CN104177886B - 一种保温多彩喷塑涂料 - Google Patents
一种保温多彩喷塑涂料 Download PDFInfo
- Publication number
- CN104177886B CN104177886B CN201410409886.5A CN201410409886A CN104177886B CN 104177886 B CN104177886 B CN 104177886B CN 201410409886 A CN201410409886 A CN 201410409886A CN 104177886 B CN104177886 B CN 104177886B
- Authority
- CN
- China
- Prior art keywords
- parts
- thermal insulation
- plastic paint
- spraying plastic
- colour spraying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种保温多彩喷塑涂料，其原料按重量份数配比如下：脲醛树脂100份；聚四亚甲基醚二醇5‑15份；粉煤灰20‑30份；丙二醇乙醚醋酸酯10‑30份；硅酸钠15‑25份；对甲氧基苯酚25‑35份；去离子水80‑90份；三丙烯酸季戊四醇酯15‑35份；颜料10‑20份；异佛尔酮二异氰酸酯10‑30份；滑石粉30‑40份；二苯甲酮20‑30份；增塑剂8‑10份；聚乙二醇35‑45份；四硼酸钠20‑30份；甲苯二异氰酸酯25‑45份；产品在容器中均匀无结块，附着力100％；在水中浸泡10‑30d后不起泡、不掉粉；表干0.5‑1.5h，实干12‑18h，在饱和氢氧化钙溶液5‑15d不皱皮；涂膜彩色均匀、光滑平整，涂膜耐擦洗1500‑2500次不露底，可以广泛生产并不断代替现有材料。
Description
技术领域
本申请属于涂料领域，尤其涉及一种保温多彩喷塑涂料。
背景技术
涂料，在中国传统名称为油漆。所谓涂料是涂覆在被保护或被装饰的物体表面，并能与被涂物形成牢固附着的连续薄膜，通常是以树脂、或油、或乳液为主，添加或不添加颜料、填料，添加相应助剂，用有机溶剂或硅酸钠配制而成的粘稠液体。中国涂料界比较权威的《涂料工艺》一书是这样定义的：“涂料是一种材料，这种材料可以用不同的施工工艺涂覆在物件表面，形成粘附牢固、具有一定强度、连续的固态薄膜。这样形成的膜通称涂膜，又称漆膜或涂层。”涂料涂饰于物体表面能与基体材料很好粘结并形成完整而坚韧保护膜的物料，称为涂料。涂料与油漆是同一概念。油漆是人们沿用已久的习惯名称，引进我国后，就一直利用在建筑行业。涂料的作用可以概括为三个方面：保护作用，装饰作用，特殊功能作用。涂料的一般组成：包含成膜物质、颜填料、溶剂、助剂。
涂料是指应用于物体表面而能结成坚韧保护膜的物料的总称，建筑涂料是涂料中的一个重要类别，在我国，一般将用于建筑物内墙，外墙，顶棚，地面，卫生间的涂料称为建筑涂料。尿素与甲醛反应得到的聚合物。又称脲甲醛树脂。英文缩写UF。加工成型时发生交联，制品为不溶不熔的热固性树脂。固化后的脲醛树脂颜色比酚醛树脂浅，呈半透明状，耐弱酸、弱碱，绝缘性能好，耐磨性极佳，价格便宜，但遇强酸、强碱易分解，耐候性较差。
所谓保温多彩喷塑涂料是由不相容的两相成分组成，其中一相分散介质为连续相，另一相为分散相，涂装时，通过一次性喷涂，便可得到豪华、美观、多彩的图案。脲醛树脂一般为水溶性树脂，较易固化，固化后的树脂无毒、无色、耐光性好，长期使用不变色，热成型时也不变色，可加入各种着色剂以制备各种色泽鲜艳的制品。而随着人性化理念的普及，及新型和谐社会的构成，设计一种耐水性、耐擦洗性及耐碱性优异的保温多彩喷塑涂料是非常必要的。
发明内容
解决的技术问题：
本申请针对上述技术问题，提供一种保温多彩喷塑涂料，解决现有保温多彩喷塑涂料耐水性和耐擦洗性差、干燥慢、不耐碱腐蚀等技术问题。
技术方案：
一种保温多彩喷塑涂料，所述保温多彩喷塑涂料的原料按重量份数配比如下：脲醛树脂100份；聚四亚甲基醚二醇5-15份；粉煤灰20-30份；丙二醇乙醚醋酸酯10-30份；硅酸钠15-25份；对甲氧基苯酚25-35份；去离子水80-90份；三丙烯酸季戊四醇酯15-35份；颜料10-20份；异佛尔酮二异氰酸酯10-30份；滑石粉30-40份；二苯甲酮20-30份；增塑剂8-10份；聚乙二醇35-45份；四硼酸钠20-30份；甲苯二异氰酸酯25-45份。
作为本发明的一种优选技术方案：所述保温多彩喷塑涂料的原料按重量份数配比如下：脲醛树脂100份；聚四亚甲基醚二醇10份；粉煤灰25份；丙二醇乙醚醋酸酯20份；硅酸钠20份；对甲氧基苯酚30份；去离子水85份；三丙烯酸季戊四醇酯25份；颜料15份；异佛尔酮二异氰酸酯20份；滑石粉35份；二苯甲酮25份；增塑剂9份；聚乙二醇40份；四硼酸钠25份；甲苯二异氰酸酯35份。
作为本发明的一种优选技术方案：所述颜料采用氧化铁棕、氧化铁黄或氧化铁黑。
作为本发明的一种优选技术方案：所述增塑剂采用邻苯二甲酸二丁酯。
有益效果：
本发明所述一种保温多彩喷塑涂料采用以上技术方案与现有技术相比，具有以下技术效果：1、产品在容器中均匀无结块，附着力100％；2、在水中浸泡10-30d后不起泡、不掉粉；3、表干0.5-1.5h，实干12-18h，在饱和氢氧化钙溶液5-15d不皱皮；4、涂膜彩色均匀、光滑平整，涂膜耐擦洗1500-2500次不露底，可以广泛生产并不断代替现有材料。
具体实施方式
实施例1:
一种保温多彩喷塑涂料，其原料按重量份数配比如下：脲醛树脂100份；聚四亚甲基醚二醇5份；粉煤灰20份；丙二醇乙醚醋酸酯10份；硅酸钠15份；对甲氧基苯酚25份；去离子水80份；三丙烯酸季戊四醇酯15份；氧化铁棕10份；异佛尔酮二异氰酸酯10份；滑石粉30份；二苯甲酮20份；邻苯二甲酸二丁酯8份；聚乙二醇35份；四硼酸钠20份；甲苯二异氰酸酯25份。
将脲醛树脂、粉煤灰、丙二醇乙醚醋酸酯、硅酸钠和对甲氧基苯酚加入去离子水中，加热至40℃搅拌3h，加入三丙烯酸季戊四醇酯、异佛尔酮二异氰酸酯、滑石粉、二苯甲酮、四硼酸钠和邻苯二甲酸二丁酯，升温至50℃用球磨机球磨10min，加入聚四亚甲基醚二醇和剩余原料，升温至60℃搅拌10h后既得成品。
涂膜表干1.5h，实干18h，耐擦洗1500次不露底；在饱和氢氧化钙溶液5d不皱皮，在水中浸泡10d后不起泡、不掉粉。
实施例2:
一种保温多彩喷塑涂料，其原料按重量份数配比如下：脲醛树脂100份；聚四亚甲基醚二醇15份；粉煤灰30份；丙二醇乙醚醋酸酯30份；硅酸钠25份；对甲氧基苯酚35份；去离子水90份；三丙烯酸季戊四醇酯35份；氧化铁黄20份；异佛尔酮二异氰酸酯30份；滑石粉40份；二苯甲酮30份；邻苯二甲酸二丁酯10份；聚乙二醇45份；四硼酸钠30份；甲苯二异氰酸酯45份。
将脲醛树脂、粉煤灰、丙二醇乙醚醋酸酯、硅酸钠和对甲氧基苯酚加入去离子水中，加热至40℃搅拌3h，加入三丙烯酸季戊四醇酯、异佛尔酮二异氰酸酯、滑石粉、二苯甲酮、四硼酸钠和邻苯二甲酸二丁酯，升温至50℃用球磨机球磨10min，加入聚四亚甲基醚二醇和剩余原料，升温至60℃搅拌10h后既得成品。
涂膜表干1h，实干15h，耐擦洗2000次不露底；在饱和氢氧化钙溶液10d不皱皮，在水中浸泡20d后不起泡、不掉粉。
实施例3:
一种保温多彩喷塑涂料，其原料按重量份数配比如下：脲醛树脂100份；聚四亚甲基醚二醇10份；粉煤灰25份；丙二醇乙醚醋酸酯20份；硅酸钠20份；对甲氧基苯酚30份；去离子水85份；三丙烯酸季戊四醇酯25份；氧化铁黑15份；异佛尔酮二异氰酸酯20份；滑石粉35份；二苯甲酮25份；邻苯二甲酸二丁酯9份；聚乙二醇40份；四硼酸钠25份；甲苯二异氰酸酯35份。
将脲醛树脂、粉煤灰、丙二醇乙醚醋酸酯、硅酸钠和对甲氧基苯酚加入去离子水中，加热至40℃搅拌3h，加入三丙烯酸季戊四醇酯、异佛尔酮二异氰酸酯、滑石粉、二苯甲酮、四硼酸钠和邻苯二甲酸二丁酯，升温至50℃用球磨机球磨10min，加入聚四亚甲基醚二醇和剩余原料，升温至60℃搅拌10h后既得成品。
涂膜表干0.5h，实干12h，耐擦洗2500次不露底；在饱和氢氧化钙溶液15d不皱皮，在水中浸泡30d后不起泡、不掉粉。
以上实施例中的组合物所有组分均可以商业购买。
上述实施例只是用于对本发明的内容进行阐述，而不是限制，因此在与本发明的权利要求书相当的含义和范围内的任何改变，都应该认为是包括在权利要求书的范围内。
Claims (1)
1.一种保温多彩喷塑涂料，其特征在于所述保温多彩喷塑涂料的原料按重量份数配比如下：脲醛树脂100份；聚四亚甲基醚二醇10份；粉煤灰25份；丙二醇乙醚醋酸酯20份；硅酸钠20份；对甲氧基苯酚30份；去离子水85份；三丙烯酸季戊四醇酯25份；颜料15份；异佛尔酮二异氰酸酯20份；滑石粉35份；二苯甲酮25份；增塑剂9份；聚乙二醇40份；四硼酸钠25份；甲苯二异氰酸酯35份；
所述颜料采用氧化铁棕、氧化铁黄或氧化铁黑；
所述增塑剂采用邻苯二甲酸二丁酯。