CN103570262A - 一种高强度水泥 - Google Patents
一种高强度水泥 Download PDFInfo
- Publication number
- CN103570262A CN103570262A CN201310443824.1A CN201310443824A CN103570262A CN 103570262 A CN103570262 A CN 103570262A CN 201310443824 A CN201310443824 A CN 201310443824A CN 103570262 A CN103570262 A CN 103570262A
- Authority
- CN
- China
- Prior art keywords
- strength cement
- furnace
- stove
- fly ash
- fluorgypsum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种高强度水泥,属于建筑领域。包括如下配方:熟料、混合材料、氟石膏和粉煤灰渣的比例为60%:20%:15%:5%,所述的混合材料包括矿渣、煤矸石、粉煤灰,熟石膏,上述材料按配比配好后送入炉中,经过700-800℃炉窑煅烧熟化,送入粉碎机粉碎即得成品。本发明的优点:工艺简单,材料来源广,材料成本低,生产过程中不污染环境。
Description
技术领域:
本发明属于建筑领域,特别涉及一种高强度水泥。
背景技术:
目前的水泥配方中水泥强度不高,无法用于大跨度、高强度建筑。
发明内容:
本发明针对现有技术的不足,提供一种水泥。
包括如下配方:熟料、混合材料、氟石膏和粉煤灰渣的比例为60%:20%:15%:5%,所述的混合材料包括矿渣、煤矸石、粉煤灰,熟石膏,上述材料按配比配好后送入炉中,经过700-800℃炉窑煅烧熟化,送入粉碎机粉碎即得成品。
本发明的优点:工艺简单,材料来源广,材料成本低,生产过程中不污染环境。
具体实施方式:
本发明通过以下实施例进行说明:
本发明针对现有技术的不足,提供一种水泥。
包括如下配方:熟料、混合材料、氟石膏和粉煤灰渣的比例为60%:20%:15%:5%,所述的混合材料包括矿渣、煤矸石、粉煤灰,熟石膏,上述材料按配比配好后送入炉中,经过700-800℃炉窑煅烧熟化,送入粉碎机粉碎即得成品。
Claims (1)
1.一种高强度水泥,其特征在于:包括如下配方:熟料、混合材料、氟石膏和粉煤灰渣的比例为60%:20%:15%:5%,所述的混合材料包括矿渣、煤矸石、粉煤灰,熟石膏,上述材料按配比配好后送入炉中,经过700-800℃炉窑煅烧熟化,送入粉碎机粉碎即得成品。