CN104130642A - 一种聚乙烯醇系水型涂料 - Google Patents
一种聚乙烯醇系水型涂料 Download PDFInfo
- Publication number
- CN104130642A CN104130642A CN201410374278.5A CN201410374278A CN104130642A CN 104130642 A CN104130642 A CN 104130642A CN 201410374278 A CN201410374278 A CN 201410374278A CN 104130642 A CN104130642 A CN 104130642A
- Authority
- CN
- China
- Prior art keywords
- parts
- series water
- water type
- type coating
- polyvinyl alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种聚乙烯醇系水型涂料,其原料按重量份数配比如下:聚乙烯醇100份;硼酸钠5-15份;聚醋酸乙烯20-30份;二甲苯40-50份;磷酸二丁酯10-20份;丁醇5-25份;去离子水80-90份;环烷酸钙15-25份;颜料10-20份;环烷酸锌15-35份;羟乙基纤维素30-40份;三乙胺10-30份;增塑剂4-10份;硅酮20-40份;氨水35-45份;二缩乙二醇单丁醚25-35份;涂膜耐擦洗4000-6000次不露底;在20℃水中浸泡50-60d后不起泡、不掉粉;表干30-50min,实干4-6h;25℃贮存8-10个月,可以广泛生产并不断代替现有材料。
Description
技术领域
本申请属于涂料领域,尤其涉及一种聚乙烯醇系水型涂料。
背景技术
涂料,在中国传统名称为油漆。所谓涂料是涂覆在被保护或被装饰的物体表面,并能与被涂物形成牢固附着的连续薄膜,通常是以树脂、或油、或乳液为主,添加或不添加颜料、填料,添加相应助剂,用有机溶剂或磷酸二丁酯配制而成的粘稠液体。中国涂料界比较权威的《涂料工艺》一书是这样定义的:“涂料是一种材料,这种材料可以用不同的施工工艺涂覆在物件表面,形成粘附牢固、具有一定强度、连续的固态薄膜。这样形成的膜通称涂膜,又称漆膜或涂层。”涂料涂饰于物体表面能与基体材料很好粘结并形成完整而坚韧保护膜的物料,称为涂料。涂料与油漆是同一概念。油漆是人们沿用已久的习惯名称,引进我国后,就一直利用在建筑行业。涂料的作用可以概括为三个方面:保护作用,装饰作用,特殊功能作用。涂料的一般组成:包含成膜物质、颜填料、溶剂、助剂。
涂料是指应用于物体表面而能结成坚韧保护膜的物料的总称,建筑涂料是涂料中的一个重要类别,在我国,一般将用于建筑物内墙,外墙,顶棚,地面,卫生间的涂料称为建筑涂料。聚乙烯醇,有机化合物,白色片状、絮状或粉末状固体,无味。溶于水,不溶于汽油、煤油、植物油、苯、甲苯、二氯乙烷、四氯化碳、丙酮、醋酸乙酯、甲醇、乙二醇等。微溶于二甲基亚砜。聚乙烯醇是重要的化工原料,用于制造聚乙烯醇缩醛、耐汽油管道和维尼纶合成纤维、织物处理剂、乳化剂、纸张涂层、粘合剂等。
所谓聚乙烯醇系水型涂料是由不相容的两相成分组成,其中一相分散介质为连续相,另一相为分散相,涂装时,通过一次性喷涂,便可得到豪华、美观、聚乙烯醇系水型的图案。而随着人性化理念的普及,及新型和谐社会的构成,设计一种干燥快,耐水性、耐擦洗性及耐磨性优异的聚乙烯醇系水型涂料是非常必要的。
发明内容
解决的技术问题:
本申请针对上述技术问题,提供一种聚乙烯醇系水型涂料,解决现有聚乙烯醇系水型涂料耐水性和耐擦洗性差、干燥慢、不耐摩擦等技术问题。
技术方案:
一种聚乙烯醇系水型涂料,所述聚乙烯醇系水型涂料的原料按重量份数配比如下:聚乙烯醇 100份;硼酸钠 5-15份;聚醋酸乙烯 20-30份;二甲苯 40-50份;磷酸二丁酯 10-20份;丁醇 5-25份;去离子水 80-90份;环烷酸钙 15-25份;颜料 10-20份;环烷酸锌 15-35份;羟乙基纤维素 30-40份;三乙胺 10-30份;增塑剂 4-10份;硅酮 20-40份;氨水 35-45份;二缩乙二醇单丁醚 25-35份。
作为本发明的一种优选技术方案:所述聚乙烯醇系水型涂料的原料按重量份数配比如下:聚乙烯醇 100份;硼酸钠 10份;聚醋酸乙烯 25份;二甲苯 42份;磷酸二丁酯 12份;丁醇 15份;去离子水82份;环烷酸钙 20份;颜料 15份;环烷酸锌 25份;羟乙基纤维素35份;三乙胺 20份;增塑剂 7份;硅酮 30份;氨水 40份;二缩乙二醇单丁醚 30份。
作为本发明的一种优选技术方案:所述颜料采用氧化铁红、氧化铁绿或氧化铁黄。
作为本发明的一种优选技术方案:所述增塑剂采用邻苯二甲酸二丁酯。
有益效果:
本发明所述一种聚乙烯醇系水型涂料采用以上技术方案与现有技术相比,具有以下技术效果:1、涂膜耐擦洗4000-6000次不露底;2、在20℃水中浸泡50-60d后不起泡、不掉粉;3、表干30-50min,实干4-6h;4、25℃贮存8-10个月,可以广泛生产并不断代替现有材料。
具体实施方式
实施例1:
一种聚乙烯醇系水型涂料,其原料按重量份数配比如下:聚乙烯醇 100份;硼酸钠 5份;聚醋酸乙烯 20份;二甲苯 40份;磷酸二丁酯 10份;丁醇 5份;去离子水 80份;环烷酸钙 15份;氧化铁绿 10份;环烷酸锌 15份;羟乙基纤维素 30份;三乙胺 10份;邻苯二甲酸二丁酯 4份;硅酮 20份;氨水 35份;二缩乙二醇单丁醚 25份。
将聚乙烯醇、聚醋酸乙烯、二甲苯、磷酸二丁酯和丁醇加入去离子水中,加热至40℃搅拌3h,加入环烷酸钙、环烷酸锌、羟乙基纤维素、三乙胺、氨水和邻苯二甲酸二丁酯,升温至50℃用球磨机球磨10min,加入硼酸钠和剩余原料,升温至60℃搅拌10h后既得成品。
涂膜耐擦洗4000次不露底;在20℃水中浸泡50d后不起泡、不掉粉;表干50min,实干6h;25℃贮存8个月。
实施例2:
一种聚乙烯醇系水型涂料,其原料按重量份数配比如下:聚乙烯醇 100份;硼酸钠 15份;聚醋酸乙烯 30份;二甲苯 50份;磷酸二丁酯 20份;丁醇 25份;去离子水 90份;环烷酸钙 25份;氧化铁红20份;环烷酸锌 35份;羟乙基纤维素 40份;三乙胺 30份;邻苯二甲酸二丁酯 10份;硅酮 40份;氨水 45份;二缩乙二醇单丁醚 35份。
将聚乙烯醇、聚醋酸乙烯、二甲苯、磷酸二丁酯和丁醇加入去离子水中,加热至40℃搅拌3h,加入环烷酸钙、环烷酸锌、羟乙基纤维素、三乙胺、氨水和邻苯二甲酸二丁酯,升温至50℃用球磨机球磨10min,加入硼酸钠和剩余原料,升温至60℃搅拌10h后既得成品。
涂膜耐擦洗5000次不露底;在20℃水中浸泡55d后不起泡、不掉粉;表干40min,实干5h;25℃贮存9个月。
实施例3:
一种聚乙烯醇系水型涂料,其原料按重量份数配比如下:聚乙烯醇 100份;硼酸钠 10份;聚醋酸乙烯 25份;二甲苯 42份;磷酸二丁酯 12份;丁醇 15份;去离子水 82份;环烷酸钙 20份;氧化铁黄15份;环烷酸锌 25份;羟乙基纤维素 35份;三乙胺 20份;邻苯二甲酸二丁酯 7份;硅酮 30份;氨水 40份;二缩乙二醇单丁醚 30份。
将聚乙烯醇、聚醋酸乙烯、二甲苯、磷酸二丁酯和丁醇加入去离子水中,加热至40℃搅拌3h,加入环烷酸钙、环烷酸锌、羟乙基纤维素、三乙胺、氨水和邻苯二甲酸二丁酯,升温至50℃用球磨机球磨10min,加入硼酸钠和剩余原料,升温至60℃搅拌10h后既得成品。
涂膜耐擦洗6000次不露底;在20℃水中浸泡60d后不起泡、不掉粉;表干30min,实干4h;25℃贮存10个月。
以上实施例中的组合物所有组分均可以商业购买。
上述实施例只是用于对本发明的内容进行阐述,而不是限制,因此在与本发明的权利要求书相当的含义和范围内的任何改变,都应该认为是包括在权利要求书的范围内。
Claims (4)
1.一种聚乙烯醇系水型涂料,其特征在于所述聚乙烯醇系水型涂料的原料按重量份数配比如下:聚乙烯醇 100份;硼酸钠 5-15份;聚醋酸乙烯 20-30份;二甲苯 40-50份;磷酸二丁酯 10-20份;丁醇5-25份;去离子水 80-90份;环烷酸钙 15-25份;颜料 10-20份;环烷酸锌 15-35份;羟乙基纤维素 30-40份;三乙胺 10-30份;增塑剂 4-10份;硅酮 20-40份;氨水 35-45份;二缩乙二醇单丁醚 25-35份。
2.根据权利要求1所述的一种聚乙烯醇系水型涂料,其特征在于所述聚乙烯醇系水型涂料的原料按重量份数配比如下:聚乙烯醇100份;硼酸钠 10份;聚醋酸乙烯 25份;二甲苯 42份;磷酸二丁酯 12份;丁醇 15份;去离子水 82份;环烷酸钙 20份;颜料 15份;环烷酸锌 25份;羟乙基纤维素 35份;三乙胺 20份;增塑剂 7份;硅酮 30份;氨水 40份;二缩乙二醇单丁醚 30份。
3.根据权利要求1所述的一种聚乙烯醇系水型涂料,其特征在于:所述颜料采用氧化铁红、氧化铁绿或氧化铁黄。
4.根据权利要求1所述的一种聚乙烯醇系水型涂料,其特征在于:所述增塑剂采用邻苯二甲酸二丁酯。