CN109054522A - A kind of environment-friendly exterior wall emulsion paint and preparation method thereof - Google Patents

A kind of environment-friendly exterior wall emulsion paint and preparation method thereof Download PDF

Info

Publication number
CN109054522A
CN109054522A CN201810658104.XA CN201810658104A CN109054522A CN 109054522 A CN109054522 A CN 109054522A CN 201810658104 A CN201810658104 A CN 201810658104A CN 109054522 A CN109054522 A CN 109054522A
Authority
CN
China
Prior art keywords
parts
agent
thickener
diluent
added
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201810658104.XA
Other languages
Chinese (zh)
Inventor
魏明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHUZHOU MAISITE NEW BUILDING MATERIAL Co Ltd
Original Assignee
CHUZHOU MAISITE NEW BUILDING MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHUZHOU MAISITE NEW BUILDING MATERIAL Co Ltd filed Critical CHUZHOU MAISITE NEW BUILDING MATERIAL Co Ltd
Priority to CN201810658104.XA priority Critical patent/CN109054522A/en
Publication of CN109054522A publication Critical patent/CN109054522A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses a kind of environment-friendly exterior wall emulsion paints, consist of the following compositions: water, diluent, propylene glycol, dispersing agent, wetting agent, thickener, defoaming agent, titanium dioxide, kaolin, wollastonite, alumina silicate, talcum powder, preservative, styrene-acrylic emulsion, levelling agent, thixotropic agent；The invention also discloses a kind of preparation methods of environment-friendly exterior wall emulsion paint, part thickener, diluent, propylene glycol, dispersing agent, wetting agent, defoaming agent, titanium dioxide, kaolin, wollastonite, alumina silicate, talcum powder, preservative, levelling agent, thixotropic agent are added to the water, stirred evenly；Propylene glycol, titanium dioxide, kaolin, wollastonite, alumina silicate, talcum powder is added, stirs evenly；Lotion is added, is stirred evenly；It is eventually adding the thickener of surplus, stirring, grinding.Environment-friendly exterior wall emulsion paint of the invention have good weatherability, adhesive force are strong, mould proof, antibacterial, abrasion resistance is strong, persistently washing it is multiple it is new, durability is excellent, quick construction when using, conveniently.

Description

A kind of environment-friendly exterior wall emulsion paint and preparation method thereof
Technical field
The present invention relates to technical field of coatings more particularly to a kind of environment-friendly exterior wall emulsion paint and preparation method thereof fields.
Background technique
According to the classification for the chemical products that the modern times pass through, coating belongs to fine chemical product.Modern coating is gradually It is an important industry in chemical industry as a kind of multi-functional engineering material.
Exterior coating is to build outside wall for brushing, so a most important index is exactly that uvioresistant is shone Penetrate, it is desirable that reach for a long time irradiate it is non-discolouring.As the improvement of people's living standards, the exterior coating of environmental protection is increasingly by people Pay close attention to, but existing most of exterior coating heavy contaminations have harm to human body.
Summary of the invention
The first technical problem to be solved by the present invention is, provides a kind of environment-friendly exterior wall emulsion paint.
The second technical problem to be solved by the present invention is the provision of a kind of preparation method of environment-friendly exterior wall emulsion paint, Improve exterior wall latex paint weatherability, adhesive force, mould proof, antibacterial, abrasion resistance.
The present invention is to solve a kind of one of above-mentioned technical problem: environment-friendly exterior wall emulsion paint by the following technical programs, It consists of the following compositions: water, diluent, propylene glycol, dispersing agent, wetting agent, thickener, defoaming agent, titanium dioxide, kaolin, silicon Lime stone, alumina silicate, talcum powder, preservative, styrene-acrylic emulsion, levelling agent, thixotropic agent；Each component parts by weight are as follows: 60-80 parts of water, 1-2 parts of diluent, 20-30 parts of propylene glycol, 0.5-1.5 parts of dispersing agent, 1-2 parts of wetting agent, 0.5-1.5 parts of thickener, defoaming agent 0.5-1.5 parts, 10-20 parts of titanium dioxide, 10-20 parts of kaolin, 5-15 parts of wollastonite, 5-15 parts of alumina silicate, talcum powder 10-20 Part, 1-2 parts of preservative, 30-40 parts of styrene-acrylic emulsion, 0.5-1.5 parts of levelling agent, 0.5-1.5 parts of thixotropic agent；Diluent is acrylic acid Lacquer diluent, thickener are hydroxyethyl cellulose, and wetting agent is propylene glycol, and dispersing agent is tripolyphosphate, and defoaming agent is poly- two Methylsiloxane class, preservative are sodium benzoate, and levelling agent is acrylic acid, and thixotropic agent is asbestos.
As one of preferred embodiment of the invention, each component parts by weight are as follows: 60 parts of water, 1 part of diluent, propylene glycol 20 Part, 0.5 part of dispersing agent, 1 part of wetting agent, 0.5 part of thickener, 0.5 part of defoaming agent, 10 parts of titanium dioxide, 10 parts of kaolin, wollastonite 5 parts, 5 parts of alumina silicate, 10 parts of talcum powder, 1 part of preservative, 30 parts of styrene-acrylic emulsion, 0.5 part of levelling agent, 0.5 part of thixotropic agent.
As one of preferred embodiment of the invention, each component parts by weight are as follows: 70 parts of water, 1.5 parts of diluent, propylene glycol 25 Part, 1 part of dispersing agent, 1.5 parts of wetting agent, 1 part of thickener, 1 part of defoaming agent, 15 parts of titanium dioxide, 15 parts of kaolin, wollastonite 10 Part, 10 parts of alumina silicate, 15 parts of talcum powder, 1.5 parts of preservative, 35 parts of styrene-acrylic emulsion, 1 part of levelling agent, 1 part of thixotropic agent.
As one of preferred embodiment of the invention, each component parts by weight are as follows: 80 parts of water, 2 parts of diluent, propylene glycol 30 Part, 1.5 parts of dispersing agent, 2 parts of wetting agent, 1.5 parts of thickener, 1.5 parts of defoaming agent, 20 parts of titanium dioxide, 20 parts of kaolin, wollastonite 15 parts, 15 parts of alumina silicate, 20 parts of talcum powder, 2 parts of preservative, 40 parts of styrene-acrylic emulsion, 1.5 parts of levelling agent, 1.5 parts of thixotropic agent.
As one of preferred embodiment of the invention, the preparation method is as follows:
The following steps are included:
Step 1: material preparation phase, by weight component weigh preparation good material；
Step 2: by part thickener, diluent, propylene glycol, dispersing agent, wetting agent, defoaming agent, titanium dioxide, kaolin, Wollastonite, alumina silicate, talcum powder, preservative, levelling agent, thixotropic agent are added to the water, and mixing stirs evenly；
Step 3: propylene glycol, titanium dioxide, kaolin, wollastonite, alumina silicate, cunning being added into the mixture that step 2 obtains Mountain flour stirs evenly；
Step 4: styrene-acrylic emulsion is added into the mixture that step 3 obtains, stirs evenly；
Step 5: the thickener of surplus being added into the mixture that step 4 obtains, stirring, grinding obtain the latex Paint.
The present invention is a kind of the two of solution above-mentioned technical problem by the following technical programs: environment-friendly exterior wall emulsion paint Preparation method, comprising the following steps:
Step 1: material preparation phase, by weight component weigh preparation good material；
Step 2: by part thickener, diluent, propylene glycol, dispersing agent, wetting agent, defoaming agent, titanium dioxide, kaolin, Wollastonite, alumina silicate, talcum powder, preservative, levelling agent, thixotropic agent are added to the water, and mixing stirs evenly；
Step 3: propylene glycol, titanium dioxide, kaolin, wollastonite, alumina silicate, cunning being added into the mixture that step 2 obtains Mountain flour stirs evenly；
Step 4: styrene-acrylic emulsion is added into the mixture that step 3 obtains, stirs evenly；
Step 5: the thickener of surplus being added into the mixture that step 4 obtains, stirring, grinding obtain the latex Paint.
The present invention compared with prior art the advantages of be: the invention provide environment-friendly exterior wall emulsion paint have weatherability It is good, adhesive force is strong, mould proof, antibacterial, abrasion resistance is strong, persistently washing it is multiple it is new, durability is excellent, quick construction when using, facilitates Characteristic is a kind of environment-friendly exterior wall emulsion paint decorated and protected for concrete or cement mortar outer surface of wall.
Specific embodiment
It elaborates below to the embodiment of the present invention, the present embodiment carries out under the premise of the technical scheme of the present invention Implement, the detailed implementation method and specific operation process are given, but protection scope of the present invention is not limited to following implementation Example.
Embodiment 1
1, material preparation phase, by weight component weigh preparation good material；60 parts of water, 1 part of diluent, 20 parts of propylene glycol, 0.5 part of dispersing agent, 1 part of wetting agent, 0.5 part of thickener, 0.5 part of defoaming agent, 10 parts of titanium dioxide, 10 parts of kaolin, wollastonite 5 Part, 5 parts of alumina silicate, 10 parts of talcum powder, 1 part of preservative, 30 parts of styrene-acrylic emulsion, 0.5 part of levelling agent, 0.5 part of thixotropic agent；
2, by part thickener, diluent, propylene glycol, dispersing agent, wetting agent, defoaming agent, titanium dioxide, kaolin, silicon ash Stone, alumina silicate, talcum powder, preservative, levelling agent, thixotropic agent are added to the water, and mixing stirs evenly；
3, propylene glycol, titanium dioxide, kaolin, wollastonite, alumina silicate, talcum powder are added into the mixture that step 2 obtains, It stirs evenly；
4, styrene-acrylic emulsion is added into the mixture that step 3 obtains, stirs evenly；
5, the thickener of surplus is added into the mixture that step 4 obtains, stirring, grinding obtain the emulsion paint.
Embodiment 2
1, material preparation phase, by weight component weigh preparation good material；70 parts of water, 1.5 parts of diluent, propylene glycol 25 Part, 1 part of dispersing agent, 1.5 parts of wetting agent, 1 part of thickener, 1 part of defoaming agent, 15 parts of titanium dioxide, 15 parts of kaolin, wollastonite 10 Part, 10 parts of alumina silicate, 15 parts of talcum powder, 1.5 parts of preservative, 35 parts of styrene-acrylic emulsion, 1 part of levelling agent, 1 part of thixotropic agent.
2, by part thickener, diluent, propylene glycol, dispersing agent, wetting agent, defoaming agent, titanium dioxide, kaolin, silicon ash Stone, alumina silicate, talcum powder, preservative, levelling agent, thixotropic agent are added to the water, and mixing stirs evenly；
3, propylene glycol, titanium dioxide, kaolin, wollastonite, alumina silicate, talcum powder are added into the mixture that step 2 obtains, It stirs evenly；
4, styrene-acrylic emulsion is added into the mixture that step 3 obtains, stirs evenly；
5, the thickener of surplus is added into the mixture that step 4 obtains, stirring, grinding obtain the emulsion paint.
Embodiment 3
1, material preparation phase, by weight component weigh preparation good material；80 parts of water, 2 parts of diluent, 30 parts of propylene glycol, 1.5 parts of dispersing agent, 2 parts of wetting agent, 1.5 parts of thickener, 1.5 parts of defoaming agent, 20 parts of titanium dioxide, 20 parts of kaolin, wollastonite 15 Part, 15 parts of alumina silicate, 20 parts of talcum powder, 2 parts of preservative, 40 parts of styrene-acrylic emulsion, 1.5 parts of levelling agent, 1.5 parts of thixotropic agent.
2, by part thickener, diluent, propylene glycol, dispersing agent, wetting agent, defoaming agent, titanium dioxide, kaolin, silicon ash Stone, alumina silicate, talcum powder, preservative, levelling agent, thixotropic agent are added to the water, and mixing stirs evenly；
3, propylene glycol, titanium dioxide, kaolin, wollastonite, alumina silicate, talcum powder are added into the mixture that step 2 obtains, It stirs evenly；
4, styrene-acrylic emulsion is added into the mixture that step 3 obtains, stirs evenly；
5, the thickener of surplus is added into the mixture that step 4 obtains, stirring, grinding obtain the emulsion paint.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention Made any modifications, equivalent replacements, and improvements etc., should all be included in the protection scope of the present invention within mind and principle.

Claims (6)

1. a kind of environment-friendly exterior wall emulsion paint, which is characterized in that consist of the following compositions: water, diluent, propylene glycol, dispersing agent, Wetting agent, thickener, defoaming agent, titanium dioxide, kaolin, wollastonite, alumina silicate, talcum powder, preservative, styrene-acrylic emulsion, levelling Agent, thixotropic agent；Each component parts by weight are as follows: 60-80 parts of water, 1-2 parts of diluent, 20-30 parts of propylene glycol, dispersing agent 0.5-1.5 Part, 1-2 parts of wetting agent, 0.5-1.5 parts of thickener, 0.5-1.5 parts of defoaming agent, 10-20 parts of titanium dioxide, 10-20 parts of kaolin, silicon 5-15 parts of lime stone, 5-15 parts of alumina silicate, 10-20 parts of talcum powder, 1-2 parts of preservative, 30-40 parts of styrene-acrylic emulsion, levelling agent 0.5- 1.5 parts, 0.5-1.5 parts of thixotropic agent；Diluent is acrylic paint diluent, and thickener is hydroxyethyl cellulose, wetting agent third Glycol, dispersing agent are tripolyphosphate, and defoaming agent is dimethyl silicone polymer class, and preservative is sodium benzoate, levelling agent third Olefin(e) acid, thixotropic agent are asbestos.
2. a kind of environment-friendly exterior wall emulsion paint according to claim 1, which is characterized in that each component parts by weight are as follows: water 60 parts, 1 part of diluent, 20 parts of propylene glycol, 0.5 part of dispersing agent, 1 part of wetting agent, 0.5 part of thickener, 0.5 part of defoaming agent, titanium white 10 parts of powder, 10 parts of kaolin, 5 parts of wollastonite, 5 parts of alumina silicate, 10 parts of talcum powder, 1 part of preservative, 30 parts of styrene-acrylic emulsion, levelling 0.5 part of agent, 0.5 part of thixotropic agent.
3. a kind of environment-friendly exterior wall emulsion paint according to claim 1, which is characterized in that each component parts by weight are as follows: water 70 parts, 1.5 parts of diluent, 25 parts of propylene glycol, 1 part of dispersing agent, 1.5 parts of wetting agent, 1 part of thickener, 1 part of defoaming agent, titanium dioxide 15 parts, 15 parts of kaolin, 10 parts of wollastonite, 10 parts of alumina silicate, 15 parts of talcum powder, 1.5 parts of preservative, 35 parts of styrene-acrylic emulsion, stream 1 part of flat agent, 1 part of thixotropic agent.
4. a kind of environment-friendly exterior wall emulsion paint according to claim 1, which is characterized in that each component parts by weight are as follows: water 80 parts, 2 parts of diluent, 30 parts of propylene glycol, 1.5 parts of dispersing agent, 2 parts of wetting agent, 1.5 parts of thickener, 1.5 parts of defoaming agent, titanium white 20 parts of powder, 20 parts of kaolin, 15 parts of wollastonite, 15 parts of alumina silicate, 20 parts of talcum powder, 2 parts of preservative, 40 parts of styrene-acrylic emulsion, stream 1.5 parts of flat agent, 1.5 parts of thixotropic agent.
5. a kind of environment-friendly exterior wall emulsion paint according to claim 1, which is characterized in that the preparation method is as follows:
The following steps are included:
Step 1: material preparation phase, by weight component weigh preparation good material；
Step 2: part thickener, diluent, dispersing agent, wetting agent, defoaming agent, preservative, levelling agent, thixotropic agent are added to In water, mixing is stirred evenly；
Step 3: propylene glycol, titanium dioxide, kaolin, wollastonite, alumina silicate, talcum powder are added into the mixture that step 2 obtains, It stirs evenly；
Step 4: styrene-acrylic emulsion is added into the mixture that step 3 obtains, stirs evenly；
Step 5: the thickener of surplus being added into the mixture that step 4 obtains, stirring, grinding obtain the emulsion paint.
6. a kind of preparation method of environment-friendly exterior wall emulsion paint as described in claim 1, which is characterized in that including following step It is rapid:
Step 1: material preparation phase, by weight component weigh preparation good material；
Step 2: part thickener, diluent, dispersing agent, wetting agent, defoaming agent, preservative, levelling agent, thixotropic agent are added to In water, mixing is stirred evenly；
Step 3: propylene glycol, titanium dioxide, kaolin, wollastonite, alumina silicate, talcum powder are added into the mixture that step 2 obtains, It stirs evenly；
Step 4: styrene-acrylic emulsion is added into the mixture that step 3 obtains, stirs evenly；
Step 5: the thickener of surplus being added into the mixture that step 4 obtains, stirring, grinding obtain the emulsion paint.
CN201810658104.XA 2018-06-25 2018-06-25 A kind of environment-friendly exterior wall emulsion paint and preparation method thereof Withdrawn CN109054522A (en)