CN104087133A - 抑菌木器面漆 - Google Patents
抑菌木器面漆 Download PDFInfo
- Publication number
- CN104087133A CN104087133A CN201410365683.0A CN201410365683A CN104087133A CN 104087133 A CN104087133 A CN 104087133A CN 201410365683 A CN201410365683 A CN 201410365683A CN 104087133 A CN104087133 A CN 104087133A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- intermediate product
- bacteriostatic
- wood
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抑菌木器面漆,属于涂料技术领域。本发明按重量份数计,以水溶性饱和聚酯树脂40份~50份,水溶性氨基树脂8份~12份,磺胺异恶唑0.05份~0.1份,两面针挥发油0.1份~1份,己二异氰酸酯30份~45份,乙醇5份~8份,颜料15份~20份,膨润土2份~5份,二氧化硅8份~10份,硅油1份~3份以及水5份~10份作为原料制备而成。与现有的木器面漆相比,本发明抑菌效果明显,其抑菌率高达100%。
Description
技术领域
本发明属于涂料技术领域,尤其涉及一种抑菌木器面漆。
背景技术
受南方多雨、潮湿天气的影响,很多木器类的家具表面容易滋生大肠杆菌、金葡萄杆菌等细菌,从而使家具表面发霉、变色,不仅影响着家具的美观,也造成了细菌繁殖传播疾病。然而,虽然市场上销售的木器面漆品种繁多,但大多主要起着装饰和保护的作用,并不具备抑菌作用,即使有些木器面漆具有抑菌作用,但其抑菌效果并不是十分理想。
发明内容
本发明解决的技术问题是提供一种具有抑菌作用的抑菌木器面漆。
为了解决上述技术问题,本发明所采用的技术方案是:
一种抑菌木器面漆,由以下重量份数的原料制成:
水溶性饱和聚酯树脂 40份~50份;
水溶性氨基树脂 8份~12份;
磺胺异恶唑 0.05份~0.1份;
两面针挥发油 0.1份~1份;
己二异氰酸酯 30份~45份;
乙醇 5份~8份;
颜料 15份~20份;
膨润土 2份~5份;
二氧化硅 8份~10份;
硅油 1份~3份;
水 5份~10份;
其制备方法包括以下步骤:
A、按上述重量份数,将己二异氰酸酯和乙醇放入反应器中混合,进行反应,直至NCO值小于0.5,得到中间产物Ⅰ,备用;
B、将磺胺异恶唑,颜料,膨润土,二氧化硅,水以及A步骤制得的中间产物Ⅰ放入研磨机中,研磨至细度小于10微米,得到中间产物Ⅱ;
C、将B步骤制得的中间产物Ⅱ倒入高速分散机中,加入水溶性饱和聚酯树脂,水溶性氨基树脂,两面针挥发油以及硅油以900转/分钟~1000转/分的转速分散2小时~3小时,制得。
由于采用上述技术方案,本发明得到的有益效果是:
1.本发明抑菌效果明显,其抑菌率高达100%。
2.本发明由于采用全封闭的己二异氰酸酯和氨基树脂两种固化树脂混合使用,使得本发明的抑菌木器面漆可以在较低温度下进行固化。
具体实施方式
以下结合具体实施例对本发明作进一步详述,而本发明的保护范围并非仅仅局限于以下实施例。
实施例1
本抑菌木器面漆包括以下制备原料:水溶性饱和聚酯树脂4.0kg,水溶性氨基树脂1.2kg,磺胺异恶唑0.01kg,两面针挥发油0.1kg,己二异氰酸酯4.5kg,乙醇0.5kg,颜料1.5kg,膨润土0.5kg,二氧化硅1.0kg,硅油0.1kg以及水1.0kg;
其制备方法包括以下步骤:
A、将上述己二异氰酸酯和乙醇放入反应器中混合,进行反应,直至NCO值小于0.5,得到中间产物Ⅰ,备用;
B、将磺胺异恶唑,颜料,膨润土,二氧化硅,水以及A步骤制得的中间产物Ⅰ放入研磨机中,研磨至细度小于10微米,得到中间产物Ⅱ;
C、将B步骤制得的中间产物Ⅱ倒入高速分散机中,加入水溶性饱和聚酯树脂,水溶性氨基树脂,两面针挥发油以及硅油以900转/分钟的转速分散3小时,制得。
经测试,本实施例制得的抑菌木器面漆的抑菌率为100%。
实施例2
本抑菌木器面漆包括以下制备原料:水溶性饱和聚酯树脂5.0kg,水溶性氨基树脂0.8kg,磺胺异恶唑0.005kg,两面针挥发油0.01kg,己二异氰酸酯3.0kg,乙醇0.8kg,颜料2.0kg,膨润土0.2kg,二氧化硅0.8kg,硅油0.3kg以及水0.5kg;
其制备方法包括以下步骤:
A、将上述己二异氰酸酯和乙醇放入反应器中混合,进行反应,直至NCO值小于0.5,得到中间产物Ⅰ,备用;
B、将磺胺异恶唑,颜料,膨润土,二氧化硅,水以及A步骤制得的中间产物Ⅰ放入研磨机中,研磨至细度小于10微米,得到中间产物Ⅱ;
C、将B步骤制得的中间产物Ⅱ倒入高速分散机中,加入水溶性饱和聚酯树脂,水溶性氨基树脂,两面针挥发油以及硅油以980转/分的转速分散2.5小时,制得。
经测试,本实施例制得的抑菌木器面漆的抑菌率为100%。
实施例3
本抑菌木器面漆包括以下制备原料:水溶性饱和聚酯树脂4.7kg,水溶性氨基树脂1.1kg,磺胺异恶唑0.009kg,两面针挥发油0.04kg,己二异氰酸酯3.6kg,乙醇0.6kg,颜料1.8kg,膨润土0.4kg,二氧化硅0.9kg,硅油0.2kg以及水0.7kg;
其制备方法包括以下步骤:
A、将上述己二异氰酸酯和乙醇放入反应器中混合,进行反应,直至NCO值小于0.5,得到中间产物Ⅰ,备用;
B、将磺胺异恶唑,颜料,膨润土,二氧化硅,水以及A步骤制得的中间产物Ⅰ放入研磨机中,研磨至细度小于10微米,得到中间产物Ⅱ;
C、将B步骤制得的中间产物Ⅱ倒入高速分散机中,加入水溶性饱和聚酯树脂,水溶性氨基树脂,两面针挥发油以及硅油以1000转/分的转速分散2小时,制得。
经测试,本实施例制得的抑菌木器面漆的抑菌率为100%。
Claims (1)
1.一种抑菌木器面漆,其特征在于由以下重量份数的原料制成:
水溶性饱和聚酯树脂 40份~50份;
水溶性氨基树脂 8份~12份;
磺胺异恶唑 0.05份~0.1份;
两面针挥发油 0.1份~1份;
己二异氰酸酯 30份~45份;
乙醇 5份~8份;
颜料 15份~20份;
膨润土 2份~5份;
二氧化硅 8份~10份;
硅油 1份~3份;
水 5份~10份;
其制备方法包括以下步骤:
A、按上述重量份数,将己二异氰酸酯和乙醇放入反应器中混合,进行反应,直至NCO值小于0.5,得到中间产物Ⅰ,备用;
B、将磺胺异恶唑,颜料,膨润土,二氧化硅,水以及A步骤制得的中间产物Ⅰ放入研磨机中,研磨至细度小于10微米,得到中间产物Ⅱ;
C、将B步骤制得的中间产物Ⅱ倒入高速分散机中,加入水溶性饱和聚酯树脂,水溶性氨基树脂,两面针挥发油以及硅油以900转/分钟~1000转/分的转速分散2小时~3小时,制得。