CN109021741A - Wall emulsion paint and preparation method thereof inside and outside a kind of - Google Patents
Wall emulsion paint and preparation method thereof inside and outside a kind of Download PDFInfo
- Publication number
- CN109021741A CN109021741A CN201810658219.9A CN201810658219A CN109021741A CN 109021741 A CN109021741 A CN 109021741A CN 201810658219 A CN201810658219 A CN 201810658219A CN 109021741 A CN109021741 A CN 109021741A
- Authority
- CN
- China
- Prior art keywords
- parts
- emulsion paint
- outside wall
- agent
- revolving speed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of inside and outside wall emulsion paints, consist of the following compositions: water, dispersing agent, defoaming agent, kaolin, titanium dioxide, coarse whiting, coalescing agent, propylene glycol, preservative, lotion, aluminium polychloride.The invention also discloses a kind of preparation methods of inside and outside wall emulsion paint, the specific steps are that: water pours into beaker, and aluminium polychloride is poured slowly into water, and stirring to aluminium polychloride is dissolved；Dispersing agent is added, defoaming agent improves revolving speed, adds kaolin, titanium dioxide, disperses after coarse whiting；Coalescing agent, propylene glycol, preservative are added after being uniformly dispersed, and reduces revolving speed, disperses, to reach uniformly without particle；It is eventually adding lotion, dispersion is completed again.Emulsion paint of the invention is high-quality, pollution-free, at low cost, the building coating suitable for building inner-outer wall.
Description
Technical field
The present invention relates to technical field of coatings more particularly to a kind of inside and outside wall emulsion paint and preparation method thereof fields.
Background technique
According to the classification for the chemical products that the modern times pass through, coating belongs to fine chemical product.Modern coating is gradually
It is an important industry in chemical industry as a kind of multi-functional engineering material.
Emulsion paint is a kind of using very extensive building coating, there is faster development in recent years.Current inner-outer wall
Emulsion paint is second-rate, containing a large amount of toxic, harmful organic solvents, damages to people, serious to will cause life-long disease
And cause environmental pollution.
Summary of the invention
The first technical problem to be solved by the present invention is, provides a kind of high-quality, pollution-free, at low cost inner-outer wall
Emulsion paint.
The second technical problem to be solved by the present invention is the provision of a kind of preparation method of inside and outside wall emulsion paint.
The present invention is to solve one of above-mentioned technical problem by the following technical programs: a kind of inside and outside wall emulsion paint, by with
It is lower at being grouped as: it is water, dispersing agent, defoaming agent, kaolin, titanium dioxide, coarse whiting, coalescing agent, propylene glycol, preservative, lotion, poly-
Close aluminium chloride；Each component parts by weight are as follows: 80-100 parts of water, 0.5-1.5 parts of dispersing agent, 0.5-1.5 parts of defoaming agent, kaolin
15-25 parts, 15-25 parts of titanium dioxide, 150-200 parts of coarse whiting, 5-10 parts of coalescing agent, 2-5 parts of propylene glycol, preservative 0.5-1.5
Part, 40-60 parts of lotion, 10-20 parts of aluminium polychloride；Dispersing agent is tripolyphosphate, and defoaming agent is dimethyl silicone polymer class,
Preservative is sodium benzoate, and coalescing agent is propandiol butyl ether.
As one of preferred embodiment of the invention, lotion selects acrylic emulsion.
As one of preferred embodiment of the invention, a kind of inside and outside wall emulsion paint, the preparation method is as follows:
The following steps are included:
Step 1: component weighs preparation good material by weight；
Step 2, water pour into beaker, and aluminium polychloride is poured slowly into water, and stirring to aluminium polychloride is dissolved；
Dispersing agent is added in step 3, and defoaming agent improves revolving speed, adds kaolin, titanium dioxide, after coarse whiting
Dispersion；
Step 4 is added coalescing agent, propylene glycol, preservative, and reduces revolving speed after being uniformly dispersed, dispersion,
Reach uniformly without particle；
Lotion is added in step 5, disperses to complete for 25-35 minutes again.
As one of preferred embodiment of the invention, mixing speed is 200-600 revs/min in step 2, mixing time 10-
20 minutes.
As one of preferred embodiment of the invention, revolving speed is 1800-2000 revs/min in step 3, jitter time 25-35
Minute.
As one of preferred embodiment of the invention, revolving speed is 700-900 revs/min in step 4, and jitter time is 10-20 points
Clock.
The present invention is to solve the two of above-mentioned technical problem by the following technical programs: a kind of preparation of inside and outside wall emulsion paint
Method, comprising the following steps:
Step 1: component weighs preparation good material by weight；
Step 2, water pour into beaker, and aluminium polychloride is poured slowly into water, and stirring to aluminium polychloride is dissolved；
Dispersing agent is added in step 3, and defoaming agent improves revolving speed, adds kaolin, titanium dioxide, coarse whiting,
Disperse after water；
Step 4 is added coalescing agent, propylene glycol, preservative, defoaming agent, and reduces revolving speed after being uniformly dispersed,
Dispersion, will reach uniformly without particle；
Lotion is added in step 5, disperses to complete for 25-35 minutes again.
As one of preferred embodiment of the invention, mixing speed is 200-600 revs/min in step 2, mixing time 10-
20 minutes.
As one of preferred embodiment of the invention, revolving speed is 1800-2000 revs/min in step 3, jitter time 25-35
Minute.
As one of preferred embodiment of the invention, revolving speed is 700-900 revs/min in step 4, and jitter time is 10-20 points
Clock.
The present invention compared with prior art the advantages of be: emulsion paint of the invention is high-quality, pollution-free, at low cost, be applicable in
In the building coating of building inner-outer wall.
Specific embodiment
It elaborates below to the embodiment of the present invention, the present embodiment carries out under the premise of the technical scheme of the present invention
Implement, the detailed implementation method and specific operation process are given, but protection scope of the present invention is not limited to following implementation
Example.
Embodiment 1
1,80 parts of water, 0.5 part of dispersing agent, 0.5 part of defoaming agent, 15 parts of kaolin, 15 parts of titanium dioxide, 150 parts of coarse whiting, film forming
5 parts of auxiliary agent, 2 parts of propylene glycol, 0.5 part of preservative, 40 parts of lotion, 10 parts of aluminium polychloride.
2, water pours into beaker, and aluminium polychloride is poured slowly into water, and stirring to aluminium polychloride is dissolved, and mixing speed is
200 revs/min, mixing time is 10 minutes.
3, dispersing agent is added, defoaming agent improves revolving speed to 1800 revs/min, adds kaolin, titanium dioxide, after coarse whiting point
It dissipates 25 minutes.
4, coalescing agent, propylene glycol, preservative are added after being uniformly dispersed, and reduces revolving speed to 700 revs/min, disperses 10 points
Clock will reach uniformly without particle.
5, lotion is added, disperses to complete for 25 minutes again.
Embodiment 2
1,90 parts of water, 1 part of dispersing agent, 1 part of defoaming agent, 20 parts of kaolin, 20 parts of titanium dioxide, 175 parts of coarse whiting, coalescing agent
8 parts, 3.5 parts of propylene glycol, 1 part of preservative, 50 parts of lotion, 15 parts of aluminium polychloride.
2, water pours into beaker, and aluminium polychloride is poured slowly into water, and stirring to aluminium polychloride is dissolved, and mixing speed is
400 revs/min, mixing time is 15 minutes.
3, dispersing agent is added, defoaming agent improves revolving speed to 1900 revs/min, adds kaolin, titanium dioxide, after coarse whiting point
It dissipates 30 minutes.
4, coalescing agent, propylene glycol, preservative are added after being uniformly dispersed, and reduces revolving speed to 800 revs/min, disperses 15 points
Clock will reach uniformly without particle.
5, lotion is added, disperses to complete for 30 minutes again.
Embodiment 3
1,100 parts of water, 1.5 parts of dispersing agent, 1.5 parts of defoaming agent, 25 parts of kaolin, 25 parts of titanium dioxide, 200 parts of coarse whiting, at
10 parts of film auxiliary agent, 5 parts of propylene glycol, 1.5 parts of preservative, 60 parts of lotion, 20 parts of aluminium polychloride.
2, water pours into beaker, and aluminium polychloride is poured slowly into water, and stirring to aluminium polychloride is dissolved, and mixing speed is
600 revs/min, mixing time is 20 minutes.
3, dispersing agent is added, defoaming agent improves revolving speed to 2000 revs/min, adds kaolin, titanium dioxide, after coarse whiting point
It dissipates 35 minutes.
4, coalescing agent, propylene glycol, preservative are added after being uniformly dispersed, and reduces revolving speed to 900 revs/min, disperses 20 points
Clock will reach uniformly without particle.
5, lotion is added, disperses to complete for 35 minutes again.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Made any modifications, equivalent replacements, and improvements etc., should all be included in the protection scope of the present invention within mind and principle.
Claims (10)
1. a kind of inside and outside wall emulsion paint, which is characterized in that consist of the following compositions: water, dispersing agent, defoaming agent, kaolin, titanium white
Powder, coarse whiting, coalescing agent, propylene glycol, preservative, lotion, aluminium polychloride；Each component parts by weight are as follows: 80-100 parts of water divides
0.5-1.5 parts of powder, 0.5-1.5 parts of defoaming agent, 15-25 parts of kaolin, 15-25 parts of titanium dioxide, 150-200 parts of coarse whiting, film forming
5-10 parts of auxiliary agent, 2-5 parts of propylene glycol, 0.5-1.5 parts of preservative, 40-60 parts of lotion, 10-20 parts of aluminium polychloride；Dispersing agent is
Tripolyphosphate, defoaming agent are dimethyl silicone polymer class, and preservative is sodium benzoate, and coalescing agent is propandiol butyl ether.
2. a kind of inside and outside wall emulsion paint according to claim 1, which is characterized in that lotion selects acrylic emulsion.
3. a kind of inside and outside wall emulsion paint according to claim 1, which is characterized in that the preparation method is as follows: including following step
It is rapid:
Step 1: component weighs preparation good material by weight；
Step 2, water pour into beaker, and aluminium polychloride is poured slowly into water, and stirring to aluminium polychloride is dissolved；
Dispersing agent is added in step 3, and defoaming agent improves revolving speed, adds kaolin, titanium dioxide, disperses after coarse whiting；
Step 4 is added coalescing agent, propylene glycol, preservative, and reduces revolving speed after being uniformly dispersed, dispersion,
Reach uniformly without particle；
Lotion is added in step 5, disperses to complete for 25-35 minutes again.
4. a kind of inside and outside wall emulsion paint according to claim 3, mixing speed is 200-600 revs/min in step 2, stirring
Time is 10-20 minutes.
5. a kind of inside and outside wall emulsion paint according to claim 3, revolving speed is 1800-2000 revs/min in step 3, when dispersion
Between be 25-35 minutes.
6. a kind of inside and outside wall emulsion paint according to claim 3, revolving speed is 700-900 revs/min in step 4, jitter time
It is 10-20 minutes.
7. a kind of preparation method of inside and outside wall emulsion paint as described in claim 1, which comprises the following steps:
Step 1: component weighs preparation good material by weight；
Step 2, water pour into beaker, and aluminium polychloride is poured slowly into water, and stirring to aluminium polychloride is dissolved；
Dispersing agent is added in step 3, and defoaming agent improves revolving speed, adds kaolin, titanium dioxide, coarse whiting,
Disperse after water；
Step 4 is added coalescing agent, propylene glycol, preservative, defoaming agent, and reduces revolving speed after being uniformly dispersed,
Dispersion, will reach uniformly without particle；
Lotion is added in step 5, disperses to complete for 25-35 minutes again.
8. a kind of inside and outside wall emulsion paint according to claim 7, mixing speed is 200-600 revs/min in step 2, stirring
Time is 10-20 minutes.
9. a kind of inside and outside wall emulsion paint according to claim 7, revolving speed is 1800-2000 revs/min in step 3, when dispersion
Between be 25-35 minutes.
10. a kind of inside and outside wall emulsion paint according to claim 7, revolving speed is 700-900 revs/min in step 4, jitter time
It is 10-20 minutes.