CN105368321A - High-performance anticorrosive durable coating and process thereof - Google Patents
High-performance anticorrosive durable coating and process thereof Download PDFInfo
- Publication number
- CN105368321A CN105368321A CN201410435052.1A CN201410435052A CN105368321A CN 105368321 A CN105368321 A CN 105368321A CN 201410435052 A CN201410435052 A CN 201410435052A CN 105368321 A CN105368321 A CN 105368321A
- Authority
- CN
- China
- Prior art keywords
- water
- defoamer
- minutes
- turns
- permanent seal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a process of a high-performance anticorrosive durable coating. The process includes the steps of stirring 250 g of water and 5 g of +PAC at the rotating speed of 800 resolutions for dissolving, adding 5.4 g of dispersing agent to be stirred at the rotating speed of 2000 resolutions for 30 minutes, adding 0.5 g of antifoaming agent, 421 g of calcium triple superphosphate, 50 g of kaolin, 14 g of water, 50 g of titanium dioxide and 951 g of AMP to be stirred at the rotating speed of 800 resolutions for 10-20 minutes, adding 10 g of film forming agent, 5 g of propylene glycol, 1 g of preservative, 1.5 g of antifoaming agent and 120 g of emulsion to be stirred at the rotating speed of 800 resolutions for 30 minutes, and finally adding 69 g of water. According to the high-performance anticorrosive durable coating, the service life can reach 30 years or longer, pollution can be reduced, the environment is improved, energy can be saved, cost is reduced, and economic benefits are improved.
Description
Technical field
The invention belongs to material engineering field, particularly relate to a kind of high-performance anticorrosion permanent seal cooling coating and technique thereof.
Background technology
Coating, is be applied to body surface can be formed and have protection, the class I liquid I of solid-state film of decoration or property (as insulation, anticorrosion, mark etc.) or the general name of solid material, comprises oil (property) paint, water-miscible paint, powder coating.Paint is flowable liquid coating, comprises oil (property) paint and water-miscible paint.Paint take organic solvent as medium or high solid, solvent-free oil-base paint.Water-miscible paint is used water dissolving or the coating with water-dispersion.Coating is as one of the main material of house decoration, and the large percentage accounted in decorations, buys the whether qualified environment directly having influence on overall finishing effect and room of coating, sometimes even can produce harm greatly to the health of human body.
Coating normally based on resin or oil, and adds or does not add face, filler, the thick liquid modulated with organic solvent or water, has also occurred with the coating new variety of solid form existence as powder coating.No matter the form (liquid or solid) of all kinds of coating coating variety, at least should be made up of two or three basal component.Namely main film forming substance is divided into; Film forming subsidiary material matter and auxiliary film forming matter.Coating can be coated on substrate surface and form the liquid or solid macromolecular material of tough and tensile continuous film (paint film).Be once called as paint, paint.Be mainly used to play decoration and provide protection to by painting surface.Some coating also has specific function, as high temperature resistant, cold-resistant, radioprotective etc.Coating is widely used in the aspects such as building, boats and ships, vehicle, metal products.
Summary of the invention
The invention provides a kind of high-performance anticorrosion permanent seal cooling coating and technique thereof, to solve the problems of the prior art.
To achieve these goals, the present invention is by the following technical solutions:
A kind of high-performance anticorrosion permanent seal cooling coating, comprises water 333g ,+PAC5g, dispersion agent 5.4g, defoamer 2g, coarse whiting 421g, kaolin 50g, titanium dioxide 50g, AMP951g, film coalescence aid 10g, propylene glycol 5g, sanitas 1g, emulsion 120g.
Further, described water 333g divides 3 times and adds in batching, be respectively water 250g, water 14g, water 69g.
Further, described defoamer 2g divides 2 times and adds in batching, be respectively defoamer 1.5g, defoamer 0.5g.
Further, described water is deionized water.
Step is water 250g ,+PAC5g, stirs 800 turns, dissolves; Add dispersion agent 5.4g, stir 2000 turns, 30 minutes; Add defoamer 0.5g, coarse whiting, 421g, kaolin 50g, water 14g, titanium dioxide 50g, AMP951g again, stir 800 turns of 10-20 minute; Then add film coalescence aid 10g, propylene glycol 5g, sanitas 1g, defoamer 1.5g, emulsion 120g, stir 800 turns 30 minutes; Finally add water 69g.
Beneficial effect of the present invention: high-performance anticorrosion permanent seal cooling coating provided by the invention, reaching work-ing life can more than 30 year, not only can decreasing pollution, and environmental protect, can also economize on resources, reduce costs, increase economic efficiency.
Embodiment
The technique means realized for making the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with embodiment, setting forth the present invention further.
A kind of high-performance anticorrosion permanent seal cooling coating, comprises water 333g ,+PAC5g, dispersion agent 5.4g, defoamer 2g, coarse whiting 421g, kaolin 50g, titanium dioxide 50g, AMP951g, film coalescence aid 10g, propylene glycol 5g, sanitas 1g, emulsion 120g.
Described water 333g divides 3 times and adds in batching, be respectively water 250g, water 14g, water 69g.
Described defoamer 2g divides 2 times and adds in batching, be respectively defoamer 1.5g, defoamer 0.5g.
Described water is deionized water.
Step is water 250g ,+PAC5g, stirs 800 turns, dissolves; Add dispersion agent 5.4g, stir 2000 turns, 30 minutes; Add defoamer 0.5g, coarse whiting, 421g, kaolin 50g, water 14g, titanium dioxide 50g, AMP951g again, stir 800 turns of 10-20 minute; Then add film coalescence aid 10g, propylene glycol 5g, sanitas 1g, defoamer 1.5g, emulsion 120g, stir 800 turns 30 minutes; Finally add water 69g.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof
.
Claims (5)
1. a high-performance anticorrosion permanent seal cooling coating, is characterized in that: comprise water 333g ,+PAC5g, dispersion agent 5.4g, defoamer 2g, coarse whiting 421g, kaolin 50g, titanium dioxide 50g, AMP951g, film coalescence aid 10g, propylene glycol 5g, sanitas 1g, emulsion 120g.
2. high-performance anticorrosion permanent seal cooling coating according to claim 1, is characterized in that: described water 333g divides 3 times and adds in batching, be respectively water 250g, water 14g, water 69g.
3. high-performance anticorrosion permanent seal cooling coating according to claim 1, is characterized in that: described defoamer 2g divides 2 times and adds in batching, be respectively defoamer 1.5g, defoamer 0.5g.
4. high-performance anticorrosion permanent seal cooling coating according to claim 1, is characterized in that: described water is deionized water.
5. a technique for high-performance anticorrosion permanent seal cooling coating, is characterized in that: step is water 250g ,+PAC5g, stirs 800 turns, dissolves; Add dispersion agent 5.4g, stir 2000 turns, 30 minutes; Add defoamer 0.5g, coarse whiting, 421g, kaolin 50g, water 14g, titanium dioxide 50g, AMP951g again, stir 800 turns of 10-20 minute; Then add film coalescence aid 10g, propylene glycol 5g, sanitas 1g, defoamer 1.5g, emulsion 120g, stir 800 turns 30 minutes; Finally add water 69g.