CN104326686A - 一种硅废石水泥混合材 - Google Patents

一种硅废石水泥混合材 Download PDF

Info

Publication number
CN104326686A
CN104326686A CN201410520857.6A CN201410520857A CN104326686A CN 104326686 A CN104326686 A CN 104326686A CN 201410520857 A CN201410520857 A CN 201410520857A CN 104326686 A CN104326686 A CN 104326686A
Authority
CN
China
Prior art keywords
parts
cement
silicon
tons
waste stone
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410520857.6A
Other languages
English (en)
Inventor
杨万
樊志刚
张永辉
刘丽芬
郑改转
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ORDOS MENGXI BUILDING MATERIALS Co Ltd
Original Assignee
ORDOS MENGXI BUILDING MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ORDOS MENGXI BUILDING MATERIALS Co Ltd filed Critical ORDOS MENGXI BUILDING MATERIALS Co Ltd
Priority to CN201410520857.6A priority Critical patent/CN104326686A/zh
Publication of CN104326686A publication Critical patent/CN104326686A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种硅废石水泥混合材，其特征在于，其包括如下重量份的组分，石灰石2.10份-4.98份，硅废石3.14份-3.24份，粉煤灰24.65份-28.55份，微硅粉1.88份-2份，石膏或脱硫石膏3.78份-4.69份。本发明以硅废石代替炉渣，对水泥性能没有任何有害影响，完全可以直接代替炉渣作为混合材在水泥生产中使用，且利用硅废石生产的水泥3天、28天抗压强度均优于利用炉渣生产的水泥，提高了混凝土耐久性；本发明一方面解决了混合材短缺的问题，增加了水泥混合材的新领域，同时降低了生产成本0.41元/吨；另一方面解决了硅废石对环境污染的问题，有利于环境保护。

Description

一种硅废石水泥混合材
技术领域：
本发明涉及一种水泥混合材，特别涉及一种硅废石水泥混合材。
背景技术：
传统的生产水泥的混合材一般是炉渣、矿渣、石灰石，受现阶段金融危机的影响，周边地区的小型电厂、铁厂纷纷关闭，导致混合材的资源匮乏。
硅石广泛用于无线电工业、超声波技术及现代国防和尖端技术，纯的石英岩具有旋光性和透过紫外线性能，可制造各种光学仪器和医疗用的石英灯等、而这些工业要求使用的硅石纯度较高，故开采硅石时会剥离出大量SiO2含量较低硅石尾矿，其本身是国家例入的废渣，目前无好的处理方法，长期以来被堆弃在硅废石矿附近，占用了大量的土地。
发明内容：
本发明的目的在于提供一种可以解决硅废石占用土地、无需改变任何生产工艺的硅废石水泥混合材。
本发明由如下技术方案实施：一种硅废石水泥混合材，其包括如下重量份的组分：石灰石2.10份-4.98份，硅废石3.14份-3.24份，粉煤灰24.65份-28.55份，微硅粉1.88份-2份，石膏或脱硫石膏3.78份-4.69份。
优选的，所述一种硅废石水泥混合材包括如下重量份的组分，所述石灰石4.98份，所述硅废石3.14份，所述粉煤灰24.65份，所述微硅粉2份，所述石膏4.69份。
优选的，所述一种硅废石水泥混合材包括如下重量份的组分：所述石灰石2.10份，所述硅废石3.24份，所述粉煤灰28.55份，所述微硅粉1.88份，所述脱硫石膏3.78份。
本发明的优点：本发明以硅废石代替炉渣，对水泥性能没有任何有害影响，完全可以直接代替炉渣作为混合材在水泥生产中使用，且利用硅废石生产的水泥3天、28天抗压强度均优于利用炉渣生产的水泥，提高了混凝土耐久性；本发明一方面解决了混合材短缺的问题，增加了水泥混合材的新领域，同时降低了生产成本0.41元/吨；另一方面解决了硅废石对环境污染的问题，有利于环境保护。
具体实施方式：
实施例1：
一种硅废石水泥混合材，其包括如下重量的组分：石灰石4.98吨，硅废石3.14吨，粉煤灰24.65吨，微硅粉2吨，石膏4.69吨。
实施例2：
一种硅废石水泥的混合材，其包括如下重量的组分，石灰石2.10吨，硅废石3.24吨，粉煤灰28.55吨，微硅粉1.88吨，脱硫石膏3.78吨。
实施例3：
一种硅废石水泥的混合材，其包括如下重量的组分，石灰石3.03吨，硅废石3.19吨，粉煤灰26.02吨，微硅粉1.91吨，脱硫石膏4.17吨。
实施例4：
1号水泥为现有熟料与现有混合材混合磨制的水泥，其包括如下重量的组分，熟料60.69吨，石灰石5.00吨，炉渣3.13吨，粉煤灰24.92吨，微硅粉2.05吨，石膏3.13吨；
2号水泥为现有熟料与本发明混合材混合磨制的水泥，其包括如下重量的组分，熟料60.49吨，石灰石4.98吨，硅废石3.14吨，粉煤灰24.65吨，微硅粉2吨，石膏4.69吨；
3号水泥为现有熟料与本发明混合材混合磨制的水泥，其包括如下重量的组分，熟料60.45吨，石灰石2.10吨，硅废石3.24吨，粉煤灰28.55吨，微硅粉1.88吨，脱硫石膏3.78吨；
4号水泥为现有熟料与本发明混合材混合磨制的水泥，其包括如下重量的组分，熟料60.49吨，石灰石3.03吨，硅废石3.19吨，粉煤灰26.02吨，微硅粉1.91吨，脱硫石膏4.17吨；
其中，上述现有熟料均为蒙西生产经营中心通用硅酸盐水泥熟料，上述硅废石化学成分分析如表1所示；对上述水泥进行物检及化学分析，结果如表2所示。
表1硅废石化学成分分析
SiO2(％) Fe2O3(％) Ai2O3(％) CaO(％) MgO(％) LOSS(％)
73.74 1.45 3.19 10.63 1.1 9.89
表2为1号水泥、2号水泥、3号水泥和4号水泥大磨试验的物检和化学分析结果统计：
通用硅酸盐水泥国家指标：抗折强度：3d≥2.5MPa，28d≥5.5MPa；抗压强度：3d≥10MPa，28d≥32.5MPa；MgO≤6.0％；CI-≤0.06％；SO3≤3.5％。
由表2可知，1号水泥、2号水泥、3号水泥和4号水泥的抗压强度、抗折强度、MgO、CI-、SO3均符合通用硅酸盐水泥国家指标；且添加本发明混合材混合磨制的2号水泥、3号水泥和4号水泥与1号水泥相比，其3天抗压强度和28天抗压强度均有所提高。

Claims (3)

1.一种硅废石水泥混合材，其特征在于，其包括如下重量份的组分：石灰石2.10份-4.98份，硅废石3.14份-3.24份，粉煤灰24.65份-28.55份，微硅粉1.88份-2份，石膏或脱硫石膏3.78份-4.69份。
2.根据权利要求1所述一种硅废石水泥混合材，其特征在于，其包括如下重量份的组分：所述石灰石4.98份，所述硅废石3.14份，所述粉煤灰24.65份，所述微硅粉2份，所述石膏4.69份。
3.根据权利要求1所述一种硅废石水泥混合材，其特征在于，其包括如下重量份的组分：所述石灰石2.10份，所述硅废石3.24份，所述粉煤灰28.55份，所述微硅粉1.88份，所述脱硫石膏3.78份。
CN201410520857.6A 2014-09-30 2014-09-30 一种硅废石水泥混合材 Pending CN104326686A (zh)