CN104109309A - 宽幅pvc中空板材及其生产工艺 - Google Patents
宽幅pvc中空板材及其生产工艺 Download PDFInfo
- Publication number
- CN104109309A CN104109309A CN201410306633.5A CN201410306633A CN104109309A CN 104109309 A CN104109309 A CN 104109309A CN 201410306633 A CN201410306633 A CN 201410306633A CN 104109309 A CN104109309 A CN 104109309A
- Authority
- CN
- China
- Prior art keywords
- parts
- pvc hollow
- wide cut
- board material
- hollow board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
宽幅PVC中空板材及其生产工艺,涉及共挤型材技术领域,其特征在于:所述的宽幅PVC中空板材及其生产工艺的宽度为1米以上,原料包括基础料共挤层料,所述的基础料为PVC树脂100份,复合稳定润滑剂2.5~5.5份,抗冲改性剂3.0~8.0份,加工助剂1.0~3.0份,填充剂10~50份。包括下列步骤,挤出,冷却定型牵引,定尺切割,成品检验和上光。
Description
技术领域
本发明涉及共挤型材技术领域,具体涉及宽幅PVC中空板材及其生产工艺。
背景技术
硬质聚氯乙烯(PVC-U)挤出中空板材是以聚氯乙烯树脂为主要原料,加入适量助剂(复合稳定润滑剂、抗冲改性剂、加工助剂、填充剂等),经热混、冷混、挤出、冷却定型牵引等工艺加工而成。PVC中空板主要用于办公隔断、卫生间隔断、办公家具、广告标牌、活动房墙体、吊顶、各种内门及在养殖行业应用于母猪产床、小猪保育床、保温床等,为自动化养猪设备的专用材料,该产品易于管理,安装效率高、节约成本,越来越受广大用户的欢迎。目前板材表面可以覆膜、上光处理,现发明共挤,可以根据需要共挤彩色或特殊配方的材料,加工组装都很方便。该产品具有质轻、防水、防潮、耐腐蚀性强、阻燃、保温、隔音、耐候性好、无挥发性有毒气体且可重复利用等特点,符合“以塑代木”、“以塑代钢”的国家产业政策,是国家重点鼓励发展的产品,是新一代节能环保型化学建材,但是现有生产这种板材的幅宽都很窄,一般的幅宽不会超过0.6m,一旦宽度过宽,板材很容易出现弯曲,表面不平整,甚至出现裂纹等,而且强度低,使用寿命短。
发明内容
本发明所要解决的技术问题在于提供一种强度高,表面平整,不容易产生弯曲的宽幅PVC中空板材及其生产工艺。
本发明所要解决的技术问题采用以下技术方案来实现:
宽幅PVC中空板材及其生产工艺,其特征在于:所述的宽幅PVC中空板材及其生产工艺的宽度为1米以上,原料包括基础料共挤层料,所述的基础料为PVC树脂100份,复合稳定润滑剂2.5~5.5份,抗冲改性剂3.0~8.0份,加工助剂1.0~3.0份,填充剂10~50份。
所述的复合稳定润滑剂为聚氯乙烯中添加铅盐稳定剂。
所述的抗冲改性剂为CPE抗冲改性剂,其CPE的氯含量控制在34%~37%之间。
所述的填充剂为活性碳酸钙,其纯度在98%以上。
所述的加工改性助剂为甲基丙烯酸甲酯和丙烯酸酯、苯乙烯等单体的共聚物。
所述的宽幅PVC中空板材及其生产工艺的生产工艺,其特征在于:包括下列步骤,挤出,冷却定型牵引,定尺切割,成品检验和上光。
原材料选用
PVC树脂的选择
PVC树脂的选择包括型号的选择及生产厂家的选择两个方面。PVC型材是未经增塑的,因此从材料挤出流动性和制品拉伸强度均衡考虑,因此为保证其具有良好的加工流动性,应选用分子量稍低的树脂,分子量太低又不易满足强度要求。综合两方面因素考虑,一般选用聚合度为1000左右的SG-5型PVC树脂。目前我国聚氯乙烯树脂生产厂家不少,规模大小不一,生产工艺不相同,其粒状结构、粒径分布等产品质量都有差距。频繁更换树脂生产厂家会造成生产工艺的不稳定,直接影响型材的产品质量,因此选择质量可靠、工艺先进的厂家生产的树脂,并按国标进行逐项检测,是生产合格型材的第一关。通过化验室用标准筛法检定其粒径分布,用显微镜观察其粒度形状以及PVC树脂在生产线使用的实际情况,一般PVC树脂的粘数控制在108~114,表观密度为0.5~0.6g/ml即可。
复合稳定润滑剂
聚氯乙烯的热稳定性较差,尤其在加工过程中。在较高的温度下,同时伴随机械剪切作用,聚氯乙烯的热不稳定性倾向显著增强。因此,聚氯乙烯只有经过热稳定处理才具有使用价值。通常采用的方法是向聚氯乙烯中添加一些热稳定剂,可以有效地阻止聚氯乙烯热降解。热稳定剂的作用在于可以很好地抑制聚氯乙烯组成物的降解,并可以稳定配方要求的色泽、机械性能及使用性能等。经综合考虑,PVC型材一般选择铅盐稳定剂,配方使用量2.5~5.5份。
抗冲改性剂
PVC树脂是硬脆性材料,抗冲击强度差,单纯的PVC树脂抗冲击强度不能满足使用的要求,尤其是低温抗冲性能。因此PVC型材配方设计时必须要考虑加入抗冲改性剂,以改善PVC树脂在这方面的性能。目前我国绝大多数PVC板材生产厂仍在使用CPE抗冲改性剂。其CPE的氯含量控制在34%~37%之间,配方使用量为5.0~8.0份。
填充剂
填充剂也称填料,在聚合物中主要起增容、降低成本作用,但多数填料对聚合物的物理机械性能具有一定的损害作用,这种损害作用一般是随着填充量的增加而加剧。在硬质PVC异型材中添加适量的填料,目的并不全是为了增容、降低成本,也是为了提高软化温度和硬度,提高型材挤出稳定性和尺寸稳定性,减少收缩,避免型材翘曲,在硬质PVC中使用超细碳酸钙可以改善冲击强度。为了进一步提高碳酸钙在PVC以及其它塑料中的分散性、补强性,降低对机械的磨损及其它性能,采用脂肪酸和各种偶联剂等表面活性剂处理碳酸钙粒子表面,可以大大提高与聚合物之间的亲和性,提高聚合物对其“润湿”能力,提高熔体的流动性,这种碳酸钙称为活性碳酸钙,其主含量控制在98%以上,白度控制在91%以上,配方使用量为10~50份。
加工改性助剂
由于PVC熔体延展性差,易导致熔体破碎;PVC熔体松弛慢,易导致制品表面粗糙、无光泽及鲨鱼皮等。因此,PVC加工时往往需要加人加工助剂,以改善其熔体上述缺陷。加工助剂为可以改善树脂加工性能的助剂,其主要作用方式有三种:促进树脂熔融、改善熔体流变性能及赋予润滑功能。常用加工改性剂一ACR,ACR为甲基丙烯酸甲酯和丙烯酸酯、苯乙烯等单体的共聚物。在PVC制品中一般使用ACR201或ACR401,用量为1.0~3.0份。
本发明的有益效果是:本发明的板材强度高,共几层表面平整无裂纹,不容易产生弯曲,使用寿命长,幅宽较宽,使用范围广。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
宽幅PVC中空板材及其生产工艺,宽幅PVC中空板材及其生产工艺的宽度为1.200米,原料包括基础料共挤层料,基础料为PVC树脂100份,复合稳定润滑剂4份,抗冲改性剂5.0份,加工助剂2.0份,填充剂30份。
PVC树脂的粘数控制在112,表观密度为0.5g/ml。
复合稳定润滑剂为聚氯乙烯中添加铅盐稳定剂。
抗冲改性剂为CPE抗冲改性剂,其CPE的氯含量控制在35%之间。
填充剂为活性碳酸钙,其纯度在99%。
加工改性助剂为甲基丙烯酸甲酯和丙烯酸酯、苯乙烯单体的共聚物。
宽幅PVC中空板材及其生产工艺的生产工艺,包括下列步骤,挤出,冷却定型牵引,定尺切割,成品检验和上光。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (7)
1.宽幅PVC中空板材,其特征在于:所述的宽幅PVC中空板材及其生产工艺的宽度为1米以上,原料包括基础料共挤层料,所述的基础料为PVC树脂100份,复合稳定润滑剂2.5~5.5份,抗冲改性剂3.0~8.0份,加工助剂1.0~3.0份,填充剂10~50份。
2.根据权利要求1所述的宽幅PVC中空板材,其特征在于:所述的PVC树脂的粘数控制在108~114,表观密度为0.5~0.6g/ml。
3.根据权利要求1所述的宽幅PVC中空板材,其特征在于:所述的复合稳定润滑剂为聚氯乙烯中添加铅盐稳定剂。
4.根据权利要求1所述的宽幅PVC中空板材,其特征在于:所述的抗冲改性剂为CPE抗冲改性剂,其CPE的氯含量控制在34%~37%之间。
5.根据权利要求1所述的宽幅PVC中空板材艺,其特征在于:所述的填充剂为活性碳酸钙,其纯度在98%以上。
6.根据权利要求1所述的宽幅PVC中空板材,其特征在于:所述的加工改性助剂为甲基丙烯酸甲酯和丙烯酸酯、苯乙烯单体的共聚物。
7.根据权利要求1所述的宽幅PVC中空板材及其生产工艺,其特征在于:包括下列步骤,挤出,冷却定型牵引,定尺切割,成品检验和上光。