CN104087036B - Shop primer - Google Patents
Shop primer Download PDFInfo
- Publication number
- CN104087036B CN104087036B CN201410363083.0A CN201410363083A CN104087036B CN 104087036 B CN104087036 B CN 104087036B CN 201410363083 A CN201410363083 A CN 201410363083A CN 104087036 B CN104087036 B CN 104087036B
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- shop primer
- weight
- kilograms
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of shop primer, relate to technical field of coatings, it is made up of two components of first, second, wherein, each component of first component and parts by weight are respectively as follows: potassium silicate solution 15 20 parts, Ludox 5 10 parts, polyacrylate emulsion 5 10 parts, organobentonite 5 10 parts, polydimethylsiloxane 0.1 0.5 parts, organic silicon defoamer 0.1 0.5 parts;Each component of second component and parts by weight are respectively as follows: zinc powder 30 55 parts, filler 10 25 parts, pigment 5 20 parts.The present invention is compared to prior art, its Heat stability is good, and adhesive force is strong, and film quality is good, and paint film smooths, and without the bad phenomenon stuck up skin, come off, antiseptic property is good.
Description
Technical field
The present invention relates to technical field of coatings, especially a kind of shop primer.
Background technology
In the building course such as boats and ships and large-scale steel structure; in order to improve build guality and rust cleaning efficiency; after the steel entering factory are carried out surface process; one layer of build priming paint below 25 microns is sprayed as interim protection immediately at steel surface; that causes in order to prevent steel from getting rusty during processing and shipbuilding is corrosion-damaged, and this priming paint is referred to as shop primer or steeis pretreament priming paint.Current shop primer contains resin mostly, this shop primer during carrying out high-temperature soldering or cutting operation, its poor heat resistance, paint film can be made to occur that adhesive force is bad, even stick up the situation of skin, reduce the antiseptic property of priming paint, shorten the antirust time limit.
Summary of the invention
It is an object of the invention to provide a kind of shop primer, this shop primer can solve poor heat resistance and the low problem of rustless property.
In order to solve the problems referred to above, the technical solution used in the present invention is: this shop primer is made up of two components of first, second, wherein, each component of first component and parts by weight are respectively as follows: potassium silicate solution 15-20 part, Ludox 5-10 part, polyacrylate emulsion 5-10 part, organobentonite 5-10 part, polydimethylsiloxane 0.1-0.5 part, organic silicon defoamer 0.1-0.5 part;Each component of second component and parts by weight are respectively as follows: zinc powder 30-55 part, filler 10-25 part, pigment 5-20 part.
In the technical scheme of above-mentioned shop primer, more specifically technical scheme is it may also is that described filler is Kaolin or Pulvis Talci.
Further, described pigment is zinc phosphate or titanium dioxide.
Further, potassium silicate solution 18 parts, Ludox 8 parts, polyacrylate emulsion 8 parts, organobentonite 8 parts, polydimethylsiloxane 0.3 part, organic silicon defoamer 0.2 part;Zinc powder 45 parts, filler 15 parts, pigment 10 parts.
Further, the fineness of zinc powder is 500 mesh.
Owing to have employed technique scheme, the present invention compared with prior art has the advantages that Heat stability is good, and adhesive force is strong, and film quality is good, and paint film smooths, and without the bad phenomenon stuck up skin, come off, antiseptic property is good.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described:
Embodiment 1
The shop primer of the present embodiment is made up of two components of first, second, wherein, each component of first component and parts by weight are respectively as follows: potassium silicate solution 15 kilograms, Ludox 5 kilograms, polyacrylate emulsion 5 kilograms, 5 kilograms of parts of organobentonite, polydimethylsiloxane 0.1 kilogram, organic silicon defoamer 0.1 kilogram;Each component of second component and parts by weight are respectively as follows: zinc powder 30 kilograms, Kaolin 10 kilograms, zinc phosphate 5 kilograms, and the fineness of zinc powder is 500 mesh.
By potassium silicate solution, Ludox and polyacrylate emulsion mix and blend, in whipping process, after addition organobentonite is uniformly dispersed, adds polydimethylsiloxane and organic silicon defoamer stirs, be distributed to fineness 70, after filtration, be packaged into first component;After each component mix homogeneously of second component, separate packaging with first component.During use, first component and second component mix homogeneously are obtained required shop primer, can construct.
Gained shop primer presses GB6747-2008 standard testing, the key technical indexes is: paint film is smooth, film thickness 20 microns, surface drying 3 minutes, do solid work 5 minutes, adhesion 1 grade, get rusty in ocean the weatherability in environment: 6 months 1 grade, solderable, cutting, thermostability (400 DEG C, 24 hours): light discolouration, salt fog resistance (1000 hours): non-foaming, non-corroding.
Embodiment 2
The shop primer of the present embodiment is made up of two components of first, second, wherein, each component of first component and parts by weight are respectively as follows: potassium silicate solution 18 kilograms, Ludox 8 kilograms, polyacrylate emulsion 8 kilograms, 8 kilograms of parts of organobentonite, polydimethylsiloxane 0.3 kilogram, organic silicon defoamer 0.2 kilogram;Each component of second component and parts by weight are respectively as follows: zinc powder 45 kilograms, Kaolin 15 kilograms, zinc phosphate 10 kilograms, and the fineness of zinc powder is 500 mesh.
By potassium silicate solution, Ludox and polyacrylate emulsion mix and blend, in whipping process, after addition organobentonite is uniformly dispersed, adds polydimethylsiloxane and organic silicon defoamer stirs, be distributed to fineness 70, after filtration, be packaged into first component;After each component mix homogeneously of second component, separate packaging with first component.During use, first component and second component mix homogeneously are obtained required shop primer, can construct.
Gained shop primer presses GB6747-2008 standard testing, the key technical indexes is: paint film is smooth, film thickness 20 microns, surface drying 3 minutes, do solid work 4 minutes, adhesion 1 grade, get rusty in ocean the weatherability in environment: 12 months 1 grade, solderable, cutting, thermostability (400 DEG C, 24 hours): light discolouration, salt fog resistance (1000 hours): non-foaming, non-corroding.
Embodiment 3
The shop primer of the present embodiment is made up of two components of first, second, wherein, each component of first component and parts by weight are respectively as follows: potassium silicate solution 20 kilograms, Ludox 10 kilograms, polyacrylate emulsion 10 kilograms, 10 kilograms of parts of organobentonite, polydimethylsiloxane 0.5 kilogram, organic silicon defoamer 0.5 kilogram;Each component of second component and parts by weight are respectively as follows: zinc powder 55 kilograms, Pulvis Talci 25 kilograms, titanium dioxide 20 kilograms, and the fineness of zinc powder is 500 mesh.
By potassium silicate solution, Ludox and polyacrylate emulsion mix and blend, in whipping process, after addition organobentonite is uniformly dispersed, adds polydimethylsiloxane and organic silicon defoamer stirs, be distributed to fineness 70, after filtration, be packaged into first component;After each component mix homogeneously of second component, separate packaging with first component.During use, first component and second component mix homogeneously are obtained required shop primer, can construct.
Gained shop primer presses GB6747-2008 standard testing, the key technical indexes is: paint film is smooth, film thickness 20 microns, surface drying 3 minutes, do solid work 5 minutes, adhesion 1 grade, get rusty in ocean the weatherability in environment: 6 months 1 grade, solderable, cutting, thermostability (400 DEG C, 24 hours): light discolouration, salt fog resistance (1000 hours): non-foaming, non-corroding.
Claims (5)
1. a shop primer, it is characterized in that: be made up of two components of first, the second that weight ratio is 1:1, wherein, each component of first component and parts by weight are respectively as follows: potassium silicate solution 15-20 part, Ludox 5-10 part, polyacrylate emulsion 5-10 part, organobentonite 5-10 part, polydimethylsiloxane 0.1-0.5 part, organic silicon defoamer 0.1-0.5 part;
Each component of second component and parts by weight are respectively as follows: preservative 30-55 part, filler 10-25 part, pigment 5-20 part;Described preservative is zinc powder.
Shop primer the most according to claim 1, it is characterised in that: described filler is Kaolin or Pulvis Talci.
Shop primer the most according to claim 1, it is characterised in that: described pigment is zinc phosphate or titanium dioxide.
4. according to the shop primer described in any one of claims 1 to 3, it is characterised in that: potassium silicate solution 18 parts, Ludox 8 parts, polyacrylate emulsion 8 parts, organobentonite 8 parts, polydimethylsiloxane 0.3 part, organic silicon defoamer 0.2 part;Zinc powder 45 parts, filler 15 parts, pigment 10 parts.
Shop primer the most according to claim 4, it is characterised in that: the fineness of zinc powder is 500 mesh.