CN104071998A - 利用工业废渣生产高强度水泥的工艺 - Google Patents

利用工业废渣生产高强度水泥的工艺 Download PDF

Info

Publication number
CN104071998A
CN104071998A CN201410272918.1A CN201410272918A CN104071998A CN 104071998 A CN104071998 A CN 104071998A CN 201410272918 A CN201410272918 A CN 201410272918A CN 104071998 A CN104071998 A CN 104071998A
Authority
CN
China
Prior art keywords
cement
raw materials
flyash
cement clinker
produce
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410272918.1A
Other languages
English (en)
Other versions
CN104071998B (zh
Inventor
刘振海
周和云
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANDONG LIANHE WANGCHAO CEMENT Co Ltd
Original Assignee
SHANDONG LIANHE WANGCHAO CEMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANDONG LIANHE WANGCHAO CEMENT Co Ltd filed Critical SHANDONG LIANHE WANGCHAO CEMENT Co Ltd
Priority to CN201410272918.1A priority Critical patent/CN104071998B/zh
Publication of CN104071998A publication Critical patent/CN104071998A/zh
Application granted granted Critical
Publication of CN104071998B publication Critical patent/CN104071998B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

利用工业废渣生产高强度水泥的工艺，其工艺过程步骤如下：1、生产水泥熟料：按高硅率、高铝氧率和高石灰石饱和率配料方案，用微机选用石灰石、石英砂选矿污泥、铁粉矿选矿污泥、粉煤灰四种原料按照重量百分比例进行配料并控制下料进行生料粉磨、生料均化，然后使生料进入到回转煅烧窑中进行煅烧，进而生产出水泥熟料；2、生产水泥产品：用微机选用粉煤灰、煤矸石、水泥熟料、脱硫石膏、矿粉五种原料按照重量百分比例进行配料并控制下料进行水泥粉磨、水泥均化，进而生产出水泥产品，本发明的优点是：既符合保护环境、降低污染的环保理念，而且具有变废为宝、降低工业废渣处置和生产成本的积极社会效果，生产的水泥质量稳定，强度较高。

Description

利用工业废渣生产高强度水泥的工艺
技术领域
本发明涉及水泥生产技术领域，尤其涉及利用工业废渣生产高强度水泥的工艺。
背景技术
利用工业废渣生产水泥不仅符合保护环境、降低污染的环保理念，而且具有变废为宝、降低工业废渣处置和生产成本的积极社会效果，目前，已有一些水泥企业成功的利用工业废渣生产出水泥，然而，从现有利用工业废渣生产的公开技术中不难看到主要存在以下不足：水泥质量不稳定，强度低，不能满足大型建筑工程使用。
发明内容
本发明的目的是提供利用工业废渣生产高强度水泥的工艺，该工艺既符合保护环境、降低污染的环保理念，而且具有变废为宝、降低工业废渣处置和生产成本的积极社会效果，且该工艺生产的水泥质量稳定，强度较高，能满足大型建筑工程使用。
为实现上述目的，本发明所采用的技术方案为：利用工业废渣生产高强度水泥的工艺，其特点在于：工艺过程步骤如下：1、生产水泥熟料：按高硅率N＝3.20、高铝氧率P＝1.85和高石灰石饱和率KH＝0.90配料方案，用微机选用石灰石、石英砂选矿污泥、铁粉矿选矿污泥、粉煤灰四种原料按照重量百分比例进行配料并控制下料进行生料粉磨、生料均化，然后使生料进入到回转煅烧窑中进行煅烧，进而生产出水泥熟料。2、生产水泥产品：用微机选用粉煤灰、煤矸石、水泥熟料、脱硫石膏、矿粉五种原料按照重量百分比例进行配料并控制下料进行水泥粉磨、水泥均化，进而生产出水泥产品。
根据上述的利用工业废渣生产高强度水泥的工艺，其特点在于：所述的生产水泥熟料中的用微机选用石灰石、石英砂选矿污泥、铁粉矿选矿污泥、粉煤灰四种原料按照重量百分比例为：石灰石为82.66％、石英砂选矿污泥为4.71％、铁粉矿选矿污泥为3.33％、粉煤灰为9.30％。
根据上述的利用工业废渣生产高强度水泥的工艺，其特点在于：所述的生产水泥产品中的用微机选用粉煤灰、煤矸石、水泥熟料、脱硫石膏、矿粉五种原料按照重量百分比例为：粉煤灰为23％、煤矸石为5％、水泥熟料为62％、脱硫石膏5％、矿粉为5％。
本发明的优点是：本发明既符合保护环境、降低污染的环保理念，而且具有变废为宝、降低工业废渣处置和生产成本的积极社会效果，且生产的水泥质量稳定，强度较高，能满足大型建筑工程使用。
具体实施方式
下面结合具体实施例对本发明作进一步描述：
利用工业废渣生产高强度水泥的工艺，其工艺过程步骤如下：1、生产水泥熟料：按高硅率N＝3.20、高铝氧率P＝1.85和高石灰石饱和率KH＝0.90配料方案，用微机选用石灰石、石英砂选矿污泥、铁粉矿选矿污泥、粉煤灰四种原料按照重量百分比例进行配料并控制下料进行生料粉磨、生料均化，然后使生料进入到回转煅烧窑中进行煅烧，进而生产出水泥熟料。2、生产水泥产品：用微机选用粉煤灰、煤矸石、水泥熟料、脱硫石膏、矿粉五种原料按照重量百分比例进行配料并控制下料进行水泥粉磨、水泥均化，进而生产出水泥产品。
在本实施例中：所述的生产水泥熟料中的用微机选用石灰石、石英砂选矿污泥、铁粉矿选矿污泥、粉煤灰四种原料按照重量百分比例为：石灰石为82.66％、石英砂选矿污泥为4.71％、铁粉矿选矿污泥为3.33％、粉煤灰为9.30％。
在本实施例中：所述的生产水泥产品中的用微机选用粉煤灰、煤矸石、水泥熟料、脱硫石膏、矿粉五种原料按照重量百分比例为：粉煤灰为23％、煤矸石为5％、水泥熟料为62％、脱硫石膏5％、矿粉为5％。
本发明有益效果：本发明既符合保护环境、降低污染的环保理念，而且具有变废为宝、降低工业废渣处置和生产成本的积极社会效果，且生产的水泥质量稳定，强度较高，能满足大型建筑工程使用。
上面所述的实施例仅仅是对本发明的优选实施方式进行描述，并非对本发明的构思和保护范围进行限定，在不脱离本发明设计构思的前提下，本领域中普通工程技术人员对本发明的技术方案作出的各种变型和改进，均应落入本发明的保护范围。

Claims (3)

1.利用工业废渣生产高强度水泥的工艺，其特征在于：其工艺过程步骤如下：1、生产水泥熟料：按高硅率N＝3.20、高铝氧率P＝1.85和高石灰石饱和率KH＝0.90配料方案，用微机选用石灰石、石英砂选矿污泥、铁粉矿选矿污泥、粉煤灰四种原料按照重量百分比例进行配料并控制下料进行生料粉磨、生料均化，然后使生料进入到回转煅烧窑中进行煅烧，进而生产出水泥熟料。2、生产水泥产品：用微机选用粉煤灰、煤矸石、水泥熟料、脱硫石膏、矿粉五种原料按照重量百分比例进行配料并控制下料进行水泥粉磨、水泥均化，进而生产出水泥产品。
2.根据权利要求1所述的，其特征在于：所述的生产水泥熟料中的用微机选用石灰石、石英砂选矿污泥、铁粉矿选矿污泥、粉煤灰四种原料按照重量百分比例为：石灰石为82.66％、石英砂选矿污泥为4.71％、铁粉矿选矿污泥为3.33％、粉煤灰为9.30％。
3.根据权利要求1所述的，其特征在于：所述的生产水泥产品中的用微机选用粉煤灰、煤矸石、水泥熟料、脱硫石膏、矿粉五种原料按照重量百分比例为：粉煤灰为23％、煤矸石为5％、水泥熟料为62％、脱硫石膏5％、矿粉为5％。
CN201410272918.1A 2014-06-13 2014-06-13 利用工业废渣生产高强度水泥的工艺 Active CN104071998B (zh)