CN104082067A - 一种钢塑复合玻璃钢圃架及制作方法 - Google Patents
一种钢塑复合玻璃钢圃架及制作方法 Download PDFInfo
- Publication number
- CN104082067A CN104082067A CN201410331634.5A CN201410331634A CN104082067A CN 104082067 A CN104082067 A CN 104082067A CN 201410331634 A CN201410331634 A CN 201410331634A CN 104082067 A CN104082067 A CN 104082067A
- Authority
- CN
- China
- Prior art keywords
- fiber reinforced
- glass fiber
- frame
- steel
- garden
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种钢塑复合玻璃钢圃架及制作方法，属于钢塑复合，即金属型材与玻璃钢复合材料，其制作方法其特征在于成分按重量比是金属型材20-60％，玻璃纤维10-28％，不饱和聚酯树脂15-25％，抗老化剂0.1-0.5％，阻燃剂18-50％，内脱模剂硬酯酸锌1-5％。首先预处理配料按上述比例搅拌混配，然后在30-40℃的加温室中熟化24-48小时，再装填模具型腔与金属型材模压成型，其成型温度是130-140℃，模压压力是65-75kg/cm2，成型时间是2-10分钟。所说的抗老化剂是UV-531，阻燃剂是AL(OH)3，脱模剂是硬酯酸锌经过2次加工研磨粒度小于45微米(纳米级)的粉末。这种复合材料特别适用于蔬菜花卉栽培大棚、家庭院落、室内阳台、花卉商店、苗木蔬菜展会的便捷组装的栽培蔬菜花卉圃棚架，其使用寿命可提高10倍以上。
Description
技术领域 本发明涉及一种钢塑复合玻璃钢圃架及制作方法，属于钢塑复合材料及其制备方法，这种复合材料特别适用于制作蔬菜花卉栽培大棚、家庭院落、室内阳台、花卉商店、苗木蔬菜展会的便捷组装的栽培蔬菜花卉圃棚架。
背景技术 传统的栽培蔬菜花卉圃棚架多是钢或竹木单一结构，这种结构多是焊接或捆扎方法实施，虽然有简易的优点，但是容易锈蚀和老化，寿命短一槽烂，不便于活动更换和安装，更不便于工厂化生产蔬菜花卉。所以市场急需一种钢塑耐老化复合材料标准件栽培架，目的是把钢塑玻璃钢栽培架做成标准件便于安装，型钢外包裹玻璃钢防止锈蚀和老化。
发明内容 本发明的目的在于提供一种钢塑耐老化玻璃钢圃架及制作方法，把钢塑玻璃钢栽培架做成标准件便于安装，型钢外包裹玻璃钢防止锈蚀和老化。
本发明是这样实现的：一种钢塑复合玻璃钢圃架及制作方法，其特征在于所述一种钢塑复合玻璃钢圃架是由中空管纵向架、横向架、可调倾斜角框、腔体插件、圃盘、盆盘托板组成，纵向架、横向架设有变换组装的圃盘、盆盘托板，横向架上部设有营养液罐、液调控器、营养液滴管、转动滴液杆，纵向架中部设有转动轴槽、固定环，可调倾斜角框设有调节环勾，圃盘设有14、圃盘送液管、勾盘沿、盘格栅、槽盘沿，盆盘托板边缘设有防护板架栏，腔体插件拼接中空管纵向架、横向架，可调倾斜角框上端头部与转动轴槽连接，调节环勾与固定环连接，圃盘、盆盘托板与纵向架、横向架连接固定。
一种钢塑复合玻璃钢圃架及制作方法，其特征在于所述一种钢塑复合玻璃钢圃架制作方法是，法复合玻璃钢是由薄壁中空异型金属型材，玻璃纤维，不饱和聚酯树脂，经过2次细化处理的抗老化剂、阻燃剂、内脱模剂填充料，经预处理配料、填充、在预热模具内模压成型。
所述的一种钢塑复合玻璃钢圃架制作方法，其特征在于成分按重量比是金属型材20-60％，玻璃纤维10-28％，不饱和聚酯树脂15-25％，抗老化剂UV-531是0.1-0.5％，阻燃剂AL(OH)3是18-50％，内脱模剂硬酯酸锌1-5％。
述的一种钢塑复合玻璃钢圃架制作方法，其特征在于首先预处理配料是将树脂、抗老化剂、阻燃剂按上述比例搅拌混配，然后在30-40℃的加温室中熟化24-48小时，树脂配料均匀渗透玻璃纤维或玻璃布再装填模具型腔与金属型材模压成型，其成型温度是130-140℃，模压压力是65-75kg/cm2，成型时间是2-10分钟。
所述的一种钢塑复合玻璃钢圃架制作方法，其特征在于所说的抗老化剂UV-531、阻燃剂是AL(OH)3，脱模剂硬酯酸锌经过2次加工研磨粒度是纳米级的粉末。
本发明达到了预期的设计目的与原有技术相比，本发明具有显著的技术进步，由于设置薄壁中空金属型材增加了强度提高了寿命，添加了抗老化剂阻燃剂提高了抗的性能和使用寿命，中空型材压制成各种标准连接件，腔体插件，便于中空管纵向架、横向架快捷组装。更便于拆装，提高了工作效率。本发明实用美观，设有大小不同规格，安装便捷，可根据空间大小选择不同规格，能保障种植效果。
附图说明 结合附图进一步描述：
图1是一种钢塑复合玻璃钢圃架薄壁金属圆管框架整体结构图
图2是一种钢塑复合玻璃钢圃架中的盆盘托板结构图
图3是一种钢塑复合玻璃钢圃架中的设有圃盘送液管的圃盘结构图
图中：1、纵向框 2、横向框 3、可调倾斜角框 4、调节环勾 5、固定环 6、转动轴槽 8、圃盘 9、营养液罐 10、液调控器11、腔体插件 12、营养液滴管 13、转动滴液秆 14、圃盘送液管15、勾盘沿 16、盘格栅 17、槽盘沿 18、盆盘托板 19、托板防护架栏
具体实施方式 根据本发明的设计方案，发明人给出3个实施例。
实施例1
根据本发明的设计方案，发明人试制了一种钢塑复合玻璃钢圃架薄壁金属圆管框架，见附图1，钢塑复合玻璃钢圃架薄壁金属圆管框架的金属型材采用薄壁金属圆管，按重量比计算，金属型材50％，玻璃纤维10％，不饱和聚脂树脂15％，抗老化剂UV-531是0.1％，阻燃剂AL(OH)3是24％，内脱模剂硬酯酸锌其余。首先预处理配料是将树脂、抗老化剂UV-531、阻燃剂AL(OH)3、内脱模剂是硬酯酸锌，按上述比例搅拌混配，然后在40℃的控温室中熟化30小时，树脂配料均匀渗透玻璃纤维，再装填模具型腔与中间的金属型材复合模压成型，其模压温度是140℃，模压压力是65kg/cm2，成型时间是5分钟。所说的抗老化剂是UV-531，阻燃剂是AL(OH)3，脱模剂是硬酯酸锌经经过2次加工研磨粒度小于45微米相当于纳米级的粉末。经试用，效果良好，与原有技术相比，本发明具有显著的技术进步，由于设置薄壁中空金属型材增加了强度，添加了抗老化剂、阻燃剂提高了抗老化的性能和使用寿命，据估算可使用50-60年，提高了寿命10倍，中空型材压制成各种标准连接件，腔体插件，便于中空管纵向架、横向架快捷组装。更便于拆装，提高了工作效率。
实施例2
根据本发明的设计方案，发明人试制了一种钢塑复合玻璃钢圃架中的盆盘托板，见附图2。钢塑复合玻璃钢圃架中的盆盘托板的金属型材采用预制的带有波棱的低碳钢薄板，按重量比计算，金属型材25％，玻璃纤维25％，不饱和聚脂树脂18％，抗老化剂UV-531是0.11％，阻燃剂AL(OH)3是36％，内脱模剂硬酯酸锌其余。首先预处理配料是将树脂、抗老化剂UV-531、阻燃剂AL(OH)3、内脱模剂是硬酯酸锌，按上述比例搅拌混配，然后在38℃的控温室中熟化38小时，树脂配料均匀渗透玻璃纤维，再装填模具型腔与中间的金属型材复合模压成型，其模压温度是135℃，模压压力是70kg/cm2，成型时间是6分钟。所说的抗老化剂是UV-531，阻燃剂是AL(OH)3，脱模剂是硬酯酸锌经经过2次加工研磨粒度小于45微米相当于纳米级的粉末。经试用效果良好，比单一的玻璃布玻璃钢板更具有重量轻，强度大，耐腐蚀，寿命长，具有更强的抗弯曲度等特点。
实施例3、
根据本发明的设计方案，发明人试制了一种钢塑复合玻璃钢圃架中的设有圃盘送液管的圃盘见附图3。圃盘其中送液管是采用与送液配套的钢管，既有输送营养液的功能，也发挥容器骨架增加强度的优势，其材料按重量比计算，金属管型材20％，玻璃纤维20％，不饱和聚脂树脂25％，抗老化剂UV-531是0.5％，阻燃剂AL(OH)3是34％，内脱模剂硬酯酸锌其余。首先预处理配料是将树脂、抗老化剂UV-531、阻燃剂AL(OH)3、内脱模剂是硬酯酸锌，按上述比例搅拌混配，然后在35℃的控温室中熟化48小时，树脂配料均匀渗透玻璃纤维，再装填模具型腔与中间的金属型材复合模压成型，其模压温度是140℃，模压压力是75kg/cm2，成型时间是5分钟。所说的抗老化剂是UV-531，阻燃剂是AL(OH)3，脱模剂是硬酯酸锌经经过2次加工研磨粒度小于45微米相当于纳米级的粉末。本发制备容器也显示出更有强的技术优势，经试用，具有耐腐蚀、强度大、寿命长，便于配套安装等优点。
通过上述3个实例，本发明达到了预期的设计目的与原有技术相比，本发明具有显著的技术进步，薄壁中空金属型材增加了强度提高了寿命，添加了抗老化剂阻燃剂提高了抗的性能和使用寿命，中空型材压制成各种标准连接件，腔体插件，便于中空管纵向架、横向架快捷组装。更便于拆装，提高了工作效率。本发明实用美观，设有大小不同规格，安装便捷，可根据空间大小选择不同规格，据测算，使用寿命比单一的钢结构可提高10倍左右。该圃架经试用，效果良好，能够有效的利用阳台空间，占地空间小，便捷组装，经久耐用，美化环境，便于组装，既能够栽培食用蔬菜，又能栽培观赏花卉，可广泛适用于无土栽培种植，特别适合家庭院落、室内阳台、花卉商店、苗木蔬菜展会的便捷组装的栽培蔬菜花卉圃架，达到了预期的设计目的。
Claims (5)
1.一种钢塑复合玻璃钢圃架及制作方法，其特征在于所述一种钢塑复合玻璃钢圃架由中空管纵向架(1)、横向架(2)、可调倾斜角框(3)、腔体插件(11)、圃盘(8)、盆盘托板(18)组成，纵向架(1)、横向架(2)设有变换组装的圃盘(8)、盆盘托板(18)，横向架(2)上部设有营养液罐(9)、液调控器(10)、营养液滴管(12)、转动滴液杆(13)，纵向架(1)中部设有转动轴槽(6)、固定环(5)，可调倾斜角框(3)设有调节环勾(4)，圃盘(8)设有14、圃盘送液管(14)、勾盘沿(15)、盘格栅(16)、槽盘沿(17)，盆盘托板(18)边缘设有防护板架栏(19)，腔体插件(11)拼接中空管纵向架(1)、横向架(2)，可调倾斜角框(3)上端头部与转动轴槽(6)连接，调节环勾(4)与固定环(5)连接，圃盘(8)、盆盘托板(18)与纵向架(1)、横向架(2)连接固定。
2.一种钢塑复合玻璃钢圃架及制作方法，其特征在于所述一种钢塑复合玻璃钢圃架制作方法是，法复合玻璃钢是由薄壁中空异型金属型材，玻璃纤维，不饱和聚酯树脂，经过2次细化处理的抗老化剂、阻燃剂、内脱模剂填充料，经预处理配料、填充、在预热模具内模压成型。
3.根据权利要求2所述的一种钢塑复合玻璃钢圃架制作方法，其特征在于成分按重量比是金属型材20-60％，玻璃纤维10-28％，不饱和聚酯树脂15-25％，抗老化剂UV-531是0.1-0.5％，阻燃剂AL(OH)3是18-50％，内脱模剂硬酯酸锌1-5％。
4.根据权利要求2所述的一种钢塑复合玻璃钢圃架制作方法，其特征在于首先预处理配料是将树脂、抗老化剂、阻燃剂按上述比例搅拌混配，然后在30-40℃的加温室中熟化24-48小时，树脂配料均匀渗透玻璃纤维或玻璃布再装填模具型腔与金属型材模压成型，其成型温度是130-140℃，模压压力是65-75kg/cm2，成型时间是2-10分钟。
5.根据权利要求2所述的一种钢塑复合玻璃钢圃架制作方法，其特征在于所说的抗老化剂UV-531、阻燃剂是AL(OH)3，脱模剂硬酯酸锌经过2次加工研磨粒度是纳米级的粉末。