CN104109752A - 马氏体不锈钢丝在线淬火处理方法 - Google Patents

马氏体不锈钢丝在线淬火处理方法 Download PDF

Info

Publication number
CN104109752A
CN104109752A CN201410343803.7A CN201410343803A CN104109752A CN 104109752 A CN104109752 A CN 104109752A CN 201410343803 A CN201410343803 A CN 201410343803A CN 104109752 A CN104109752 A CN 104109752A
Authority
CN
China
Prior art keywords
stainless steel
steel wire
martensitic stainless
heating
take
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410343803.7A
Other languages
English (en)
Other versions
CN104109752B (zh
Inventor
刘翔
谭佃龙
华祝元
陈炎
徐钦华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fasten Group Co Ltd
Original Assignee
Fasten Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fasten Group Co Ltd filed Critical Fasten Group Co Ltd
Priority to CN201410343803.7A priority Critical patent/CN104109752B/zh
Publication of CN104109752A publication Critical patent/CN104109752A/zh
Application granted granted Critical
Publication of CN104109752B publication Critical patent/CN104109752B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种马氏体不锈钢丝在线淬火处理方法，所述方法包括以下工艺步骤：将放线盘上的马氏体不锈钢丝放线后通过一感应加热装置进行加热，加热温度为950℃~1050℃，加热时间为5s~10s，感应加热线圈长度为2000mm；而后将加热后的马氏体不锈钢丝通过一冷却油池进行冷却；将冷却好的马氏体不锈钢丝通过一超声波清洗池进行超声波清洗，而后再通过烘箱烘干；将清洗、烘干后的马氏体不锈钢丝通过一收线装置进行收线，收线速率20~50m/min。本发明淬火后的马氏体不锈钢丝强度、硬度、耐磨性和疲劳性能均得到有效提高，从而满足各种机械零件和工具的不同使用要求，且生产效率高，零件废品率较低，整套设备紧凑，占地面积小，使用简便，加热速度快。

Description

马氏体不锈钢丝在线淬火处理方法
技术领域
本发明涉及一种马氏体不锈钢丝的热处理方法。属于金属热处理工艺技术领域。
背景技术
淬火是将金属工件加热到某一适当温度并保持一段时间，随即浸入淬冷介质中快速冷却的金属热处理工艺。淬火可以提高金属工件的硬度及耐磨性，因而广泛用于各种工、模、量具及要求表面耐磨的零件（如齿轮、轧辊、渗碳零件等）。
传统淬火工艺加热时间长，零件表面氧化脱碳较多，零件废品率较高。且设备占地面积大，操作较繁琐，生产过程中高温，劳动条件差，污染相对较严重。
感应加热淬火是利用电磁感应的原理，使零件在交变磁场中切割磁力线，在表面产生感应电流，又根据交流电的集肤效应。以涡流形式将零件表面快速加热，而后急冷的淬火方法。感应加热属于内热源直接加热，热损失小，因此加热速度快，热效率高。它在热处理领域中占有重要地位，是未来淬火工艺的发展方向。
发明内容
本发明的目的在于克服上述不足，提供一种具有设备紧凑、占地面积小、使用简便、加热速度快和零件废品率较低的马氏体不锈钢丝的热处理方法。
本发明的目的是这样实现的：一种马氏体不锈钢丝在线淬火处理方法，所述方法包括以下工艺步骤：
步骤一、加热
将放线盘上的马氏体不锈钢丝放线后通过一感应加热装置进行加热，加热温度为950℃~1050℃，加热时间为5s~10s，感应加热线圈长度为2000mm；
步骤二、冷却
而后将加热后的马氏体不锈钢丝通过一冷却油池进行冷却；
步骤三、清洗
将冷却好的马氏体不锈钢丝通过一超声波清洗池进行超声波清洗，而后再通过烘箱烘干，烘箱温度为200℃，烘箱长度为4m；
步骤四、收线
将清洗、烘干后的马氏体不锈钢丝通过一收线装置进行收线，收线速率20~50m/min。
与现有技术相比，本发明的有益效果是： 
本发明淬火后的马氏体不锈钢丝强度、硬度、耐磨性和疲劳性能均得到有效提高，从而满足各种机械零件和工具的不同使用要求，且生产效率高，零件废品率较低，整套设备紧凑，占地面积小，使用简便，加热速度快。
具体实施方式
下面从实施例进一步描述和理解本发明，但未限于所举的实施例。
实施例1：
一种马氏体不锈钢丝在线淬火处理方法，所述方法包括以下工艺步骤：
1、取牌号为420J1，线径为2.5mm的马氏体不锈钢丝放置于放线盘上；
2、将放线盘上的马氏体不锈钢丝放线后通过一感应加热装置进行加热，加热温度为950℃，加热时间为5s，感应加热线圈长度为2000mm；
3、而后将加热后的马氏体不锈钢丝通过一冷却油池进行冷却；
4、将冷却好的马氏体不锈钢丝通过一超声波清洗池进行超声波清洗，而后再通过烘箱烘干，烘箱温度为200℃，烘箱长度为4m。
5、将清洗、烘干后的马氏体不锈钢丝通过一收线装置进行收线，收线速率50m/min，即可得到高硬度，耐腐蚀性强的目标产物。
实施例2：
一种马氏体不锈钢丝在线淬火处理方法，所述方法包括以下工艺步骤：
1、取牌号为420J1，线径为5.0mm的马氏体不锈钢丝放置于放线盘上；
2、将放线盘上的马氏体不锈钢丝放线后通过一感应加热装置进行加热，加热温度为1050℃，加热时间为10s，感应加热线圈长度为2000mm；
3、而后将加热后的马氏体不锈钢丝通过一冷却油池进行冷却；
4、将冷却好的马氏体不锈钢丝通过一超声波清洗池进行超声波清洗，而后在线通过烘箱烘干，烘箱温度为200℃，烘箱长度为4m。
5、将清洗、烘干后的马氏体不锈钢丝通过一收线装置进行收线，收线速率20m/min，即可得到高硬度，耐腐蚀性强的目标产物。
本发明方法通过控制感应加热装置的电参数和收线速度来满足不同线径和材质的马氏体不锈钢丝的淬火要求。

Claims (2)

1.一种马氏体不锈钢丝在线淬火处理方法，其特征在于：所述方法包括以下工艺步骤：
步骤一、加热
将放线盘上的马氏体不锈钢丝放线后通过一感应加热装置进行加热，加热温度为950℃~1050℃，加热时间为5s~10s，感应加热线圈长度为2000mm；
步骤二、冷却
而后将加热后的马氏体不锈钢丝通过一冷却油池进行冷却；
步骤三、清洗
将冷却好的马氏体不锈钢丝通过一超声波清洗池进行超声波清洗，而后再通过烘箱烘干，烘箱温度为200℃，烘箱长度为4m；
步骤四、收线
将清洗、烘干后的马氏体不锈钢丝通过一收线装置进行收线，收线速率20~50m/min。
2.根据权利要求1所述的一种马氏体不锈钢丝在线淬火处理方法，其特征在于：所述步骤三的烘箱温度为200℃，烘箱长度为4m。
CN201410343803.7A 2014-07-19 2014-07-19 马氏体不锈钢丝在线淬火处理方法 Active CN104109752B (zh)