CN104087204A - 一种汽车内饰件用热熔胶 - Google Patents

一种汽车内饰件用热熔胶 Download PDF

Info

Publication number
CN104087204A
CN104087204A CN201410293108.4A CN201410293108A CN104087204A CN 104087204 A CN104087204 A CN 104087204A CN 201410293108 A CN201410293108 A CN 201410293108A CN 104087204 A CN104087204 A CN 104087204A
Authority
CN
China
Prior art keywords
parts
melt adhesive
add
hot melt
minute
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410293108.4A
Other languages
English (en)
Other versions
CN104087204B (zh
Inventor
李勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chuzhou City Guang Wei Chemical Co Ltd
Original Assignee
Chuzhou City Guang Wei Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chuzhou City Guang Wei Chemical Co Ltd filed Critical Chuzhou City Guang Wei Chemical Co Ltd
Priority to CN201410293108.4A priority Critical patent/CN104087204B/zh
Publication of CN104087204A publication Critical patent/CN104087204A/zh
Application granted granted Critical
Publication of CN104087204B publication Critical patent/CN104087204B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种汽车内饰件用热熔胶，它是由下述重量份的原料组成的：乙烯-醋酸乙烯共聚物65-71、洋甘菊精油0.4-0.6、甘草酸二钾1-2、邻苯二甲酸二辛脂4-5、聚异丁烯1-2、聚丙烯酸2-3、陶瓷粉0.3-1、二硬脂酰氧异丙氧基铝酸酯0.1-0.2、氢化松香甘油酯10-13、六溴环十二烷0.5-1、聚乙烯醇缩丁醛酯3-4、粘结助剂12-16；本发明制备的热熔胶，无有毒化学物挥发、无气味，对人体健康无害；生产过程中无污染、无毒害，安全环保，且用途广泛，可用于不同材料间的粘帖，如汽车车灯组装、内饰件组合，车内地毯、毛毡、非金属装饰物等的黏结、贴合等。

Description

一种汽车内饰件用热熔胶
技术领域
    本发明主要涉及一种热熔胶粉末，尤其涉及一种汽车内饰件用热熔胶。
背景技术
    热熔胶是一种可塑性的粘合剂，在一定温度范围内其物理状态随温度改变而改变，而化学特性不变，其无毒无味，属环保型化学产品。
发明内容
本发明目的就是提供一种汽车内饰件用热熔胶。
本发明是通过以下技术方案实现的：
一种汽车内饰件用热熔胶，它是由下述重量份的原料组成的：
乙烯-醋酸乙烯共聚物65-71、洋甘菊精油0.4-0.6、甘草酸二钾1-2、邻苯二甲酸二辛脂4-5、聚异丁烯1-2、聚丙烯酸2-3、陶瓷粉0.3-1、二硬脂酰氧异丙氧基铝酸酯0.1-0.2、氢化松香甘油酯10-13、六溴环十二烷0.5-1、聚乙烯醇缩丁醛酯3-4、粘结助剂12-16；
所述的增粘结助剂是由下述重量份的原料组成的：
液体石蜡24-30、亚麻籽胶2-3、氟化石墨1-2、EVA树脂4-5、马来酸二丁酯3-4、油酸钾皂0.6-2、丙基三甲氧基硅烷0.2-0.5；
将EVA树脂加热软化，加入马来酸二丁酯，搅拌均匀，加入丙基三甲氧基硅烷，在50-60℃下保温搅拌10-15分钟，加入到液体石蜡中，搅拌均匀，得粘结液；
将亚麻籽胶与油酸钾皂混合，搅拌均匀后加入氟化石墨，球磨均匀，加入到上述粘结液中，60-80转/分搅拌分散3-4分钟，即得所述粘结助剂。
一种汽车内饰件用热熔胶的制备方法，包括以下步骤：
将氢化松香甘油酯加热熔化后加入聚乙烯醇缩丁醛酯、聚丙烯酸，在上述熔化温度下保温搅拌10-15分钟，加入陶瓷粉、聚异丁烯、二硬脂酰氧异丙氧基铝酸酯，搅拌至常温，在常温下继续搅拌20-30分钟，加入除了粘结助剂以外的各原料，在25-30℃下保温静置1-2小时，加入粘结助剂，送入混炼机，加热升温至90-100℃，混炼20-30min；将混炼均匀后的产物经过真空脱泡后加入到双螺杆挤出机，挤出产物经冷却、造粒，即得所述汽车内饰件用热熔胶。
本发明的优点是：
    本发明制备的热熔胶，无有毒化学物挥发、无气味，对人体健康无害；生产过程中无污染、无毒害，安全环保，且用途广泛，可用于不同材料间的粘帖，如汽车车灯组装、内饰件组合，车内地毯、毛毡、非金属装饰物等的黏结、贴合等。。
具体实施方式
实施例1
一种汽车内饰件用热熔胶，它是由下述重量份（公斤）的原料组成的：
乙烯-醋酸乙烯共聚物71、洋甘菊精油0.6、甘草酸二钾1、邻苯二甲酸二辛脂4、聚异丁烯2、聚丙烯酸2-3、陶瓷粉0.3、二硬脂酰氧异丙氧基铝酸酯0.2、氢化松香甘油酯13、六溴环十二烷0.5、聚乙烯醇缩丁醛酯3、粘结助剂16；
所述的增粘结助剂是由下述重量份的原料组成的：
液体石蜡30、亚麻籽胶3、氟化石墨2、EVA树脂5、马来酸二丁酯3、油酸钾皂0.6、丙基三甲氧基硅烷0.5；
将EVA树脂加热软化，加入马来酸二丁酯，搅拌均匀，加入丙基三甲氧基硅烷，在60℃下保温搅拌10-15分钟，加入到液体石蜡中，搅拌均匀，得粘结液；
将亚麻籽胶与油酸钾皂混合，搅拌均匀后加入氟化石墨，球磨均匀，加入到上述粘结液中，60转/分搅拌分散4分钟，即得所述粘结助剂。
一种汽车内饰件用热熔胶的制备方法，其特征在于包括以下步骤：
将氢化松香甘油酯加热熔化后加入聚乙烯醇缩丁醛酯、聚丙烯酸，在上述熔化温度下保温搅拌15分钟，加入陶瓷粉、聚异丁烯、二硬脂酰氧异丙氧基铝酸酯，搅拌至常温，在常温下继续搅拌30分钟，加入除了粘结助剂以外的各原料，在30℃下保温静置2小时，加入粘结助剂，送入混炼机，加热升温至100℃，混炼30min；将混炼均匀后的产物经过真空脱泡后加入到双螺杆挤出机，挤出产物经冷却、造粒，即得所述汽车内饰件用热熔胶。
性能测试
软化点100℃；
剥离强度：98N/25mm。

Claims (2)

1.一种汽车内饰件用热熔胶，其特征在于它是由下述重量份的原料组成的：
乙烯-醋酸乙烯共聚物65-71、洋甘菊精油0.4-0.6、甘草酸二钾1-2、邻苯二甲酸二辛脂4-5、聚异丁烯1-2、聚丙烯酸2-3、陶瓷粉0.3-1、二硬脂酰氧异丙氧基铝酸酯0.1-0.2、氢化松香甘油酯10-13、六溴环十二烷0.5-1、聚乙烯醇缩丁醛酯3-4、粘结助剂12-16；
所述的增粘结助剂是由下述重量份的原料组成的：
液体石蜡24-30、亚麻籽胶2-3、氟化石墨1-2、EVA树脂4-5、马来酸二丁酯3-4、油酸钾皂0.6-2、丙基三甲氧基硅烷0.2-0.5；
将EVA树脂加热软化，加入马来酸二丁酯，搅拌均匀，加入丙基三甲氧基硅烷，在50-60℃下保温搅拌10-15分钟，加入到液体石蜡中，搅拌均匀，得粘结液；
将亚麻籽胶与油酸钾皂混合，搅拌均匀后加入氟化石墨，球磨均匀，加入到上述粘结液中，60-80转/分搅拌分散3-4分钟，即得所述粘结助剂。
2.一种如权利要求1所述的汽车内饰件用热熔胶的制备方法，其特征在于包括以下步骤：
将氢化松香甘油酯加热熔化后加入聚乙烯醇缩丁醛酯、聚丙烯酸，在上述熔化温度下保温搅拌10-15分钟，加入陶瓷粉、聚异丁烯、二硬脂酰氧异丙氧基铝酸酯，搅拌至常温，在常温下继续搅拌20-30分钟，加入除了粘结助剂以外的各原料，在25-30℃下保温静置1-2小时，加入粘结助剂，送入混炼机，加热升温至90-100℃，混炼20-30min；将混炼均匀后的产物经过真空脱泡后加入到双螺杆挤出机，挤出产物经冷却、造粒，即得所述汽车内饰件用热熔胶。
CN201410293108.4A 2014-06-26 2014-06-26 一种汽车内饰件用热熔胶 Active CN104087204B (zh)