CN104098306B - A kind of baking-free water-permeable brick and preparation method thereof - Google Patents
A kind of baking-free water-permeable brick and preparation method thereof Download PDFInfo
- Publication number
- CN104098306B CN104098306B CN201410350308.9A CN201410350308A CN104098306B CN 104098306 B CN104098306 B CN 104098306B CN 201410350308 A CN201410350308 A CN 201410350308A CN 104098306 B CN104098306 B CN 104098306B
- Authority
- CN
- China
- Prior art keywords
- desulfurization slag
- cement
- orders
- brick
- sio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of baking-free water-permeable brick belonging to floor tile preparing technical field and preparation method thereof.Described water-permeable brick take desulfurization slag as aggregate, and cement is toughener and binding agent, Na
2siO
39H
2o and NaOH is exciting agent; By desulfurization slag different for grade, cement, NaOH, Na
2siO
39H
2o mixes according to a certain percentage, is positioned in model, normal temperature consolidated shaping; Through maintenance process, be prepared into water-permeable strong, good water-retaining property, the anti-skid wearable baking-free water-permeable brick that intensity is high.
Description
Technical field
The invention belongs to floor tile preparing technical field, particularly a kind of baking-free water-permeable brick and preparation method thereof.
Background technology
Desulfurization slag is the waste residue produced in circulating fluidized bed (CFB) boiler desulfurization operation, because its particle is comparatively large, is settled down to furnace bottom, can obtains through slag-drip opening because wind speed is not enough to make its fluidisation.Desulfurization slag is trade waste, is one of industrial residue that the current discharge capacity of China is larger.Desulfurization slag has a kind ofly misplaced local resource, and Appropriate application desulfurization slag is a problem in the urgent need to address.
Traditional water-permeable brick is prepared into cellular concrete mainly with common rubble and forms, or is more senior polymer fiber concrete permeable brick, ecological husky base water-permeable brick etc.Be at present that the research that seepy material prepared by aggregate is left to be desired with desulfurization slag.
Patent 201110442054.X describes a kind of method utilizing sugared filter mud to prepare water-permeable brick, and the method is that thermal power plants flyash is main raw material, and clay makes binding agent, waste ceramic is aggregate in employing with industrial residue sugar filter mud for pore former.Raw material through batching, stir, the operation acquisition finished product such as old, shaping, dry, sintering.Above-mentioned water-permeable brick is main raw material with solid waste coal ash, but in preparation process, need sintering, makees binding agent, waste coal resources in a large number, damage to land with clay.Patent 201220733300.7 describes a kind of double-deck seepage brick utilizing slag and Desert Sand to do aggregate, and described seepage brick upper strata is the desert sand bed of Desert Sand and aqueous high molecular binding agent mixing compacting; Seepage brick bottom is the inorganic material layer being mixed compacting by slag, water and silicate cement, take full advantage of Waste Slag, but its binding agent adopted is one of aqueous epoxy resins, polyvinyl acetate resin, polyvinyl alcohol or combination, belong to macromolecular material, considerably increase preparation cost.
Summary of the invention
The object of this invention is to provide a kind of baking-free water-permeable brick and preparation method thereof, it is characterized in that, described baking-free water-permeable brick take desulfurization slag as aggregate, and cement is toughener and binding agent, Na
2siO
39H
2o and NaOH is exciting agent, mixes, normal temperature consolidated formation; Wherein, desulfurization slag accounts for 40 ~ 76wt.% of raw material total mass, and cement accounts for 20 ~ 50wt.% of raw material total mass, NaOH and Na
2siO
39H
2o accounts for 4 ~ 10wt.% of raw material total mass.
Described desulfurization slag proportioning is 30 orders: 40 orders: 50 object ratios of quality and the number of copies are 1:1:1 ~ 6:1:1.
Described NaOH and Na
2siO
39H
2the mass ratio of O is 1:1.
The preparation method of described baking-free water-permeable brick, is characterized in that, comprises step:
1) carry out stage treatment to desulfurization slag, obtain the desulfurization slag that grade is different, its grade is 30 orders, 40 orders and 50 orders;
2) by desulfurization slag different for grade in mass ratio proportioning be 30 orders: 40 orders: 50 orders=1:1:1 ~ 6:1:1, mixes;
3) NaOH and Na
2siO
39H
2o weighs for 1:1 in mass ratio, adds tap water and stirs, make it to dissolve completely;
4) account for 40 ~ 76wt.% of raw material total mass by desulfurization slag, cement accounts for 20 ~ 50wt.% of raw material total mass, NaOH and Na
2siO
39H
2the ratio that O accounts for 4 ~ 10wt.% of raw material total mass mixes;
5) be positioned in model by the compound of step 4), conveniently brickmaking compression molding, natural consolidation, maintenance at normal temperatures obtains finished product.
Described maintenance is to the water-permeable brick maintenance more than 28 days under wet environment and room temperature condition after shaping.
The invention has the beneficial effects as follows that achieve the second stage employ of resource, compared with vitrified brick, the present invention avoids sintering, has saved a large amount of coal resources with solid waste desulfurization slag for aggregate.There is good water-permeable and humidity-preserving type, city can be alleviated very well due to the municipal drainage pressure that caused by waterproof ground bedding and tropical island effect, be conducive to the water balance keeping city, the edatope of ground vegetation growth can be improved, regulate the eubiosis, can in the anti-skid on snow raising ground, sky.Realize save energy resource, reduce the discharge of solid waste, promote water cycle, improve the ecological environment.Be mainly used in the laying of the pavior brick of the public place such as walkway, square, gardens needing infiltration rapidly.
Embodiment
The invention provides a kind of baking-free water-permeable brick and preparation method thereof, below by several concrete case study on implementation, the present invention is further elaborated.
Embodiment 1
Take NaOH, Na of equivalent
2siO
39H
2o is 18g altogether, puts into beaker, adds suitable quantity of water, stirs, obtains dissolving completely; According to size fractionated mass ratio 30 order: 40 orders: 50=1:1:1 takes desulfurization slag 72g and cement 90g.
Desulfurization slag and cement are put into agitator for cement mortar container stir, add and dissolve NaOH, Na completely
2siO
39H
2the solution of O, continues to stir, and desulfurization slag, cement and dissolution homogeneity are mixed.The rectangular parallelepiped experiment fragment of brick of 94*46*22mm is made by the method for compression molding.To the maintenance 28 days under wet environment and room temperature condition of the experiment fragment of brick after shaping.Carry out water permeability to experiment fragment of brick, compressive property is tested.Test result is ultimate compression strength 41.09MPa, permeability rate 0.0156cm/s.
Embodiment 2
Take NaOH, Na of equivalent
2siO
39H
2o is 12.6g altogether, puts into beaker, adds suitable quantity of water, stirs, obtains dissolving completely; According to size fractionated mass ratio 30 order: 40 orders: 50=4:1:1 takes desulfurization slag 78g and cement 90g.
Desulfurization slag and cement are put into agitator for cement mortar container stir, add and dissolve NaOH, Na completely
2siO
39H
2the solution of O, continues to stir, and desulfurization slag, cement and dissolution homogeneity are mixed.The rectangular parallelepiped experiment fragment of brick of 94*46*22mm is made by the method for compression molding.To the maintenance 32 days under wet environment and room temperature condition of the experiment fragment of brick after shaping.Carry out water permeability to experiment fragment of brick, compressive property is tested.Test result is ultimate compression strength 40.68MPa, permeability rate 0.0261cm/s.
Embodiment 3
Take NaOH, Na of equivalent
2siO
39H
2o is 7.5g altogether, puts into beaker, adds suitable quantity of water, stirs, obtains dissolving completely; According to size fractionated mass ratio 30 order: 40 orders: 50=3:1:1 takes desulfurization slag 83g and cement 90g.
Desulfurization slag and cement are put into agitator for cement mortar container stir, add and dissolve NaOH, Na completely
2siO
39H
2the solution of O, continues to stir, and desulfurization slag, cement and dissolution homogeneity are mixed.The rectangular parallelepiped experiment fragment of brick of 94*46*22mm is made by the method for compression molding.To the maintenance 30 days under wet environment and room temperature condition of the experiment fragment of brick after shaping.Carry out water permeability to experiment fragment of brick, compressive property is tested.Test result is ultimate compression strength 40.59MPa, permeability rate 0.0192cm/s.
Embodiment 4
Take NaOH, Na of equivalent
2siO
39H
2o is 18g altogether, puts into beaker, adds suitable quantity of water, stirs, obtains dissolving completely; According to size fractionated mass ratio 30 order: 40 orders: 50=2:1:1 takes desulfurization slag 90g and cement 72g.
Desulfurization slag and cement are put into agitator for cement mortar container stir, add and dissolve NaOH, Na completely
2siO
39H
2the solution of O, continues to stir, and desulfurization slag, cement and dissolution homogeneity are mixed.The rectangular parallelepiped experiment fragment of brick of 94*46*22mm is made by the method for compression molding.To the maintenance 29 days under wet environment and room temperature condition of the experiment fragment of brick after shaping.Carry out water permeability to experiment fragment of brick, compressive property is tested.Test result is ultimate compression strength 36.23MPa, permeability rate 0.0187cm/s.
Embodiment 5
Take NaOH, Na of equivalent
2siO
39H
2o is 12.6g altogether, puts into beaker, adds suitable quantity of water, stirs, obtains dissolving completely; According to size fractionated mass ratio 30 order: 40 orders: 50=6:1:1 takes desulfurization slag 96g and cement 72g.
Desulfurization slag and cement are put into agitator for cement mortar container stir, stir, dissolve solution completely, continue to stir, desulfurization slag, cement and dissolution homogeneity are mixed.The rectangular parallelepiped experiment fragment of brick of 94*46*22mm is made by the method for compression molding.To the maintenance 28 days under wet environment and room temperature condition of the experiment fragment of brick after shaping.Carry out water permeability to experiment fragment of brick, compressive property is tested.Test result is ultimate compression strength 35.98MPa, permeability rate 0.0329cm/s.
Embodiment 6
Take NaOH, Na of equivalent
2siO
39H
2o is 7.5g altogether, puts into beaker, adds suitable quantity of water, stirs, obtains dissolving completely; According to size fractionated mass ratio 30 order: 40 orders: 50=1:1:1 takes desulfurization slag 102g and cement 72g.
Desulfurization slag and cement are put into agitator for cement mortar container stir, stir, dissolve solution completely, continue to stir, desulfurization slag, cement and dissolution homogeneity are mixed.The rectangular parallelepiped experiment fragment of brick of 94*46*22mm is made by the method for compression molding.To the maintenance 28 days under wet environment and room temperature condition of the experiment fragment of brick after shaping.Carry out water permeability to experiment fragment of brick, compressive property is tested.Test result is ultimate compression strength 35.98MPa, permeability rate 0.0203cm/s.
Embodiment 7
Take NaOH, Na of equivalent
2siO
39H
2o is 18g altogether, puts into beaker, adds suitable quantity of water, stirs, obtains dissolving completely; According to size fractionated mass ratio 30 order: 40 orders: 50=4:1:1 takes desulfurization slag 108g and cement 54g.
Desulfurization slag and cement are put into agitator for cement mortar container stir, stir, dissolve solution completely, continue to stir, desulfurization slag, cement and dissolution homogeneity are mixed.The rectangular parallelepiped experiment fragment of brick of 94*46*22mm is made by the method for compression molding.To the maintenance 32 days under wet environment and room temperature condition of the experiment fragment of brick after shaping.Carry out water permeability to experiment fragment of brick, compressive property is tested.Test result is ultimate compression strength 33.66MPa, permeability rate 0.0308cm/s.
Embodiment 8
Take NaOH, Na of equivalent
2siO
39H
2o is 12.6g altogether, puts into beaker, adds suitable quantity of water, stirs, obtains dissolving completely; According to size fractionated mass ratio 30 order: 40 orders: 50=3:1:1 takes desulfurization slag 113g and cement 54g.
Desulfurization slag and cement are put into agitator for cement mortar container stir, stir, dissolve solution completely, continue to stir, desulfurization slag, cement and dissolution homogeneity are mixed.The rectangular parallelepiped experiment fragment of brick of 94*46*22mm is made by the method for compression molding.To the maintenance 28 days under wet environment and room temperature condition of the experiment fragment of brick after shaping.Carry out water permeability to experiment fragment of brick, compressive property is tested.Test result is ultimate compression strength 33.33MPa, permeability rate 0.0202cm/s.
Embodiment 9
Take NaOH, Na of equivalent
2siO
39H
2o is 7.5g altogether, puts into beaker, adds suitable quantity of water, stirs, obtains dissolving completely; According to size fractionated mass ratio 30 order: 40 orders: 50=2:1:1 takes desulfurization slag: 120g and cement 54g.
Desulfurization slag and cement are put into agitator for cement mortar container stir, stir, dissolve solution completely, continue to stir, desulfurization slag, cement and dissolution homogeneity are mixed.The rectangular parallelepiped experiment fragment of brick of 94*46*22mm is made by the method for compression molding.To the maintenance 28 days under wet environment and room temperature condition of the experiment fragment of brick after shaping.Carry out water permeability to experiment fragment of brick, compressive property is tested.Test result is ultimate compression strength 33.55MPa, permeability rate 0.0233cm/s.
Embodiment 10
Take NaOH, Na of equivalent
2siO
39H
2o is 18g altogether, puts into beaker, adds suitable quantity of water, stirs, obtains dissolving completely; According to size fractionated mass ratio 30 order: 40 orders: 50=6:1:1 takes desulfurization slag 117g and cement 45g.
Desulfurization slag and cement are put into agitator for cement mortar container stir, stir, dissolve solution completely, continue to stir, desulfurization slag, cement and dissolution homogeneity are mixed.The rectangular parallelepiped experiment fragment of brick of 94*46*22mm is made by the method for compression molding.To the maintenance 29 days under wet environment and room temperature condition of the experiment fragment of brick after shaping.Carry out water permeability to experiment fragment of brick, compressive property is tested.Test result is ultimate compression strength 32.53MPa, permeability rate 0.0400cm/s.
Embodiment 11
Take NaOH, Na of equivalent
2siO
39H
2o is 12.6g altogether, puts into beaker, adds suitable quantity of water, stirs, obtains dissolving completely; According to size fractionated mass ratio 30 order: 40 orders: 50=1:1:1 takes desulfurization slag 123g and cement 45g.
Desulfurization slag and cement are put into agitator for cement mortar container stir, stir, dissolve solution completely, continue to stir, desulfurization slag, cement and dissolution homogeneity are mixed.The rectangular parallelepiped experiment fragment of brick of 94*46*22mm is made by the method for compression molding.To the maintenance 28 days under wet environment and room temperature condition of the experiment fragment of brick after shaping.Carry out water permeability to experiment fragment of brick, compressive property is tested.Test result is ultimate compression strength 32.10MPa, permeability rate 0.0271cm/s.
Embodiment 12
Take NaOH, Na of equivalent
2siO
39H
2o is 7.2g altogether, puts into beaker, adds suitable quantity of water, stirs, obtains dissolving completely; According to size fractionated mass ratio 30 order: 40 orders: 50=1:1:1 takes desulfurization slag 127g and cement 45g.
Desulfurization slag and cement are put into agitator for cement mortar container stir, stir, dissolve solution completely, continue to stir, desulfurization slag, cement and dissolution homogeneity are mixed.The rectangular parallelepiped experiment fragment of brick of 94*46*22mm is made by the method for compression molding.To the maintenance 28 days under wet environment and room temperature condition of the experiment fragment of brick after shaping.Carry out water permeability to experiment fragment of brick, compressive property is tested.Test result is ultimate compression strength 32.70MPa, permeability rate 0.0366cm/s.
Embodiment 13
Take NaOH, Na of equivalent
2siO
39H
2o is 18g altogether, puts into beaker, adds suitable quantity of water, stirs, obtains dissolving completely; According to size fractionated mass ratio 30 order: 40 orders: 50=3:1:1 takes desulfurization slag 127g and cement 36g.
Desulfurization slag and cement are put into agitator for cement mortar container stir, stir, dissolve solution completely, continue to stir, desulfurization slag, cement and dissolution homogeneity are mixed.The rectangular parallelepiped experiment fragment of brick of 94*46*22mm is made by the method for compression molding.To the maintenance 29 days under wet environment and room temperature condition of the experiment fragment of brick after shaping.Carry out water permeability to experiment fragment of brick, compressive property is tested.Test result is ultimate compression strength 30.97Mpa, permeability rate 0.0375cm/s.
Embodiment 14
Take NaOH, Na of equivalent
2siO
39H
2o is 12.6g altogether, puts into beaker, adds suitable quantity of water, stirs, obtains dissolving completely; According to size fractionated mass ratio 30 order: 40 orders: 50=2:1:1 takes desulfurization slag 131g and cement 36g.
Desulfurization slag and cement are put into agitator for cement mortar container stir, stir, dissolve solution completely, continue to stir, desulfurization slag, cement and dissolution homogeneity are mixed.The rectangular parallelepiped experiment fragment of brick of 94*46*22mm is made by the method for compression molding.To the maintenance 29 days under wet environment and room temperature condition of the experiment fragment of brick after shaping.Carry out water permeability to experiment fragment of brick, compressive property is tested.Test result is ultimate compression strength 30.93MPa, permeability rate 0.0519cm/s.
Embodiment 15
Take NaOH, Na of equivalent
2siO
39H
2o is 7.5g altogether, puts into beaker, adds suitable quantity of water, stirs, obtains dissolving completely; According to size fractionated mass ratio 30 order: 40 orders: 50=6:1:1 takes desulfurization slag 136g and cement 36g.
Desulfurization slag and cement are put into agitator for cement mortar container stir, stir, dissolve solution completely, continue to stir, desulfurization slag, cement and dissolution homogeneity are mixed.The rectangular parallelepiped experiment fragment of brick of 94*46*22mm is made by the method for compression molding.To the maintenance 29 days under wet environment and room temperature condition of the experiment fragment of brick after shaping.Carry out water permeability to experiment fragment of brick, compressive property is tested.Test result is ultimate compression strength 30.43MPa, permeability rate 0.0782cm/s.
Claims (3)
1. a baking-free water-permeable brick, is characterized in that, described baking-free water-permeable brick take desulfurization slag as aggregate, and cement is toughener and binding agent, with the Na of mass ratio 1:1
2siO
39H
2o and NaOH is exciting agent, mixes, normal temperature consolidated formation; Wherein, desulfurization slag accounts for 40 ~ 76wt.% of raw material total mass, and cement accounts for 20 ~ 50wt.% of raw material total mass, NaOH and Na
2siO
39H
2o accounts for 4 ~ 10wt.% of raw material total mass; Described desulfurization slag grade ratio is 30 orders: 40 orders: 50 object ratios of quality and the number of copies are 1:1:1 ~ 6:1:1.
2. a preparation method for baking-free water-permeable brick, is characterized in that, comprises step:
1) carry out stage treatment to desulfurization slag, obtain the desulfurization slag that grade is different, its grade is 30 orders, 40 orders and 50 orders;
2) by desulfurization slag different for grade in mass ratio proportioning be 30 orders: 40 orders: 50 orders=1:1:1 ~ 6:1:1, mixes;
3) NaOH and Na
2siO
39H
2o weighs for 1:1 in mass ratio, adds tap water and stirs, make it to dissolve completely;
4) account for 40 ~ 76wt.% of raw material total mass by desulfurization slag, cement accounts for 20 ~ 50wt.% of raw material total mass, NaOH and Na
2siO
39H
2the ratio that O accounts for 4 ~ 10wt.% of raw material total mass mixes;
5) be positioned in model by the compound of step 4), conveniently brickmaking compression molding, natural consolidation, maintenance at normal temperatures obtains finished product.
3. the preparation method of a kind of baking-free water-permeable brick according to claim 2, is characterized in that, described maintenance is to the water-permeable brick maintenance more than 28 days under wet environment and room temperature condition after shaping.