CN104098302A - Deinsectization light partition wall plate and manufacturing method thereof - Google Patents
Deinsectization light partition wall plate and manufacturing method thereof Download PDFInfo
- Publication number
- CN104098302A CN104098302A CN201410272001.1A CN201410272001A CN104098302A CN 104098302 A CN104098302 A CN 104098302A CN 201410272001 A CN201410272001 A CN 201410272001A CN 104098302 A CN104098302 A CN 104098302A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- add
- deinsectization
- partition wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a deinsectization light partition wall plate which is characterized by comprising the following raw materials in parts by weight: 10-14 parts of cement, 14-18 parts of geopolymer, 16-19 parts of coal ash, 15-17 parts of volcano rock, 12-15 parts of pond sludge, 16-20 parts of corn stalk, 1-2 parts of dicumyl peroxide, 4-8 parts of mandarin oil, 0.4-0.7 part of sodium silicate, 0.7-1.2 part(s) of ascorbic acid, 5-8 parts of waste wool, 7-9 parts of polystyrene foam particle, 0.03-0.5 part of acetophenate, 17-19 parts of cotton-seed hull, 3-6 parts of an auxiliary agent and an appropriate amount of water. The deinsectization light partition wall plate has the advantages of sterilization, deinsectization, heat preservation, thermal insulation and high strength, nails can be completely fixed in the wall space for load-bearing, pre-embedded parts are not needed, sawing, planing, nailing and ornament pasting can be directly performed for shaping.
Description
Technical field
The present invention relates to building material field, be specifically related to a kind of deinsectization light cellular partition board and preparation method thereof.
Background technology
Light cellular partition board is made up of various industrial waste residues such as innoxious phosphogypsum, lightweight slag, flyash, a kind of novel energy-conserving walling material forming through the maintenance of frequency conversion steam pressurized, the walling that it is a kind of external form as the cassette ceiling, but there is male and female falcon groove on its both sides, when installation, only sheet material need be erected, male and female falcon is coated after a small amount of filleting mortar assembled.It has the advantages such as quality is light, intensity is high, multiple environmental protection, heat insulating, sound insulation, breathing damping, fire prevention, rapid construction, reduction body of wall cost, so enjoy favor in architecture indoor finishing field, but the shortcomings such as the light cellular partition board ultimate compression strength using is in the market low, tensile strength weak, anti-cracking performance and hanging ability is not good, production cost is high, sound-insulating weak effect.
Summary of the invention
Object of the present invention is just to provide a kind of deinsectization light cellular partition board and preparation method thereof, to overcome the deficiencies in the prior art.
The object of the present invention is achieved like this:
A kind of deinsectization light cellular partition board, it is characterized in that, made by the raw material of following weight part: cement 10-14, geopolymer 14-18, flyash 16-19, volcanics 15-17, pond mud 12-15, maize straw 16-20, dicumyl peroxide 1-2, mandarin oil 4-8, water glass 0.4-0.7, xitix 0.7-1.2, waste and old wool 5-8, polystyrene foam particles 7-9, acetofenate 0.03-0.5, cotton seed hull 17-19, auxiliary agent 3-6, suitable quantity of water.
Described auxiliary agent is made up of following raw materials in part by weight: volcanic ash 6-9, Sodium sulfate anhydrous.min(99) 2-5, magnesium chloride 3-5, magnesium oxide 2-4, polyvinyl alcohol 0.2-0.5, Starso 0.03-0.07, sodium aluminate 0.05-0.6, tartrate 0.8-2.1, organosilicon crylic acid latex 2.1-4.3, 2-imidazolidone 0.04-0.09, silicon carbide 1-3, accelerant CZ 0.03-0.05, Syzygium aromaticum stem oil 1.2-3.2, its preparation method is in 50% magnesium chloride solution, to add the magnesium oxide powder inorganic gel agent that stirs to obtain, then other leftover materials are pulverized and mixed, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter is at 2-5mm, dry and get final product.
Described geopolymer is the novel inorganic silicon-aluminum gelatinized material in a kind of structure with the network-like keyed jointing structure of space three-dimensional, does not adopt " two mills one burn " calcining process of consumption of natural resource and the energy in preparation technology, does not substantially discharge CO
2.The starting material wide material sources of geopolymer, easy to prepare, energy consumption is little, has higher mechanical property and very excellent resistance to elevated temperatures simultaneously, broken through the use range of traditional portland and alkali slag cement.The present invention, by geopolymer replacing partial cement, not only can reduce cost energy-conserving and environment-protective, and can not weaken again the pectisation of cement.
The preparation method of described a kind of deinsectization light cellular partition board, is characterized in that comprising the following steps:
(1) maize straw, cotton seed hull are sent in charring furnace, at 485-605 DEG C, 3-4 hour is processed in charing, takes out, and is ground into powder, makes it seethe spray form mandarin oil under condition, then add waste and old wool stirring and evenly mixing to the powder of gained in air blast;
(2) get geopolymer and put into the hydrochloric acid soln of 8-12% and soak 4-5 hour, filter and take out, use clear water repetitive scrubbing, dry, be added to the water, meanwhile, add flyash, water glass, xitix, grinding obtains slurry;
(3) volcanics, pond mud are calcined at 600-828 DEG C after 3-6 hour and taken out, pulverize, add acetofenate to stir 5-8 minute;
(4) step (1), (2), (3) reaction mass and the pulverizing of other leftover materials are added to suitable quantity of water stirring and evenly mixing and obtain slip, the slurry making is added to wall slab squeezing former moulding, cutting, natural curing, to obtain final product.
The present invention has following beneficial effect: the present invention has advantages of that disinfection and deinsectization, heat insulating, intensity are high, can surely follow closely load-bearing at metope completely, without any built-in fitting, can directly saw, dig, follow closely, paste decorative model.
Embodiment
Described a kind of deinsectization light cellular partition board, it is characterized in that, made by the raw material of following weight part: cement 13, geopolymer 15, flyash 16, volcanics 17, pond mud 12, maize straw 16, dicumyl peroxide 1, mandarin oil 4, water glass 0.4, xitix 0.7, waste and old wool 5, polystyrene foam particles 7, acetofenate 0.03, cotton seed hull 17, auxiliary agent 3, suitable quantity of water.
Described auxiliary agent is made up of following raw materials in part by weight: volcanic ash 8, Sodium sulfate anhydrous.min(99) 2, magnesium chloride 3, magnesium oxide 4, polyvinyl alcohol 0.2, Starso 0.03, sodium aluminate 0.05, tartrate 0.8, organosilicon crylic acid latex 2.2,2-imidazolidone 0.04, silicon carbide 1, accelerant CZ 0.03, Syzygium aromaticum stem oil 1.2, its preparation method is in 50% magnesium chloride solution, to add the magnesium oxide powder inorganic gel agent that stirs to obtain, then other leftover materials are pulverized and mixed, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter, at 2-5mm, is dried and be get final product.
Making method comprises the following steps:
(1) maize straw, cotton seed hull are sent in charring furnace, at 485-605 DEG C, 3-4 hour is processed in charing, takes out, and is ground into powder, makes it seethe spray form mandarin oil under condition, then add waste and old wool stirring and evenly mixing to the powder of gained in air blast;
(2) get geopolymer and put into the hydrochloric acid soln of 8-12% and soak 4-5 hour, filter and take out, use clear water repetitive scrubbing, dry, be added to the water, meanwhile, add flyash, water glass, xitix, grinding obtains slurry;
(3) volcanics, pond mud are calcined at 600-828 DEG C after 3-6 hour and taken out, pulverize, add acetofenate to stir 5-8 minute;
(4) step (1), (2), (3) reaction mass and the pulverizing of other leftover materials are added to suitable quantity of water stirring and evenly mixing and obtain slip, the slurry making is added to wall slab squeezing former moulding, cutting, natural curing, to obtain final product.
The technical indicator of processing the light cellular partition board obtaining by above-described embodiment is as follows:
(1) unit weight: 491kg/m
3;
(2) thermal conductivity (25 ± 2 DEG C of medial temperatures): 0.084W/ (mk);
(3) high temperature resistant, flat appearance is smooth.
Claims (2)
1. a deinsectization light cellular partition board, it is characterized in that, made by the raw material of following weight part: cement 10-14, geopolymer 14-18, flyash 16-19, volcanics 15-17, pond mud 12-15, maize straw 16-20, dicumyl peroxide 1-2, mandarin oil 4-8, water glass 0.4-0.7, xitix 0.7-1.2, waste and old wool 5-8, polystyrene foam particles 7-9, acetofenate 0.03-0.5, cotton seed hull 17-19, auxiliary agent 3-6, suitable quantity of water, described auxiliary agent is made up of following raw materials in part by weight: volcanic ash 6-9, Sodium sulfate anhydrous.min(99) 2-5, magnesium chloride 3-5, magnesium oxide 2-4, polyvinyl alcohol 0.2-0.5, Starso 0.03-0.07, sodium aluminate 0.05-0.6, tartrate 0.8-2.1, organosilicon crylic acid latex 2.1-4.3, 2-imidazolidone 0.04-0.09, silicon carbide 1-3, accelerant CZ 0.03-0.05, Syzygium aromaticum stem oil 1.2-3.2, its preparation method is in 50% magnesium chloride solution, to add the magnesium oxide powder inorganic gel agent that stirs to obtain, then other leftover materials are pulverized and mixed, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter is at 2-5mm, dry and get final product.
2. the making method of a kind of deinsectization light cellular partition board according to claim 1, is characterized in that comprising the following steps:
(1) maize straw, cotton seed hull are sent in charring furnace, at 485-605 DEG C, 3-4 hour is processed in charing, takes out, and is ground into powder, makes it seethe spray form mandarin oil under condition, then add waste and old wool stirring and evenly mixing to the powder of gained in air blast;
(2) get geopolymer and put into the hydrochloric acid soln of 8-12% and soak 4-5 hour, filter and take out, use clear water repetitive scrubbing, dry, be added to the water, meanwhile, add flyash, water glass, xitix, grinding obtains slurry;
(3) volcanics, pond mud are calcined at 600-828 DEG C after 3-6 hour and taken out, pulverize, add acetofenate to stir 5-8 minute;
(4) step (1), (2), (3) reaction mass and the pulverizing of other leftover materials are added to suitable quantity of water stirring and evenly mixing and obtain slip, the slurry making is added to wall slab squeezing former moulding, cutting, natural curing, to obtain final product.