3.根据权利要求1所述的一种耐碱多彩涂料，其特征在于：所述颜料采用氧化铁红、氧化铁绿或氧化铁黄。
4.根据权利要求1所述的一种耐碱多彩涂料，其特征在于：所述增塑剂采用邻苯二甲酸二丁酯。